The Synthesis and Characterization of High Molecular Weight Poly(phenylene sulfide/ether)

Poly（phenylene sulfide/ether） （PPSE） was synthesized from 4,4＇-dihydroxydiphenyl sulfide and 4,4＇-dichlorodiphenyl sulfide in solution by nucleophilic substitution reaction. The resulting polymer was characterized by viscosity measurement, elemental analysis, FT-IR, ^1H NMR, X-ray diffraction and thermal analysis. The results showed that the viscosities of the resulting polymer were above 0.68 dL/g, and the linear chain structure of product was confirmed. PPSE had the same reflex indices as poly（p-phenylene sulfide）, an orthorhombic crystalline with unit cell a=0.853, b=0.562, c=1.026nm. The melting temperature, glass transition temperature and initial decomposition temperature were found to be 228℃, 85℃ and 325℃, respectively. The product was soluble in common organic solvents such as NMP, N, N＇-dimethylformamide, N, N＇-dimethylacetamide and 1,2-dichloroethane.

Thermal Stability Improvement and Structural Change of Oil Gels Formed by Styrene-Butadiene-Styrene Triblock Copolymer Induced by Adding Poly(phenylene ether)

The thermal stability of oil gels formed by styrene-butadiene-styrene triblock copolymer (SBS) was improved by adding a small amount of poly(phenylene ether) (PPE), which has a higher glass transition temperature (Tg). In naphthenic oil which is a good solvent for the butadiene blocks, but a non-solvent for the styrene blocks and PPE, PPE was selectively included into styrene blocks in SBS, and induced the increase of the Tg of these blocks. The melting temperature determined by viscoelastic measurements and softening temperature of the gels were elevated by adding PPE, while no significant change was detected by adding polystyrene. The gel became opaque by adding PPE, and partially separated phases were observed by field emission scanning electron microscopy (FE-SEM). The dependence of the viscoelastic behavior on the PPE concentration can be explained by the structural change observed by FE-SEM.

Synthesis and characterization of new soluble poly(aryl ether nitrile)s containing phthalazinone moiety

A series of novel poly（aryl ether nitrile）s containing phthalazinone moiety were synthesized by the nucleophilic displacement reaction of bisphenol-like monomers （I） with 2,6-difluorobenzonitrile. The inherent viscosities ranged from 0.46 to 1.07 dL g^-1. The glass transition temperatures were in the range of 277-295℃, and the temperatures for 10% weight loss in nitrogen atmosphere were found between 495 and 527 ℃. The structures of these resultant polymers were confirmed by FT-IR and 1^H NMR. Moreover, the properties of poly（aryl ether nitrile）s including solubility and crystallinity were also studied.

Synthesis and characterization of quaternized poly(phthalazinone ether sulfone ketone)for anion-exchange membrane

Chloromethylated poly（phthalazinone ether sulfone ketone） （CMPPESK） was prepared from poly（phthalazinone ether sulfone ketone） （PPESK） using chloromethyl octyl ethers （CMOE） with lower toxicity as chloromethylated regent. CMPPESK was soluble in N-methyl-2-pyrrolidone （NMP）, N,N-dimethylacetamide （DMAc） and chloroform. Quaternized poly（phthalazinone ether sulfone ketone） （QAPPESK） was prepared from CMPPESK by quaternization. QAPPESK had excellent solvent resistance, which was only partly soluble in sulfuric acid （98%） and swollen in N,N-dimethylformamide （DMF）. The vanadium redox flow battery （V-RFB） using QAPPESK anion-exchange membrane had better performance with 88.3% of overall energy efficiency.

UV-induced Self-initiated Graft Polymerization of Acrylamide onto Poly(ether ether ketone)

Photo-grafting of hydrophilic monomer was used to enhance the hydrophilicity of poly（ether ether ketone） （PEEK） with the aim of extending its applications to biological fields. PEEK sheets were surface modified by grafting of acrylamide（AAm） with ultraviolet（UV） irradiation in the presence or absence of benzophenone（BP）. The effects of BP, irradiation time and monomer concentration on the surface wettability of PEEK were investigated. Characteriza tion of modified PEEK using scanning electron microscopy（SEM）, energy-disperse spectrometer（EDS） and water contact angle measurements shows that AAm was successfully grafted on PEEK surface both in presence and absence of BP. With the increase in irradiation time and monomer concentration, contact angles decrease to as low as 30°, demonstrating a significant improvement of surface hydrophilicity. In agreement with the decrease in contact angle, under identical conditions, the nitrogen concentration increases, suggesting the increase in grafting degree of the grafting polymerization. This investigation demonstrates a self-initiation of PEEK due to its BP-like structure in the backbone of the polymer. Though the graft polymerization proceeds more readily in the presence of BP, the self-initiated graft polymerization is clearly observed.

