A new amphoteric membrane was prepared by blending long-side-chain sulfonated poly(2,6-dimethyl-1,4-phenylene oxide)(S-L-PPO)and polybenzimidazole(PBI)for vanadium redox flow battery(VRFB)application.An acid-base pair...A new amphoteric membrane was prepared by blending long-side-chain sulfonated poly(2,6-dimethyl-1,4-phenylene oxide)(S-L-PPO)and polybenzimidazole(PBI)for vanadium redox flow battery(VRFB)application.An acid-base pair structure formed between the imidazole of PBI and sulfonic acid of S-L-PPO resulted in lowered swelling ratio.It favors to reduce the vanadium permeation.While,the increased sulfonic acid concentration ensured that proton conductivity was still at a high level.As a result,a better balance between the vanadium ion permeation(6.1×10^-9 cm^2·s^-1)and proton conductivity(50.8 m S·cm^-1)in the S-L-PPO/PBI-10%membrane was achieved.The VRFB performance with S-L-PPO/PBI-10%membrane exhibited an EE of 82.7%,which was higher than those of pristine S-L-PPO(81.8%)and Nafion 212(78.0%)at 120 m A·cm^-2.In addition,the S-LPPO/PBI-10%membrane had a much longer self-discharge duration time(142 h)than that of Nafion 212(23 h).展开更多
Experiments including C-13 spin-lattice relaxation, C-13 heteronuclear dipolar dephasing and H-1 spin diffusion are performed on poly (2,6-dimethyl-1,4-phenylene oxide) (PPO). The results show that the rotation of the...Experiments including C-13 spin-lattice relaxation, C-13 heteronuclear dipolar dephasing and H-1 spin diffusion are performed on poly (2,6-dimethyl-1,4-phenylene oxide) (PPO). The results show that the rotation of the methyl groups in solid PPO is partially restricted, which results in a surprisingly efficient spin diffusion between the aromatic proton and methyl proton characterized by a diffusion time of 150 mu s. The results also show that the aromatic ring in solid PPO is rigid and twisted, which causes all aromatic carbons to be chemically unequivalent.展开更多
Ion exchange membranes(IEMs) play a significant role in fields of energy and environment, for instance fuel cells, diffusion dialysis, electrodialysis, etc. The limited choice of commercially available IEMs has produc...Ion exchange membranes(IEMs) play a significant role in fields of energy and environment, for instance fuel cells, diffusion dialysis, electrodialysis, etc. The limited choice of commercially available IEMs has produced a strong demand of fabricating IEMs with improved properties via facile synthetic strategies over the past two decades. Poly(phenylene oxide)(PPO) is considered as a promising polymeric material for constructing practical IEMs, due to its advantages of good physicochemical properties, low manufacturing cost and easy post functionalization. In this review, we present the accumulated efforts in synthetic strategies towards diverse types of PPO-based IEMs. Relation between polymer structures and the resulted features is discussed in detail. Besides, applying IEMs from PPO and its derivatives in fuel cell, diffusion dialysis and electrodialysis is summarized and commented.展开更多
基金supported by the National Natural Science Foundation of China(U1808209)Fundamental Research Funds for the Central Universities(DUT18JC40)Liaoning Province Science and Technology Department(201601037)。
文摘A new amphoteric membrane was prepared by blending long-side-chain sulfonated poly(2,6-dimethyl-1,4-phenylene oxide)(S-L-PPO)and polybenzimidazole(PBI)for vanadium redox flow battery(VRFB)application.An acid-base pair structure formed between the imidazole of PBI and sulfonic acid of S-L-PPO resulted in lowered swelling ratio.It favors to reduce the vanadium permeation.While,the increased sulfonic acid concentration ensured that proton conductivity was still at a high level.As a result,a better balance between the vanadium ion permeation(6.1×10^-9 cm^2·s^-1)and proton conductivity(50.8 m S·cm^-1)in the S-L-PPO/PBI-10%membrane was achieved.The VRFB performance with S-L-PPO/PBI-10%membrane exhibited an EE of 82.7%,which was higher than those of pristine S-L-PPO(81.8%)and Nafion 212(78.0%)at 120 m A·cm^-2.In addition,the S-LPPO/PBI-10%membrane had a much longer self-discharge duration time(142 h)than that of Nafion 212(23 h).
文摘Experiments including C-13 spin-lattice relaxation, C-13 heteronuclear dipolar dephasing and H-1 spin diffusion are performed on poly (2,6-dimethyl-1,4-phenylene oxide) (PPO). The results show that the rotation of the methyl groups in solid PPO is partially restricted, which results in a surprisingly efficient spin diffusion between the aromatic proton and methyl proton characterized by a diffusion time of 150 mu s. The results also show that the aromatic ring in solid PPO is rigid and twisted, which causes all aromatic carbons to be chemically unequivalent.
基金supported by the National Natural Science Foundation of China (21506201, 21720102003, 91534203)the Key Technologies R&D Program of Anhui Province (17030901079)+1 种基金K. C. Wong Education Foundation (2016-11)International Partnership Program of Chinese Academy of Sciences (21134ky5b20170010)
文摘Ion exchange membranes(IEMs) play a significant role in fields of energy and environment, for instance fuel cells, diffusion dialysis, electrodialysis, etc. The limited choice of commercially available IEMs has produced a strong demand of fabricating IEMs with improved properties via facile synthetic strategies over the past two decades. Poly(phenylene oxide)(PPO) is considered as a promising polymeric material for constructing practical IEMs, due to its advantages of good physicochemical properties, low manufacturing cost and easy post functionalization. In this review, we present the accumulated efforts in synthetic strategies towards diverse types of PPO-based IEMs. Relation between polymer structures and the resulted features is discussed in detail. Besides, applying IEMs from PPO and its derivatives in fuel cell, diffusion dialysis and electrodialysis is summarized and commented.