Photosensitive polyimide/titania hybrid was prepared successfully by sol gel process. This hybrid material posseses a good photolithographic property under UV exposure. The introduction of titania leads to the increas...Photosensitive polyimide/titania hybrid was prepared successfully by sol gel process. This hybrid material posseses a good photolithographic property under UV exposure. The introduction of titania leads to the increase in refractive index of the hybrid.展开更多
Fe^3＋ -doped nanometer TiO2 photocatalysts were prepared by sol-gel technique. TiO2 powders with different Fe^3＋ / Ti^4 ＋ molar ratios ranging from 0. 05% to 25% were synthesized by calcinating the gels in the temp...Fe^3＋ -doped nanometer TiO2 photocatalysts were prepared by sol-gel technique. TiO2 powders with different Fe^3＋ / Ti^4 ＋ molar ratios ranging from 0. 05% to 25% were synthesized by calcinating the gels in the temperature range of 200-600 ℃ . The effects of the content of iron ions and calcination temperature on the physical properties of the powders and their photocatalytic activities were examined by the photodecorapositon of methyl orange in sunlight. The results show that Fe dopant can decrease the temperature of nanatase-ratile transformation. The ideal photocatalytic property was achieved when the sample with an Fe^3＋ / Ti^4＋ ratio of 20 at% was calcined at about 300 ℃ for an hour, which is superior to that of commercial Degussa P-25. The optimum microstructure of the Fe-doped TiO2 for a high photocatalytic activity in sunlight is consisted of nanatase and ratile.展开更多
Five lightweight castables containing different TiO2 additions were prepared by using porous corundum - spinel （ MgAl2O4 ） ceramics as aggregate. Corrosion of the lightweight cstables by ladle slag was conducted u...Five lightweight castables containing different TiO2 additions were prepared by using porous corundum - spinel （ MgAl2O4 ） ceramics as aggregate. Corrosion of the lightweight cstables by ladle slag was conducted using a static crucible test. The effect of the TiO2 addition on the slag resistances of the lightweight corundum -spinel castables was investigated through SEM, EDS and Fact- Sage@ software, etc. h was found that TiO2 additi,ve t,vmoted the sintering degree of the castables, deereased the average pore .size, the apparent porosity, and the contact area between the casmbles and slag, and then en- hanced the corrosion resistance. However, TiO2 additive decreased the viscosity of the penetrated .slag simultane- ously, and then deteriorated the penetration resistance.展开更多
文摘Photosensitive polyimide/titania hybrid was prepared successfully by sol gel process. This hybrid material posseses a good photolithographic property under UV exposure. The introduction of titania leads to the increase in refractive index of the hybrid.
基金Founded by the Science and Technology Foundation of AnhuiProvince (No.010301E2)
文摘Fe^3＋ -doped nanometer TiO2 photocatalysts were prepared by sol-gel technique. TiO2 powders with different Fe^3＋ / Ti^4 ＋ molar ratios ranging from 0. 05% to 25% were synthesized by calcinating the gels in the temperature range of 200-600 ℃ . The effects of the content of iron ions and calcination temperature on the physical properties of the powders and their photocatalytic activities were examined by the photodecorapositon of methyl orange in sunlight. The results show that Fe dopant can decrease the temperature of nanatase-ratile transformation. The ideal photocatalytic property was achieved when the sample with an Fe^3＋ / Ti^4＋ ratio of 20 at% was calcined at about 300 ℃ for an hour, which is superior to that of commercial Degussa P-25. The optimum microstructure of the Fe-doped TiO2 for a high photocatalytic activity in sunlight is consisted of nanatase and ratile.
基金The National Natural Science Foundation of China(Grant No.51302201)
文摘Five lightweight castables containing different TiO2 additions were prepared by using porous corundum - spinel （ MgAl2O4 ） ceramics as aggregate. Corrosion of the lightweight cstables by ladle slag was conducted using a static crucible test. The effect of the TiO2 addition on the slag resistances of the lightweight corundum -spinel castables was investigated through SEM, EDS and Fact- Sage@ software, etc. h was found that TiO2 additi,ve t,vmoted the sintering degree of the castables, deereased the average pore .size, the apparent porosity, and the contact area between the casmbles and slag, and then en- hanced the corrosion resistance. However, TiO2 additive decreased the viscosity of the penetrated .slag simultane- ously, and then deteriorated the penetration resistance.