The concern with environmental preservation is a very current and relevant topic. Regarding polymers, the search for potentially ecofriendly matters has been the subject of scientific research. In this context, this w...The concern with environmental preservation is a very current and relevant topic. Regarding polymers, the search for potentially ecofriendly matters has been the subject of scientific research. In this context, this work aimed to study the effect of adding nanocellulose (nCE) with 1, 3, and 5 wt.% on poly(butylene adipate-co-butylene terephthalate) (PBAT). Thermal, structural, relaxometric, and rheological assessments were carried out. Quantitative evaluation of PBAT copolymer by high field NMR revealed 56.4 and 43.6 m.% of the butylene adipate and butylene terephthalate segments, respectively. WAXD measurement on the deconvoluted diffraction patterns identified that nCE was a mixing of Cellulose I and Cellulose II polymorph structures. At any composition, nanocellulose interfered with the PBAT crystallisation process. Also, a series of new PBAT crystallographic planes appeared as a function of nanocellulose content. PBAT hydrogen molecular relaxation varied randomly with nanocellulose content and had a strong effect on the hydrogen relaxation. PBAT cold crystallisation and melting temperatures (T<sub>cc</sub> and T<sub>m</sub>) were almost unchangeable. Although T<sub>cc</sub> did not change during polymer solidification from PBAT molten state, the sample’s degree of crystallinity varied with composition through the transcrystallization phenomenon. Nanocomposite thermal stability decreased possibly owing to the catalytic action of sulfonated amorphous cellulose chains. For the sample with 3 wt.% of nanocellulose, the highest values of complex viscosity and storage modulus were achieved.展开更多
In order to improve the wettability and biocompatibility of the poly （butylene terephthalate） non-woven （PBTNW）, the method of surface modification is used to graft copolymerization of chitosan （CS） onto the PBT...In order to improve the wettability and biocompatibility of the poly （butylene terephthalate） non-woven （PBTNW）, the method of surface modification is used to graft copolymerization of chitosan （CS） onto the PBTNW under alkylpolyglycoside （APG） inducing. The product is thoroughly characterized with the Fourier transform infrared spectroscopy （FrIR）, the electron spectroscopy for chemical analysis （ESCA）, the thermogravimetric （TG） and the scanning electron microscopy （SEM）. It is found that chitosan is successfully grafted onto PBTNW. In addition, the water contact angles, hemolysis tests and cytotoxicity evaluation tests show an improvement in wettability and biocompatihility as a result of graft copolymerization of chitosan. So the CS-grafted PBTNW exhibits greater superiority than the original PBTNW. The CS-grafted PBTNW can be a candidate for blood filter materials and other medical applications.展开更多
In the present study,thermal behavior and crystal transition of pure poly(butylene adipate)(PBA)upon heating process were investigated by FTIR spectroscopy.To gain further insight into the thermal behavior alteration ...In the present study,thermal behavior and crystal transition of pure poly(butylene adipate)(PBA)upon heating process were investigated by FTIR spectroscopy.To gain further insight into the thermal behavior alteration and the phase transition of PBA,we performed two-dimensional(2D)correlation analysis.We found thatβ-form PBA crystal undergoes not only the melting process but also crystal transition upon the heating process.展开更多
In this article, the transesterification of poly(bisphenol A carbonate) (PC) with butylene terephthalate-caprolactone copolyester at a weight ratio 50/50 (BCL(21)) was thoroughly investigated by proton nuclear magneti...In this article, the transesterification of poly(bisphenol A carbonate) (PC) with butylene terephthalate-caprolactone copolyester at a weight ratio 50/50 (BCL(21)) was thoroughly investigated by proton nuclear magnetic resonance spectroscopy ('H-NMR), in conjunction with a model compound. The 1 H-NMR results of the annealed blend PC/BCL(21) show that the formation of bisphenol A-terephthalate ester units is the same as in the annealed blend of PC with PBT, and the transesterification actually occurs between PC and butylene terephthalate (BT) segments in BCL(21). By comparison with the model compound bisphenol A dibutyrate, the new signal appearing at δ= 2.56 in the 1H-NMR spectrum confirms the existence of bisphenol A caprolactone ester units resulting from the exchange reaction of PC with caprolactone (CL) segments. 