Synthesis and Adsorption Property of Two Polymeric Adsorbents with Pendent Ether Bonds

Two polymeric adsorbents, poly(methyl p-vinylbenzyl ether) and poly(phenyl p-vinylbenzyl ether), were synthesized from chloromethylated polystyrene. Their adsorption property for phenol in hexane solution was investigated. The results showed that the two adsorbents adsorb phenol from hexane solution through hydrogen-bonding and π-π stacking interaction.

INFLUENCE OF TRACES OF WATER ON THE SYNTHESIS AND ELECTROLUMINESCENCE PROPERTIES OF POLY(2-METHOXY, 5- (2' -ETHYLHEXYL OXY)- 1, 4-PHENYLENE VINYLENE)

It was found that traces of water in the reaction medium would result in a great increase of gel and a decrease of Molecular weight of the poly(2-methoxy,5-(2'-ethylhexyloxy)-1,4-phenylene vinylene) during the polymerization, which ultimately led to inferior film qualities and device properties. The device (ITO/PEDOT/MEH-PPV/Ba/Al) with MEH-PPV prepared under dry conditions has an external quantum efficiency of above 2.0%.

Synthesis of Novel Poly(aryl ether amide)s Containing the Phthalazinone Moiety

Two novel heterocyclic diamine monomers: 1,2-dihydro-2-(4-aminophenyl)-4-[4-(4-aminophenoxy)phenyl] (2H)phthalazin-1-one and 1,2-dihydro-2-(4-aminophenyl)-4-[4-(4-aminophenoxy)-3,5-dimethylphenyl](2H)phthalazin-1-one were successfully synthesized from readily available heterocyclic bisphenol-like monomers in two steps in high yield. A series of novel poly(aryl ether amide)s containing the phthalazinone moiety were successfully prepared by the direct polymerization of the novel diamines and aromatic dicarboxylic acids using triphenyl phosphite and pyridine as condensing agents.

Tetra-alkylsulfonate functionalized poly(aryl ether) membranes with nanosized hydrophilic channels for efficient proton conduction

The microstructure of polymer electrolyte membranes plays a key role in ion conductivity and water transport.Herein,fluorinated poly(aryl ether)s with tetra-alkylsulfonate side chains(SFPAEs)have been successfully synthesized from the copolymerization of a newly developed tetra-allyl-containing bisphenol(TABP)monomer,followed by the thiol-ene addition with sodium 3-mercapto-1-propanesulfonate to attach the ionic groups at the end of the flexible chains.Being the first of its kind,the densely distributed and lengthy alkylsulfonate group possesses the benefit of ease to self-assemble into hydrophilic domains during membrane preparation via solution casting.Indeed,the TEM characterizations revealed that distinct hydrophilic channels of 1-2 nm width had been formed,much larger than those of a home-made control sample where only di-alkylsulfonate side chains were attached.The SFPAE-4-45 with an IECw of 2.0 mmol g^-1 exhibited an enhanced proton conductivity of 143.7 m S cm^-1 at room temperature,which was superior to that of Nafion 212(91.0 m S cm^-1).Furthermore,the oxidative stabilities of SFPAEs were significantly higher than those of non-fluorinated analogs in literature.This study offered a new route to engineering the pendent structure of ionomers for well-defined microscopic morphologies.

Synthesis and characterization of novel poly(aryl ether sulfone ketone)s containing phthalazinone and biphenyl moieties

A novel series of poly（aryl ether sulfone ketone）s （PPESKs） containing phthalazinone and biphenyl moieties were prepared by two-step nucleophilic polycondensation reaction. The ^-Mw values of these copolymers were between 38,330 and 67,900. The glass transition temperatures （Tg） and 5% decomposition temperatures were ranged in 253-269 ℃ and 488-500 ℃, respectively, The structures of these copolymers were confirmed by FT-IR and ^1H NMR. Moreover, all the resultant copolymers were amorphous determined by wide angle X-ray diffraction （WAXD）.

