Poly(p-phenylene terephthalamide)(PPTA)pulp was prepared by polycondensation of the p-phenylene diamine(PPDA)with terephthaloyl chloride(TPC)in the completely anhydrous solvent system of N-methyl pyrrolidone(NMP)havin...Poly(p-phenylene terephthalamide)(PPTA)pulp was prepared by polycondensation of the p-phenylene diamine(PPDA)with terephthaloyl chloride(TPC)in the completely anhydrous solvent system of N-methyl pyrrolidone(NMP)having calcium chloride,in the presence of poly(vinyl pyrrolidone)(PVP)having a viscosity average molecular weight lower than 40 000.It was confirmed that the polycondensation could be accelerated,the inherent viscosity of the polymer could be increased,and the polymers could be fibrillated more easily by the addition of the PVP.FTIR and X-ray spectra proved that PVP had not combined into molecular chains of the resultant PPTA pulps.The morphology of the resultant pulps,the effect of viscosity average molecular weight,amount and adding mode of PVP on inherent viscosity,specific surface area,and mean length of the resultant pulps were discussed in detail.And the friction and wear properties of the compound reinforced by the resultant pulps were simply investigated.展开更多
The relationship between property and structure of poly( p-phenylene terephthalamide)( PPTA) was investigated for the purpose of obtaining products with better performance. PPTA fiber subjected to heat treatment under...The relationship between property and structure of poly( p-phenylene terephthalamide)( PPTA) was investigated for the purpose of obtaining products with better performance. PPTA fiber subjected to heat treatment under different conditions was intensively studied. Simultaneous wide-angle X-ray diffraction( WAXD) technique was introduced to study the changes of crystal structure. It was found that the tensile modulus was strongly sensitive to the levels of temperature and tension. The structure parameters including crystal size and crystal orientation after heat treatment evolve similarly to the tensile modulus,indicating a direct structure-property relationship. The lattic c-dimension increases after heat treatment and is greatly affected by the tension. An optimal temperature can be found around 400 ℃,where big change can happen in the crystal structure due to α-relaxation in the crystal region as supported in dynamic mechanical analysis( DMA).展开更多
The preparation of PPy/PPTA conductive composite films by electrochemical method is presented.The first step is to cast a thin layer of poly (p-phenylene-terephthalamide) (PPTA) on a slice of Pt working electrode. The...The preparation of PPy/PPTA conductive composite films by electrochemical method is presented.The first step is to cast a thin layer of poly (p-phenylene-terephthalamide) (PPTA) on a slice of Pt working electrode. The second step is to electrochemically polymerize pyrrole on the PPTA/Pt working electrode. Both of the electrical conductivity and the mechanical properties of the PPy/PPTA composite film are better than those of the pure PPy film, and the film has excellent flexibility at low temperature, even in liquid nitrogen.The SEM picture of the cross-section of PPy,/PPTA composite film showed that the two components were well mixed.Cyclic voltammograms of PPy,/PPTA film in aqueous solution showed that the conductive films could be reduced and reoxidized.展开更多
The potyelectrolyte of propane sulfonate(PS) grafted PPTA copolymers——PPTA-PS, PPTA[O]-PS, PPTA[C]-PS were prepared and used as electrolyte in the process of electrochemical polymerization of pyrrole to form the mol...The potyelectrolyte of propane sulfonate(PS) grafted PPTA copolymers——PPTA-PS, PPTA[O]-PS, PPTA[C]-PS were prepared and used as electrolyte in the process of electrochemical polymerization of pyrrole to form the molecular composite polypyrrole (PPY)/Polyelectrolyte.The preparation and liquid crystalline property of three kinds of polyelectrolyte, the electrical conductivity, mechanical properties, SEM and thermoproperties of PPY/polyelectrolyte are presented in detail.展开更多
