We have prepared a high-density polyaniline（PANI） paste（50 mg/m L）, with similar physical properties to those of paints or pigments. The synthesis of PANI is confirmed by Fourier transform infrared（FT-IR） spectr...We have prepared a high-density polyaniline（PANI） paste（50 mg/m L）, with similar physical properties to those of paints or pigments. The synthesis of PANI is confirmed by Fourier transform infrared（FT-IR） spectroscopy. The morphologies of PANI, doped PANI, and doped PANI paste are confirmed by scanning electron microscopy（SEM）. Particles of doped PANI paste are approximately 40–50 nm in diameter, with a uniform and cubic shape. The electrochemical performances of doped PANI paste using both liquid and solid polymer electrolytes have been measured by galvanostatic charge and discharge process. The cell fabricated with doped PANI paste and the solid polymer electrolyte exhibits a discharge capacity of ～87 μAh/cm2（64.0 m Ah/g） at the second cycle and～67 μAh/cm2（50.1 m Ah/g） at the 100 th cycle.展开更多
基金supported by a grant from the Fundamental R&D Program for Core Technology of Materials funded by the Korean Ministry of Knowledge Economy and by the Priority Research Centers Program through the National Research Foundation of Korea(NRF)funded by the Ministry of Education,Science and Technology(2009-0093818)
文摘We have prepared a high-density polyaniline（PANI） paste（50 mg/m L）, with similar physical properties to those of paints or pigments. The synthesis of PANI is confirmed by Fourier transform infrared（FT-IR） spectroscopy. The morphologies of PANI, doped PANI, and doped PANI paste are confirmed by scanning electron microscopy（SEM）. Particles of doped PANI paste are approximately 40–50 nm in diameter, with a uniform and cubic shape. The electrochemical performances of doped PANI paste using both liquid and solid polymer electrolytes have been measured by galvanostatic charge and discharge process. The cell fabricated with doped PANI paste and the solid polymer electrolyte exhibits a discharge capacity of ～87 μAh/cm2（64.0 m Ah/g） at the second cycle and～67 μAh/cm2（50.1 m Ah/g） at the 100 th cycle.