Chloromethylated poly（phthalazinone ether sulfone ketone） （CMPPESK） was prepared from poly（phthalazinone ether sulfone ketone） （PPESK） using chloromethyl octyl ethers （CMOE） with lower toxicity as chlorometh...Chloromethylated poly（phthalazinone ether sulfone ketone） （CMPPESK） was prepared from poly（phthalazinone ether sulfone ketone） （PPESK） using chloromethyl octyl ethers （CMOE） with lower toxicity as chloromethylated regent. CMPPESK was soluble in N-methyl-2-pyrrolidone （NMP）, N,N-dimethylacetamide （DMAc） and chloroform. Quaternized poly（phthalazinone ether sulfone ketone） （QAPPESK） was prepared from CMPPESK by quaternization. QAPPESK had excellent solvent resistance, which was only partly soluble in sulfuric acid （98%） and swollen in N,N-dimethylformamide （DMF）. The vanadium redox flow battery （V-RFB） using QAPPESK anion-exchange membrane had better performance with 88.3% of overall energy efficiency.展开更多
A novel series of poly（aryl ether sulfone ketone）s （PPESKs） containing phthalazinone and biphenyl moieties were prepared by two-step nucleophilic polycondensation reaction. The ^-Mw values of these copolymers were...A novel series of poly（aryl ether sulfone ketone）s （PPESKs） containing phthalazinone and biphenyl moieties were prepared by two-step nucleophilic polycondensation reaction. The ^-Mw values of these copolymers were between 38,330 and 67,900. The glass transition temperatures （Tg） and 5% decomposition temperatures were ranged in 253-269 ℃ and 488-500 ℃, respectively, The structures of these copolymers were confirmed by FT-IR and ^1H NMR. Moreover, all the resultant copolymers were amorphous determined by wide angle X-ray diffraction （WAXD）.展开更多
Trimethoxysilyl-functionalized PPEK（PKGS） films had been designed to serve as wear resistant coatings for silicon surfaces. These surface films were formed by a dip-coating technique applied to self-assembled monola...Trimethoxysilyl-functionalized PPEK（PKGS） films had been designed to serve as wear resistant coatings for silicon surfaces. These surface films were formed by a dip-coating technique applied to self-assembled monolayers（SAMs）.The formation and wetting behavior of PKGS films were characterized by means of contact angle measurement.The friction coefficient of the film prepared is very low（about 0.1）,and the anti-wear behavior is good,with a lack of failure after sliding over 1800 s.展开更多
A kind of novel heat-resistant, high performance engineering thermoplastic phthalazinone poly(aryl ether sulfone ketone) (PPESK) containing a carboxyl group in its side chain was prepared by the nucleophilic displacem...A kind of novel heat-resistant, high performance engineering thermoplastic phthalazinone poly(aryl ether sulfone ketone) (PPESK) containing a carboxyl group in its side chain was prepared by the nucleophilic displacement reaction of 4-(4-hydroxylphenyl)- 1 (2H)-phthalazinone with di(4-chlorophenyl) sulfone, 4,4'-difluoro-benzophenone and phenolphthalin in sulfolane in the presence of K2CO3 to produce high molecular weight polymers which can be dissolved in some polar solvents such as chloroform and nitrobenzene at room temperature and can be easily cast into flexible, yellowish and transparent films. PPESK is an amorphous polymer having a decomposition temperature above 400degreesC, which indicates that it has high thermal stability. At the same time, the thermal properties of PPESKs with dicyandiamide (DICY) as curing agent indicated that the heat-resistance properties of the PPESKs are improved after curing. The apparent activation energy (A-E) of the cross-linking reaction and the reaction order (n) of PPESK/DICY were found to be 52.2 kJ/mol and ca. 1.0, respectively. Therefore, the cross-linking reaction is approximately a first order reaction.展开更多
A novel poly (ether sulfone ketone) containing the phthalazinone moiety was prepared by the reaction of 4-)4-hydroxyphenyl) (2H) phthalazin-1-one with activated dichloro-monomers. The polymer was characterized by FT-I...A novel poly (ether sulfone ketone) containing the phthalazinone moiety was prepared by the reaction of 4-)4-hydroxyphenyl) (2H) phthalazin-1-one with activated dichloro-monomers. The polymer was characterized by FT-IR, H-1-NMR, DSC, TGA and X-ray diffraction.展开更多
