Melamine formaldehyde foam(MFF)generates many poisonous chemicals through the traditional recycling methods for organic resin wastes.Herein,a high MFF degradation ratio of ca.97 wt.%was achieved under the mild conditi...Melamine formaldehyde foam(MFF)generates many poisonous chemicals through the traditional recycling methods for organic resin wastes.Herein,a high MFF degradation ratio of ca.97 wt.%was achieved under the mild conditions(160℃)in a NaOH–H2O system with ammelide and ammeline as the main degradation products.The alkaline solvent had an obvious corrosion effect for MFF,as indicated by scanning electron microscopy(SEM).The reaction process and products distribution were studied by Fourier-transform infrared spectroscopy(FTIR),X-ray photoelectron spectroscopy(XPS),and ^(13)C nuclear magnetic resonance(NMR).Besides,the MFF degradation products that have the similar chemical structures and bonding performances to those of melamine can be directly used as the raw material for synthesis of melamine urea-formaldehyde resins(MUFs).Moreover,the degradation system demonstrated here showed the high degradation efficiency after reusing for 7 times.The degradation process generated few harmful pollutants and no pre-or post-treatments were required,which proves its feasibility in the safe removal or recovery of waste MFF.展开更多
Three-dimensional(3D)porous absorbents have attracted significant attention in the oily wastewater treatment technology due to their high porosity and elasticity.Given their amphiphilic surface,they have a propensity ...Three-dimensional(3D)porous absorbents have attracted significant attention in the oily wastewater treatment technology due to their high porosity and elasticity.Given their amphiphilic surface,they have a propensity to simultaneously absorb water and oil,which restricts their range of applications.In this study,a reduced graphene oxide and titanium dioxide nanocomposite(rGO/TiO_(2))was used to fabricate an ultra-hydrophobic melamine sponge(MS)through interfacial modification using a solution immersion technique.To further modify it,poly-dimethylsiloxane(PDMS)was grafted onto its surface to establish stronger covalent bonds with the composite.The water contact angle of the sponge(rGO/TiO_(2)/PDMS/MS)was 164.2°,which satisfies the condition for ultrahydrophobicity.The evidence of its water repellency was demonstrated by the Cassie-Baxter theory and the lotus leaf effect.As a result of the increased density of rGO/TiO_(2)/PDMS/MS,it recorded an initial capacity that was 2 g/g lower than the raw MS for crude oil absorption.The raw MS retained 53% of its initial absorption capacity after 20 cycles of absorption,while rGO/TiO_(2)/PDMS/MS retained 97%,suggesting good recyclability.Excellent oil and organic solvent recovery(90%-96%)was demonstrated by rGO/TiO_(2)/PDMS/MS in oil-water combinations.In a continuous separation system,it achieved a remarkable separation efficiency of 2.4×10^(6)L/(m^(3)·h),and in turbulent emulsion separation,it achieved a demulsification efficiency of 90%-91%.This study provides a practical substitute for massive oil spill cleaning.展开更多
A silylated melamine sponge(SMS)was prepared by two simple steps,namely,immersion and dehydration of a melamine sponge coated with methyltrichlorosilane.The silylated structure of SMS was characterized by FT-IR(Fourie...A silylated melamine sponge(SMS)was prepared by two simple steps,namely,immersion and dehydration of a melamine sponge coated with methyltrichlorosilane.The silylated structure of SMS was characterized by FT-IR(Fourier-transform infrared)spectroscopy,SEM(Scanning electron microscopy)and in terms of water contact angles.Its oil-water absorption and separation capacities were measured by FT-IR and UV-visible spectrophoto-metry.The experimental results have shown that oligomeric silanol covalently bonds by Si-N onto the surface of melamine sponge skeletons.SMS has shown superhydrophobicity with a water contact angle exceeding 150°±1°,a better separation efficiency with regard to diesel oil(by 99.31%(wt/wt%)in oil-water mixture and even up to 99.99%(wt/wt%)for diesel oil in its saturated aqueous solution.Moreover,SMS inherited the intrinsicflame retardancy of the melamine sponge.In general,SMS has shown superhydrophobicity,high porosity,excellent selectivity,remarkable recyclability,and better absorption capacity for various oils and organic solvents,and a high separation efficiency for oil in saturated aqueous solutions.展开更多
Objective To develop an analytical method for simultaneously qualitative and quantitative determination of melamine and triazine-related by-products including ammelide, ammeline, and cyanuric acid in milk and milk pro...Objective To develop an analytical method for simultaneously qualitative and quantitative determination of melamine and triazine-related by-products including ammelide, ammeline, and cyanuric acid in milk and milk products by gas chromatography- tandem mass spectrometry (GC-MS/MS). Methods Melamine and triazine-related by-products namely ammelide, ammeline and cyanuric acid in the samples were extracted in a solvent mixture of diethylamine, water, and acetonitrile (10:40:50, V/V/V). After centrifugation, an aliquot of the supernatant was evaporated to dryness under a gentle stream of nitrogen gas, and then melamine and triazine-related by-products were derivatized using BSTFA with 1% TMCS. The derivatives of melamine and its analogues were determined by gas chromatography/tandem mass spectrometry using multiple reactional monitoring (MRM) with 2, 6-Diamino-4-chloropyrimidine (DACP) being used as an internal standard. Results The linear detectable ranges were from 0.004 mg/kg to 1.6 mg/kg for melamine, ammelide, ammeline, and cyanuric acid with a correlation coefficient no less than 0.999. The recovery rates of the tour compounds in spiked blank milk powder at concentrations 0.5, 1, 2 mg/kg were between 61.4%-117.2%, and the relative standard deviation was no more than 11.5% (n=6). The detection limits of melamine, ammelide, ammeline and cyanuric acid in milk powder were 0.002 mg/kg with a ratio of signal to noise of 3. Conclusion This GC-MS/MS method for simultaneous determination of melamine, ammelide, ammeline, and cyanuric acid in milk and milk products is sensitive and specific.展开更多
