Synthesis and characterization of novel poly(aryl ether sulfone ketone)s containing phthalazinone and biphenyl moieties

A novel series of poly（aryl ether sulfone ketone）s （PPESKs） containing phthalazinone and biphenyl moieties were prepared by two-step nucleophilic polycondensation reaction. The ^-Mw values of these copolymers were between 38,330 and 67,900. The glass transition temperatures （Tg） and 5% decomposition temperatures were ranged in 253-269 ℃ and 488-500 ℃, respectively, The structures of these copolymers were confirmed by FT-IR and ^1H NMR. Moreover, all the resultant copolymers were amorphous determined by wide angle X-ray diffraction （WAXD）.

Allyl-containing Poly(aryl ether sulfone): Synthesis and Crosslinking

A novel type of crosslinkable poly（aryl ether sulfone）（PAES） bearing an allyl pendant（PES-OAllyl） was synthesized by a grafting reaction of hydrophenyl-containing PAES（PES-OH） and allyl bromide. PES-OH was prepared by a demethylation reaction of a methoxyphenylated PAES（PES-OCH3） in the presence of pyridine/hydrochlo- ride. The PES-OCH3 was synthesized by an aromatic nucleophilic substitution of bis（4-chlorophenyl）sulfone and （p-methoxy）phenylhydroquinone. Both DSC and solubility investigation were used to study the crosslinking behavior of PES-OAllyl. After heat treatment, the glass transition temperature（Tg） value of PES-OAllyl sharply increased from 165 ℃ to 227 ℃. Meanwhile, PES-OAllyl changed from a soluble polymer to an insoluble thermoset. In addition, TGA（thermogravimetric analysis） result suggests that the thermal stability of the crosslinked product was improved. All the data prove that the crosslinked PES-OAllyl could be a potential solvent-resistance high-performance material.

Synthesis and properties of soluble poly（aryl ether sulfone ether ketone）s copolymers containing pendant methyl groups

A series of Poly（arly ether sulfone ether ketone）s containing pendant methyl groups were synthesized by the reaction of 4,4＇-[sulfonylbis （1,4-phenylene）dioxy] dibenzoyl chloride （SODBC） with 4,4＇- diphenoxy diphenylsulfone （DPODPS）, 4,4＇- di（2-methylphenoxy） diphenylsulfone （o-Me-DPODPS）, 4,4＇- di（3-methylphenoxy） diphenylsulfone （m-Me-DPODPS）, 4,4＇- di （2,6-bimethylphenoxy） biphenylsulfone（o-Me2-DPODPS） respectively, in a mixture of 1,2-dichloroethane （DCE） and N-methylpyrrolidone （NMP）. These reactions were catalyzed by anhydrous aluminum chloride （AlCl）. The characteristic of copolymers were studied by means of advanced analytical techniques such as FT-IR,1H-NMR, DSC, TGA and WAXD. The results show glass transition temperature （Tg） in the range of 193-206℃, thermally stable in excess of 434℃ and excellent solubility in polar solvents. Methyl-substituted Poly（aryl ether sulfone ketone）s had higher glass transition temperatures, lower initial decomposition temperatures than the unsubstituted ones.

SYNTHESIS AND CHARACTERIZATION OF PHTHALAZINONE POLY(ARYL ETHER SULFONE KETONE)WITH CARBONYL GROUP

A kind of novel heat-resistant, high performance engineering thermoplastic phthalazinone poly(aryl ether sulfone ketone) (PPESK) containing a carboxyl group in its side chain was prepared by the nucleophilic displacement reaction of 4-(4-hydroxylphenyl)- 1 (2H)-phthalazinone with di(4-chlorophenyl) sulfone, 4,4'-difluoro-benzophenone and phenolphthalin in sulfolane in the presence of K2CO3 to produce high molecular weight polymers which can be dissolved in some polar solvents such as chloroform and nitrobenzene at room temperature and can be easily cast into flexible, yellowish and transparent films. PPESK is an amorphous polymer having a decomposition temperature above 400degreesC, which indicates that it has high thermal stability. At the same time, the thermal properties of PPESKs with dicyandiamide (DICY) as curing agent indicated that the heat-resistance properties of the PPESKs are improved after curing. The apparent activation energy (A-E) of the cross-linking reaction and the reaction order (n) of PPESK/DICY were found to be 52.2 kJ/mol and ca. 1.0, respectively. Therefore, the cross-linking reaction is approximately a first order reaction.