1, 2-Diliydro-4-(4-hydroxyphenyl)(2H)phthalazin-1-one(DHPZ) was sulfonated in concentrated Sulfuric acid. Poly(phthalazinone ether ketone) containing pendant sodium sulfonate group was synthesized from sulfonated and ...1, 2-Diliydro-4-(4-hydroxyphenyl)(2H)phthalazin-1-one(DHPZ) was sulfonated in concentrated Sulfuric acid. Poly(phthalazinone ether ketone) containing pendant sodium sulfonate group was synthesized from sulfonated and pure 1,2-dihydro-4-(4-hydroxyphenyl)(2H)phthalazin-1-one, and 4,4'-difluorodiphenylketone. The sulfonated monomer and sulfonated polymer were characterized with FT-IR and H-1-NMR.展开更多
A sulfonated poly（ether ether ketone） （SPEEK） membrane with fairly high degree of sulfonation （DS） swells excessively and even dissolves at high temperature. To solve these problems, sulfonated phenolphthalein p...A sulfonated poly（ether ether ketone） （SPEEK） membrane with fairly high degree of sulfonation （DS） swells excessively and even dissolves at high temperature. To solve these problems, sulfonated phenolphthalein poly（ether sulfone） （SPES-C, DS= 53.7%） is blended with the SPEEK matrix （DS= 55.1%, 61.7%） to prepare SPEEKJSPES-C blend membrane. The decrease in swelling degree and methanol permeability of the membrane is dose-dependent. Pure SPEEK （DS = 61.7%） membrane dissolves completely in water at 70℃, whereas the swelling degree of the SPEEK （DS = 61.7%）/SPES-C （40%, by mass） membrane is 29.7% at 80℃. From room temperature to 80℃, the methanol permeability of all SPEEK （DS = 55.1%）/SPES-C blend membranes is about one order of magnitude lower than that of Nafion 115. At higher temperature, the addition of SPES-C polymer increases the dimensional stability and greater proton conductivity can be achieved. The SPEEK （DS = 55.1%）/SPES-C （40%, by mass） membrane can withstand temperatures up to 150℃. The proton conductivity of SPEEK （DS = 55.1%）/SPES-C （30%, by mass） membrane approaches 0.16 S·cm^-1, matching that of Nafion 115 at 140℃ and 100% RH, while pure SPEEK （DS = 55.1%） membrane dissolves at 90℃. The SPEEK/SPES-C blend membranes are promising for use in direct methanol fuel cells because of their good dimensional stability, high proton conductivity, and low methanol permeability.展开更多
A series of Poly（arly ether sulfone ether ketone）s containing pendant methyl groups were synthesized by the reaction of 4,4＇-[sulfonylbis （1,4-phenylene）dioxy] dibenzoyl chloride （SODBC） with 4,4＇- diphenoxy d...A series of Poly（arly ether sulfone ether ketone）s containing pendant methyl groups were synthesized by the reaction of 4,4＇-[sulfonylbis （1,4-phenylene）dioxy] dibenzoyl chloride （SODBC） with 4,4＇- diphenoxy diphenylsulfone （DPODPS）, 4,4＇- di（2-methylphenoxy） diphenylsulfone （o-Me-DPODPS）, 4,4＇- di（3-methylphenoxy） diphenylsulfone （m-Me-DPODPS）, 4,4＇- di （2,6-bimethylphenoxy） biphenylsulfone（o-Me2-DPODPS） respectively, in a mixture of 1,2-dichloroethane （DCE） and N-methylpyrrolidone （NMP）. These reactions were catalyzed by anhydrous aluminum chloride （AlCl）. The characteristic of copolymers were studied by means of advanced analytical techniques such as FT-IR,1H-NMR, DSC, TGA and WAXD. The results show glass transition temperature （Tg） in the range of 193-206℃, thermally stable in excess of 434℃ and excellent solubility in polar solvents. Methyl-substituted Poly（aryl ether sulfone ketone）s had higher glass transition temperatures, lower initial decomposition temperatures than the unsubstituted ones.展开更多
A novel alkoxysilyl-functionalized poly(phthalazinone ether ketone) (PPEK) was prepared for the boundary lubricant application in micro-electro-mechanical system (MEMS). The synthesis of functionalized PPEK was starte...A novel alkoxysilyl-functionalized poly(phthalazinone ether ketone) (PPEK) was prepared for the boundary lubricant application in micro-electro-mechanical system (MEMS). The synthesis of functionalized PPEK was started from the hydroxylation of PPEK, then following with the corresponding ring-opening reaction of 3-glycidoxypropyltrimethoxysilane (GPTMS). The structures of the functional PPEK were confirmed by FTIR, 1H NMR, 29Si NMR, and UV–vis spectrum.展开更多
