To functionalize poly（vinyl chloride）（PVC） for various applications, monomers containing tertiary amine group are incorporated into PVC via atom transfer radical polymerization（ATRP） initiated by the labile chlo...To functionalize poly（vinyl chloride）（PVC） for various applications, monomers containing tertiary amine group are incorporated into PVC via atom transfer radical polymerization（ATRP） initiated by the labile chlorines in their backbones. The kinetics of synthesis was carefully investigated, and it is proven that the grafting polymerization process can be effectively controlled by regulating the reaction time. The membranes are fabricated using PVC and copolymers by non-solvent induced phase separation（NIPS） process. The hydrophilicity and pore structure of copolymer membranes were enhanced as well, these membranes are endowed with positive charge. When PDMA%（i.e., the PDMA weight percentage in copolymer） is 31.1%, the flux and Victoria blue B rejection are 26.0 L·m·^-2·h^-1（0.5 MPa） and 91.2%, respectively. Thus, the newly synthesized polymer is proven to be a promising material for dye separation with positive charges.展开更多
Poly(N,N-dimethylaminoethyl methacrylate) (polyDMAEMA) hydrogels prepared by gamma-irradiation showed obvious temperature-sensitivity in a temperature range of 38-40degreesC and pH-sensitivity at pH=2.5. They also sho...Poly(N,N-dimethylaminoethyl methacrylate) (polyDMAEMA) hydrogels prepared by gamma-irradiation showed obvious temperature-sensitivity in a temperature range of 38-40degreesC and pH-sensitivity at pH=2.5. They also showed electric response behavior although it was not typical. The hydrogels were used in controlled release at different pH, temperature, and electric voltage. The release rates of methylene blue (MB) from the gels at 52degreesC and pH=1.24 were faster than those at 20degreesC and pH=10.56, respectively. In addition, the release rate at a field voltage of 5.0 was also faster than that without electric field.展开更多
基金financially supported by the National 863 Program(No.2012AA03A602)National 973 Program(No.2009CB623402)the National Natural Science Foundation of China(No.U1134002)
文摘To functionalize poly（vinyl chloride）（PVC） for various applications, monomers containing tertiary amine group are incorporated into PVC via atom transfer radical polymerization（ATRP） initiated by the labile chlorines in their backbones. The kinetics of synthesis was carefully investigated, and it is proven that the grafting polymerization process can be effectively controlled by regulating the reaction time. The membranes are fabricated using PVC and copolymers by non-solvent induced phase separation（NIPS） process. The hydrophilicity and pore structure of copolymer membranes were enhanced as well, these membranes are endowed with positive charge. When PDMA%（i.e., the PDMA weight percentage in copolymer） is 31.1%, the flux and Victoria blue B rejection are 26.0 L·m·^-2·h^-1（0.5 MPa） and 91.2%, respectively. Thus, the newly synthesized polymer is proven to be a promising material for dye separation with positive charges.
基金This work was financially supported by the National Natural Science Foundation of China (No. 39870227) this paper was reported on International Symposium on Radiation Technology in Emerging Industry Application, held on Nov. 6-10, 2001 in Beijing, China
文摘Poly(N,N-dimethylaminoethyl methacrylate) (polyDMAEMA) hydrogels prepared by gamma-irradiation showed obvious temperature-sensitivity in a temperature range of 38-40degreesC and pH-sensitivity at pH=2.5. They also showed electric response behavior although it was not typical. The hydrogels were used in controlled release at different pH, temperature, and electric voltage. The release rates of methylene blue (MB) from the gels at 52degreesC and pH=1.24 were faster than those at 20degreesC and pH=10.56, respectively. In addition, the release rate at a field voltage of 5.0 was also faster than that without electric field.