2,4-Dichlorophenol was removed from wasterwater using a new hydrophobic poly（phthalazinone ether sulfone ketone） （PPESK） hollow fiber membrane by vacuum membrane distillation （VMD）.
To improve its limiting flux and antifouling characteristics in a submerged membrane-bioreactor （SMBR） for wastewater treatment, polypropylene hollow fiber microporous membrane （PPHFMM） was surface-modified by the...To improve its limiting flux and antifouling characteristics in a submerged membrane-bioreactor （SMBR） for wastewater treatment, polypropylene hollow fiber microporous membrane （PPHFMM） was surface-modified by the plasma-induced immobilization of poly （N-vinyl-2-pyrrolidone） （PVP） and the plasma treatment with different gases respectively. Attenuated total reflection-Fourier transform infrared spectroscopy （FT-IR/ATR）, X-ray photoelectron spectroscopy （XPS） and field emission scanning electron microscope （FE-SEM） were used to characterize the structural and morphological changes on the membrane surface. Water contact angle was measured by the sessile drop method. It was found that the water contact angle was 128.8, 72.3, 62.7, 74.4, 79.1, 86.3, and 71.3° for the nascent, PVP-immobilized, air, 02, Ar, CO2 and H2O plasma treated PPHFMM, respectively. The SMBR was operated at fixed transmembrane pressure to determine the limiting flux for the PPHFMM before and after surface modification. Results showed that the limiting flux appeared to be 103, 159, 117, 133, 136, 121 and 152 L/（m^2· h） for the nascent, PVP-immobilized, air, O2, At, CO2 and H2O plasma treated PPHFMM, respectively. After continuous operation for about 50 h in the SMBR, the antifouling characteristics were improved to some extent.展开更多
Porous polypropylene hollow fiber(PPHF) membranes are widely used in liquid purification. However, the hydrophobicity of polypropylene(PP) has limited its applications in water treatment. Herein, we demonstrate that, ...Porous polypropylene hollow fiber(PPHF) membranes are widely used in liquid purification. However, the hydrophobicity of polypropylene(PP) has limited its applications in water treatment. Herein, we demonstrate that, for the first time, atomic layer deposition(ALD) is an effective strategy to conveniently upgrade the filtration performances of PPHF membranes. The chemical and morphological changes of the deposited PPHF membranes are characterized by spectral, compositional, microscopic characterizations and protein adsorption measurements. Al_2O_3 is distributed along the cross section of the PP hollow fibers, with decreasing concentration from the outer surface to the inner surface. The pore size of the outer surface can be easily turned by altering the ALD cycles. Interestingly, the hollow fibers become much more ductile after deposition as their elongation at break is increased more than six times after deposition with 100 cycles. The deposited membranes show simultaneously enhanced water permeance and retention after deposition with moderate ALD cycle numbers.For instance, after 50 ALD cycles a 17% increase in water permeance and one-fold increase in BSA rejection are observed. Moreover, the PP membranes exhibit improved fouling-resistance after ALD deposition.展开更多
Isotactic polypropylene （iPP） hollow fiber microporous membranes were prepared using thermally induced phase separation （TIPS） method. Di-n-butyl phthalate （DBP）, dioctyl phthalate （DOP）, and the mixed solvent...Isotactic polypropylene （iPP） hollow fiber microporous membranes were prepared using thermally induced phase separation （TIPS） method. Di-n-butyl phthalate （DBP）, dioctyl phthalate （DOP）, and the mixed solvent were used as diluents. The effect of α （DOP mass fraction in diluent） on the morphology and performance of the hollow fiber was investigated. With increasing α, the morphology of the resulting hollow fiber changes from typical cellular structure to mixed structure, and then to typical particulate structure. As a result, the permeability of the hollow fiber increases sharply, and the mechanical properties of the hollow fiber decrease obviously. It is suggested that the morphology and performances of iPP hollow fiber microporous membrane can be controlled via adjusting the compatibility between iPP and diluent.展开更多
