Nonisothermal crystallization behavior of poly(butylene adipate-co-terephthalate)(PBAT) synthesized via direct esterification and polycondensation reactions was investigated by the differential scanning calorimetry(DS...Nonisothermal crystallization behavior of poly(butylene adipate-co-terephthalate)(PBAT) synthesized via direct esterification and polycondensation reactions was investigated by the differential scanning calorimetry(DSC).The Avrami equation modified by Jeziorny and the Z.S.Mo equation were employed to describe the non-isothermal crystallization kinetics of copolyester samples.The test results showed that the Avrami equation was successful in describing nonisothermal crystallization process of PBAT copolyesters.PBAT copolyester could give birth to secondary crystallization.The crystallization parameter(Zc) increased with an increasing cooling rate and the Avrami exponent(n) was around 2.3.For a given cooling rate,the value of Zc demonstrated a sagging trend with an increase in adipic acid(AA) content.The equation proposed by Z.S.Mo was successful in describing the nonisothermal crystallization kinetics of PBAT copolyesters.展开更多
In the present study,thermal behavior and crystal transition of pure poly(butylene adipate)(PBA)upon heating process were investigated by FTIR spectroscopy.To gain further insight into the thermal behavior alteration ...In the present study,thermal behavior and crystal transition of pure poly(butylene adipate)(PBA)upon heating process were investigated by FTIR spectroscopy.To gain further insight into the thermal behavior alteration and the phase transition of PBA,we performed two-dimensional(2D)correlation analysis.We found thatβ-form PBA crystal undergoes not only the melting process but also crystal transition upon the heating process.展开更多
Blends of poly(3-hydroxybutyrate-co-3-hydroxyhexanoate) (PHBHHx) and poly(butylene succinate-adipate) (PBSA), both biodegradable semicrystalline polyesters, were prepared with the ratio of PHBHHx/PBSA ranging from 80/...Blends of poly(3-hydroxybutyrate-co-3-hydroxyhexanoate) (PHBHHx) and poly(butylene succinate-adipate) (PBSA), both biodegradable semicrystalline polyesters, were prepared with the ratio of PHBHHx/PBSA ranging from 80/20 to 20/80 by melt mixing method. Differential scanning calorimetry (DSC), thermogravimetry analysis (TGA), dynamic mechanical thermal analysis (DMA), polarizing optical microscopy (POM) and wide angle X-ray diffractometer (WAXD) were used to study the miscibility and crystallization behavior of PHBHHx/PBSA blends. Experimental results indicate that PHBHHx is immiscible with PBSA as shown by the almost unchanged glass transition temperature and the biphasic melt.展开更多
The concern with environmental preservation is a very current and relevant topic. Regarding polymers, the search for potentially ecofriendly matters has been the subject of scientific research. In this context, this w...The concern with environmental preservation is a very current and relevant topic. Regarding polymers, the search for potentially ecofriendly matters has been the subject of scientific research. In this context, this work aimed to study the effect of adding nanocellulose (nCE) with 1, 3, and 5 wt.% on poly(butylene adipate-co-butylene terephthalate) (PBAT). Thermal, structural, relaxometric, and rheological assessments were carried out. Quantitative evaluation of PBAT copolymer by high field NMR revealed 56.4 and 43.6 m.% of the butylene adipate and butylene terephthalate segments, respectively. WAXD measurement on the deconvoluted diffraction patterns identified that nCE was a mixing of Cellulose I and Cellulose II polymorph structures. At any composition, nanocellulose interfered with the PBAT crystallisation process. Also, a series of new PBAT crystallographic planes appeared as a function of nanocellulose content. PBAT hydrogen molecular relaxation varied randomly with nanocellulose content and had a strong effect on the hydrogen relaxation. PBAT cold crystallisation and melting temperatures (T<sub>cc</sub> and T<sub>m</sub>) were almost unchangeable. Although T<sub>cc</sub> did not change during polymer solidification from PBAT molten state, the sample’s degree of crystallinity varied with composition through the transcrystallization phenomenon. Nanocomposite thermal stability decreased possibly owing to the catalytic action of sulfonated amorphous cellulose chains. For the sample with 3 wt.% of nanocellulose, the highest values of complex viscosity and storage modulus were achieved.展开更多