Immobilization of Bovine Serum Albumin on Poly(ether ether ketone) for Surface Biocompatibility Improvement

UV-induced graft polymerization of acrylic acid（AA） on poly（ether ether ketone）（PEEK） films was carried out to introduce ―COOH for the subsequent immobilization of bovine serum albumin（BSA）.BSA was introduced on PEEK surface based on the condensation reaction between ―NH 2 and ―COOH.The modified surface（PEEK-BSA） was characterized by energy-disperse spectrometry（EDS）,X-ray photoelectron spectroscopy（XPS）,water contact angle measurement and UV spectrum analysis.The contact angle was found to decrease from 104° for the virgin PEEK films to 63° for the BSA-immobilized PEEK films,demonstrating a significant improvement of surface hydrophilicity.Moreover,the appearance of nitrogen on PEEK film confirmed by XPS and EDS indicates the immobilization of BSA on PEEK surface.

Synthesis of Poly(phthalazinone ether ketone) Containing Sodium Sulfonate Groups via Direct Polymerization

1, 2-Diliydro-4-(4-hydroxyphenyl)(2H)phthalazin-1-one(DHPZ) was sulfonated in concentrated Sulfuric acid. Poly(phthalazinone ether ketone) containing pendant sodium sulfonate group was synthesized from sulfonated and pure 1,2-dihydro-4-(4-hydroxyphenyl)(2H)phthalazin-1-one, and 4,4'-difluorodiphenylketone. The sulfonated monomer and sulfonated polymer were characterized with FT-IR and H-1-NMR.

Allyl-containing Poly(aryl ether sulfone): Synthesis and Crosslinking

A novel type of crosslinkable poly（aryl ether sulfone）（PAES） bearing an allyl pendant（PES-OAllyl） was synthesized by a grafting reaction of hydrophenyl-containing PAES（PES-OH） and allyl bromide. PES-OH was prepared by a demethylation reaction of a methoxyphenylated PAES（PES-OCH3） in the presence of pyridine/hydrochlo- ride. The PES-OCH3 was synthesized by an aromatic nucleophilic substitution of bis（4-chlorophenyl）sulfone and （p-methoxy）phenylhydroquinone. Both DSC and solubility investigation were used to study the crosslinking behavior of PES-OAllyl. After heat treatment, the glass transition temperature（Tg） value of PES-OAllyl sharply increased from 165 ℃ to 227 ℃. Meanwhile, PES-OAllyl changed from a soluble polymer to an insoluble thermoset. In addition, TGA（thermogravimetric analysis） result suggests that the thermal stability of the crosslinked product was improved. All the data prove that the crosslinked PES-OAllyl could be a potential solvent-resistance high-performance material.

Synthesis and Thermal Crosslinking Behavior of Poly(aryl ether ketone)s Containing 1,4-Naphthalene Moieties

A new monomer, 1,4-bis(4-fluorobenzoyl) naphthalene(compound 2) was synthesized via a two-step reaction. 1,4-Naphthalenedicarboxylic acid chloride(compound 1) was prepared by using the acyl chlorization reaction of 1,4-naphthalenedicarboxylic acid with thionyl chloride. The Friedel-Crafts acylation of compound 1 with fluorobenzene afforded compound 2 in a 80% yield. The polycondensation of compound 2 with various bisphenols in tetramethylene sulfone(TMS) in the presence of excess potassium carbonate as a condensation reagent was carried out at 210 ℃ to quantitatively afford the corresponding poly(aryl ether ketone)s(compounds 3_8) containing 1,4-naphthalene moieties. Thermal analyses showed that the polymers have T g values ranging from 496 to 500 K and are thermally stable in air with initial mass loss above 500 ℃. These novel polymers exhibited an excellent solubility in organic solvents including NMP, DMAc, and chloroform, etc. In addition, the glass transition temperatures of these polymers increased and the polymers became insoluble in chloroform after treated at 260 ℃, indicating the occurrence of a thermal crosslinking reaction.

