A two-component waterborne polyurethane(2K-WPU) was prepared by mixing water-soluble acrylic resin and hexamethylene diisocyanate biuret, and then diluted for phase inversion with water. Compared with water-soluble ac...A two-component waterborne polyurethane(2K-WPU) was prepared by mixing water-soluble acrylic resin and hexamethylene diisocyanate biuret, and then diluted for phase inversion with water. Compared with water-soluble acrylic resin, the phase inversion of 2K-WPU occurs at lower water content. It is indicated by TEM that 2K-WPU parti-cles show a core-shell structure, in which HDI biuret is encapsulated by hydrophilic acrylic resin. 2K-WPU emulsion with HDI biuret has larger particle size and narrower distribution index, while for 2K-WPU emulsion with HDI iso-cyanurate, the latex not only has large particle size, but also has two-peak distribution. FTIR shows that the reaction be-tween HDI biuret and acrylic resin can complete in 12h. In addition, studies on effect of composition of acrylic resin on performance of 2K-WPU show that narrowing the polar difference between water-soluble acrylic resin and HDI biuret and improving the miscibility of two components are the key to prepare the transparent and high gloss films with high crosslinking density.展开更多
We determined the effects of adhesive type and loose tenon dimensions （length and thickness） on bending strength of T-shaped mor- tise and loose-tenon joints. Polyvinyl acetate （PVAc） and two-component polyuretha...We determined the effects of adhesive type and loose tenon dimensions （length and thickness） on bending strength of T-shaped mor- tise and loose-tenon joints. Polyvinyl acetate （PVAc） and two-component polyurethane （PU） adhesives were used to construct joint specimens. The bending moment capacity of joints increased significantly with increased length and thickness of the loose tenon. Bending moment capacity of joints constructed with PU adhesive was approximately 13% higher than for joints constructed with PVAc adhesive. We developed a predictive equation as a function of adhesive type and loose tenon dimensions to estimate the strength of the joints constructed of oriental beech （Fagus orientalis L.） under uniaxial bending load.展开更多
文摘A two-component waterborne polyurethane(2K-WPU) was prepared by mixing water-soluble acrylic resin and hexamethylene diisocyanate biuret, and then diluted for phase inversion with water. Compared with water-soluble acrylic resin, the phase inversion of 2K-WPU occurs at lower water content. It is indicated by TEM that 2K-WPU parti-cles show a core-shell structure, in which HDI biuret is encapsulated by hydrophilic acrylic resin. 2K-WPU emulsion with HDI biuret has larger particle size and narrower distribution index, while for 2K-WPU emulsion with HDI iso-cyanurate, the latex not only has large particle size, but also has two-peak distribution. FTIR shows that the reaction be-tween HDI biuret and acrylic resin can complete in 12h. In addition, studies on effect of composition of acrylic resin on performance of 2K-WPU show that narrowing the polar difference between water-soluble acrylic resin and HDI biuret and improving the miscibility of two components are the key to prepare the transparent and high gloss films with high crosslinking density.
文摘We determined the effects of adhesive type and loose tenon dimensions （length and thickness） on bending strength of T-shaped mor- tise and loose-tenon joints. Polyvinyl acetate （PVAc） and two-component polyurethane （PU） adhesives were used to construct joint specimens. The bending moment capacity of joints increased significantly with increased length and thickness of the loose tenon. Bending moment capacity of joints constructed with PU adhesive was approximately 13% higher than for joints constructed with PVAc adhesive. We developed a predictive equation as a function of adhesive type and loose tenon dimensions to estimate the strength of the joints constructed of oriental beech （Fagus orientalis L.） under uniaxial bending load.