1H-NMR analysis of the transesterification rates reveals that the reaction of PC with aromatic and aliphatic segments in BCL(21) proceeds in a random manner. The miscibility of the blend PC/BCL(21) copolyester is favorable for the transesterification of PC with BT segments and CL segments.展开更多
Poly(glycolic acid)(PGA)is derived from glycolide obtained by fermenting pineapples or sugarcane,which has excellent gas barrier properties and a small carbon footprint.PGA is a potential substitute for the current al...Poly(glycolic acid)(PGA)is derived from glycolide obtained by fermenting pineapples or sugarcane,which has excellent gas barrier properties and a small carbon footprint.PGA is a potential substitute for the current aluminum-plastic composite films used in high barrier packaging applications.However,its poor ductility and narrow processing window limit its application in food packaging.Herein,poly(butylene succinate-co-butylene adipate)(PBSA)was used to fabricate PGA/PBSA blend films through an in situ fibrillation technique and blown film extrusion.Under the elongational flow field used during the extrusion process,a unique hierarchical structure based on the PBSA nanofibrils and interfacially oriented PGA crystals was obtained.This structure enhances the strength,ductility and gas barrier properties of the PGA/PBSA blend film.In addition,an epoxy chain extender(ADR4468)was used as a compatibilizer to further enhance the interfacial adhesion between PGA and PBSA.70PGA/0.7ADR exhibited a very low oxygen permeability(2.34×10^(-4)Barrer)with significantly high elongating at break(604.4%),tensile strength(47.4 MPa),and transparency,which were superior to those of petroleum-based polymers.Thus,the 70PGA/0.7ADR blown films could satisfy the requirements for most instant foods such as coffee,peanuts,and fresh meat.展开更多
The pyrolysis of poly(ethylene terephthalate)(PET)/poly(butylene terephthalate)(PBT)catalyzed by five alkaline earth metal-based minerals/wastes,namely calcined dolomite,calcite,magnesite,calcium carbide slag(CCS),and...The pyrolysis of poly(ethylene terephthalate)(PET)/poly(butylene terephthalate)(PBT)catalyzed by five alkaline earth metal-based minerals/wastes,namely calcined dolomite,calcite,magnesite,calcium carbide slag(CCS),and ophicalcitum,was conducted by a pyrolyzer-gas chromatography-mass spectrometer(Py-GC-MS)with the objective of recovering benzenes-enriched oil.Compared with magnesium-based catalysts and pure CaO,the calcium-based catalysts with calcium hydroxide as the main component performed better catalytic effect,which could simultaneously promote the hydrolysis of ester products and the decarboxylation of aromatic acids after hydrolysis.For PET,the addition of solid base catalysts at 600℃promoted the complete degradation of aromatic acids and aryl esters,which accounted for 32.6%and 30.7%of the pyrolysis oil,respectively.The content of benzene in oil increased from 8.8%to 31.7%–78.8%.For PBT,the addition of solid base catalysts at 600℃completely decomposed the aromatic acids,which accounted for 67.1%of the pyrolysis oil,and the content of benzene in oil increased from 12.3%to 34.5%–81.0%.During the deoxygenation of polyester pyrolysis products,increasing temperature was more effective for the decomposition/conversion of acetone and tetrahydrofuran,while increasing the alkalinity of the reaction environment contributed to the rapid decrease in acetaldehyde and aryl ketone contents.展开更多
Rare earth （Nd, Y, La, Dy） stearates have been synthesized and used as single component catalysts for the polycondensation of dimethyl terephthalate, adipic acid and 1,4-butanediol for the first time preparing biode...Rare earth （Nd, Y, La, Dy） stearates have been synthesized and used as single component catalysts for the polycondensation of dimethyl terephthalate, adipic acid and 1,4-butanediol for the first time preparing biodegradable poly（butylene adipate-co-terephthalate） （PBAT） with high molecular weight, The microstructures of PBAT were characterized by ^1H NMR spectra. The PBAT exhibits good mechanical properties such as high tensile strength （ca. 20 MPa） and long break elongation （〉700%）.展开更多