Poly(glycolic acid)(PGA)is derived from glycolide obtained by fermenting pineapples or sugarcane,which has excellent gas barrier properties and a small carbon footprint.PGA is a potential substitute for the current al...Poly(glycolic acid)(PGA)is derived from glycolide obtained by fermenting pineapples or sugarcane,which has excellent gas barrier properties and a small carbon footprint.PGA is a potential substitute for the current aluminum-plastic composite films used in high barrier packaging applications.However,its poor ductility and narrow processing window limit its application in food packaging.Herein,poly(butylene succinate-co-butylene adipate)(PBSA)was used to fabricate PGA/PBSA blend films through an in situ fibrillation technique and blown film extrusion.Under the elongational flow field used during the extrusion process,a unique hierarchical structure based on the PBSA nanofibrils and interfacially oriented PGA crystals was obtained.This structure enhances the strength,ductility and gas barrier properties of the PGA/PBSA blend film.In addition,an epoxy chain extender(ADR4468)was used as a compatibilizer to further enhance the interfacial adhesion between PGA and PBSA.70PGA/0.7ADR exhibited a very low oxygen permeability(2.34×10^(-4)Barrer)with significantly high elongating at break(604.4%),tensile strength(47.4 MPa),and transparency,which were superior to those of petroleum-based polymers.Thus,the 70PGA/0.7ADR blown films could satisfy the requirements for most instant foods such as coffee,peanuts,and fresh meat.展开更多
Rare earth （Nd, Y, La, Dy） stearates have been synthesized and used as single component catalysts for the polycondensation of dimethyl terephthalate, adipic acid and 1,4-butanediol for the first time preparing biode...Rare earth （Nd, Y, La, Dy） stearates have been synthesized and used as single component catalysts for the polycondensation of dimethyl terephthalate, adipic acid and 1,4-butanediol for the first time preparing biodegradable poly（butylene adipate-co-terephthalate） （PBAT） with high molecular weight, The microstructures of PBAT were characterized by ^1H NMR spectra. The PBAT exhibits good mechanical properties such as high tensile strength （ca. 20 MPa） and long break elongation （〉700%）.展开更多
The effects of crystallization temperature and blend ratio on the polymorphic crystal structures of poly（butylene adipate） （PBA） in poly（butylene succinate） （PBS）/poly（butylene adipate） （PBS/PBA） blends we...The effects of crystallization temperature and blend ratio on the polymorphic crystal structures of poly（butylene adipate） （PBA） in poly（butylene succinate） （PBS）/poly（butylene adipate） （PBS/PBA） blends were studied by means of differential scanning calorimetry （DSC）, wide-angle X-ray diffraction （XRD） and atomic force microscopy （AFM）. It was revealed that the polymorphism of PBA can be regulated by the blend ratio even in a non-isothermal crystallization process. The results demonstrate that high temperature favors fiat-on α crystals, while low temperature contributes to edge-on β crystals. It was also found that the effect of blend ratio on the crystallization mechanism of PBA is well coincident with that of the crystallization temperature. The increment of PBS content in the PBS/PBA blend gives rise to more β-form crystals of PBA. For those PBS/PBA blends with low PBA content, the interlamellar phase segregation of PBA makes its molecular chains so difficult to diffuse from one isolated microdomain to another that high crystallization temperature and sufficiently long crystallization time will be required if the PBA α-type crystals are targeted.展开更多
Oriented and non-oriented Teflon films, which were found to have the same crystalline structure, but different surface morphologies, were used to sandwich poly（butylene adipate） （PBA） films during isothermal cryst...Oriented and non-oriented Teflon films, which were found to have the same crystalline structure, but different surface morphologies, were used to sandwich poly（butylene adipate） （PBA） films during isothermal crystallization. It was found that both the Teflon surface structure and the PBA polymorphic structure are the determining factors to induce epitaxial crystallization. The oriented Teflon film was able to induce epitaxial crystallization of PBA α crystal, while the non-oriented Teflon did not induce any epitaxial crystallization of PBA. Epitaxial crystallization did not occurred for PBA β crystals between neither the oriented nor the non-oriented Teflon films. The enzymatic degradation rate of PBA films was not determined by the epitaxial crystallization, in fact it was still dependent on the polymorphic crystal structure of PBA. The morphological changes of PBA films after enzymatic degradation confirmed again that the epitaxial crystallization only occurred for the PBA film with α crystal structure which was produced by being sandwiched between oriented Teflon films, and it happened only on the surface of PBA films.展开更多