A sulfonated poly（ether ether ketone） （SPEEK） membrane with a fairly high degree of sulfonation （DS） can swell excessively and even dissolve at high temperature. To solve these problems, insolvable functionalize...A sulfonated poly（ether ether ketone） （SPEEK） membrane with a fairly high degree of sulfonation （DS） can swell excessively and even dissolve at high temperature. To solve these problems, insolvable functionalized silica powder with sulfonic acid groups （SiOx-S） was added into the SPEEK matrix （DS = 55.1%） to prepare SPEEK/ SiOx-S composite membranes. The decrease in both the swelling degree and the methanol permeability of the membranes was a dose-dependent result of addition of the SiOx-S powder. Pure SPEEK membrane swelled 52.6% at 80℃, whereas the SPEEK/SiOx-S （15%, by mass） membrane swelled only 27.3% at the same temperature. From room temperature to 80℃, all SPEEK/SPEEK/SiOx-S composite membranes had methanol permeability of about one order of magnitude lower than that ofNafion115. Compared with pure SPEEK membranes, the addition of the SiOx-S powder not only leads to higher proton conductivity, but also increases the dimensional stability at higher temperatures, and greater proton conductivity can be achieved at higher temperature. The SPEEK/SiO4-S （20%, by mass） membrane could withstand temperature up to 145℃, at which in 100% relative humidity （RH） its proton conductivity exceeded slightly that of Nafion 1 15 membrane and reached 0.17 S·cm^-1, while pure SPEEK membrane dissolved at 90℃. The SPEEK/SiOx-S composite membranes are promising for use in direct methanol fuel cells because of their good dimensional stability, high proton conductivity, and low methanol permeability.展开更多
Polyoxometalates(POMs)are classified as solid superacids which can exhibit notable proton conductivity,making them a promising functional inorganic filler for enhancing the proton conductivity of proton exchange membr...Polyoxometalates(POMs)are classified as solid superacids which can exhibit notable proton conductivity,making them a promising functional inorganic filler for enhancing the proton conductivity of proton exchange membranes(PEMs).In this study,a series of hybrid membranes were obtained by molecular-level hybridization of Weakley-type POM Na_(7)H_(2)LaW_(10)O_(36)(LaW_(10))clusters into sulfonated poly(aryl ether ketone sulfone)(SPAEKS).All hybrid membranes exhibited greater proton conductivity than the pristine membrane in the 30–80℃temperature range.When the doping amount of LaW 10 reached 7 wt.%,the proton conductivity of M-LaW 10^(-7)achieved 64 mS·cm^(−1)at 80℃.Lanthanide ions'high coordination number property and variable coordination environment can aid to attract more water molecules from the environment.LaW 10 and these bound water can construct denser hydrogen bonds with–SO_(3)H of SPAEKS.These intensive hydrogen bonds will facilitate the constitution of more continuous proton transport channels,and improve the proton conductivity of the hybrid membrane.This work off ers a fresh approach to using POMs containing rare-earth components in PEMs.展开更多
A ternary hybrid membrane architecture consisting of sulfonated fluorinated multi-block copolymer （SFMC）, sulfonated （poly ether ether ketone） （SPEEK） and I or 5 wt% graphene oxide （GO） was fabricated through ...A ternary hybrid membrane architecture consisting of sulfonated fluorinated multi-block copolymer （SFMC）, sulfonated （poly ether ether ketone） （SPEEK） and I or 5 wt% graphene oxide （GO） was fabricated through a facile solution casting approach. The simple, but effective monomer sulfonation was performed for SFMC to create compact and rigid hydrophobic backbone structures, while conventional random sulfonation was carried-out for SPEEK. Hydrophilic-hydrophobic-hydrophilic structure of SFMC enhances the compatibility with SPEEK and GO and allows for an unprecedented approach to alter me- chanical strength and proton conductivity of ternary hybrid membrane, as verified from universal test machine （UTM） curves and alternating current （AC） impedance plots. The impact of GO integration on the morphology and roughness of hybrid membrane was scrutinized using field emission scanning electron microscope （FE-SEM） and atomic force microscope （AFM）. Ternary hybrid showed uniform intercalation of GO nanosheets throughout the entire surface of membrane with an increased surface roughness of 8.91 nm. The constructed ternary