Synthesis and Characterization of Poly(ether imide)s Containing m-Methyl and Phthalazinone Moieties

Three novel poly(ether imide)s were synthesized by one-step solution polymerization from 2-(3, 4-dicarboxyl-N-phenyl)-4-(3, 4-dicarboxyl-phenoxyl-4-(2-methyl)-phenyl)-2, 3- phthal-azin-1-one dianhydride and three amines, and characterized. The polymers show good solubility and thermal properties.

Characterization and tribological investigation of self-assembled trimethoxysilyl-functionalized poly(phthalazinone ether ketone)thin films on glass substrates

Trimethoxysilyl-functionalized PPEK（PKGS） films had been designed to serve as wear resistant coatings for silicon surfaces. These surface films were formed by a dip-coating technique applied to self-assembled monolayers（SAMs）.The formation and wetting behavior of PKGS films were characterized by means of contact angle measurement.The friction coefficient of the film prepared is very low（about 0.1）,and the anti-wear behavior is good,with a lack of failure after sliding over 1800 s.

SYNTHESIS AND PROPERTIES OF SULFONATED POLY(ARYLENE ETHER) CONTAINING TRIPHENYL METHANE MOIETIES FROM ISOCYNATE MASKED BISPHENOL

A novel sulfonated poly（arylene ether） containing triphenylmethane moieties was synthesized by the sulfonation of a designed parent polymer using chlorosulfonic acid as sulfonation agent. The sulfonation took place at the para position of the pendant phenyl rings because of the specially designed parent polymer. The position and degree of sulfonation were characterized by ^1H-NMR and elemental analysis. The sulfonated polymers are highly soluble in common organic solvents, such as dimethylsulfoxide, N,N＇-dimethylacetamide, dimethylformamide, ethylene glycol monomethyl ether, and can be readily cast into tough and smooth films from solutions. The films showed good thermal and hydrolysis stabilities. Moreover, Fenton＇s reagent test revealed that the films exhibited superior stability to oxidation. The proton conductivities of the films were comparable with Nation 117 under same conditions. The membrane electrode assembly （MEA） prepared with the asmade film （706 EW, 100 μm dry thickness） shows better cell performance than Nation 115-MEA in the whole current density range.

SYNTHESIS AND CHARACTERIZATION OF POLY(ARYL ETHER KETONE)CONTAINING BIPHENYLPHTHALAZINONE MOIETY

A new poly(aryl ether ketone) containing biphenylphthalazinone moiety was prepared by the reaction of 4-(4-hydroxybiphenyl) phthalazine-1-one with 4, 4'-difluorobenzophenone. The monomer and the polymer were characterized by FT-IR and H-1-NMR. Some properties of this polymer were described.

NOVEL HYPERBRANCHED POLY(PHENYLENE OXIDE)S WITH PHENOLIC TERMINAL GROUPS: EFFECTS OF REACTION TIME AND CORE MOLECULES ON THE MOLECULAR WEIGHT AND POLYDISPERSITY

A novel hyperbranched poly（phenylene oxide） （HPPO） with phenolic terminal groups was prepared from 4-bromo-4＇,4＂-dihydroxytriphenylmethane as AB2 monomer in dimethylsulfoxide （DMSO） via a modified Ullmann reaction. The molecular weight and polydispersity （PD） of the resulting polymers increased with increasing reaction time. In the presence of core molecules （bisphenol A and 1,3,5-trihydroxybenzene）, which have the similar molecular backbones to the reactive monomer, the molecular weight could be controlled by varying the core-to-monomer ratio. Incorporation of a very small amount of core molecules could lead to a higher molecular weight as compared with that without the addition of core molecules. However, when the core content reached certain extent, the molecular weight would decrease with the further increase in the core content. A new similar behavior of control over the PD was also obtained. The resulting polymers were characterized by ^1H-NMR, ^13C-NMR, FT-IR, and GPC.

Synthesis and characterization of poly(phthalazinone ether nitrile) (PPEN)-polydimethylsiloxane (PDMS) block copolymers

Block copolymers with different backbone compositions have been prepared by the condensation of dimethylamino terminated poly（dimethylsiloxane） （PDMS） and hydroquinone terminated poly（phthalazinone ether nitrile） （PPEN） in the presence of chlorobenzcne/N-methyl pyrrolidone （NMP） as solvents. The products were characterized by FTIR, ^1H NMR and gel permeation chromatography. Differential scanning calorimetry analysis indicated that the block copolymers showed separated microphase.