Objective To investigate the occurrence and concentrations of melamine and its analogues in tainted infant formula and to identify the etiologic factors for the urinary stones epidemic in infants and young children in...Objective To investigate the occurrence and concentrations of melamine and its analogues in tainted infant formula and to identify the etiologic factors for the urinary stones epidemic in infants and young children in China in 2008. Methods Sanlu infant formula samples were collected from families of the affected children in Gansu province, and markets in Gansu and Hebei provinces and Beijing city. Melamine and its analogues, including cyanuric acid, ammeline, and ammelide were measured by gas chromatography/tandem mass spectrometry. Results High prevalence and concentrations of melamine were found in Sanlu infant formula samples, with low concentrations of cyanuric acid, ammeline and ammelide. Melamine were detected in 87 out of 111 Sanlu infant formula samples with a range of 118 to 4 700 mg/kg, Conclusion The results provide strong evidence for melamine as the etiological factor for the urinary stones epidemic in infants and young children in China in 2008.展开更多
An improved method for preparing melamine cyanurate (MCA) based flame retardant polyamide 6 (FRPA6) materials has been proposed. This processing method, i.e., improved in situ polymerization, was used to synthesiz...An improved method for preparing melamine cyanurate (MCA) based flame retardant polyamide 6 (FRPA6) materials has been proposed. This processing method, i.e., improved in situ polymerization, was used to synthesize flame retardant PA6. In situ formed MCA nanoparticles were supposed to be linked to PA6 chains in the ε-caprolactam hydrolytic polymerization system to obtain startype polymers for the first time. Through TEM photographs, it can be found that the in situ formed MCA nanoparticles with diametric size of less than 50 nm, are nanoscaled, highly uniformly dispersed in the PA6 matrix. Synthesized flame retardant PA6 have good fire performance which can achieve UL-94 V-0 rating at 1.6 mm thickness with the presence of 7.34 wt.% MCA in the matrix.展开更多
Objectives To study the migration of melamine into foods from plastic food packaging materials and dairy product containers commonly used in China. Methods 37 samples were collected from the market. The EU migration t...Objectives To study the migration of melamine into foods from plastic food packaging materials and dairy product containers commonly used in China. Methods 37 samples were collected from the market. The EU migration testing conditions were adopted with distilled water, 3% acetic acid, n-hexane and 15% ethanol being chosen as the simulating solutions. The HPLC method was used to detect melamine. Results No melamine was detected in 15 dairy product containers. Among the 22 plastic samples, 16 of polypropylene, and polycarbonate types had no detectable amount melamine while a low level of melamine was found in 3 of the 6 melamine resin containers. Conclusion Migration of melamine from food packaging materials in China market is in line with the requirements of EU.展开更多
Surface electropositivity and low internal resistance are important factors to improve the anode performance in microbial fuel cells (MFCs). Nitrogen doping is an effective way for the modification of traditional carb...Surface electropositivity and low internal resistance are important factors to improve the anode performance in microbial fuel cells (MFCs). Nitrogen doping is an effective way for the modification of traditional carbon materials. In this work, heat treatment and melamine were used to modify carbon felts to enhance electrogenesis capacity of MFCs. The modified carbon felts were characterized using X-ray photoelectron spectroscopy (XPS), scanning electron microscope (SEM), atomic force microscopy (AFM) and malvern zeta potentiometer. Results show that the maximum power densities under heat treatment increase from 276.1 to 423.4 mW/m(2) (700 degrees C) and 461.5 mW/m(2) (1200 degrees C) and further increase to 472.5 mW/m(2) (700 degrees C) and 515.4 mW/m(2) (1200 degrees C) with the co-carbonization modification of melamine. The heat treatment reduces the material resistivity, improves the zeta potential which is beneficial to microbial adsorption and electron transfer. The addition of melamine leads to the higher content of surface pyridinic and quaternary nitrogen and higher zeta potential. It is related to higher MFCs performance. Generally, the melamine modification at high temperature increases the feasibility of carbon felt as MFCs's anode materials. (C) 2016 Science Press and Dalian Institute of Chemical Physics, Chinese Academy of Sciences. Published by Elsevier B.V. and Science Press. All rights reserved.展开更多
A general and versatile strategy to prepare melamine-formaldehyde(MF)microcapsules encapsulating oil-based fragrances by combining solvent evaporation and in situ polymerization was proposed in this work.The oil-based...A general and versatile strategy to prepare melamine-formaldehyde(MF)microcapsules encapsulating oil-based fragrances by combining solvent evaporation and in situ polymerization was proposed in this work.The oil-based fragrance was pre-encapsulated by an inner polyacrylate membrane via solvent evaporation,followed by in situ polymerization of MF precondensates as an outer shell.The polyacrylate membrane is used as an intermediate bridging layer to stabilize the oil-based fragrance,and to provide driving forces for in situ polymerization of MF precondensates through electrostatic attractions between carboxyl groups and ammonium ions.It was demonstrated that MF microcapsules containing clove oil were prepared successfully.The amount and the composition of the intermediate polyacrylate bridging layer were critical.Smooth and sphere-shaped MF-clove oil microcapsules were prepared when the weight ratio of polyacrylate to clove oil was over 60 wt%and the concentration of acrylic acid(AA)increased to 10 wt%in polyacrylate.In addition,MF microcapsules containing sunflower oil and hexyl salicylate were prepared by using this method.The work suggests that this new approach can be potentially used to encapsulate various core materials,tuning the shell properties of microcapsules such as thickness,mechanical strength and release properties.展开更多
