Synthesis and characterization of quaternized poly(phthalazinone ether sulfone ketone)for anion-exchange membrane

Chloromethylated poly（phthalazinone ether sulfone ketone） （CMPPESK） was prepared from poly（phthalazinone ether sulfone ketone） （PPESK） using chloromethyl octyl ethers （CMOE） with lower toxicity as chloromethylated regent. CMPPESK was soluble in N-methyl-2-pyrrolidone （NMP）, N,N-dimethylacetamide （DMAc） and chloroform. Quaternized poly（phthalazinone ether sulfone ketone） （QAPPESK） was prepared from CMPPESK by quaternization. QAPPESK had excellent solvent resistance, which was only partly soluble in sulfuric acid （98%） and swollen in N,N-dimethylformamide （DMF）. The vanadium redox flow battery （V-RFB） using QAPPESK anion-exchange membrane had better performance with 88.3% of overall energy efficiency.

Synthesis and characterization of novel poly(aryl ether sulfone ketone)s containing phthalazinone and biphenyl moieties

A novel series of poly（aryl ether sulfone ketone）s （PPESKs） containing phthalazinone and biphenyl moieties were prepared by two-step nucleophilic polycondensation reaction. The ^-Mw values of these copolymers were between 38,330 and 67,900. The glass transition temperatures （Tg） and 5% decomposition temperatures were ranged in 253-269 ℃ and 488-500 ℃, respectively, The structures of these copolymers were confirmed by FT-IR and ^1H NMR. Moreover, all the resultant copolymers were amorphous determined by wide angle X-ray diffraction （WAXD）.

Synthesis of Poly(phthalazinone ether ketone) Containing Sodium Sulfonate Groups via Direct Polymerization

1, 2-Diliydro-4-(4-hydroxyphenyl)(2H)phthalazin-1-one(DHPZ) was sulfonated in concentrated Sulfuric acid. Poly(phthalazinone ether ketone) containing pendant sodium sulfonate group was synthesized from sulfonated and pure 1,2-dihydro-4-(4-hydroxyphenyl)(2H)phthalazin-1-one, and 4,4'-difluorodiphenylketone. The sulfonated monomer and sulfonated polymer were characterized with FT-IR and H-1-NMR.

Characterization and tribological investigation of self-assembled trimethoxysilyl-functionalized poly(phthalazinone ether ketone)thin films on glass substrates

Trimethoxysilyl-functionalized PPEK（PKGS） films had been designed to serve as wear resistant coatings for silicon surfaces. These surface films were formed by a dip-coating technique applied to self-assembled monolayers（SAMs）.The formation and wetting behavior of PKGS films were characterized by means of contact angle measurement.The friction coefficient of the film prepared is very low（about 0.1）,and the anti-wear behavior is good,with a lack of failure after sliding over 1800 s.

Synthesis and characterization of trimethoxysilyl-functionalized poly(phthalazinone ether ketone)

A novel alkoxysilyl-functionalized poly(phthalazinone ether ketone) (PPEK) was prepared for the boundary lubricant application in micro-electro-mechanical system (MEMS). The synthesis of functionalized PPEK was started from the hydroxylation of PPEK, then following with the corresponding ring-opening reaction of 3-glycidoxypropyltrimethoxysilane (GPTMS). The structures of the functional PPEK were confirmed by FTIR, 1H NMR, 29Si NMR, and UV–vis spectrum.

Synthesis and characterization of new soluble poly(aryl ether nitrile)s containing phthalazinone moiety

A series of novel poly（aryl ether nitrile）s containing phthalazinone moiety were synthesized by the nucleophilic displacement reaction of bisphenol-like monomers （I） with 2,6-difluorobenzonitrile. The inherent viscosities ranged from 0.46 to 1.07 dL g^-1. The glass transition temperatures were in the range of 277-295℃, and the temperatures for 10% weight loss in nitrogen atmosphere were found between 495 and 527 ℃. The structures of these resultant polymers were confirmed by FT-IR and 1^H NMR. Moreover, the properties of poly（aryl ether nitrile）s including solubility and crystallinity were also studied.

Synthesis of Novel Poly(aryl ether amide)s Containing the Phthalazinone Moiety

Two novel heterocyclic diamine monomers: 1,2-dihydro-2-(4-aminophenyl)-4-[4-(4-aminophenoxy)phenyl] (2H)phthalazin-1-one and 1,2-dihydro-2-(4-aminophenyl)-4-[4-(4-aminophenoxy)-3,5-dimethylphenyl](2H)phthalazin-1-one were successfully synthesized from readily available heterocyclic bisphenol-like monomers in two steps in high yield. A series of novel poly(aryl ether amide)s containing the phthalazinone moiety were successfully prepared by the direct polymerization of the novel diamines and aromatic dicarboxylic acids using triphenyl phosphite and pyridine as condensing agents.

Synthesis and Characterization of Poly(ether imide)s Containing m-Methyl and Phthalazinone Moieties

Three novel poly(ether imide)s were synthesized by one-step solution polymerization from 2-(3, 4-dicarboxyl-N-phenyl)-4-(3, 4-dicarboxyl-phenoxyl-4-(2-methyl)-phenyl)-2, 3- phthal-azin-1-one dianhydride and three amines, and characterized. The polymers show good solubility and thermal properties.