We successfully use a co-precipitation method to prepare inclusion complex between poly（butylene adipate） （PBA） chains （guest component） and urea molecules （host component）. The PBA/urea inclusion complex is c...We successfully use a co-precipitation method to prepare inclusion complex between poly（butylene adipate） （PBA） chains （guest component） and urea molecules （host component）. The PBA/urea inclusion complex is confirmed to adopt a hexagonal crystal modification with lattice parameters ofa = 8.14 A and c = 10.92 A, and the interaction between PBA chains and urea is van der Waals force. The singly isolated PBA chains are suggested to take some gauche conformation, which is different from the all-trans conformation in r-form PBA. Furthermore, we employ the isolated PBA chains which are uniformly pre-established in a specific conformation in urea channels to regulate the crystal form of PBA for the first time. After removing the host urea molecules, the coalesced PBA chains are found to solely crystallize into a-form crystals at different coalescing temperatures. By comparing the FTIR spectra, it is found that PBA chains in inclusion complex plausibly contain some similar conformers as those in a-form crystal, which is suggested to be the intrinsic reason for the sole formation of a-form crystals. This research proves that inclusion complex can be used as a very effective method to regulate polymorphism of semi-crystalline polymers.展开更多
In this study, the isothermal crystallization kinetics and crystalline morphology of poly（butylene adipate-co-butylene 1,4-cyclohexanedicarboxylate）（PBAC）, which refers to a copolyester containing a non-planar rin...In this study, the isothermal crystallization kinetics and crystalline morphology of poly（butylene adipate-co-butylene 1,4-cyclohexanedicarboxylate）（PBAC）, which refers to a copolyester containing a non-planar ring structure, were investigated by differential scanning calorimetry and polarized optical microscopy, and compared with those of neat poly（butylene 1,4-cyclohexanedicarboxylate）（PBC）. The results indicate that the introduction of butylene adipate（BA） unit into PBAC did not change the intrinsical crystallization mechanism. But, the crystallization rate and ability, and equilibrium melting temperature of PBAC copolymers were reduced. All PBC and PBAC copolymers could only form high density of nucleation from melt at given supercooling, while no Maltese cross or ring-banded spherulites could be observed. PBAC copolymers with a high amount of BA unit became amorphous after quenching with liquid nitrogen from melt, while PBC and PBAC copolymers with a low amount of BA unit could still form a large amount of nuclei under the same treatment.展开更多
文摘Nonisothermal crystallization behavior of poly(butylene adipate-co-terephthalate)(PBAT) synthesized via direct esterification and polycondensation reactions was investigated by the differential scanning calorimetry(DSC).The Avrami equation modified by Jeziorny and the Z.S.Mo equation were employed to describe the non-isothermal crystallization kinetics of copolyester samples.The test results showed that the Avrami equation was successful in describing nonisothermal crystallization process of PBAT copolyesters.PBAT copolyester could give birth to secondary crystallization.The crystallization parameter(Zc) increased with an increasing cooling rate and the Avrami exponent(n) was around 2.3.For a given cooling rate,the value of Zc demonstrated a sagging trend with an increase in adipic acid(AA) content.The equation proposed by Z.S.Mo was successful in describing the nonisothermal crystallization kinetics of PBAT copolyesters.
文摘In the present study,thermal behavior and crystal transition of pure poly(butylene adipate)(PBA)upon heating process were investigated by FTIR spectroscopy.To gain further insight into the thermal behavior alteration and the phase transition of PBA,we performed two-dimensional(2D)correlation analysis.We found thatβ-form PBA crystal undergoes not only the melting process but also crystal transition upon the heating process.
基金The National Natural Science Foundation of China (No. 20374032) and Tianjin Science and Technology Key Project (No. 05YFSZSF02200)
文摘Blends of poly(3-hydroxybutyrate-co-3-hydroxyhexanoate) (PHBHHx) and poly(butylene succinate-adipate) (PBSA), both biodegradable semicrystalline polyesters, were prepared with the ratio of PHBHHx/PBSA ranging from 80/20 to 20/80 by melt mixing method. Differential scanning calorimetry (DSC), thermogravimetry analysis (TGA), dynamic mechanical thermal analysis (DMA), polarizing optical microscopy (POM) and wide angle X-ray diffractometer (WAXD) were used to study the miscibility and crystallization behavior of PHBHHx/PBSA blends. Experimental results indicate that PHBHHx is immiscible with PBSA as shown by the almost unchanged glass transition temperature and the biphasic melt.