A sensitive chemiluminescence(CL) method was developed for determining melamine in urine and plasma samples based on the fact that melamine can remarkably enhance the chemiluminescence of Luminol-K3 Fe(CN)6 system...A sensitive chemiluminescence(CL) method was developed for determining melamine in urine and plasma samples based on the fact that melamine can remarkably enhance the chemiluminescence of Luminol-K3 Fe(CN)6 system in alkaline medium. The determination conditions were optimized. Under optimum conditions, the chemiluminescence intensity had a good linear relationship with melamine in the range of 9.0 × 10^-9 - 7.0 × 10^-6 g/mL with a correlation coefficient of 0. 9992. The detection limits (3o) were 3.54 ng/mL for urine sample and 6.58 ng/mL for plasma sample. The average recoveries of melamine were 102.6% for urine sample and 95.1% for plasma sample. Melamine in samples was extracted with liquid-liquid extraction procedures and the assay results coincided very well with that determined with flow injection chemiluminescence method. The method provides a reproducible and stable approach for sensitive detection and quantification of melamine in urine and plasma samples.展开更多
The development of multifunctional and efficient electromagnetic wave absorbing materials is a challenging research hotspot.Here,the magnetized Ni flower/MXene hybrids are successfully assembled on the surface of mela...The development of multifunctional and efficient electromagnetic wave absorbing materials is a challenging research hotspot.Here,the magnetized Ni flower/MXene hybrids are successfully assembled on the surface of melamine foam(MF)through electrostatic self-assembly and dip-coating adsorption process,realizing the integration of microwave absorption,infrared stealth,and flame retardant.Remarkably,the Ni/MXene-MF achieves a minimum reflection loss(RLmin)of−62.7 dB with a corresponding effective absorption bandwidth(EAB)of 6.24 GHz at 2 mm and an EAB of 6.88 GHz at 1.8 mm.Strong electromagnetic wave absorption is attributed to the three-dimensional magnetic/conductive networks,which provided excellent impedance matching,dielectric loss,magnetic loss,interface polarization,and multiple attenuations.In addition,the Ni/MXene-MF endows low density,excellent heat insulation,infrared stealth,and flame-retardant functions.This work provided a new development strategy for the design of multifunctional and efficient electromagnetic wave absorbing materials.展开更多
Melamine formaldehyde (MF) foam is kind of fire-retardant material and has great potential in acoustic and thermal insulation area. In this article, MF resin foam was prepared by microwave radiation. We discussed the ...Melamine formaldehyde (MF) foam is kind of fire-retardant material and has great potential in acoustic and thermal insulation area. In this article, MF resin foam was prepared by microwave radiation. We discussed the thermal stability of MF foam and the effect of different emulsifiers on its morphology, apparent density, fire-retardancy and mechanical property. The decomposition temperature of MF foam we prepared is nearly 400℃ and the constitution of residue after combustion is made up of carbon and graphite. Emulsifier influenced the apparent density of MF foam and using coemulsifiers can get flexible foam with uniform cell size, good morphology and low apparent density. When the fire-retardant MF foam’s apparent density is low of 5.53 kg/cm-3, its value of LOI can reach 32.4. The mechanical property of foam is consistent with apparent density.展开更多
Objective We tested whether melamine nephrotoxicity was exacerbated by urate(a typical component of renal stones in humans)in rats with hyperuricemiainduced by the uricase inhibitor,potassium oxonate(Oxo).Methods Rats...Objective We tested whether melamine nephrotoxicity was exacerbated by urate(a typical component of renal stones in humans)in rats with hyperuricemiainduced by the uricase inhibitor,potassium oxonate(Oxo).Methods Rats were exposed to melamine or Oxo alone or combinations of melamine(200-400 mg/kg)and Oxo(200-600 mg/kg)for 3 consecutive days.Kidney injury was evaluated by renal biochemical functions,histomorphology,and lipid peroxidation.Kidney crystals were analyzed for their composition.Results Nephrotoxicity was minimal in animals administered melamine or Oxo alone,but it was demonstrable in animals administered at least 800 mg/kg of the two compounds combined.All rats in the 400+600(melamine+Oxo)and 400+400 mg/kg groups and 4 out of 6 in the 200+600 mg/kg group died within 3 days;no rat died in the 200+400 or 200+200 mg/kg group.Dose-dependent renal damage resembling clinical findings in affected patients was observed in rats administered the two compounds.Crystal composition determination revealed the existence of melamine and uric acid in the affected kidneys,resembling human stones.Conclusion Our findings suggest that uric acid plays a key role in melamine-related kidney injury in humans.Future studies should consider uric acid together with melamine when examining adverse effects in humans.展开更多
Objective To determine the prevalence of urolithiasis in young children fed infant formula(IF) contaminated with melamine,and the association between IF consumption and urolithiasis.Design A total of 2 733 children ...Objective To determine the prevalence of urolithiasis in young children fed infant formula(IF) contaminated with melamine,and the association between IF consumption and urolithiasis.Design A total of 2 733 children ≤3 years of age on September 1,2008 in two townships of Gansu Province,China were studied.Cases of urolithiasis were diagnosed by ultrasonography.Milk product consumption was determined by their caregivers.Remaining IF samples were tested for melamine and cyanuric acid.Results Of 2 733 eligible children in the two townships,2 186(80%) were enrolled in our study.Overall,16.6%(362) of 2 186 children had urolithiasis.The prevalence was 24.6% in children exclusively fed Sanlu brand IF,9.7% in those fed other IF,and 8.5% in those fed exclusively on other milk products.For children exclusively breast-fed,no urolithiasis was found(P0.05).The prevalence of urolithiasis was 11.4% in children fed 400 g of Sanlu IF,rising to 37.5% in children fed over 25 600 g.Of 48 Sanlu IF samples,91.7% contained melamine(median=1 800 ppm;range=45-4 700) and 66.7% contained cyanuric acid(median=1.2 ppm;range=0.4-6.3).Melamine was also detected in 22.2% of 36 other brand IF(median=27.5 ppm,range=4-50).Conclusions Urolithiasis was associated with melamine-contaminated IF.Although one product caused most morbidity,other milk products may have also contributed to the outbreak.展开更多
