Silane coupling agent KH560 was used to modify the surface of nano-α-Al<sub>2</sub>O<sub>3</sub> in ethanol-aqueous solution with different proportions. The particle size of nano-α-Al<sub&...Silane coupling agent KH560 was used to modify the surface of nano-α-Al<sub>2</sub>O<sub>3</sub> in ethanol-aqueous solution with different proportions. The particle size of nano-α-Al<sub>2</sub>O<sub>3</sub> was determined by nano-particle size analyzer, and the effects of nano-α-Al<sub>2</sub>O<sub>3</sub> content, ethanol-aqueous solution ratio and KH560 dosage on the dispersion and particle size of nano-α-Al<sub>2</sub>O<sub>3</sub> were investigated. The material structure before and after modification was determined by Fourier transform infrared spectroscopy (FTIR). Aqueous polyurethane resin and inorganic components are combined with modified nano-α-Al<sub>2</sub>O<sub>3</sub> dispersion to form chromium-free passivation solution. The solution is coated on the galvanized sheet, the adhesion and surface hardness are tested, the bonding strength of the coating and the surface hardness of the substrate are discussed. The corrosion resistance and surface morphology of the matrix were investigated by electrochemical test, neutral salt spray test and scanning electron microscope test. The chromium-free passivation film formed after the modification of nano-α-Al<sub>2</sub>O<sub>3</sub> increases the surface hardness of galvanized sheet by about 85%. The corrosion resistance of the film is better than that of a single polyurethane film. The results show that the surface hardness and corrosion resistance of polyurethane resin composite passivation film are significantly improved by the introduction of nano-α-Al<sub>2</sub>O<sub>3</sub>.展开更多
A series of transparent casting polyurethane resins (TCPU) were synthesized from cycloaliphatic diisocyanate (IPDI or H_(12)MDI), polyol, chain extender, crosslinking agents, catalyst and special aids (T),which were c...A series of transparent casting polyurethane resins (TCPU) were synthesized from cycloaliphatic diisocyanate (IPDI or H_(12)MDI), polyol, chain extender, crosslinking agents, catalyst and special aids (T),which were characterized by FTIR. The thermal stabilities of the obtained TCPU were examined by DSC and TGA, the glass transition temperature (T_g) was in the range of 95-110 ℃, the initial decomposition temperature (5% weight loss) was 250-265 ℃, and 10% weight loss at the temperature was in the range of 260-286℃ in nitrogen atmosphere. The morphologies of the fractured surfaces of TCPU were revealed by a scanning electron microscope (SEM). The crystalline-amorphous characters of TCPU were studied by WAXD, the result shows that TCPU possesses amorphous glassy characters. The optical properties of TCPU were studied by a UV-7500 visible light absorbance measurement. All the samples exhibited excellent optical properties and possessed light transmittance in the range of 91%-93%.展开更多
As the important matrix material,epoxy resin has been widely used in the composites for various fields.On account of the poor toughness of epoxy resin limiting their suitability for advanced applications,considerable ...As the important matrix material,epoxy resin has been widely used in the composites for various fields.On account of the poor toughness of epoxy resin limiting their suitability for advanced applications,considerable interests have been conducted to modify the epoxy resin to meet the engineering requirements.In this study,the bio-based polyurethane(PU)modified resin was adopted to modify the pure bisphenol-A epoxy by blending method with various proportions.Aiming to illuminate the curing behavior,mechanical and thermal properties,the blended epoxy systems were characterized by viscosity-time analysis,dynamic mechanical analysis(DMA)at different frequencies and temperatures,mechanical tensile test,thermogravimetric analysis(TGA)and Fourier transform infrared(FT-IR)spectroscopy.The results indicated that the introduction of PU modified epoxy was found to significantly inhibit the viscosity growth rates especially when the content of PU modified epoxy resin is higher than 60%.Notwithstanding the dynamic modulus and T_(g)reduced with the increment of PU modified epoxy,remarkable increment on the elongation at break was found and the flexibility was greatly promoted with the introduction of PU modified epoxy.The proportion of PU modified epoxy in the blends should be put balance considerations to obtain optimal mechanical properties.TGA results and FTIR spectrum demonstrated that the addition of PU modified epoxy did not change the thermal decomposition mechanism and chemical reaction mechanism,but the addition of PU modified epoxy inhibits the curing reaction of epoxy resin by measured and calculated the damping temperature domainT from 35.7℃ to 48.9℃.展开更多
