Poly(p-phenylene terephthalamide)(PPTA)pulp was prepared by polycondensation of the p-phenylene diamine(PPDA)with terephthaloyl chloride(TPC)in the completely anhydrous solvent system of N-methyl pyrrolidone(NMP)havin...Poly(p-phenylene terephthalamide)(PPTA)pulp was prepared by polycondensation of the p-phenylene diamine(PPDA)with terephthaloyl chloride(TPC)in the completely anhydrous solvent system of N-methyl pyrrolidone(NMP)having calcium chloride,in the presence of poly(vinyl pyrrolidone)(PVP)having a viscosity average molecular weight lower than 40 000.It was confirmed that the polycondensation could be accelerated,the inherent viscosity of the polymer could be increased,and the polymers could be fibrillated more easily by the addition of the PVP.FTIR and X-ray spectra proved that PVP had not combined into molecular chains of the resultant PPTA pulps.The morphology of the resultant pulps,the effect of viscosity average molecular weight,amount and adding mode of PVP on inherent viscosity,specific surface area,and mean length of the resultant pulps were discussed in detail.And the friction and wear properties of the compound reinforced by the resultant pulps were simply investigated.展开更多
High viscous PPTA copolymer is prepared by low temperature solution copolycondensation of terephth-aloylchloride, p-phenylenediamine and p, p'-diamino-phenylpiperazine in the NMP-CaCl2 solvent system. The inherent...High viscous PPTA copolymer is prepared by low temperature solution copolycondensation of terephth-aloylchloride, p-phenylenediamine and p, p'-diamino-phenylpiperazine in the NMP-CaCl2 solvent system. The inherent viscosity of all copolymers is more than 5. If more quantity of 3rd monomer is introduced into the macromolecular chain, the inherent viscosity becomes higher. The copolymer's ash content is less than 1000 μg/g. The heat durability of copolymer is close to that of PPTA, and its dissolubility is superior to that of PPTA.展开更多
文摘Poly(p-phenylene terephthalamide)(PPTA)pulp was prepared by polycondensation of the p-phenylene diamine(PPDA)with terephthaloyl chloride(TPC)in the completely anhydrous solvent system of N-methyl pyrrolidone(NMP)having calcium chloride,in the presence of poly(vinyl pyrrolidone)(PVP)having a viscosity average molecular weight lower than 40 000.It was confirmed that the polycondensation could be accelerated,the inherent viscosity of the polymer could be increased,and the polymers could be fibrillated more easily by the addition of the PVP.FTIR and X-ray spectra proved that PVP had not combined into molecular chains of the resultant PPTA pulps.The morphology of the resultant pulps,the effect of viscosity average molecular weight,amount and adding mode of PVP on inherent viscosity,specific surface area,and mean length of the resultant pulps were discussed in detail.And the friction and wear properties of the compound reinforced by the resultant pulps were simply investigated.
文摘High viscous PPTA copolymer is prepared by low temperature solution copolycondensation of terephth-aloylchloride, p-phenylenediamine and p, p'-diamino-phenylpiperazine in the NMP-CaCl2 solvent system. The inherent viscosity of all copolymers is more than 5. If more quantity of 3rd monomer is introduced into the macromolecular chain, the inherent viscosity becomes higher. The copolymer's ash content is less than 1000 μg/g. The heat durability of copolymer is close to that of PPTA, and its dissolubility is superior to that of PPTA.