With the increasing energy demand together with the deteriorating environment and decreasing fossil fuel resources,the development of highly efficient energy conversion and storage devices is one of the key challenges...With the increasing energy demand together with the deteriorating environment and decreasing fossil fuel resources,the development of highly efficient energy conversion and storage devices is one of the key challenges of both fundamental and applied research in energy technology.Melamine sponges(MS)with low density,high nitrogen content,and high porosity have been used to design and obtain three‐dimensional porous carbon electrode materials.More importantly,they are inexpensive,environment‐friendly,and easy to synthesize.There have been many reports on the modification of carbonized MS and MS‐based composites for supercapacitor and lithium battery electrode materials.In this paper,recent studies on the fabrication of electrode materials using MS as raw materials have been mainly reviewed,including carbonation,doping activation,and composite modification of MS,and expectations for the development of porous carbon materials for energy storage as a reference with excellent performance,environment‐friendliness,and long life.展开更多
Objective To estimate the dietary melamine exposure in Chinese infants and young children from the consumption of melamine adulterated Sanlu infant formula. Methods Four age groups of infants and young children (3, 6...Objective To estimate the dietary melamine exposure in Chinese infants and young children from the consumption of melamine adulterated Sanlu infant formula. Methods Four age groups of infants and young children (3, 6, 12, and 24 months) were chosen as the assessed subjects and the maximum amount of infant formula consumption was estimated based on the recommended usage level in the package insert of Sanlu infant formula and other brands. Melamine was analyzed in 111 Sanlu infant fbrmula samples collected from the markets in Beijing and Gansu province using the LC-MS-MS with a limit of quantification of 0.05 mg/kg. Four levels of melamine concentration were chosen to estimate the dietary intakes, including the mean, median, 90th percentile, and maximum. Results The infants of 3 months had the highest intake of melamine, and with the increase of the age (inonth), the intake decreased. Based on the median melamine concentration (1 000 mg/kg) as an example, the melamine intakes fur the infants of 3, 6, 12, and 24 months were 23.4, 21.4, 15.0, and 8.6 mg/kg bw/d, respectively. Conclusion Dietary melamine intakes from tainted Sanln infant formula significantly exceeded the TDI level (0.2 mg/kg bw/d) recommended by the WHO Expert Meeting in 2008. However, the present assessment has some limitations including the poor representative samples, the varied melamine concentrations in the adulterated Sanlu infant formula, and other brand infant formula possibly consumed by these infants.展开更多
The toxicity of melamine has attracted much attention since the recent outbreaks of renal injury in pets and infants. Previous studies indicated that melamine by itself had low toxicity, whereas a mixture of melamine ...The toxicity of melamine has attracted much attention since the recent outbreaks of renal injury in pets and infants. Previous studies indicated that melamine by itself had low toxicity, whereas a mixture of melamine and cyanuric acid (M+CA) could cause serious renal damage. At present, most researches on the toxicity of M+CA are focused on the kidney. However, little is known about the adverse effects of this mixture on the reproductive system. In the present study, the toxicity of M+CA to testes was investigated. Immature male mice were orally dosed with 0, 0.6, 3, and 15 mg kg-1 d-1 of a 1:1 M+CA for 28 d. Pathological changes occurred in germ cells, such as loose arrangement, reduced numbers and karyopyknosis, indicating that this mixture was toxic to spermatogenesis. Compared with the control group, the TUNEL- positive germ cells increased significantly and the ratio of Bcl-2 to Bax, total antioxidant capacity and superoxide dismutase activity decreased significantly in the 3 and 15 mg kg-1 d- M+CA treated group, while the activities of caspase-3, caspase- 8 and caspase-9 remained unchanged. The results suggest that M+CA can induce apoptosis in the mice testes. The downregulation of Bcl-2/Bax and oxidative stress may play a pivotal role in the induction of apoptosis by M+CA in mice testes.展开更多
A fluorescent competitive assay for melamine was first developed utilizing dummy molecularly imprinted polymers(DMIPs) as artificial antibodies. This method is based on the competition between fluorescent substances...A fluorescent competitive assay for melamine was first developed utilizing dummy molecularly imprinted polymers(DMIPs) as artificial antibodies. This method is based on the competition between fluorescent substances and the unlabeled analyte for binding sites in synthesized DMIPs and the decreased binding of fluorescent substances to DMIPs due to increased concentrations of melamine in the solutions. DMIPs for melamine were synthesized under a hot water bath in the presence of the initiator azobisisobutyronitrile(AIBN) using 2,4-diamino-6-methyl-1,3,5-triazine(DAMT) as a dummy template, methacrylic acid(MAA) as a functional monomer, and ethylene glycol dimethacrylate(EGDMA) as a crosslinking agent. The adsorption capacity and selectivity of DMIPs for melamine were evaluated by the isothermal adsorption curve and Scatchard analysis. The evaluation results showed that the synthesized DMIPs had specific recognition sites for melamine and the maximum adsorption amount was 1 066.33 μg g^(-1). Later, 5-(4,6-d ichlorotriazinyl) amino fluorescein(DTAF) with a triazine ring, which s lightly resembles m elamine, w as selected as the fluorescent substance. The fluorescent competitive assay using DMIPs as t he antibody mimics was finally established by selecting and optimizing the reaction solvents, DMIPs amount, DTAF concentration, and incubation time. The optimal detection system showed a linear response w ithin range of 0.05-40 mg L^(-1) and the limit of detection(LOD) was 1.23 μg L^(-1). It was successfully applied to the detection of melamine in spiked milk samples wi th satisfactory recoveries(71.9 to 86.3%). According to the comparative analysis, the result of optimized fluorescent competitive assay re vealed excellent agreement with the HPLC-MS/MS result for melamine.展开更多
