Crystallization Behavior of Poly(ethylene terephthalate-co-ethylene isophthalate)

Crystallization behavior of poly(ethylene terephthalate-co-ethylene isophthalate)(PEIT) with different isoph-thalate contents (4%, 8% and 12%, designated asPEIT4,PEIT8 and PEIT12 respectively) has been inves-tigated by DSC and density measurement methods. Theresults show that the crystailinity of PEIT decreases withincreasing isophthalate content. However the crystallinity of PEIT8 is much smaller than that of PEIT12 whencooling from melt at a constant rate.The crystailinity ofPEIT8 cold-drawn filament shows almost the same val-

生物基2,5–呋喃二甲酸及其聚酯合成研究进展

如何通过高效、廉价的方法制备2,5-呋喃二甲酸(2,5-FDCA)及其聚合物已成为近几年的研究热点。重点介绍了2,5-FDCA的合成路线、聚2,5-呋喃二甲酸乙二醇酯(PEF)及其共聚酯的研究进展,并对其进行了分析。分析结果表明,目前2,5-FDCA的合成以5-羟甲基糠醛(HMF)氧化路线为主,其中催化剂采用贵金属,价格比较昂贵,建议对高效低价的新型催化剂体系进行开发。另外,为提高材料的各种性能,研究FDCA基聚酯改性的高性能产品,对经济、社会发展有着重大应用价值。

PEFT等温结晶动力学及多重熔融行为

为探究共聚单元2,5-呋喃二甲酸(FDCA)对聚对苯二甲酸-2,5-呋喃二甲酸乙二醇共聚酯(PEFT)的等温结晶动力学和多重熔融行为的影响,首先,利用差示扫描量热(DSC)仪研究聚对苯二甲酸乙二醇酯(PET)和PEFT在固定降温和升温速率下的熔融结晶和冷结晶行为。其次,研究PET和PEFT在不同结晶温度下的等温熔融结晶和冷结晶动力学,采用Avrami方程和Arrhenius方程计算相应的动力学参数。最后,研究PET和PEFT熔融结晶后的多重熔融行为,计算平衡熔点。结果表明,FDCA共聚单元破坏了PET分子链的对称性和规整性,降低了PEFT的结晶温度和熔融温度;FDCA共聚单元含量和结晶温度是影响PEFT等温熔融结晶和冷结晶动力学的两大重要因素;PET和PEFT在熔融结晶后的多重熔融行为对结晶温度具有明显的依赖性,且平衡熔点随着共聚酯中FDCA含量的增加而减小。

PEFT共聚酯的热氧化分解行为研究

采用热重(TG)分析法研究2,5-呋喃二甲酸(FDCA)质量分数分别为0,25%,50%,75%,100%的聚对苯二甲酸-2,5-呋喃二甲酸乙二醇共聚酯(PEFT)的热氧化分解行为,使用Kinssinger法、Ozawa法和Coats-Redfen法对PEFT热氧化分解的表观活化能(E_(a))和反应机理进行了分析。结果表明:PEFT的热氧化分解分为2个阶段,第一阶段主要是共聚酯的热氧化降解,质量变化率(w)为0~80%,第二阶段为第一阶段碳化物的分解,w为80%~100%,其初始分解温度和最大分解速度温度随着FDCA含量的增加而降低;Kinnsinger法得到的是在最大分解速度温度下PEFT的E_(a),不能显示E_(a)随w的整体变化趋势;Ozawa法和Coats-Redfen法计算结果一致,FDCA质量分数为75%时PEFT的E_(a)最大,为233.9 kJ/mol,FDCA质量分数为0时PEFT的E a最小,为139.8 kJ/mol;由Coats-Redfen法可知,PEFT的热氧化分解机理更接近一级反应。