hybrid membrane revealed excellent water absorption, ion exchange capacity and gas barrier properties, while retaining reasonable dimensional stability. The well-optimized ternary hybrid membrane containing 5 wt% GO revealed a maximum proton conductivity of 111.9 mS/cm, which is higher by a factor of two-fold with respect to that of bare SFMC membrane. The maximum PEMFC power density of 528.07mW/cm2 was yielded by ternary hybrid membrane at a load current density of 1321.1 mA/cm2 when operating the cell at 70 ℃ under 100% relative humidity （RH）. In comparison, a maximum power density of only 182.06 mW/cm2 was exhibited by the bare SFMC membrane at a load current density of 455.56 mA/cm2 under same operating conditions.展开更多
Prolonged hydrothermal treatment for sulfonated poly(ether ether ketone) membranes induces mechanical degradation and developing hydrophilic-hydrophobic phase separation, simultaneously. The enhanced phase separation ...Prolonged hydrothermal treatment for sulfonated poly(ether ether ketone) membranes induces mechanical degradation and developing hydrophilic-hydrophobic phase separation, simultaneously. The enhanced phase separation provides incremental proton conductivity to the membranes, whereas mechanical degradation drastically reduces device stability. On this basis, we describe here the effects of two different ex situ aging processes on sulfonated poly(ether ether ketone) membranes: hydrationdehydration cycling and prolonged hydrothermal treatment. Both aged membranes exhibited enhanced phase separation under the hydrated conditions, as characterized by small angle X-ray scattering.However, when the aged membranes were dried again, the nanostructure of the membranes aged via the hydration-dehydration cycling was recoverable, whereas that of the membranes aged via prolonged hydrothermal treatment was irreversible. Furthermore, the two differently aged membranes showed clear differences in thermal, mechanical, and electrochemical properties. Finally, we implemented both aged membranes in fuel cell application. The sample aged via hydration-dehydration cycling maintained its improved cell performance, whereas the sample aged via hydrothermal treatment showed drastically reduced cell performance after durability test for 50 h.展开更多
A new interfacial polymerization （IP） procedure is developed in order to synthesize polypiperazine-amide thin-film membrane on the inner surface of poly（phthalazinone ether sulfone ketone） （PPESK） hollow fiber u...A new interfacial polymerization （IP） procedure is developed in order to synthesize polypiperazine-amide thin-film membrane on the inner surface of poly（phthalazinone ether sulfone ketone） （PPESK） hollow fiber ultrafiltration （UF） membrane. A hollow fiber composite membrane with good performance was prepared and studied by PT-IR and scanning electron microscopy.展开更多
基金partly financed by the Major State Basic Research Development Program of China(No.2003 CB615700)the National Natural Science Foundation of China(No.20604005).
文摘Chloromethylated poly（phthalazinone ether sulfone ketone） （CMPPESK） was prepared from poly（phthalazinone ether sulfone ketone） （PPESK） using chloromethyl octyl ethers （CMOE） with lower toxicity as chloromethylated regent. CMPPESK was soluble in N-methyl-2-pyrrolidone （NMP）, N,N-dimethylacetamide （DMAc） and chloroform. Quaternized poly（phthalazinone ether sulfone ketone） （QAPPESK） was prepared from CMPPESK by quaternization. QAPPESK had excellent solvent resistance, which was only partly soluble in sulfuric acid （98%） and swollen in N,N-dimethylformamide （DMF）. The vanadium redox flow battery （V-RFB） using QAPPESK anion-exchange membrane had better performance with 88.3% of overall energy efficiency.
文摘A novel series of poly（aryl ether sulfone ketone）s （PPESKs） containing phthalazinone and biphenyl moieties were prepared by two-step nucleophilic polycondensation reaction. The ^-Mw values of these copolymers were between 38,330 and 67,900. The glass transition temperatures （Tg） and 5% decomposition temperatures were ranged in 253-269 ℃ and 488-500 ℃, respectively, The structures of these copolymers were confirmed by FT-IR and ^1H NMR. Moreover, all the resultant copolymers were amorphous determined by wide angle X-ray diffraction （WAXD）.