[ Objective] The research aimed to develop a new molecular imprinting solid-phase extraction column for the separation and enrichment of melamine in feed. [ Method] The molecular imprinting polymer of melamine was pre...[ Objective] The research aimed to develop a new molecular imprinting solid-phase extraction column for the separation and enrichment of melamine in feed. [ Method] The molecular imprinting polymer of melamine was prepared by mass polymerization method. This polymer was used as filler to prepare molecular imprinting polymer solid-phase extraction(MIP-SPE) column of melamine. The solid-phase extraction conditions were optimized and melamine content in concentrated solution was determined by using HPLC. [ Result] Melamine eould be separated selectively from feed and enriehed by self-made MIP-SPE column. It could wipe off complex matrix from feed and the addition recovery rate was 95%. The contrast experiment between MIP-SPE column and NMIP-SPE ( non-imprinted polymer- solid phase extraction) column showed that the extraction efficiency of the former was obviously higher than the latter. [ Conclusion] The home-made MIP- SPE column could be used to separate and enrich melamine in feed efficiently, with a broad application prospect.展开更多
基金supported by the National Natural Science Foundation of China(No.21774139)China,Key Research and Development Program of Shanxi Province,China(No,202102040201009)special fund of Beijing Key Laboratory of Clean Fuels and Efficient Catalytic Emission Reduction Technology and the Fund for Shanxi“1331 Project”.Thanks to Ningbo Kejiang Culture Sci.&Tech.Development Co.,Ltd.for the help in schematic drawing。
文摘Melamine formaldehyde foam(MFF)generates many poisonous chemicals through the traditional recycling methods for organic resin wastes.Herein,a high MFF degradation ratio of ca.97 wt.%was achieved under the mild conditions(160℃)in a NaOH–H2O system with ammelide and ammeline as the main degradation products.The alkaline solvent had an obvious corrosion effect for MFF,as indicated by scanning electron microscopy(SEM).The reaction process and products distribution were studied by Fourier-transform infrared spectroscopy(FTIR),X-ray photoelectron spectroscopy(XPS),and ^(13)C nuclear magnetic resonance(NMR).Besides,the MFF degradation products that have the similar chemical structures and bonding performances to those of melamine can be directly used as the raw material for synthesis of melamine urea-formaldehyde resins(MUFs).Moreover,the degradation system demonstrated here showed the high degradation efficiency after reusing for 7 times.The degradation process generated few harmful pollutants and no pre-or post-treatments were required,which proves its feasibility in the safe removal or recovery of waste MFF.
基金supported by the Universiti Brunei Darussalam Research Funding(Grant No.UBD/OAVCRI/CRGWG(022)/171001).
文摘Three-dimensional(3D)porous absorbents have attracted significant attention in the oily wastewater treatment technology due to their high porosity and elasticity.Given their amphiphilic surface,they have a propensity to simultaneously absorb water and oil,which restricts their range of applications.In this study,a reduced graphene oxide and titanium dioxide nanocomposite(rGO/TiO_(2))was used to fabricate an ultra-hydrophobic melamine sponge(MS)through interfacial modification using a solution immersion technique.To further modify it,poly-dimethylsiloxane(PDMS)was grafted onto its surface to establish stronger covalent bonds with the composite.The water contact angle of the sponge(rGO/TiO_(2)/PDMS/MS)was 164.2°,which satisfies the condition for ultrahydrophobicity.The evidence of its water repellency was demonstrated by the Cassie-Baxter theory and the lotus leaf effect.As a result of the increased density of rGO/TiO_(2)/PDMS/MS,it recorded an initial capacity that was 2 g/g lower than the raw MS for crude oil absorption.The raw MS retained 53% of its initial absorption capacity after 20 cycles of absorption,while rGO/TiO_(2)/PDMS/MS retained 97%,suggesting good recyclability.Excellent oil and organic solvent recovery(90%-96%)was demonstrated by rGO/TiO_(2)/PDMS/MS in oil-water combinations.In a continuous separation system,it achieved a remarkable separation efficiency of 2.4×10^(6)L/(m^(3)·h),and in turbulent emulsion separation,it achieved a demulsification efficiency of 90%-91%.This study provides a practical substitute for massive oil spill cleaning.
基金funded by Qingyang Science and Technology Support Project(KT2019-03)。
文摘A silylated melamine sponge(SMS)was prepared by two simple steps,namely,immersion and dehydration of a melamine sponge coated with methyltrichlorosilane.The silylated structure of SMS was characterized by FT-IR(Fourier-transform infrared)spectroscopy,SEM(Scanning electron microscopy)and in terms of water contact angles.Its oil-water absorption and separation capacities were measured by FT-IR and UV-visible spectrophoto-metry.The experimental results have shown that oligomeric silanol covalently bonds by Si-N onto the surface of melamine sponge skeletons.SMS has shown superhydrophobicity with a water contact angle exceeding 150°±1°,a better separation efficiency with regard to diesel oil(by 99.31%(wt/wt%)in oil-water mixture and even up to 99.99%(wt/wt%)for diesel oil in its saturated aqueous solution.Moreover,SMS inherited the intrinsicflame retardancy of the melamine sponge.In general,SMS has shown superhydrophobicity,high porosity,excellent selectivity,remarkable recyclability,and better absorption capacity for various oils and organic solvents,and a high separation efficiency for oil in saturated aqueous solutions.