文摘The concern with environmental preservation is a very current and relevant topic. Regarding polymers, the search for potentially ecofriendly matters has been the subject of scientific research. In this context, this work aimed to study the effect of adding nanocellulose (nCE) with 1, 3, and 5 wt.% on poly(butylene adipate-co-butylene terephthalate) (PBAT). Thermal, structural, relaxometric, and rheological assessments were carried out. Quantitative evaluation of PBAT copolymer by high field NMR revealed 56.4 and 43.6 m.% of the butylene adipate and butylene terephthalate segments, respectively. WAXD measurement on the deconvoluted diffraction patterns identified that nCE was a mixing of Cellulose I and Cellulose II polymorph structures. At any composition, nanocellulose interfered with the PBAT crystallisation process. Also, a series of new PBAT crystallographic planes appeared as a function of nanocellulose content. PBAT hydrogen molecular relaxation varied randomly with nanocellulose content and had a strong effect on the hydrogen relaxation. PBAT cold crystallisation and melting temperatures (T<sub>cc</sub> and T<sub>m</sub>) were almost unchangeable. Although T<sub>cc</sub> did not change during polymer solidification from PBAT molten state, the sample’s degree of crystallinity varied with composition through the transcrystallization phenomenon. Nanocomposite thermal stability decreased possibly owing to the catalytic action of sulfonated amorphous cellulose chains. For the sample with 3 wt.% of nanocellulose, the highest values of complex viscosity and storage modulus were achieved.
文摘In order to improve the wettability and biocompatibility of the poly （butylene terephthalate） non-woven （PBTNW）, the method of surface modification is used to graft copolymerization of chitosan （CS） onto the PBTNW under alkylpolyglycoside （APG） inducing. The product is thoroughly characterized with the Fourier transform infrared spectroscopy （FrIR）, the electron spectroscopy for chemical analysis （ESCA）, the thermogravimetric （TG） and the scanning electron microscopy （SEM）. It is found that chitosan is successfully grafted onto PBTNW. In addition, the water contact angles, hemolysis tests and cytotoxicity evaluation tests show an improvement in wettability and biocompatihility as a result of graft copolymerization of chitosan. So the CS-grafted PBTNW exhibits greater superiority than the original PBTNW. The CS-grafted PBTNW can be a candidate for blood filter materials and other medical applications.
文摘In the present study,thermal behavior and crystal transition of pure poly(butylene adipate)(PBA)upon heating process were investigated by FTIR spectroscopy.To gain further insight into the thermal behavior alteration and the phase transition of PBA,we performed two-dimensional(2D)correlation analysis.We found thatβ-form PBA crystal undergoes not only the melting process but also crystal transition upon the heating process.
文摘In this article, the transesterification of poly(bisphenol A carbonate) (PC) with butylene terephthalate-caprolactone copolyester at a weight ratio 50/50 (BCL(21)) was thoroughly investigated by proton nuclear magnetic resonance spectroscopy ('H-NMR), in conjunction with a model compound. The 1 H-NMR results of the annealed blend PC/BCL(21) show that the formation of bisphenol A-terephthalate ester units is the same as in the annealed blend of PC with PBT, and the transesterification actually occurs between PC and butylene terephthalate (BT) segments in BCL(21). By comparison with the model compound bisphenol A dibutyrate, the new signal appearing at δ= 2.56 in the 1H-NMR spectrum confirms the existence of bisphenol A caprolactone ester units resulting from the exchange reaction of PC with caprolactone (CL) segments. 1H-NMR analysis of the transesterification rates reveals that the reaction of PC with aromatic and aliphatic segments in BCL(21) proceeds in a random manner. The miscibility of the blend PC/BCL(21) copolyester is favorable for the transesterification of PC with BT segments and CL segments.