文摘Silane coupling agent KH560 was used to modify the surface of nano-α-Al<sub>2</sub>O<sub>3</sub> in ethanol-aqueous solution with different proportions. The particle size of nano-α-Al<sub>2</sub>O<sub>3</sub> was determined by nano-particle size analyzer, and the effects of nano-α-Al<sub>2</sub>O<sub>3</sub> content, ethanol-aqueous solution ratio and KH560 dosage on the dispersion and particle size of nano-α-Al<sub>2</sub>O<sub>3</sub> were investigated. The material structure before and after modification was determined by Fourier transform infrared spectroscopy (FTIR). Aqueous polyurethane resin and inorganic components are combined with modified nano-α-Al<sub>2</sub>O<sub>3</sub> dispersion to form chromium-free passivation solution. The solution is coated on the galvanized sheet, the adhesion and surface hardness are tested, the bonding strength of the coating and the surface hardness of the substrate are discussed. The corrosion resistance and surface morphology of the matrix were investigated by electrochemical test, neutral salt spray test and scanning electron microscope test. The chromium-free passivation film formed after the modification of nano-α-Al<sub>2</sub>O<sub>3</sub> increases the surface hardness of galvanized sheet by about 85%. The corrosion resistance of the film is better than that of a single polyurethane film. The results show that the surface hardness and corrosion resistance of polyurethane resin composite passivation film are significantly improved by the introduction of nano-α-Al<sub>2</sub>O<sub>3</sub>.
文摘A series of transparent casting polyurethane resins (TCPU) were synthesized from cycloaliphatic diisocyanate (IPDI or H_(12)MDI), polyol, chain extender, crosslinking agents, catalyst and special aids (T),which were characterized by FTIR. The thermal stabilities of the obtained TCPU were examined by DSC and TGA, the glass transition temperature (T_g) was in the range of 95-110 ℃, the initial decomposition temperature (5% weight loss) was 250-265 ℃, and 10% weight loss at the temperature was in the range of 260-286℃ in nitrogen atmosphere. The morphologies of the fractured surfaces of TCPU were revealed by a scanning electron microscope (SEM). The crystalline-amorphous characters of TCPU were studied by WAXD, the result shows that TCPU possesses amorphous glassy characters. The optical properties of TCPU were studied by a UV-7500 visible light absorbance measurement. All the samples exhibited excellent optical properties and possessed light transmittance in the range of 91%-93%.
基金The authors acknowledge the financial support of the National Natural Science Foundation of China(No.51908330)the Qilu Young Scholars Program of Shandong University,Natural Science Foundation of Shandong Province(CN)(No.ZR2020ME244),the Fundamental Research Funds of Shandong University(No.2020GN059)the Fundamental Research Funds for the Central Universities,CHD(No.300102210502)and Scientific Research Project of Shandong High-speed Group Co.,Ltd.,(No.SDGS-KJCX-2020-006-08).
文摘As the important matrix material,epoxy resin has been widely used in the composites for various fields.On account of the poor toughness of epoxy resin limiting their suitability for advanced applications,considerable interests have been conducted to modify the epoxy resin to meet the engineering requirements.In this study,the bio-based polyurethane(PU)modified resin was adopted to modify the pure bisphenol-A epoxy by blending method with various proportions.Aiming to illuminate the curing behavior,mechanical and thermal properties,the blended epoxy systems were characterized by viscosity-time analysis,dynamic mechanical analysis(DMA)at different frequencies and temperatures,mechanical tensile test,thermogravimetric analysis(TGA)and Fourier transform infrared(FT-IR)spectroscopy.The results indicated that the introduction of PU modified epoxy was found to significantly inhibit the viscosity growth rates especially when the content of PU modified epoxy resin is higher than 60%.Notwithstanding the dynamic modulus and T_(g)reduced with the increment of PU modified epoxy,remarkable increment on the elongation at break was found and the flexibility was greatly promoted with the introduction of PU modified epoxy.The proportion of PU modified epoxy in the blends should be put balance considerations to obtain optimal mechanical properties.TGA results and FTIR spectrum demonstrated that the addition of PU modified epoxy did not change the thermal decomposition mechanism and chemical reaction mechanism,but the addition of PU modified epoxy inhibits the curing reaction of epoxy resin by measured and calculated the damping temperature domainT from 35.7℃ to 48.9℃.