文摘Objective To develop an analytical method for simultaneously qualitative and quantitative determination of melamine and triazine-related by-products including ammelide, ammeline, and cyanuric acid in milk and milk products by gas chromatography- tandem mass spectrometry (GC-MS/MS). Methods Melamine and triazine-related by-products namely ammelide, ammeline and cyanuric acid in the samples were extracted in a solvent mixture of diethylamine, water, and acetonitrile (10:40:50, V/V/V). After centrifugation, an aliquot of the supernatant was evaporated to dryness under a gentle stream of nitrogen gas, and then melamine and triazine-related by-products were derivatized using BSTFA with 1% TMCS. The derivatives of melamine and its analogues were determined by gas chromatography/tandem mass spectrometry using multiple reactional monitoring (MRM) with 2, 6-Diamino-4-chloropyrimidine (DACP) being used as an internal standard. Results The linear detectable ranges were from 0.004 mg/kg to 1.6 mg/kg for melamine, ammelide, ammeline, and cyanuric acid with a correlation coefficient no less than 0.999. The recovery rates of the tour compounds in spiked blank milk powder at concentrations 0.5, 1, 2 mg/kg were between 61.4%-117.2%, and the relative standard deviation was no more than 11.5% (n=6). The detection limits of melamine, ammelide, ammeline and cyanuric acid in milk powder were 0.002 mg/kg with a ratio of signal to noise of 3. Conclusion This GC-MS/MS method for simultaneous determination of melamine, ammelide, ammeline, and cyanuric acid in milk and milk products is sensitive and specific.
文摘Objective To investigate the occurrence and concentrations of melamine and its analogues in tainted infant formula and to identify the etiologic factors for the urinary stones epidemic in infants and young children in China in 2008. Methods Sanlu infant formula samples were collected from families of the affected children in Gansu province, and markets in Gansu and Hebei provinces and Beijing city. Melamine and its analogues, including cyanuric acid, ammeline, and ammelide were measured by gas chromatography/tandem mass spectrometry. Results High prevalence and concentrations of melamine were found in Sanlu infant formula samples, with low concentrations of cyanuric acid, ammeline and ammelide. Melamine were detected in 87 out of 111 Sanlu infant formula samples with a range of 118 to 4 700 mg/kg, Conclusion The results provide strong evidence for melamine as the etiological factor for the urinary stones epidemic in infants and young children in China in 2008.
文摘An improved method for preparing melamine cyanurate (MCA) based flame retardant polyamide 6 (FRPA6) materials has been proposed. This processing method, i.e., improved in situ polymerization, was used to synthesize flame retardant PA6. In situ formed MCA nanoparticles were supposed to be linked to PA6 chains in the ε-caprolactam hydrolytic polymerization system to obtain startype polymers for the first time. Through TEM photographs, it can be found that the in situ formed MCA nanoparticles with diametric size of less than 50 nm, are nanoscaled, highly uniformly dispersed in the PA6 matrix. Synthesized flame retardant PA6 have good fire performance which can achieve UL-94 V-0 rating at 1.6 mm thickness with the presence of 7.34 wt.% MCA in the matrix.
文摘Objectives To study the migration of melamine into foods from plastic food packaging materials and dairy product containers commonly used in China. Methods 37 samples were collected from the market. The EU migration testing conditions were adopted with distilled water, 3% acetic acid, n-hexane and 15% ethanol being chosen as the simulating solutions. The HPLC method was used to detect melamine. Results No melamine was detected in 15 dairy product containers. Among the 22 plastic samples, 16 of polypropylene, and polycarbonate types had no detectable amount melamine while a low level of melamine was found in 3 of the 6 melamine resin containers. Conclusion Migration of melamine from food packaging materials in China market is in line with the requirements of EU.
文摘Surface electropositivity and low internal resistance are important factors to improve the anode performance in microbial fuel cells (MFCs). Nitrogen doping is an effective way for the modification of traditional carbon materials. In this work, heat treatment and melamine were used to modify carbon felts to enhance electrogenesis capacity of MFCs. The modified carbon felts were characterized using X-ray photoelectron spectroscopy (XPS), scanning electron microscope (SEM), atomic force microscopy (AFM) and malvern zeta potentiometer. Results show that the maximum power densities under heat treatment increase from 276.1 to 423.4 mW/m(2) (700 degrees C) and 461.5 mW/m(2) (1200 degrees C) and further increase to 472.5 mW/m(2) (700 degrees C) and 515.4 mW/m(2) (1200 degrees C) with the co-carbonization modification of melamine. The heat treatment reduces the material resistivity, improves the zeta potential which is beneficial to microbial adsorption and electron transfer. The addition of melamine leads to the higher content of surface pyridinic and quaternary nitrogen and higher zeta potential. It is related to higher MFCs performance. Generally, the melamine modification at high temperature increases the feasibility of carbon felt as MFCs's anode materials. (C) 2016 Science Press and Dalian Institute of Chemical Physics, Chinese Academy of Sciences. Published by Elsevier B.V. and Science Press. All rights reserved.
基金the financial support from the National Basic Research Program of China(No. 2009CB623200)the National Natural Science Foundation of China(No.50539040)the Scientific Research Foundation of Graduate School of Southeast University(No.YBJJ 0725).
基金Supported by the National Natural Science Foundation of China(21466016,21577053)the Natural Science Foundation of Yunnan Province(2016FB024).
文摘A general and versatile strategy to prepare melamine-formaldehyde(MF)microcapsules encapsulating oil-based fragrances by combining solvent evaporation and in situ polymerization was proposed in this work.The oil-based fragrance was pre-encapsulated by an inner polyacrylate membrane via solvent evaporation,followed by in situ polymerization of MF precondensates as an outer shell.The polyacrylate membrane is used as an intermediate bridging layer to stabilize the oil-based fragrance,and to provide driving forces for in situ polymerization of MF precondensates through electrostatic attractions between carboxyl groups and ammonium ions.It was demonstrated that MF microcapsules containing clove oil were prepared successfully.The amount and the composition of the intermediate polyacrylate bridging layer were critical.Smooth and sphere-shaped MF-clove oil microcapsules were prepared when the weight ratio of polyacrylate to clove oil was over 60 wt%and the concentration of acrylic acid(AA)increased to 10 wt%in polyacrylate.In addition,MF microcapsules containing sunflower oil and hexyl salicylate were prepared by using this method.The work suggests that this new approach can be potentially used to encapsulate various core materials,tuning the shell properties of microcapsules such as thickness,mechanical strength and release properties.