基金This project was financially supported by National High Technology and Development Program of China(863 Program)(No.2003AA33G030)
文摘Trimethoxysilyl-functionalized PPEK（PKGS） films had been designed to serve as wear resistant coatings for silicon surfaces. These surface films were formed by a dip-coating technique applied to self-assembled monolayers（SAMs）.The formation and wetting behavior of PKGS films were characterized by means of contact angle measurement.The friction coefficient of the film prepared is very low（about 0.1）,and the anti-wear behavior is good,with a lack of failure after sliding over 1800 s.
基金This project was supported by the National Ninth Five-Year-Plan Key Project "The pilot-scale production and the applied development of polyaryl ether concerning phthalazinone moiety" (No. 97-564-01-07).
文摘A kind of novel heat-resistant, high performance engineering thermoplastic phthalazinone poly(aryl ether sulfone ketone) (PPESK) containing a carboxyl group in its side chain was prepared by the nucleophilic displacement reaction of 4-(4-hydroxylphenyl)- 1 (2H)-phthalazinone with di(4-chlorophenyl) sulfone, 4,4'-difluoro-benzophenone and phenolphthalin in sulfolane in the presence of K2CO3 to produce high molecular weight polymers which can be dissolved in some polar solvents such as chloroform and nitrobenzene at room temperature and can be easily cast into flexible, yellowish and transparent films. PPESK is an amorphous polymer having a decomposition temperature above 400degreesC, which indicates that it has high thermal stability. At the same time, the thermal properties of PPESKs with dicyandiamide (DICY) as curing agent indicated that the heat-resistance properties of the PPESKs are improved after curing. The apparent activation energy (A-E) of the cross-linking reaction and the reaction order (n) of PPESK/DICY were found to be 52.2 kJ/mol and ca. 1.0, respectively. Therefore, the cross-linking reaction is approximately a first order reaction.
文摘A novel poly (ether sulfone ketone) containing the phthalazinone moiety was prepared by the reaction of 4-)4-hydroxyphenyl) (2H) phthalazin-1-one with activated dichloro-monomers. The polymer was characterized by FT-IR, H-1-NMR, DSC, TGA and X-ray diffraction.
基金the National Natural Science Foundation of China for financial support.
文摘1, 2-Diliydro-4-(4-hydroxyphenyl)(2H)phthalazin-1-one(DHPZ) was sulfonated in concentrated Sulfuric acid. Poly(phthalazinone ether ketone) containing pendant sodium sulfonate group was synthesized from sulfonated and pure 1,2-dihydro-4-(4-hydroxyphenyl)(2H)phthalazin-1-one, and 4,4'-difluorodiphenylketone. The sulfonated monomer and sulfonated polymer were characterized with FT-IR and H-1-NMR.
基金Supported by the State Key Development Program for Basic Research of China （2008CB617502）, the National Natural Science Foundation of China （20606025）, and Program for Changjiang Scholars and Innovative Research Team in University of China （IRT0641）.
文摘A sulfonated poly（ether ether ketone） （SPEEK） membrane with fairly high degree of sulfonation （DS） swells excessively and even dissolves at high temperature. To solve these problems, sulfonated phenolphthalein poly（ether sulfone） （SPES-C, DS= 53.7%） is blended with the SPEEK matrix （DS= 55.1%, 61.7%） to prepare SPEEKJSPES-C blend membrane. The decrease in swelling degree and methanol permeability of the membrane is dose-dependent. Pure SPEEK （DS = 61.7%） membrane dissolves completely in water at 70℃, whereas the swelling degree of the SPEEK （DS = 61.7%）/SPES-C （40%, by mass） membrane is 29.7% at 80℃. From room temperature to 80℃, the methanol permeability of all SPEEK （DS = 55.1%）/SPES-C blend membranes is about one order of magnitude lower than that of Nafion 115. At higher temperature, the addition of SPES-C polymer increases the dimensional stability and greater proton conductivity can be achieved. The SPEEK （DS = 55.1%）/SPES-C （40%, by mass） membrane can withstand temperatures up to 150℃. The proton conductivity of SPEEK （DS = 55.1%）/SPES-C （30%, by mass） membrane approaches 0.16 S·cm^-1, matching that of Nafion 115 at 140℃ and 100% RH, while pure SPEEK （DS = 55.1%） membrane dissolves at 90℃. The SPEEK/SPES-C blend membranes are promising for use in direct methanol fuel cells because of their good dimensional stability, high proton conductivity, and low methanol permeability.