Synthesis and characterization of new soluble poly(aryl ether nitrile)s containing phthalazinone moiety

A series of novel poly（aryl ether nitrile）s containing phthalazinone moiety were synthesized by the nucleophilic displacement reaction of bisphenol-like monomers （I） with 2,6-difluorobenzonitrile. The inherent viscosities ranged from 0.46 to 1.07 dL g^-1. The glass transition temperatures were in the range of 277-295℃, and the temperatures for 10% weight loss in nitrogen atmosphere were found between 495 and 527 ℃. The structures of these resultant polymers were confirmed by FT-IR and 1^H NMR. Moreover, the properties of poly（aryl ether nitrile）s including solubility and crystallinity were also studied.

Synthesis and characterization of quaternized poly(phthalazinone ether sulfone ketone)for anion-exchange membrane

Chloromethylated poly（phthalazinone ether sulfone ketone） （CMPPESK） was prepared from poly（phthalazinone ether sulfone ketone） （PPESK） using chloromethyl octyl ethers （CMOE） with lower toxicity as chloromethylated regent. CMPPESK was soluble in N-methyl-2-pyrrolidone （NMP）, N,N-dimethylacetamide （DMAc） and chloroform. Quaternized poly（phthalazinone ether sulfone ketone） （QAPPESK） was prepared from CMPPESK by quaternization. QAPPESK had excellent solvent resistance, which was only partly soluble in sulfuric acid （98%） and swollen in N,N-dimethylformamide （DMF）. The vanadium redox flow battery （V-RFB） using QAPPESK anion-exchange membrane had better performance with 88.3% of overall energy efficiency.

Synthesis of Novel Poly(aryl ether amide)s Containing the Phthalazinone Moiety

Two novel heterocyclic diamine monomers: 1,2-dihydro-2-(4-aminophenyl)-4-[4-(4-aminophenoxy)phenyl] (2H)phthalazin-1-one and 1,2-dihydro-2-(4-aminophenyl)-4-[4-(4-aminophenoxy)-3,5-dimethylphenyl](2H)phthalazin-1-one were successfully synthesized from readily available heterocyclic bisphenol-like monomers in two steps in high yield. A series of novel poly(aryl ether amide)s containing the phthalazinone moiety were successfully prepared by the direct polymerization of the novel diamines and aromatic dicarboxylic acids using triphenyl phosphite and pyridine as condensing agents.

Synthesis and Thermal Crosslinking Behavior of Poly(aryl ether ketone)s Containing 1,4-Naphthalene Moieties

A new monomer, 1,4-bis(4-fluorobenzoyl) naphthalene(compound 2) was synthesized via a two-step reaction. 1,4-Naphthalenedicarboxylic acid chloride(compound 1) was prepared by using the acyl chlorization reaction of 1,4-naphthalenedicarboxylic acid with thionyl chloride. The Friedel-Crafts acylation of compound 1 with fluorobenzene afforded compound 2 in a 80% yield. The polycondensation of compound 2 with various bisphenols in tetramethylene sulfone(TMS) in the presence of excess potassium carbonate as a condensation reagent was carried out at 210 ℃ to quantitatively afford the corresponding poly(aryl ether ketone)s(compounds 3_8) containing 1,4-naphthalene moieties. Thermal analyses showed that the polymers have T g values ranging from 496 to 500 K and are thermally stable in air with initial mass loss above 500 ℃. These novel polymers exhibited an excellent solubility in organic solvents including NMP, DMAc, and chloroform, etc. In addition, the glass transition temperatures of these polymers increased and the polymers became insoluble in chloroform after treated at 260 ℃, indicating the occurrence of a thermal crosslinking reaction.