Surface modification of microporous polypropylene hollow fiber membranes was performed by radical-induced graft polymerization of N,N-dimethylaminoethyl methacrylate (DMAEMA). The influences of temperature, monomer co...Surface modification of microporous polypropylene hollow fiber membranes was performed by radical-induced graft polymerization of N,N-dimethylaminoethyl methacrylate (DMAEMA). The influences of temperature, monomer concentration and pre-adsorbed amount of benzoyl peroxide on grafting degree were studied respectively. It was found that the appropriate graft temperature was 75 'C, at which the grafting degree was the highest and the hydrolytic decomposition of DMAEMA the lowest. Scanning electron photomicrography and the average pore diameters of the modified membranes demonstrated that part of the micropores on the membrane surface was plugged by the grafted polyDMAEMA chains, especially at high grafting degree. Contact angle and water swelling experiments showed that a moderate grafting degree could improve the hydrophilicity of the membranes. In the range of 11.3%-12.0% grafting degree, the water swelling percentage reached its maximum (51.1%) and the contact angle reached its minimum (74 degrees). The bovine serum albumin (BSA) adsorption experiment indicated that the grafted polyDMAEMA had a dual effect on protein adsorption. At the first stage, the BSA adsorption decreased with increasing of DMAEMA grafting degree. As the interaction between BSA and polyDMAEMA on membrane surface increased, the BSA adsorption increased with increasing of DMAEMA grafting degree.展开更多
在热致相分离法制备聚丙烯(iPP)中空纤维膜的过程中,通过添加疏水性TiO2纳米颗粒来提高膜的疏水性能,获得具有不同TiO2添加量的iPP/TiO2杂化膜.利用XRD、SEM、接触角测量仪以及光学显微镜等手段对膜的元素组成、形貌结构、疏水性以及油...在热致相分离法制备聚丙烯(iPP)中空纤维膜的过程中,通过添加疏水性TiO2纳米颗粒来提高膜的疏水性能,获得具有不同TiO2添加量的iPP/TiO2杂化膜.利用XRD、SEM、接触角测量仪以及光学显微镜等手段对膜的元素组成、形貌结构、疏水性以及油水分离效果等进行表征.结果表明,TiO2的添加改善了膜的疏水性能,对油包水乳化液表现出优异的分离效果;当TiO 2的添加量为0.5%时,膜的接触角达到147°,平均孔径和孔隙率同步增大,杂化膜的油通量达到了纯膜通量的150%.此外,粒径在0.5~1.5μm范围内的油包水乳化液经iPP Ti 5膜过滤后,其滤液中的水滴在光学显微镜下不可见.展开更多
文摘2,4-Dichlorophenol was removed from wasterwater using a new hydrophobic poly（phthalazinone ether sulfone ketone） （PPESK） hollow fiber membrane by vacuum membrane distillation （VMD）.
基金The Hi-Tech Research and Development Program (863) of China (No. 2002AA601230)
文摘To improve its limiting flux and antifouling characteristics in a submerged membrane-bioreactor （SMBR） for wastewater treatment, polypropylene hollow fiber microporous membrane （PPHFMM） was surface-modified by the plasma-induced immobilization of poly （N-vinyl-2-pyrrolidone） （PVP） and the plasma treatment with different gases respectively. Attenuated total reflection-Fourier transform infrared spectroscopy （FT-IR/ATR）, X-ray photoelectron spectroscopy （XPS） and field emission scanning electron microscope （FE-SEM） were used to characterize the structural and morphological changes on the membrane surface. Water contact angle was measured by the sessile drop method. It was found that the water contact angle was 128.8, 72.3, 62.7, 74.4, 79.1, 86.3, and 71.3° for the nascent, PVP-immobilized, air, 02, Ar, CO2 and H2O plasma treated PPHFMM, respectively. The SMBR was operated at fixed transmembrane pressure to determine the limiting flux for the PPHFMM before and after surface modification. Results showed that the limiting flux appeared to be 103, 159, 117, 133, 136, 121 and 152 L/（m^2· h） for the nascent, PVP-immobilized, air, O2, At, CO2 and H2O plasma treated PPHFMM, respectively. After continuous operation for about 50 h in the SMBR, the antifouling characteristics were improved to some extent.
