This paper reports that amorphous silicon nitride （a-SiNx） overcoats were deposited at room temperature by microwave ECR plasma enhanced unbalanced magnetron sputtering. The 2 nm a-SiNs overcoat has better anti-corr...This paper reports that amorphous silicon nitride （a-SiNx） overcoats were deposited at room temperature by microwave ECR plasma enhanced unbalanced magnetron sputtering. The 2 nm a-SiNs overcoat has better anti-corrosion properties than that of reference a-CNx overcoats （2 4.5 nm）. The superior anti-corrosion performance is attributed to its stoichiometric bond structure, where 94.8% Si atoms form Si-N asymmetric stretching vibration bonds. The N/Si ratio is 1.33 as in the stoichiometry of Si3N4 and corresponds to the highest hardness of 25.0 GPa. The surface is atomically smooth with RMS 〈 0.2 nm. The ultra-thin a-SiNx overcoats are promising for hard disks and read/write heads protective coatings.展开更多
基金Project supported by the Major Program of the National Natural Science Foundation of China (Grant No 50390060)the National Natural Science Foundation of China (Grant Nos 60576022 and 50572012)
文摘This paper reports that amorphous silicon nitride （a-SiNx） overcoats were deposited at room temperature by microwave ECR plasma enhanced unbalanced magnetron sputtering. The 2 nm a-SiNs overcoat has better anti-corrosion properties than that of reference a-CNx overcoats （2 4.5 nm）. The superior anti-corrosion performance is attributed to its stoichiometric bond structure, where 94.8% Si atoms form Si-N asymmetric stretching vibration bonds. The N/Si ratio is 1.33 as in the stoichiometry of Si3N4 and corresponds to the highest hardness of 25.0 GPa. The surface is atomically smooth with RMS 〈 0.2 nm. The ultra-thin a-SiNx overcoats are promising for hard disks and read/write heads protective coatings.