Synthesis and Characterization of Poly (ether imide)s Containing Phthalazinone and Isopropyl Moieties

A novel poly(ether imide)s containing phthalazinone and isopropyl moieties derived from 2-(4-aminophenyl)-4-[4-(4-aminophenoxy)phenyl]-phthalazin-1-one and bisphenol-A diphthalic anhydride was synthesized by one-step solution condensation polymerization in nr-cresol. The polymer was characterized by FTIR, NMR, molecular weights, glass transition temperature, thermal degradation temperature and WAXD.

Synthesis and properties of soluble poly（aryl ether sulfone ether ketone）s copolymers containing pendant methyl groups

A series of Poly（arly ether sulfone ether ketone）s containing pendant methyl groups were synthesized by the reaction of 4,4＇-[sulfonylbis （1,4-phenylene）dioxy] dibenzoyl chloride （SODBC） with 4,4＇- diphenoxy diphenylsulfone （DPODPS）, 4,4＇- di（2-methylphenoxy） diphenylsulfone （o-Me-DPODPS）, 4,4＇- di（3-methylphenoxy） diphenylsulfone （m-Me-DPODPS）, 4,4＇- di （2,6-bimethylphenoxy） biphenylsulfone（o-Me2-DPODPS） respectively, in a mixture of 1,2-dichloroethane （DCE） and N-methylpyrrolidone （NMP）. These reactions were catalyzed by anhydrous aluminum chloride （AlCl）. The characteristic of copolymers were studied by means of advanced analytical techniques such as FT-IR,1H-NMR, DSC, TGA and WAXD. The results show glass transition temperature （Tg） in the range of 193-206℃, thermally stable in excess of 434℃ and excellent solubility in polar solvents. Methyl-substituted Poly（aryl ether sulfone ketone）s had higher glass transition temperatures, lower initial decomposition temperatures than the unsubstituted ones.

SYNTHESIS AND CHARACTERIZATION OF POLY(PHTHALAZINONE ETHER PHOSPHINE OXIDE)S BY N-C COUPLING REACTION

Based on several unsymmetrical, twist, noncoplanar phthalazinone-containing monomers 2a-2e and an active bis（4-fluorophenyl）phenyl phosphine oxide （BFPPO） monomer, a series of novel poly（phthalazinone ether phosphine oxide）s （PPEPO） was synthesized by anhydrous K2CO3 mediated N-C coupling reaction in DMAc. The polymers exhibited good thermal properties with Tgs ranging from 267℃ to 306℃ and 5% weight loss temperatures in nitrogen higher than 430℃, together with high char yield upon prolonged heating at 800℃ （35%-56%）. Moreover, the polymers were readily soluble in common organic solvents, such as N-methyl-2-pyrrolidone, chloroform and m-cresol. These polymers had inherent viscosities in the range of 0.45-0.72 dL/g and could be cast into flexible and colorless films by spin coating or casting approach.

SYNTHESIS AND CRYSTALLIZATION BEHAVIOR OF POLY(ETHER ETHER KETONE ETHER KETONE)(PEEKEK)

In this paper, the synthesis and crystallization behavior of poly(ether ether ketone ether ketone) (PEEKEK) are reported. PEEKEK was prepared from 4,4'-bis(p-fluorobenzoyl) diphenyl ether (4,4'-FBDE) and hydroquinone along the nucleophilic substitution route. The thermal properties were investigated by using DSC and TGA. The crystallization behavior of PEEKEK under several conditions, i.e., crystallization from the molten state (melt crystallization), crystallization from a quenched sample (cold crystallization) and crystallization induced by exposing glassy sample to methylene chloride (solvent-induced crystallization) has also been investigated. The results show that crystallization of PEEKEK could be induced by the above methods, and no polymorphism was found. The differences in the crystallization of PEEKEK induced by the above methods are seen in their degree of crystallinity.

Synthesis and characterization functionalized poly(ether ether ketone)s with carboxylic groups

A novel type of aromatic poly（ ether ether ketone） s with carboxyl groups were prepared by polycondensation of 4,4-bis（4-hydroxyphenyl）pentanoic acid with difluoro-monomers. Their mo- lecular structures were determined by ^1H-NMR and IR, respectively. Their molecular weights were measured by gel permeation chromatography （ GPC ）, which showed that all the polymers had high molecule weights （ 〉 42 000）. Due to the long side chains of polymers, all the polymers had good solubility （soluble in NMP, DMAc, THF, etc. ）. The differential scanning calorimeter （DSC） detected their excellent glass transition temperatures （ Tg ） up to 195 ℃. The Tg increased with the content of carboxylic units in the polymer chains, because the interactions of H bonds increased with increasing content of carboxylic. The polymers could form transparent and flexible films, which make them a candidate for membrane materials.