Proton-exchange Sulfonated Poly（ether ether ketone）/Sulfonated Phenolphthalein Poly（ether sulfone） Blend Membranes in DMFCs

A sulfonated poly（ether ether ketone） （SPEEK） membrane with fairly high degree of sulfonation （DS） swells excessively and even dissolves at high temperature. To solve these problems, sulfonated phenolphthalein poly（ether sulfone） （SPES-C, DS= 53.7%） is blended with the SPEEK matrix （DS= 55.1%, 61.7%） to prepare SPEEKJSPES-C blend membrane. The decrease in swelling degree and methanol permeability of the membrane is dose-dependent. Pure SPEEK （DS = 61.7%） membrane dissolves completely in water at 70℃, whereas the swelling degree of the SPEEK （DS = 61.7%）/SPES-C （40%, by mass） membrane is 29.7% at 80℃. From room temperature to 80℃, the methanol permeability of all SPEEK （DS = 55.1%）/SPES-C blend membranes is about one order of magnitude lower than that of Nafion 115. At higher temperature, the addition of SPES-C polymer increases the dimensional stability and greater proton conductivity can be achieved. The SPEEK （DS = 55.1%）/SPES-C （40%, by mass） membrane can withstand temperatures up to 150℃. The proton conductivity of SPEEK （DS = 55.1%）/SPES-C （30%, by mass） membrane approaches 0.16 S·cm^-1, matching that of Nafion 115 at 140℃ and 100% RH, while pure SPEEK （DS = 55.1%） membrane dissolves at 90℃. The SPEEK/SPES-C blend membranes are promising for use in direct methanol fuel cells because of their good dimensional stability, high proton conductivity, and low methanol permeability.

SYNTHESIS AND PROPERTIES OF SULFONATED POLY(ARYLENE ETHER) CONTAINING TRIPHENYL METHANE MOIETIES FROM ISOCYNATE MASKED BISPHENOL

A novel sulfonated poly（arylene ether） containing triphenylmethane moieties was synthesized by the sulfonation of a designed parent polymer using chlorosulfonic acid as sulfonation agent. The sulfonation took place at the para position of the pendant phenyl rings because of the specially designed parent polymer. The position and degree of sulfonation were characterized by ^1H-NMR and elemental analysis. The sulfonated polymers are highly soluble in common organic solvents, such as dimethylsulfoxide, N,N＇-dimethylacetamide, dimethylformamide, ethylene glycol monomethyl ether, and can be readily cast into tough and smooth films from solutions. The films showed good thermal and hydrolysis stabilities. Moreover, Fenton＇s reagent test revealed that the films exhibited superior stability to oxidation. The proton conductivities of the films were comparable with Nation 117 under same conditions. The membrane electrode assembly （MEA） prepared with the asmade film （706 EW, 100 μm dry thickness） shows better cell performance than Nation 115-MEA in the whole current density range.

SYNTHESIS AND CHARACTERIZATION OF POLY(ARYL ETHER KETONE)CONTAINING BIPHENYLPHTHALAZINONE MOIETY

A new poly(aryl ether ketone) containing biphenylphthalazinone moiety was prepared by the reaction of 4-(4-hydroxybiphenyl) phthalazine-1-one with 4, 4'-difluorobenzophenone. The monomer and the polymer were characterized by FT-IR and H-1-NMR. Some properties of this polymer were described.

Synthesis and Characterization of Ion-exchange Sulfonated Poly (ether sulfone)

N,N＇-Bis（3-hydroxyphenyl）-1,8,4,5-naphthalenetetracarboxylic bisimide was prepared from the reaction of 1,8,4,5-naphthalenetetrcarboxylic acid dianhydride and 2-aminophenol in N, N-dimethylformamide. Polymerization of this bisimide with 4,4＇-difluorodiphenylsulfone and disodium 3,3＇-disulfonate4,4＇-difluorodiphenylsulfone gave ion-exchange sulfonated poly（ether sulfone）. The structure of the title compound was characterized with H-NMR and its polymer was characterized with FT-IR.

SYNTHESIS AND CHARACTERIZATION OF POLY(ARYL ETHER KETONE)FROM 4-(3-PHENYL-4-HYDROXYPHENYL)PHTHALAZINONE

A novel soluble poly(aryl ether ketone) was prepared by the reaction of 4-(3-phenyl-4-hydroxyphenyl)phthalazinone with 4,4'-difluorobenzophenone. The polymer was characterized by DSC, TGA and X-ray diffraction.

Synthesis and Characterization of Reactive Poly(Aryl Ether Ketone Ketone) Containing Cyclohexene Ring

A novel heterocyclic poly (aryl ether ketone ketone) (PPEKK) containing cyclohexenering was prepared from 1-methyl-cyclohex-1-ene-4, 5 -diyl-bis(4-chlorophenyl methanone) and 4 (4-hydroxyphenyl)(2H) phthalazin-1-one. The polymer was characterized by FTIR, 1HNMR, DSC,TG and X-ray analysis.

