Ti-6A1-4V (TC4) alloys were plasma carbonized at different temperatures (900, 950, and 1 000 ℃) for duration of 3 h. Graphite rod was employed as carbon supplier to avoid the hydrogen brittleness which is ubiquit...Ti-6A1-4V (TC4) alloys were plasma carbonized at different temperatures (900, 950, and 1 000 ℃) for duration of 3 h. Graphite rod was employed as carbon supplier to avoid the hydrogen brittleness which is ubiquitous in traditional gas carbonizing process. Two distinguished structures including a thin compound layer (carbides layer) and a thick layer with the mixed microstructure of TiC and the a-Ti in carburing layer were formed during carburizing. Furthermore, it was found that the microstructure and the properties of TC4 alloy were significantly related to the carbonizing temperature. The specimen plasma carbonized at 950 ~2 obtained maximum value both in the hardness and wear resistance.展开更多
This paper deals with the cause of intergranular fracture occurred in the retained austenitic region in plasma carburized layer.The results show that the presence of retained austenite, which has a good effect on the ...This paper deals with the cause of intergranular fracture occurred in the retained austenitic region in plasma carburized layer.The results show that the presence of retained austenite, which has a good effect on the impact toughness,has no relation to this embrittlement.Analy- sis by Auger electron spectroscopy shows that the impurities S and P segregate at the grain boundaries is the main reason of the intergranular embrittlement in carburized layer. However,the segregation of P and S can be removed by reheating and quenching treatment.展开更多
Novel hybrid coatings on pure magnesium were prepared by combining plasma electrolytic carburizing(PEC)with micro-arc oxidation(MAO)to further enhance the anti-corrosion property in this paper.Scanning electron micros...Novel hybrid coatings on pure magnesium were prepared by combining plasma electrolytic carburizing(PEC)with micro-arc oxidation(MAO)to further enhance the anti-corrosion property in this paper.Scanning electron microscopy(SEM)was used to observe the microstructure of the coatings,meanwhile,energy dispersive spectrometry(EDS)and X-ray diffraction(XRD)were separately used to investigate the elemental as well as phase compositions of the coatings.The anti-corrosion property of the coatings was evaluated by potentiodynamic polarization curves as well as electrochemical impedance spectroscopy(EIS).The results show that PEC process is closely related with the effects of adsorption as well as diffusion of the activated carbon atoms,and it can provide a favorable pretreatment surface with predesigned chemical composition to obtain a new kind of phase,namely Si C with superior corrosion resistance and chemical stability,in the following PEC+MAO hybrid coatings.Meanwhile,PEC preprocessing also can afford an excellent micro-structure to increase the coating thickness as well as to improve the compactness of the PEC+MAO hybrid coatings.During the fabrication process of the PEC+MAO hybrid coatings,an overlapping phenomenon in regard to coating thickness can be observed instead of heaping up layer by layer.Compared with both single PEC surface modification layers as well as single MAO coatings,the PEC+MAO hybrid coatings exhibit more superior anti-corrosion property.Especially,the EIS data reveal that the PEC+MAO hybrid coatings can act as an effective protection system to provide relatively excellent long-range anti-corrosion protection.Note also that employing same MAO technique for both single MAO treatment as well as PEC+MAO combining procedure is the key to this research.展开更多
基金Funded in part by National Natural Science Foundation of China(No.51301023)the Fundamental Research Funds for the Central Universities,Chang'an University(No.CHD2011JC126,2013G1311054 and 310831151079)
文摘Ti-6A1-4V (TC4) alloys were plasma carbonized at different temperatures (900, 950, and 1 000 ℃) for duration of 3 h. Graphite rod was employed as carbon supplier to avoid the hydrogen brittleness which is ubiquitous in traditional gas carbonizing process. Two distinguished structures including a thin compound layer (carbides layer) and a thick layer with the mixed microstructure of TiC and the a-Ti in carburing layer were formed during carburizing. Furthermore, it was found that the microstructure and the properties of TC4 alloy were significantly related to the carbonizing temperature. The specimen plasma carbonized at 950 ~2 obtained maximum value both in the hardness and wear resistance.
文摘This paper deals with the cause of intergranular fracture occurred in the retained austenitic region in plasma carburized layer.The results show that the presence of retained austenite, which has a good effect on the impact toughness,has no relation to this embrittlement.Analy- sis by Auger electron spectroscopy shows that the impurities S and P segregate at the grain boundaries is the main reason of the intergranular embrittlement in carburized layer. However,the segregation of P and S can be removed by reheating and quenching treatment.
基金financially supported by the Creative Research Group Fund Grant of Gansu Province,China(1111RJDA011)。
文摘Novel hybrid coatings on pure magnesium were prepared by combining plasma electrolytic carburizing(PEC)with micro-arc oxidation(MAO)to further enhance the anti-corrosion property in this paper.Scanning electron microscopy(SEM)was used to observe the microstructure of the coatings,meanwhile,energy dispersive spectrometry(EDS)and X-ray diffraction(XRD)were separately used to investigate the elemental as well as phase compositions of the coatings.The anti-corrosion property of the coatings was evaluated by potentiodynamic polarization curves as well as electrochemical impedance spectroscopy(EIS).The results show that PEC process is closely related with the effects of adsorption as well as diffusion of the activated carbon atoms,and it can provide a favorable pretreatment surface with predesigned chemical composition to obtain a new kind of phase,namely Si C with superior corrosion resistance and chemical stability,in the following PEC+MAO hybrid coatings.Meanwhile,PEC preprocessing also can afford an excellent micro-structure to increase the coating thickness as well as to improve the compactness of the PEC+MAO hybrid coatings.During the fabrication process of the PEC+MAO hybrid coatings,an overlapping phenomenon in regard to coating thickness can be observed instead of heaping up layer by layer.Compared with both single PEC surface modification layers as well as single MAO coatings,the PEC+MAO hybrid coatings exhibit more superior anti-corrosion property.Especially,the EIS data reveal that the PEC+MAO hybrid coatings can act as an effective protection system to provide relatively excellent long-range anti-corrosion protection.Note also that employing same MAO technique for both single MAO treatment as well as PEC+MAO combining procedure is the key to this research.