文摘A sensitive chemiluminescence(CL) method was developed for determining melamine in urine and plasma samples based on the fact that melamine can remarkably enhance the chemiluminescence of Luminol-K3 Fe(CN)6 system in alkaline medium. The determination conditions were optimized. Under optimum conditions, the chemiluminescence intensity had a good linear relationship with melamine in the range of 9.0 × 10^-9 - 7.0 × 10^-6 g/mL with a correlation coefficient of 0. 9992. The detection limits (3o) were 3.54 ng/mL for urine sample and 6.58 ng/mL for plasma sample. The average recoveries of melamine were 102.6% for urine sample and 95.1% for plasma sample. Melamine in samples was extracted with liquid-liquid extraction procedures and the assay results coincided very well with that determined with flow injection chemiluminescence method. The method provides a reproducible and stable approach for sensitive detection and quantification of melamine in urine and plasma samples.
基金The authors thank National Natural Science Foundation of China(51803190)National Key R&D Program of China(2019YFA0706802)financial support.
文摘The development of multifunctional and efficient electromagnetic wave absorbing materials is a challenging research hotspot.Here,the magnetized Ni flower/MXene hybrids are successfully assembled on the surface of melamine foam(MF)through electrostatic self-assembly and dip-coating adsorption process,realizing the integration of microwave absorption,infrared stealth,and flame retardant.Remarkably,the Ni/MXene-MF achieves a minimum reflection loss(RLmin)of−62.7 dB with a corresponding effective absorption bandwidth(EAB)of 6.24 GHz at 2 mm and an EAB of 6.88 GHz at 1.8 mm.Strong electromagnetic wave absorption is attributed to the three-dimensional magnetic/conductive networks,which provided excellent impedance matching,dielectric loss,magnetic loss,interface polarization,and multiple attenuations.In addition,the Ni/MXene-MF endows low density,excellent heat insulation,infrared stealth,and flame-retardant functions.This work provided a new development strategy for the design of multifunctional and efficient electromagnetic wave absorbing materials.
文摘Melamine formaldehyde (MF) foam is kind of fire-retardant material and has great potential in acoustic and thermal insulation area. In this article, MF resin foam was prepared by microwave radiation. We discussed the thermal stability of MF foam and the effect of different emulsifiers on its morphology, apparent density, fire-retardancy and mechanical property. The decomposition temperature of MF foam we prepared is nearly 400℃ and the constitution of residue after combustion is made up of carbon and graphite. Emulsifier influenced the apparent density of MF foam and using coemulsifiers can get flexible foam with uniform cell size, good morphology and low apparent density. When the fire-retardant MF foam’s apparent density is low of 5.53 kg/cm-3, its value of LOI can reach 32.4. The mechanical property of foam is consistent with apparent density.
基金supported by National Natural Science Foundation of China(grant number:81072372)
文摘Objective We tested whether melamine nephrotoxicity was exacerbated by urate(a typical component of renal stones in humans)in rats with hyperuricemiainduced by the uricase inhibitor,potassium oxonate(Oxo).Methods Rats were exposed to melamine or Oxo alone or combinations of melamine(200-400 mg/kg)and Oxo(200-600 mg/kg)for 3 consecutive days.Kidney injury was evaluated by renal biochemical functions,histomorphology,and lipid peroxidation.Kidney crystals were analyzed for their composition.Results Nephrotoxicity was minimal in animals administered melamine or Oxo alone,but it was demonstrable in animals administered at least 800 mg/kg of the two compounds combined.All rats in the 400+600(melamine+Oxo)and 400+400 mg/kg groups and 4 out of 6 in the 200+600 mg/kg group died within 3 days;no rat died in the 200+400 or 200+200 mg/kg group.Dose-dependent renal damage resembling clinical findings in affected patients was observed in rats administered the two compounds.Crystal composition determination revealed the existence of melamine and uric acid in the affected kidneys,resembling human stones.Conclusion Our findings suggest that uric acid plays a key role in melamine-related kidney injury in humans.Future studies should consider uric acid together with melamine when examining adverse effects in humans.
文摘Objective To determine the prevalence of urolithiasis in young children fed infant formula(IF) contaminated with melamine,and the association between IF consumption and urolithiasis.Design A total of 2 733 children ≤3 years of age on September 1,2008 in two townships of Gansu Province,China were studied.Cases of urolithiasis were diagnosed by ultrasonography.Milk product consumption was determined by their caregivers.Remaining IF samples were tested for melamine and cyanuric acid.Results Of 2 733 eligible children in the two townships,2 186(80%) were enrolled in our study.Overall,16.6%(362) of 2 186 children had urolithiasis.The prevalence was 24.6% in children exclusively fed Sanlu brand IF,9.7% in those fed other IF,and 8.5% in those fed exclusively on other milk products.For children exclusively breast-fed,no urolithiasis was found(P0.05).The prevalence of urolithiasis was 11.4% in children fed 400 g of Sanlu IF,rising to 37.5% in children fed over 25 600 g.Of 48 Sanlu IF samples,91.7% contained melamine(median=1 800 ppm;range=45-4 700) and 66.7% contained cyanuric acid(median=1.2 ppm;range=0.4-6.3).Melamine was also detected in 22.2% of 36 other brand IF(median=27.5 ppm,range=4-50).Conclusions Urolithiasis was associated with melamine-contaminated IF.Although one product caused most morbidity,other milk products may have also contributed to the outbreak.
基金The authors appreciate the support from the Natural Science Foundation of Shandong Province(ZR2019MB019,ZR2018MEM020)We also acknowledge financial support from the Key Research and Development Program of Shandong Province(2019GSF111047).