The kinetics of mesophase formation of a lyotropic aromatic polyamide from isotropic state has been studied by means of depolarized light intensity. Avrami type analysis of the data gives an exponent close to 1, which...The kinetics of mesophase formation of a lyotropic aromatic polyamide from isotropic state has been studied by means of depolarized light intensity. Avrami type analysis of the data gives an exponent close to 1, which suggests the nucleation followed by one-dimensional growth. No influence of blending flexible chain from nylon 6 to the aromatic polyamide on the kinetics of mesophase formation was observed.展开更多
文摘Poly(p-phenylene terephthalamide)(PPTA)pulp was prepared by polycondensation of the p-phenylene diamine(PPDA)with terephthaloyl chloride(TPC)in the completely anhydrous solvent system of N-methyl pyrrolidone(NMP)having calcium chloride,in the presence of poly(vinyl pyrrolidone)(PVP)having a viscosity average molecular weight lower than 40 000.It was confirmed that the polycondensation could be accelerated,the inherent viscosity of the polymer could be increased,and the polymers could be fibrillated more easily by the addition of the PVP.FTIR and X-ray spectra proved that PVP had not combined into molecular chains of the resultant PPTA pulps.The morphology of the resultant pulps,the effect of viscosity average molecular weight,amount and adding mode of PVP on inherent viscosity,specific surface area,and mean length of the resultant pulps were discussed in detail.And the friction and wear properties of the compound reinforced by the resultant pulps were simply investigated.
基金National Basic Research Program of China(973 Program)(No.2011CB606103)National High-Tech Research and Development Program of China(863 Program)(No.2012AA03212)the Fundamental Research Funds for the Central Universities,China(No.11D10625)
文摘The relationship between property and structure of poly( p-phenylene terephthalamide)( PPTA) was investigated for the purpose of obtaining products with better performance. PPTA fiber subjected to heat treatment under different conditions was intensively studied. Simultaneous wide-angle X-ray diffraction( WAXD) technique was introduced to study the changes of crystal structure. It was found that the tensile modulus was strongly sensitive to the levels of temperature and tension. The structure parameters including crystal size and crystal orientation after heat treatment evolve similarly to the tensile modulus,indicating a direct structure-property relationship. The lattic c-dimension increases after heat treatment and is greatly affected by the tension. An optimal temperature can be found around 400 ℃,where big change can happen in the crystal structure due to α-relaxation in the crystal region as supported in dynamic mechanical analysis( DMA).
文摘The preparation of PPy/PPTA conductive composite films by electrochemical method is presented.The first step is to cast a thin layer of poly (p-phenylene-terephthalamide) (PPTA) on a slice of Pt working electrode. The second step is to electrochemically polymerize pyrrole on the PPTA/Pt working electrode. Both of the electrical conductivity and the mechanical properties of the PPy/PPTA composite film are better than those of the pure PPy film, and the film has excellent flexibility at low temperature, even in liquid nitrogen.The SEM picture of the cross-section of PPy,/PPTA composite film showed that the two components were well mixed.Cyclic voltammograms of PPy,/PPTA film in aqueous solution showed that the conductive films could be reduced and reoxidized.
基金This work was supported by the National Natural Science Foundation of China
文摘The potyelectrolyte of propane sulfonate(PS) grafted PPTA copolymers——PPTA-PS, PPTA[O]-PS, PPTA[C]-PS were prepared and used as electrolyte in the process of electrochemical polymerization of pyrrole to form the molecular composite polypyrrole (PPY)/Polyelectrolyte.The preparation and liquid crystalline property of three kinds of polyelectrolyte, the electrical conductivity, mechanical properties, SEM and thermoproperties of PPY/polyelectrolyte are presented in detail.
基金This work was supported by Academia Sinica selected Research Program and National Natural Science Foundation of China
文摘The kinetics of mesophase formation of a lyotropic aromatic polyamide from isotropic state has been studied by means of depolarized light intensity. Avrami type analysis of the data gives an exponent close to 1, which suggests the nucleation followed by one-dimensional growth. No influence of blending flexible chain from nylon 6 to the aromatic polyamide on the kinetics of mesophase formation was observed.