基金the National Key Research and Development Program of China(No.2022YFB3704900)the National Natural Science Foundation of China(No.52073004)China National Tobacco Corporation Guizhou Company(No.2023XM24)。
文摘Poly(glycolic acid)(PGA)is derived from glycolide obtained by fermenting pineapples or sugarcane,which has excellent gas barrier properties and a small carbon footprint.PGA is a potential substitute for the current aluminum-plastic composite films used in high barrier packaging applications.However,its poor ductility and narrow processing window limit its application in food packaging.Herein,poly(butylene succinate-co-butylene adipate)(PBSA)was used to fabricate PGA/PBSA blend films through an in situ fibrillation technique and blown film extrusion.Under the elongational flow field used during the extrusion process,a unique hierarchical structure based on the PBSA nanofibrils and interfacially oriented PGA crystals was obtained.This structure enhances the strength,ductility and gas barrier properties of the PGA/PBSA blend film.In addition,an epoxy chain extender(ADR4468)was used as a compatibilizer to further enhance the interfacial adhesion between PGA and PBSA.70PGA/0.7ADR exhibited a very low oxygen permeability(2.34×10^(-4)Barrer)with significantly high elongating at break(604.4%),tensile strength(47.4 MPa),and transparency,which were superior to those of petroleum-based polymers.Thus,the 70PGA/0.7ADR blown films could satisfy the requirements for most instant foods such as coffee,peanuts,and fresh meat.
基金would like to gratefully acknowledge the National Key Research and Development Program(No.2018YFC1901300)the Key Research and Development Program of Zhejiang Province(No.2020C03084).
文摘The pyrolysis of poly(ethylene terephthalate)(PET)/poly(butylene terephthalate)(PBT)catalyzed by five alkaline earth metal-based minerals/wastes,namely calcined dolomite,calcite,magnesite,calcium carbide slag(CCS),and ophicalcitum,was conducted by a pyrolyzer-gas chromatography-mass spectrometer(Py-GC-MS)with the objective of recovering benzenes-enriched oil.Compared with magnesium-based catalysts and pure CaO,the calcium-based catalysts with calcium hydroxide as the main component performed better catalytic effect,which could simultaneously promote the hydrolysis of ester products and the decarboxylation of aromatic acids after hydrolysis.For PET,the addition of solid base catalysts at 600℃promoted the complete degradation of aromatic acids and aryl esters,which accounted for 32.6%and 30.7%of the pyrolysis oil,respectively.The content of benzene in oil increased from 8.8%to 31.7%–78.8%.For PBT,the addition of solid base catalysts at 600℃completely decomposed the aromatic acids,which accounted for 67.1%of the pyrolysis oil,and the content of benzene in oil increased from 12.3%to 34.5%–81.0%.During the deoxygenation of polyester pyrolysis products,increasing temperature was more effective for the decomposition/conversion of acetone and tetrahydrofuran,while increasing the alkalinity of the reaction environment contributed to the rapid decrease in acetaldehyde and aryl ketone contents.
基金Project supported by the National Natural Science Foundation of China （No. 20434020）, the Major State Basic Research Development Program （No. 2005CB623802）, and China Postdoctor Science Foundation （No. 20060390334）.
文摘Rare earth （Nd, Y, La, Dy） stearates have been synthesized and used as single component catalysts for the polycondensation of dimethyl terephthalate, adipic acid and 1,4-butanediol for the first time preparing biodegradable poly（butylene adipate-co-terephthalate） （PBAT） with high molecular weight, The microstructures of PBAT were characterized by ^1H NMR spectra. The PBAT exhibits good mechanical properties such as high tensile strength （ca. 20 MPa） and long break elongation （〉700%）.