SYNTHESIS AND PROPERTIES OF SULFONATED POLY(ETHER KETONE)S CONTAINING 3,5-DIMETHYL PHTHALAZINONE MOIETIES AS PROTON EXCHANGE MEMBRANE MATERIALS

Sulfonated poly（ether ketone）s containing 3,5-dimethyl phthalazinone moieties （SPPEK-DMs） with different degrees of sulfonation （DS） were synthesized via direct polycondensation from 4-（3,5-dimethyl-4-hydroxyphenyl）-2,3- phthalazinone, 4,4＇-difluorobenzophenone and 3,3＇-disulfonate-4,4＇-difluorobenzophenone. The chemical structure of SPPEK-DMs was characterized by FTIR and 1H-NMR. Thermal stability of SPPEK-DMs was characterized by the thermogravimetric analysis. The membranes prepared from SPPEK-DMs exhibited ion exchange capacities （IEC） ranging from 0.93 mmol.g-1 to 1.86 mmol.g-1. Water uptake, swelling, oxidative stability and methanol permeability of SPPEK- DMs membranes were investigated. SPPEK-DMs membranes exhibited high oxidative stability. The methanol permeability values of SPPEK-DMs membranes were in the range 5.15× 10^-8-6.61×10^-7 cm^2.s-1, which was much lower than those of Nafion117. The proton conductivity of SPPEK-DM40 membranes was 1.1 ×10^-2 S.cm^-1 at 70℃.

Highly stable side-chain-type cardo poly(aryl ether ketone)s membranes for vanadium flow battery

Vanadium flow batteries(VFBs)have drawn considerable attention as an emerging technology for largescale energy storage systems(ESSs).One of the pivotal challenges is the availability of eligible ion exchange membranes(ICMs)that provide high ion selectivity,proton conductivity,and stability under rigorous condition.Herein,a‘side-chain-type’strategy has been employed to fabricate highly stable phenolphthalein-based cardo poly(arylene ether ketone)s(PAEKs)membrane with low area resistance(0.058Ωcm^(2)),in which flexible alkyl spacers effectively alleviated inductive withdrawing effect from terminal ion exchange groups thus enabling a stable backbone.The assembled VFBs based on PAEKs bearing pendent alkyl chain terminated with quaternary ammonium(Q-PPhEK)demonstrated an energy efficiency above 80%over 700 cycles at 160 mA/cm^(2).Such a remarkable results revealed that the side-chain-type strategy contributed to enhancing the ICMs stability in strong oxidizing environment,meanwhile,more interesting backbones would be woken with this design engaging in stable ICMs for VFBs.

HYDROPHILIC MODIFICATION OF PPESK POROUS MEMBRANES VIA AQUEOUS SURFACE-INITIATED ATOM TRANSFER RADICAL POLYMERIZATION

Hydrophilic surface modification of poly(phthalazinone ether sulfone ketone)(PPESK) porous membranes was achieved via surface-initiated atom transfer radical polymerization(ATRP) in aqueous medium.Prior to ATRP.chloromethyl groups were introduced onto PPESK main chains by chloromethylation.Chloromethvlated PPESK(CMPPESK) was fabricated into porous membrane through phase inversion technique.Hydrophilic poly(poly(ethylene glycol) methyl ether methacrylate)(P(PEGMA)) brushes were grafted from CMPPESK membrane ...

Synthesis of polypiperazine-amide thin-film membrane on PPESK hollow fiber UF membrane

A new interfacial polymerization （IP） procedure is developed in order to synthesize polypiperazine-amide thin-film membrane on the inner surface of poly（phthalazinone ether sulfone ketone） （PPESK） hollow fiber ultrafiltration （UF） membrane. A hollow fiber composite membrane with good performance was prepared and studied by PT-IR and scanning electron microscopy.

SYNTHESIS OF AN AMPHIPHILIC PPESK-g-P(PEGMA)GRAFT COPOLYMER VIA ATRP AND ITS USE IN BLEND MODIFICATION OF PPESK MEMBRANES

Preparation of an amphiphilic graft copolymer having poly(phthalazinone ether sulfone ketone)(PPESK) as main chains was carried out by atom transfer radical polymerization(ATRP).The precursor,chloromethylated PPESK (CMPPESK),was prepared by using chioromethylether as chloromethylation agent.Then,poly(ethylene glycol) methyl ether methacrylate(PEGMA) was used as monomer to synthesize PPESK-g-P(PEGMA) by ATRP method under the catalysis of a cuprous chloride/2,2'-bipyridyl system.PPESK/PPESK-g-P(PEGMA) blend m...

Ionic liquids as green reaction media for synthesis of poly(aryl ether ketone)s

Poly(aryl ether ketone)s (PAEKs) were successfully synthesized via nucleophilic aromatic substitution (SNAR) mechanism, using ionic liquids as green reaction media. The influence of various reaction parameters including monomer concentration, dehydration time, polymerization temperature and duration, IL's cations and anions nature, upon PAEKs molecular weight was investigated. In addition, the peculiarities of hydrogen-bonding ability of ILs were investigated. The interaction of 2,2-bis(4-hydroxyphenyl) propane (bisphenol A) with ILs has a strong influence on PAEKs synthesis. Various moderate molecular weight PAEKs have been obtained in high yields with molecular weights ranging from 10000 to 18000g mol-1.