文摘The concern with environmental preservation is a very current and relevant topic. Regarding polymers, the search for potentially ecofriendly matters has been the subject of scientific research. In this context, this work aimed to study the effect of adding nanocellulose (nCE) with 1, 3, and 5 wt.% on poly(butylene adipate-co-butylene terephthalate) (PBAT). Thermal, structural, relaxometric, and rheological assessments were carried out. Quantitative evaluation of PBAT copolymer by high field NMR revealed 56.4 and 43.6 m.% of the butylene adipate and butylene terephthalate segments, respectively. WAXD measurement on the deconvoluted diffraction patterns identified that nCE was a mixing of Cellulose I and Cellulose II polymorph structures. At any composition, nanocellulose interfered with the PBAT crystallisation process. Also, a series of new PBAT crystallographic planes appeared as a function of nanocellulose content. PBAT hydrogen molecular relaxation varied randomly with nanocellulose content and had a strong effect on the hydrogen relaxation. PBAT cold crystallisation and melting temperatures (T<sub>cc</sub> and T<sub>m</sub>) were almost unchangeable. Although T<sub>cc</sub> did not change during polymer solidification from PBAT molten state, the sample’s degree of crystallinity varied with composition through the transcrystallization phenomenon. Nanocomposite thermal stability decreased possibly owing to the catalytic action of sulfonated amorphous cellulose chains. For the sample with 3 wt.% of nanocellulose, the highest values of complex viscosity and storage modulus were achieved.
基金the National Key Research and Development Program of China(No.2022YFB3704900)the National Natural Science Foundation of China(No.52073004)China National Tobacco Corporation Guizhou Company(No.2023XM24)。
文摘Poly(glycolic acid)(PGA)is derived from glycolide obtained by fermenting pineapples or sugarcane,which has excellent gas barrier properties and a small carbon footprint.PGA is a potential substitute for the current aluminum-plastic composite films used in high barrier packaging applications.However,its poor ductility and narrow processing window limit its application in food packaging.Herein,poly(butylene succinate-co-butylene adipate)(PBSA)was used to fabricate PGA/PBSA blend films through an in situ fibrillation technique and blown film extrusion.Under the elongational flow field used during the extrusion process,a unique hierarchical structure based on the PBSA nanofibrils and interfacially oriented PGA crystals was obtained.This structure enhances the strength,ductility and gas barrier properties of the PGA/PBSA blend film.In addition,an epoxy chain extender(ADR4468)was used as a compatibilizer to further enhance the interfacial adhesion between PGA and PBSA.70PGA/0.7ADR exhibited a very low oxygen permeability(2.34×10^(-4)Barrer)with significantly high elongating at break(604.4%),tensile strength(47.4 MPa),and transparency,which were superior to those of petroleum-based polymers.Thus,the 70PGA/0.7ADR blown films could satisfy the requirements for most instant foods such as coffee,peanuts,and fresh meat.
基金Project supported by the National Natural Science Foundation of China （No. 20434020）, the Major State Basic Research Development Program （No. 2005CB623802）, and China Postdoctor Science Foundation （No. 20060390334）.
文摘Rare earth （Nd, Y, La, Dy） stearates have been synthesized and used as single component catalysts for the polycondensation of dimethyl terephthalate, adipic acid and 1,4-butanediol for the first time preparing biodegradable poly（butylene adipate-co-terephthalate） （PBAT） with high molecular weight, The microstructures of PBAT were characterized by ^1H NMR spectra. The PBAT exhibits good mechanical properties such as high tensile strength （ca. 20 MPa） and long break elongation （〉700%）.
