The hot compressive deformation behavior of cast Mg-Gd-Y-Zn-Zr alloys with and without LPSO phase in their initial microstructures

Samples of Mg-8.2Gd-3.8Y-1.1Zn-0.4Zr alloy with and without an intragranular lamellae-shaped long period stacking ordered(LPSO)phase were prepared through heat treatment and a series of hot compression tests on these materials were conducted to examine and evaluate the influence of LPSO on the hot compressive deformation behavior and deformation mechanisms at a given alloy composition.The values of activation energy for plastic flow(Qc)of the solution treated(without LPSO phase)and annealed alloys(with intragranular LPSO phase)were larger than that for pure Mg,indicating that the presence of a high amount of rare earth(RE)elements and LPSO in the Mg matrix significantly increases Qc.The Qcvalue of the annealed alloy was larger than that of the solution treated alloy at all the strain levels(223.3 vs.195.5 k J/mol in average)and the largest difference in Qcbetween the two alloys was recorded at the smallest strain of 0.1 where precipitation of LPSO during deformation was limited in the solution treated alloy.These observations imply that the formation of LPSO phase out of the RE-rich solid solution matrix during deformation increases Qc,but the increment is not so large.Analysis of the hot compressive data of the alloys with LPSO phase and the alloys with RE-rich solid solution matrix in literatures indicates the similarity of the effect of the LPSO and RE-rich solid solution matrix phases on Qcand high-temperature strength.

Deformation behavior of Fe-Mn-C TWIP steel within the temperature range of hot rolling

The hot-deformation behavior of Fe-Mn-C twinning induced plasticity （TWIP） steel was investigated by conducting hot compression tests within a recommended hot rolling temperature range at various strain rates. Flow resistance curves during hot-deformation were obtained, and strain rate sensitivities and activation energies for plastic deformation were calculated using the power law. It is found that the addition of Al and Si clearly increases the peak stresses for the present alloys, especially at 950℃. But Mn has a minor effect on the stress-strain curves and activation energy when its content varies from 15 mass% to 22 mass% for the present alloys.