Synthesis and Properties of Poly(aryl ether ketone) Copolymers Containing 2,7-Naphthalene Moieties

Poly（ aryl ether ketone） copolymers containing 2,7-naphthylene and hydroquinone（HQ） moieties with various compositions were prepared by the reaction of 4,4＇-difluorobenzophenone（DFB） 2,7-naphthylene and hydroquinone in the presence of sodium carbonate and potassium carbonate （ 19： 1, mass ratio） in diphenyl sulfone （DPS）. The thermal analysis results of the copolymers show that the glass transition temperatures（Tgs） increase, while the melting temperatures（Tra） and tile 5.0% weight loss temperatures （ Td ） decrease with the increase of the 2,7-naphthalene moieties. For the copolymers synthesized at a molar fraction of 2,7-naphthalene in the difluoro monomers being over 0.30, no peaks corresponding to the cold crystallization temperature and the melting temperature could be detected, indicating that these copolymers are almost amorphous. The crystal structures of the copolymers with a molar fraction of 2,7-naphthalene being less than 0. 30 are rhombic.

STRUCTURE AND PROPERTIES OF PHOSPHROUS-CONTAINING POLY(ARYLETHER KETONE)WITH BISPHENOL-A MOIETY

A phosphrous-containing poly（aryl ether ketone） was synthesized derived from bisphenol-A and bis[4-（4- fluorobenzoyl）phenyl] phenyl phosphine oxide （FPPPO） by nucleophilic substitution reaction. The structure of the polymer was characterized by FT-IR, ^1H-NMR and ^31p-NMR. The thermal property of the PAEK was measured by DSC and TGA. The glass transition temperature （Tg） of the polymer was 205℃, and the 5% weight loss temperature under nitrogen was 475℃. Good solubility of the polymer in organic solvents, such as N-methylpyrrolidone, dimethylformamide, dimethylacetamide, dimethylsulfoxide and chloroalkanes was observed, flexible film was obtained from the polymer＇s CH2Cl2 solution. The limiting oxygen index （LOI） of the PAEK was 40, which indicated that organic phosphorus moiety can offer good flame retardant property to the polymer.

Sulfonated poly(aryl ether ketone sulfone)modified by polyoxometalates LaW_(10) clusters for proton exchange membranes with high proton conduction performance

Polyoxometalates(POMs)are classified as solid superacids which can exhibit notable proton conductivity,making them a promising functional inorganic filler for enhancing the proton conductivity of proton exchange membranes(PEMs).In this study,a series of hybrid membranes were obtained by molecular-level hybridization of Weakley-type POM Na_(7)H_(2)LaW_(10)O_(36)(LaW_(10))clusters into sulfonated poly(aryl ether ketone sulfone)(SPAEKS).All hybrid membranes exhibited greater proton conductivity than the pristine membrane in the 30–80℃temperature range.When the doping amount of LaW 10 reached 7 wt.%,the proton conductivity of M-LaW 10^(-7)achieved 64 mS·cm^(−1)at 80℃.Lanthanide ions'high coordination number property and variable coordination environment can aid to attract more water molecules from the environment.LaW 10 and these bound water can construct denser hydrogen bonds with–SO_(3)H of SPAEKS.These intensive hydrogen bonds will facilitate the constitution of more continuous proton transport channels,and improve the proton conductivity of the hybrid membrane.This work off ers a fresh approach to using POMs containing rare-earth components in PEMs.

Dynamic Rheological Characterization of A Thermotropic Liquid Crystalline Poly (aryl ether ketone)

The rheometries ARES rheometer was applied to determining the rheological behavior of a thermotropic liquid crystalline poly (aryl ether ketone). The viscosity of the material decreases with increasing temperature. reaching a minimum in the nematic state, then slightly increases with further raising the temperature in the biphase.

Synthesis of Poly(aryl ether ketone) Copolymers Containing Adamantyl-substituted Naphthalene Rings

High performance polymers have received considerable attention over the past decade owing to their increased demands as replacements for metals or ceramics in automotive, aerospace, and microelectronic industries. Poly（aryl ether ketone）s（PAEKs） are a class of important high-performance aromatic polymers with excellent mechanical properties, good solvent resistance, size-accuracy, electrical characteristics, and superior thermal stability. However,