基金financially supported by the National Natural Science Foundation of China(Nos.21204045 and 21276151)Natural Science Basic Research Plan in Shaanxi Province of China(No.2011JQ2004)Key Scientific Research Group of Shaanxi Province(No.2013KCT-08)
文摘The effects of crystallization temperature and blend ratio on the polymorphic crystal structures of poly（butylene adipate） （PBA） in poly（butylene succinate） （PBS）/poly（butylene adipate） （PBS/PBA） blends were studied by means of differential scanning calorimetry （DSC）, wide-angle X-ray diffraction （XRD） and atomic force microscopy （AFM）. It was revealed that the polymorphism of PBA can be regulated by the blend ratio even in a non-isothermal crystallization process. The results demonstrate that high temperature favors fiat-on α crystals, while low temperature contributes to edge-on β crystals. It was also found that the effect of blend ratio on the crystallization mechanism of PBA is well coincident with that of the crystallization temperature. The increment of PBS content in the PBS/PBA blend gives rise to more β-form crystals of PBA. For those PBS/PBA blends with low PBA content, the interlamellar phase segregation of PBA makes its molecular chains so difficult to diffuse from one isolated microdomain to another that high crystallization temperature and sufficiently long crystallization time will be required if the PBA α-type crystals are targeted.
基金financially supported by the National Natural Science Foundation of China(No.51025314)the Oticon Foundation in Denmark
文摘Oriented and non-oriented Teflon films, which were found to have the same crystalline structure, but different surface morphologies, were used to sandwich poly（butylene adipate） （PBA） films during isothermal crystallization. It was found that both the Teflon surface structure and the PBA polymorphic structure are the determining factors to induce epitaxial crystallization. The oriented Teflon film was able to induce epitaxial crystallization of PBA α crystal, while the non-oriented Teflon did not induce any epitaxial crystallization of PBA. Epitaxial crystallization did not occurred for PBA β crystals between neither the oriented nor the non-oriented Teflon films. The enzymatic degradation rate of PBA films was not determined by the epitaxial crystallization, in fact it was still dependent on the polymorphic crystal structure of PBA. The morphological changes of PBA films after enzymatic degradation confirmed again that the epitaxial crystallization only occurred for the PBA film with α crystal structure which was produced by being sandwiched between oriented Teflon films, and it happened only on the surface of PBA films.
基金financially supported by the National Natural Science Foundation of China(No.21674128)China University of Petroleum(Beijing)
文摘We successfully use a co-precipitation method to prepare inclusion complex between poly（butylene adipate） （PBA） chains （guest component） and urea molecules （host component）. The PBA/urea inclusion complex is confirmed to adopt a hexagonal crystal modification with lattice parameters ofa = 8.14 A and c = 10.92 A, and the interaction between PBA chains and urea is van der Waals force. The singly isolated PBA chains are suggested to take some gauche conformation, which is different from the all-trans conformation in r-form PBA. Furthermore, we employ the isolated PBA chains which are uniformly pre-established in a specific conformation in urea channels to regulate the crystal form of PBA for the first time. After removing the host urea molecules, the coalesced PBA chains are found to solely crystallize into a-form crystals at different coalescing temperatures. By comparing the FTIR spectra, it is found that PBA chains in inclusion complex plausibly contain some similar conformers as those in a-form crystal, which is suggested to be the intrinsic reason for the sole formation of a-form crystals. This research proves that inclusion complex can be used as a very effective method to regulate polymorphism of semi-crystalline polymers.
基金financially supported by the National Natural Science Foundation of China(No.51503217)Zhejiang Province Public Welfare Project(No.2017C31081)+1 种基金the Open Project Program of MOE Key Laboratory of Macromolecular Synthesis and Functionalization,Zhejiang University(No.2016MSF001)Youth Innovation Promotion Association CAS(No.2017339)
文摘In this study, the isothermal crystallization kinetics and crystalline morphology of poly（butylene adipate-co-butylene 1,4-cyclohexanedicarboxylate）（PBAC）, which refers to a copolyester containing a non-planar ring structure, were investigated by differential scanning calorimetry and polarized optical microscopy, and compared with those of neat poly（butylene 1,4-cyclohexanedicarboxylate）（PBC）. The results indicate that the introduction of butylene adipate（BA） unit into PBAC did not change the intrinsical crystallization mechanism. But, the crystallization rate and ability, and equilibrium melting temperature of PBAC copolymers were reduced. All PBC and PBAC copolymers could only form high density of nucleation from melt at given supercooling, while no Maltese cross or ring-banded spherulites could be observed. PBAC copolymers with a high amount of BA unit became amorphous after quenching with liquid nitrogen from melt, while PBC and PBAC copolymers with a low amount of BA unit could still form a large amount of nuclei under the same treatment.