基金Supported by the National Basic Research Program of China(2015CB655301)the Natural Science Foundation of Jiangsu Province(BK20150063)+1 种基金the Program of Excellent Innovation Teams of Jiangsu Higher Education Institutionsthe Project of Priority Academic Program Development of Jiangsu Higher Education Institutions(PAPD)
文摘Porous polypropylene hollow fiber(PPHF) membranes are widely used in liquid purification. However, the hydrophobicity of polypropylene(PP) has limited its applications in water treatment. Herein, we demonstrate that, for the first time, atomic layer deposition(ALD) is an effective strategy to conveniently upgrade the filtration performances of PPHF membranes. The chemical and morphological changes of the deposited PPHF membranes are characterized by spectral, compositional, microscopic characterizations and protein adsorption measurements. Al_2O_3 is distributed along the cross section of the PP hollow fibers, with decreasing concentration from the outer surface to the inner surface. The pore size of the outer surface can be easily turned by altering the ALD cycles. Interestingly, the hollow fibers become much more ductile after deposition as their elongation at break is increased more than six times after deposition with 100 cycles. The deposited membranes show simultaneously enhanced water permeance and retention after deposition with moderate ALD cycle numbers.For instance, after 50 ALD cycles a 17% increase in water permeance and one-fold increase in BSA rejection are observed. Moreover, the PP membranes exhibit improved fouling-resistance after ALD deposition.
基金Supported by the National Natural Science Foundation of China （No.20236030）.
文摘Isotactic polypropylene （iPP） hollow fiber microporous membranes were prepared using thermally induced phase separation （TIPS） method. Di-n-butyl phthalate （DBP）, dioctyl phthalate （DOP）, and the mixed solvent were used as diluents. The effect of α （DOP mass fraction in diluent） on the morphology and performance of the hollow fiber was investigated. With increasing α, the morphology of the resulting hollow fiber changes from typical cellular structure to mixed structure, and then to typical particulate structure. As a result, the permeability of the hollow fiber increases sharply, and the mechanical properties of the hollow fiber decrease obviously. It is suggested that the morphology and performances of iPP hollow fiber microporous membrane can be controlled via adjusting the compatibility between iPP and diluent.
基金The work was supported by the National Natural Science Foundation of China (Grant No. 20074033) and the High-TechResearch and Development Program of China (Grant no. 2002AA601230).
文摘Surface modification of microporous polypropylene hollow fiber membranes was performed by radical-induced graft polymerization of N,N-dimethylaminoethyl methacrylate (DMAEMA). The influences of temperature, monomer concentration and pre-adsorbed amount of benzoyl peroxide on grafting degree were studied respectively. It was found that the appropriate graft temperature was 75 'C, at which the grafting degree was the highest and the hydrolytic decomposition of DMAEMA the lowest. Scanning electron photomicrography and the average pore diameters of the modified membranes demonstrated that part of the micropores on the membrane surface was plugged by the grafted polyDMAEMA chains, especially at high grafting degree. Contact angle and water swelling experiments showed that a moderate grafting degree could improve the hydrophilicity of the membranes. In the range of 11.3%-12.0% grafting degree, the water swelling percentage reached its maximum (51.1%) and the contact angle reached its minimum (74 degrees). The bovine serum albumin (BSA) adsorption experiment indicated that the grafted polyDMAEMA had a dual effect on protein adsorption. At the first stage, the BSA adsorption decreased with increasing of DMAEMA grafting degree. As the interaction between BSA and polyDMAEMA on membrane surface increased, the BSA adsorption increased with increasing of DMAEMA grafting degree.
文摘在热致相分离法制备聚丙烯(iPP)中空纤维膜的过程中,通过添加疏水性TiO2纳米颗粒来提高膜的疏水性能,获得具有不同TiO2添加量的iPP/TiO2杂化膜.利用XRD、SEM、接触角测量仪以及光学显微镜等手段对膜的元素组成、形貌结构、疏水性以及油水分离效果等进行表征.结果表明,TiO2的添加改善了膜的疏水性能,对油包水乳化液表现出优异的分离效果;当TiO 2的添加量为0.5%时,膜的接触角达到147°,平均孔径和孔隙率同步增大,杂化膜的油通量达到了纯膜通量的150%.此外,粒径在0.5~1.5μm范围内的油包水乳化液经iPP Ti 5膜过滤后,其滤液中的水滴在光学显微镜下不可见.