文摘With the increasing energy demand together with the deteriorating environment and decreasing fossil fuel resources,the development of highly efficient energy conversion and storage devices is one of the key challenges of both fundamental and applied research in energy technology.Melamine sponges(MS)with low density,high nitrogen content,and high porosity have been used to design and obtain three‐dimensional porous carbon electrode materials.More importantly,they are inexpensive,environment‐friendly,and easy to synthesize.There have been many reports on the modification of carbonized MS and MS‐based composites for supercapacitor and lithium battery electrode materials.In this paper,recent studies on the fabrication of electrode materials using MS as raw materials have been mainly reviewed,including carbonation,doping activation,and composite modification of MS,and expectations for the development of porous carbon materials for energy storage as a reference with excellent performance,environment‐friendliness,and long life.
文摘Objective To estimate the dietary melamine exposure in Chinese infants and young children from the consumption of melamine adulterated Sanlu infant formula. Methods Four age groups of infants and young children (3, 6, 12, and 24 months) were chosen as the assessed subjects and the maximum amount of infant formula consumption was estimated based on the recommended usage level in the package insert of Sanlu infant formula and other brands. Melamine was analyzed in 111 Sanlu infant fbrmula samples collected from the markets in Beijing and Gansu province using the LC-MS-MS with a limit of quantification of 0.05 mg/kg. Four levels of melamine concentration were chosen to estimate the dietary intakes, including the mean, median, 90th percentile, and maximum. Results The infants of 3 months had the highest intake of melamine, and with the increase of the age (inonth), the intake decreased. Based on the median melamine concentration (1 000 mg/kg) as an example, the melamine intakes fur the infants of 3, 6, 12, and 24 months were 23.4, 21.4, 15.0, and 8.6 mg/kg bw/d, respectively. Conclusion Dietary melamine intakes from tainted Sanln infant formula significantly exceeded the TDI level (0.2 mg/kg bw/d) recommended by the WHO Expert Meeting in 2008. However, the present assessment has some limitations including the poor representative samples, the varied melamine concentrations in the adulterated Sanlu infant formula, and other brand infant formula possibly consumed by these infants.
基金supported by the National Natural Science Foundation of China(30871853)
文摘The toxicity of melamine has attracted much attention since the recent outbreaks of renal injury in pets and infants. Previous studies indicated that melamine by itself had low toxicity, whereas a mixture of melamine and cyanuric acid (M+CA) could cause serious renal damage. At present, most researches on the toxicity of M+CA are focused on the kidney. However, little is known about the adverse effects of this mixture on the reproductive system. In the present study, the toxicity of M+CA to testes was investigated. Immature male mice were orally dosed with 0, 0.6, 3, and 15 mg kg-1 d-1 of a 1:1 M+CA for 28 d. Pathological changes occurred in germ cells, such as loose arrangement, reduced numbers and karyopyknosis, indicating that this mixture was toxic to spermatogenesis. Compared with the control group, the TUNEL- positive germ cells increased significantly and the ratio of Bcl-2 to Bax, total antioxidant capacity and superoxide dismutase activity decreased significantly in the 3 and 15 mg kg-1 d- M+CA treated group, while the activities of caspase-3, caspase- 8 and caspase-9 remained unchanged. The results suggest that M+CA can induce apoptosis in the mice testes. The downregulation of Bcl-2/Bax and oxidative stress may play a pivotal role in the induction of apoptosis by M+CA in mice testes.
基金supported by the National Natural Science Foundation of China (31260620, 31471654)the Special Fund for Agro-scientific Research in the Public Interest of China (201203094)
文摘A fluorescent competitive assay for melamine was first developed utilizing dummy molecularly imprinted polymers(DMIPs) as artificial antibodies. This method is based on the competition between fluorescent substances and the unlabeled analyte for binding sites in synthesized DMIPs and the decreased binding of fluorescent substances to DMIPs due to increased concentrations of melamine in the solutions. DMIPs for melamine were synthesized under a hot water bath in the presence of the initiator azobisisobutyronitrile(AIBN) using 2,4-diamino-6-methyl-1,3,5-triazine(DAMT) as a dummy template, methacrylic acid(MAA) as a functional monomer, and ethylene glycol dimethacrylate(EGDMA) as a crosslinking agent. The adsorption capacity and selectivity of DMIPs for melamine were evaluated by the isothermal adsorption curve and Scatchard analysis. The evaluation results showed that the synthesized DMIPs had specific recognition sites for melamine and the maximum adsorption amount was 1 066.33 μg g^(-1). Later, 5-(4,6-d ichlorotriazinyl) amino fluorescein(DTAF) with a triazine ring, which s lightly resembles m elamine, w as selected as the fluorescent substance. The fluorescent competitive assay using DMIPs as t he antibody mimics was finally established by selecting and optimizing the reaction solvents, DMIPs amount, DTAF concentration, and incubation time. The optimal detection system showed a linear response w ithin range of 0.05-40 mg L^(-1) and the limit of detection(LOD) was 1.23 μg L^(-1). It was successfully applied to the detection of melamine in spiked milk samples wi th satisfactory recoveries(71.9 to 86.3%). According to the comparative analysis, the result of optimized fluorescent competitive assay re vealed excellent agreement with the HPLC-MS/MS result for melamine.
基金Supported by Xiamen Science and Technology Plan Project(3502Z20123046)A-class Plan Project of Education Department of Fujian Province(JA12465)
文摘[ Objective] The research aimed to develop a new molecular imprinting solid-phase extraction column for the separation and enrichment of melamine in feed. [ Method] The molecular imprinting polymer of melamine was prepared by mass polymerization method. This polymer was used as filler to prepare molecular imprinting polymer solid-phase extraction(MIP-SPE) column of melamine. The solid-phase extraction conditions were optimized and melamine content in concentrated solution was determined by using HPLC. [ Result] Melamine eould be separated selectively from feed and enriehed by self-made MIP-SPE column. It could wipe off complex matrix from feed and the addition recovery rate was 95%. The contrast experiment between MIP-SPE column and NMIP-SPE ( non-imprinted polymer- solid phase extraction) column showed that the extraction efficiency of the former was obviously higher than the latter. [ Conclusion] The home-made MIP- SPE column could be used to separate and enrich melamine in feed efficiently, with a broad application prospect.