基金This work was supported by National Science Foundation of China （No. 20264001 ）, National Science Foundation of Jiangxi Province, Innovation Fund for Technology Based Firms of China （No. 06C26213601342）.
文摘A series of Poly（arly ether sulfone ether ketone）s containing pendant methyl groups were synthesized by the reaction of 4,4＇-[sulfonylbis （1,4-phenylene）dioxy] dibenzoyl chloride （SODBC） with 4,4＇- diphenoxy diphenylsulfone （DPODPS）, 4,4＇- di（2-methylphenoxy） diphenylsulfone （o-Me-DPODPS）, 4,4＇- di（3-methylphenoxy） diphenylsulfone （m-Me-DPODPS）, 4,4＇- di （2,6-bimethylphenoxy） biphenylsulfone（o-Me2-DPODPS） respectively, in a mixture of 1,2-dichloroethane （DCE） and N-methylpyrrolidone （NMP）. These reactions were catalyzed by anhydrous aluminum chloride （AlCl）. The characteristic of copolymers were studied by means of advanced analytical techniques such as FT-IR,1H-NMR, DSC, TGA and WAXD. The results show glass transition temperature （Tg） in the range of 193-206℃, thermally stable in excess of 434℃ and excellent solubility in polar solvents. Methyl-substituted Poly（aryl ether sulfone ketone）s had higher glass transition temperatures, lower initial decomposition temperatures than the unsubstituted ones.
文摘A novel alkoxysilyl-functionalized poly(phthalazinone ether ketone) (PPEK) was prepared for the boundary lubricant application in micro-electro-mechanical system (MEMS). The synthesis of functionalized PPEK was started from the hydroxylation of PPEK, then following with the corresponding ring-opening reaction of 3-glycidoxypropyltrimethoxysilane (GPTMS). The structures of the functional PPEK were confirmed by FTIR, 1H NMR, 29Si NMR, and UV–vis spectrum.
基金Supported by the State Key Development Program for Basic Research of China （2008CB617502）, the National Natural Science Foundation of China （20606025）, and Program for Changjiang Scholars and Innovative Research Team in University of China （IRT0641）.
文摘A sulfonated poly（ether ether ketone） （SPEEK） membrane with a fairly high degree of sulfonation （DS） can swell excessively and even dissolve at high temperature. To solve these problems, insolvable functionalized silica powder with sulfonic acid groups （SiOx-S） was added into the SPEEK matrix （DS = 55.1%） to prepare SPEEK/ SiOx-S composite membranes. The decrease in both the swelling degree and the methanol permeability of the membranes was a dose-dependent result of addition of the SiOx-S powder. Pure SPEEK membrane swelled 52.6% at 80℃, whereas the SPEEK/SiOx-S （15%, by mass） membrane swelled only 27.3% at the same temperature. From room temperature to 80℃, all SPEEK/SPEEK/SiOx-S composite membranes had methanol permeability of about one order of magnitude lower than that ofNafion115. Compared with pure SPEEK membranes, the addition of the SiOx-S powder not only leads to higher proton conductivity, but also increases the dimensional stability at higher temperatures, and greater proton conductivity can be achieved at higher temperature. The SPEEK/SiO4-S （20%, by mass） membrane could withstand temperature up to 145℃, at which in 100% relative humidity （RH） its proton conductivity exceeded slightly that of Nafion 1 15 membrane and reached 0.17 S·cm^-1, while pure SPEEK membrane dissolved at 90℃. The SPEEK/SiOx-S composite membranes are promising for use in direct methanol fuel cells because of their good dimensional stability, high proton conductivity, and low methanol permeability.
基金financially supported by the National Natural Science Foundation of China(No.22271022)the Natural Science Foundation of Jilin Province(No.YDZJ202201ZYTS342)supported by the China Scholarship Council(CSC No.201802335014).
