Plasma-MIG {metal inert gas arc welding） hybrid welding of aluminum alloy with 6 mm thickness using ER5356 welding wire was carried out. The microstructures and mechanical properties of the welded joint were inve...Plasma-MIG {metal inert gas arc welding） hybrid welding of aluminum alloy with 6 mm thickness using ER5356 welding wire was carried out. The microstructures and mechanical properties of the welded joint were investigated by optical microscopy, X-ray diffraction （XRD） , energy dispersive spectroscopy （EDS） , tensile test, hardness test and scanning electron microscope （ SEM） were used to judge the type of tensile fracture. The results showed that the tensile strength of welded joint was 142 MPa which was 53. 6% o f the strength o f the base metal. The welding seam zone was characterized by dendritic structure. In the fusion zone, the columnar grains existed at one side of the welding seam. The fibrous organization was found in the base metal, and also in the heat affected zone （HAZ） where the recrystallization occurred. The HAZ was the weakest position of the welded joint due to the coarsening of Mg2Si phase. The type of tensile fracture was ductile fracture.展开更多
The synchronous acquisition system of droplet image inspection and arc electric signals were established and the droplet transition characteristics of aluminum alloys were researched in the plasma-MIG welding process....The synchronous acquisition system of droplet image inspection and arc electric signals were established and the droplet transition characteristics of aluminum alloys were researched in the plasma-MIG welding process.Typical droplet transition modes include globular transfer mode,short circuiting transfer mode,metastable spray transfer mode and projected transfer mode.The result indicates that MIG droplet transfer frequency and droplet transfer modes are changed by introducing the plasma arc in the plasma-MIG welding process compared with the MIG welding on the aluminum alloys,which broadens the range of welding parameters when the stable welding process proceeds.The metastable spray transfer and projected transfer mode are proved to be the most optimal modes by comparing the stability of electronic signal,droplet transition,weld appearance and weld penetration.展开更多
A three-dimensional simulation model for the plasma-MIG welding process, which takes the interaction between the plasma arc and MIG arc into account, is presented and the quasi-steady temperature fields on the workpie...A three-dimensional simulation model for the plasma-MIG welding process, which takes the interaction between the plasma arc and MIG arc into account, is presented and the quasi-steady temperature fields on the workpiece are calculated with the model. The 10 mm-5A06 aluminum alloy is welded and the temperature fields are measured with the thermoelectric couple. The simulation results and measured results show that the biggest deviation of peak temperature between them is below 20 ℃, which indicates good coincidence between the simulation and measurement.展开更多
The influence of heating cycles during plasma metal inert gas (MIG) welding on the microstructure and corrosion properties of the AA5754 automotive alloy has been investigated. The high heat input during plasma-MIG we...The influence of heating cycles during plasma metal inert gas (MIG) welding on the microstructure and corrosion properties of the AA5754 automotive alloy has been investigated. The high heat input during plasma-MIG welding results in a significant modification in the microstructure of the AA5754 alloy adjacent to the fusion boundaries. As a consequence of partial melting of the Al-Fe-Mn-(Si) intermetallics at the partially melted zone (PMZ) and segregation of the high melting point elements (particularly Fe and Mn) toward the fusion zone, severe galvanic corrosion attacks can be enhanced along the PMZ of the AA5754 weld during exposure to aqueous corrosion environments.展开更多
基金Key Laboratory of Advanced Welding Technology of Jiangsu University of Science and Technology (Grant NO. JSAWT-11-02) for its financial support
文摘Plasma-MIG {metal inert gas arc welding） hybrid welding of aluminum alloy with 6 mm thickness using ER5356 welding wire was carried out. The microstructures and mechanical properties of the welded joint were investigated by optical microscopy, X-ray diffraction （XRD） , energy dispersive spectroscopy （EDS） , tensile test, hardness test and scanning electron microscope （ SEM） were used to judge the type of tensile fracture. The results showed that the tensile strength of welded joint was 142 MPa which was 53. 6% o f the strength o f the base metal. The welding seam zone was characterized by dendritic structure. In the fusion zone, the columnar grains existed at one side of the welding seam. The fibrous organization was found in the base metal, and also in the heat affected zone （HAZ） where the recrystallization occurred. The HAZ was the weakest position of the welded joint due to the coarsening of Mg2Si phase. The type of tensile fracture was ductile fracture.
文摘The synchronous acquisition system of droplet image inspection and arc electric signals were established and the droplet transition characteristics of aluminum alloys were researched in the plasma-MIG welding process.Typical droplet transition modes include globular transfer mode,short circuiting transfer mode,metastable spray transfer mode and projected transfer mode.The result indicates that MIG droplet transfer frequency and droplet transfer modes are changed by introducing the plasma arc in the plasma-MIG welding process compared with the MIG welding on the aluminum alloys,which broadens the range of welding parameters when the stable welding process proceeds.The metastable spray transfer and projected transfer mode are proved to be the most optimal modes by comparing the stability of electronic signal,droplet transition,weld appearance and weld penetration.
文摘A three-dimensional simulation model for the plasma-MIG welding process, which takes the interaction between the plasma arc and MIG arc into account, is presented and the quasi-steady temperature fields on the workpiece are calculated with the model. The 10 mm-5A06 aluminum alloy is welded and the temperature fields are measured with the thermoelectric couple. The simulation results and measured results show that the biggest deviation of peak temperature between them is below 20 ℃, which indicates good coincidence between the simulation and measurement.
文摘The influence of heating cycles during plasma metal inert gas (MIG) welding on the microstructure and corrosion properties of the AA5754 automotive alloy has been investigated. The high heat input during plasma-MIG welding results in a significant modification in the microstructure of the AA5754 alloy adjacent to the fusion boundaries. As a consequence of partial melting of the Al-Fe-Mn-(Si) intermetallics at the partially melted zone (PMZ) and segregation of the high melting point elements (particularly Fe and Mn) toward the fusion zone, severe galvanic corrosion attacks can be enhanced along the PMZ of the AA5754 weld during exposure to aqueous corrosion environments.