Bisphenol A dicyanate ester resins modified by fluorine-containing liquid crystal compound(LCFE)are applied as polymer matrix(LCFE-BADCy),poly(p-phenylene-2,6-benzobisoxazole)(PBO)fibers as rein-forcements,and fluorin...Bisphenol A dicyanate ester resins modified by fluorine-containing liquid crystal compound(LCFE)are applied as polymer matrix(LCFE-BADCy),poly(p-phenylene-2,6-benzobisoxazole)(PBO)fibers as rein-forcements,and fluorine/adamantane PBO precursor(pre FABPBO)as interfacial compatibilizer to prepare the corresponding PBO fibers/FABPBO/LCFE-BADCy wave-transparent laminated composites.LCFE could improve the order degree of BADCy cured network,in favor of enhancing the wave-transparent perfor-mance,mechanical properties,and intrinsic thermal conductivity.The dielectric constant and dielectric loss of PBO fibers/FABPBO/LCFE-BADCy composites are highly temperature(25–200℃)and frequency(10^(4)–10^(7) Hz and 8.2–12.4 GHz)stable with the value of 2.49 and 0.003 under 10^(6) Hz at 25℃,and the corresponding wave transmission efficiency is 95.0%,higher than that of 92.5%for PBO fibers/BADCy com-posites.The interlamellar shear strength and flexural strength are respectively 50.7 MPa and 682.5 MPa,38.1%and 16.2%higher than those of PBO fibers/BADCy composites.Besides,the volume resistivity,breakdown voltage,heat resistance index,glass transition temperature,flame retardant grade,and ul-timate oxygen index of PBO fibers/FABPBO/LCFE-BADCy composites are respectively 5.3×10^(15)Ωcm,29.75 kV/mm,217.2℃,245.7℃,V-1 grade,and 33.6%,expected to be performed as a new generation of“lightweight/loading/wave-transparent”electromagnetic window materials in advanced military weapons and civil communication base station.展开更多
基金The authors are grateful for the support and funding from National Scientific Research Project(Basis Strengthening Plan)State Key Laboratory of Solidification Processing in NWPU(No.SKLSP202103).
文摘Bisphenol A dicyanate ester resins modified by fluorine-containing liquid crystal compound(LCFE)are applied as polymer matrix(LCFE-BADCy),poly(p-phenylene-2,6-benzobisoxazole)(PBO)fibers as rein-forcements,and fluorine/adamantane PBO precursor(pre FABPBO)as interfacial compatibilizer to prepare the corresponding PBO fibers/FABPBO/LCFE-BADCy wave-transparent laminated composites.LCFE could improve the order degree of BADCy cured network,in favor of enhancing the wave-transparent perfor-mance,mechanical properties,and intrinsic thermal conductivity.The dielectric constant and dielectric loss of PBO fibers/FABPBO/LCFE-BADCy composites are highly temperature(25–200℃)and frequency(10^(4)–10^(7) Hz and 8.2–12.4 GHz)stable with the value of 2.49 and 0.003 under 10^(6) Hz at 25℃,and the corresponding wave transmission efficiency is 95.0%,higher than that of 92.5%for PBO fibers/BADCy com-posites.The interlamellar shear strength and flexural strength are respectively 50.7 MPa and 682.5 MPa,38.1%and 16.2%higher than those of PBO fibers/BADCy composites.Besides,the volume resistivity,breakdown voltage,heat resistance index,glass transition temperature,flame retardant grade,and ul-timate oxygen index of PBO fibers/FABPBO/LCFE-BADCy composites are respectively 5.3×10^(15)Ωcm,29.75 kV/mm,217.2℃,245.7℃,V-1 grade,and 33.6%,expected to be performed as a new generation of“lightweight/loading/wave-transparent”electromagnetic window materials in advanced military weapons and civil communication base station.
