Nonionic Polymerizable Emulsifier in High-Solids-Content Acrylate Emulsion Polymerization

Stable high-solids-content acrylate emulsion were obtained with a nonionic polymerizable emulsifier allyloxy nonylphenoxy poly （ethyleneoxy） （10） ether （ANPEO10）, and a conventional emulsifier OP-10 as a reference sample. 1H NMR proves that the polymerizable emulsifier ANPEO10 has been incorporated into the resulted acrylate polymers. TEM demonstrates that there are some differences in the particle morphologies. AFM proves that the polymerizable emulsifier ANPEO10 migrating to the surface of the emulsion film was much less than the conventional emulsifier OP-10. The polymerizable emulsifier ANPEO10 can enhance the adhesion with glass plate compared to the conventional emulsifier. Furthermore, with increasing amount of emulsifier, the surface free energy of the films first decreased and then increased, and the adhesion with glass plate is initially enhanced and then attenuated. The water-resistance and solvent-resistance of the films prepared by the polymerizable emulsifier ANPEO10 are superior to those prepared by the conventional emulsifier OP-10.

PREPARATION OF POLYSTYRENE/SiO_2 COMPOSITE NANOPARTICLES BEARING SULFONIC GROUPS ON THE SURFACE VIA EMULSION COPOLYMERIZATION USING A POLYMERIZABLE EMULSIFIER

Functionalized PS/SiO_2 composite nanoparticles bearing sulfonic groups on the surface were successfully synthesized via emulsion copolymerization using a polymerizable emulsifierαolefin solfonate(AOS).As demonstrated by transmission electron microscopy and atomic force microscopy,well-defined core-shell PS/SiO_2 composite nanoparticles with a diameter of 50 nm were obtained.Sulfonic groups introduced onto the surface of the composite nanoparticles were quantified by FTIR,and can be controlled to some exten...

Properties of Polyacrylate Latex Prepared Under Different Emulsified Systems

The polyacrylate latexes were synthesized via pre-emulsified and semi-continuous seeded emulsion polymerization technology when conventional surfactant or polymerizable surfactant was used as emulsifiers. The resultant latexes and their films were characterized with the contact angle determinator and rheometer. Effect of the polymerizable surfactant on water resistance, stability and rheology of the latex was studied. Results show that the water resistance of film is increased first then decreased with the increase of the amount of the polymerizable surfactant. There exists the optimum value of the amount of the polymerizable surfactant for the water resistance of the film. In comparison with the latex prepared with the conventional surfactant, both the mechanical stability and the freezing-thaw stability of the latex are improved when the polymerizable surfactant is used during the course of the emulsion polymerization. The resultant latex has rheological properties of pseudo-plastic fluid and belongs to non-Newtonian fluid.

STUDY ON THE POLYMERIZATION KINETICS AND STABILITY OF P(UA)/MMA MICROEMULSION

Urethane acrylate anionomer (APUA) as a kind of new type polymerizable emulsifier was synthesized using 2,4-toluene diisocyanate (TDI), polypropylene glycol (PPG), 2-hydroxyethyl methacrylate (HEMA) and dimethylolpropionic acid (DMPA). The critical micelle concentration (CMC) of APUA was measured by the methods of conductance and surface tension. The comparative studies between polymerizable emulsifier AUPA and conventional emulsifier sodium dodecyl sulfate (SDS) were carried out in the emulsion polymerization of methyl methacrylate (MMA). Polymerization kinetics, stability, size and morphology of the latex particles were investigated. It was found that in APUA both water soluble initiator potassium persulfate (KPS) and oil soluble initiator 2,2'-azobisisobutyronitrile (AlBN) can start the reaction of MMA, and the polymerization rate and yield were very high. On using AlBN as an initiator, the conversion-time behavior of MMA with APUA as emulsifier was different to that of SDS as emulsifier, signifying a different nucleation mechanism of the polymer latex particle. The average size of the two kinds of particles is about 50 nm. The particle size decreases with increasing emulsifier concentration. On using KPS as the initiator, APUA as emulsifier, cross-linking hydrogel of PMMA would be formed, but SDS was used as emulsifier and the hydrogel of PMMA was not present.