In this paper, we succeed in fabricating high-temperature fiber of polysulfonamide/ZnO. Polysulfonamide/ZnO nanocomposite was prepared by in-situ polymerization. Some studies and characterization of Polysulfonamide/ Z...In this paper, we succeed in fabricating high-temperature fiber of polysulfonamide/ZnO. Polysulfonamide/ZnO nanocomposite was prepared by in-situ polymerization. Some studies and characterization of Polysulfonamide/ Zinc oxide nanocomposite with ZnO 0.5% have been done. It includes ηr,, Crystal degree and thermal property. Experiment＇s results showed that, ZnO as filler can improve crystal degree of polysulfonamide fiber. The crystal degree has been bnproved, from lower than 20% up to 27%. ηr of polysulfonamide/ Zinc oxide nanocomposite solution with ZnO 0.5% is 2.03. The maxinum weight loss of the nanocomposite occurred at 453.5 ℃.展开更多
Polysulfonamide/zinc oxide(PSA/ZnO) nanocomposite films with w(ZnO)=0.5% were prepared by in-situ polymerization based on 4,4′-diaminodiphenylsulfone and terephthaloyl chloride in the common solvent N,N-Dimethylaceta...Polysulfonamide/zinc oxide(PSA/ZnO) nanocomposite films with w(ZnO)=0.5% were prepared by in-situ polymerization based on 4,4′-diaminodiphenylsulfone and terephthaloyl chloride in the common solvent N,N-Dimethylacetamide(DMAc). Atomic force microscopy (AFM) was employed to observe the microstructure of the composite film. The thermal property was investigated by TGA and mechanical property was characterized by DXLL-1000 electromechanical material testing machine. The results showed that the breaking strength of the film containing 0.5% ZnO was great enhanced. The average size of ZnO particles was below 100 nm. The introduction of ZnO as nano filler in PSA react as UV shield effect and make the composite mechanical property improved.展开更多
A series of polysulfonamide （PSA）/TiO 2 modifier nano-composite films were successfully prepared by in-situ polymerization at a low temperature based on 4, 4-diaminodiphenylsulfone and terephthaloyl chloride in the ...A series of polysulfonamide （PSA）/TiO 2 modifier nano-composite films were successfully prepared by in-situ polymerization at a low temperature based on 4, 4-diaminodiphenylsulfone and terephthaloyl chloride in the common solvent N, N-dimethylacetamide （DMAc）. It was shown that the nano particles were well dispersed in the polymer substrate. Mean-while, PSA/TiO 2 /modifier composites exhibited good UV-resistant properties and mechanical properties. In addition, the composites’ heat stability improved. These prepared composites are promising in preparing spinning solution and might have potential application in heat-resistant fiber.展开更多
文摘In this paper, we succeed in fabricating high-temperature fiber of polysulfonamide/ZnO. Polysulfonamide/ZnO nanocomposite was prepared by in-situ polymerization. Some studies and characterization of Polysulfonamide/ Zinc oxide nanocomposite with ZnO 0.5% have been done. It includes ηr,, Crystal degree and thermal property. Experiment＇s results showed that, ZnO as filler can improve crystal degree of polysulfonamide fiber. The crystal degree has been bnproved, from lower than 20% up to 27%. ηr of polysulfonamide/ Zinc oxide nanocomposite solution with ZnO 0.5% is 2.03. The maxinum weight loss of the nanocomposite occurred at 453.5 ℃.
基金Education Commission of Shanghai (No04AB19)Science and Technology Commission of Shanghai Municipal Government(Nano Founds No 0452NM051)
文摘Polysulfonamide/zinc oxide(PSA/ZnO) nanocomposite films with w(ZnO)=0.5% were prepared by in-situ polymerization based on 4,4′-diaminodiphenylsulfone and terephthaloyl chloride in the common solvent N,N-Dimethylacetamide(DMAc). Atomic force microscopy (AFM) was employed to observe the microstructure of the composite film. The thermal property was investigated by TGA and mechanical property was characterized by DXLL-1000 electromechanical material testing machine. The results showed that the breaking strength of the film containing 0.5% ZnO was great enhanced. The average size of ZnO particles was below 100 nm. The introduction of ZnO as nano filler in PSA react as UV shield effect and make the composite mechanical property improved.
基金Project supported by the Shanghai Leading Academic Discipline Project (Grant No.s30107)the Science and Technology Commission of Shanghai Municipality (Grant No.0852nm00600)
文摘A series of polysulfonamide （PSA）/TiO 2 modifier nano-composite films were successfully prepared by in-situ polymerization at a low temperature based on 4, 4-diaminodiphenylsulfone and terephthaloyl chloride in the common solvent N, N-dimethylacetamide （DMAc）. It was shown that the nano particles were well dispersed in the polymer substrate. Mean-while, PSA/TiO 2 /modifier composites exhibited good UV-resistant properties and mechanical properties. In addition, the composites’ heat stability improved. These prepared composites are promising in preparing spinning solution and might have potential application in heat-resistant fiber.