文摘Polyoxometalates(POMs)are classified as solid superacids which can exhibit notable proton conductivity,making them a promising functional inorganic filler for enhancing the proton conductivity of proton exchange membranes(PEMs).In this study,a series of hybrid membranes were obtained by molecular-level hybridization of Weakley-type POM Na_(7)H_(2)LaW_(10)O_(36)(LaW_(10))clusters into sulfonated poly(aryl ether ketone sulfone)(SPAEKS).All hybrid membranes exhibited greater proton conductivity than the pristine membrane in the 30–80℃temperature range.When the doping amount of LaW 10 reached 7 wt.%,the proton conductivity of M-LaW 10^(-7)achieved 64 mS·cm^(−1)at 80℃.Lanthanide ions'high coordination number property and variable coordination environment can aid to attract more water molecules from the environment.LaW 10 and these bound water can construct denser hydrogen bonds with–SO_(3)H of SPAEKS.These intensive hydrogen bonds will facilitate the constitution of more continuous proton transport channels,and improve the proton conductivity of the hybrid membrane.This work off ers a fresh approach to using POMs containing rare-earth components in PEMs.
基金supported by the Korea Institute of Energy Technology Evaluation and Planning(KETEP)the Ministry of Trade,Industry&Energy(MOTIE)of the Republic of Korea(No.20164030201070)supported by Basic Science Research Program through the National Research Foundation of Korea(NRF)funded by the Ministry of Science,ICT and future Planning(NRF-2017R1A2B4005230)
文摘A ternary hybrid membrane architecture consisting of sulfonated fluorinated multi-block copolymer （SFMC）, sulfonated （poly ether ether ketone） （SPEEK） and I or 5 wt% graphene oxide （GO） was fabricated through a facile solution casting approach. The simple, but effective monomer sulfonation was performed for SFMC to create compact and rigid hydrophobic backbone structures, while conventional random sulfonation was carried-out for SPEEK. Hydrophilic-hydrophobic-hydrophilic structure of SFMC enhances the compatibility with SPEEK and GO and allows for an unprecedented approach to alter me- chanical strength and proton conductivity of ternary hybrid membrane, as verified from universal test machine （UTM） curves and alternating current （AC） impedance plots. The impact of GO integration on the morphology and roughness of hybrid membrane was scrutinized using field emission scanning electron microscope （FE-SEM） and atomic force microscope （AFM）. Ternary hybrid showed uniform intercalation of GO nanosheets throughout the entire surface of membrane with an increased surface roughness of 8.91 nm. The constructed ternary hybrid membrane revealed excellent water absorption, ion exchange capacity and gas barrier properties, while retaining reasonable dimensional stability. The well-optimized ternary hybrid membrane containing 5 wt% GO revealed a maximum proton conductivity of 111.9 mS/cm, which is higher by a factor of two-fold with respect to that of bare SFMC membrane. The maximum PEMFC power density of 528.07mW/cm2 was yielded by ternary hybrid membrane at a load current density of 1321.1 mA/cm2 when operating the cell at 70 ℃ under 100% relative humidity （RH）. In comparison, a maximum power density of only 182.06 mW/cm2 was exhibited by the bare SFMC membrane at a load current density of 455.56 mA/cm2 under same operating conditions.
基金Byoungseok Min of Pohang Accelerator Laboratory for SAXS technical support at 4C beamline.All authors have read the manuscript and agreed to its contents。
文摘Prolonged hydrothermal treatment for sulfonated poly(ether ether ketone) membranes induces mechanical degradation and developing hydrophilic-hydrophobic phase separation, simultaneously. The enhanced phase separation provides incremental proton conductivity to the membranes, whereas mechanical degradation drastically reduces device stability. On this basis, we describe here the effects of two different ex situ aging processes on sulfonated poly(ether ether ketone) membranes: hydrationdehydration cycling and prolonged hydrothermal treatment. Both aged membranes exhibited enhanced phase separation under the hydrated conditions, as characterized by small angle X-ray scattering.However, when the aged membranes were dried again, the nanostructure of the membranes aged via the hydration-dehydration cycling was recoverable, whereas that of the membranes aged via prolonged hydrothermal treatment was irreversible. Furthermore, the two differently aged membranes showed clear differences in thermal, mechanical, and electrochemical properties. Finally, we implemented both aged membranes in fuel cell application. The sample aged via hydration-dehydration cycling maintained its improved cell performance, whereas the sample aged via hydrothermal treatment showed drastically reduced cell performance after durability test for 50 h.
文摘A new interfacial polymerization （IP） procedure is developed in order to synthesize polypiperazine-amide thin-film membrane on the inner surface of poly（phthalazinone ether sulfone ketone） （PPESK） hollow fiber ultrafiltration （UF） membrane. A hollow fiber composite membrane with good performance was prepared and studied by PT-IR and scanning electron microscopy.