Titanium dioxide(TiO2) films were prepared by cone - jet mode electrospraying a titanium ethoxideprecursor solution onto a silicon substrate.The effects of spraying time,substrate temperature and aging on thesurface m...Titanium dioxide(TiO2) films were prepared by cone - jet mode electrospraying a titanium ethoxideprecursor solution onto a silicon substrate.The effects of spraying time,substrate temperature and aging on thesurface morphology of the films prepared were studied.Thin films obtained after spraying for 600 s were aged atroom temperature to form a porous TiO2 network with pores in the size range of 100 - 500 nm.Thicker filmswere prepared by spraying for 3 000 s,but these cracked on drying although it can be concluded that films pre-pared using a higher substrate temperature were denser.By this method,SiC coating was also prepared on anAl2O3 substrate using polysilane as a precursor.The result implies the potential of an industrial production ofdye sensitized solar cells by electrospraying technique.展开更多
Porous TiO2 thin films were prepared from alkoxide solutions with and without polyethylene glycol （PEG） by sol-gel route on soda lime glass, and were characterized by atomic force microscopy （AFM）, transmission el...Porous TiO2 thin films were prepared from alkoxide solutions with and without polyethylene glycol （PEG） by sol-gel route on soda lime glass, and were characterized by atomic force microscopy （AFM）, transmission electron microscopy （TEM） and X-ray diffiaction （XRD）. The results show that TiO2 film prepared from precursor solution with- out PEG is composed of spherical particles of about 100 nm and several nanometer mesoporous pores. With the increase of the amount of PEG added to the precursor solution, the diameter and the depth of the pores in the resultant films increas on the decomposition of PEG during heat-treatment, which lead to the increase of the surface roughness of the films. XRD and TEM results show that the single anatase phase is precipitated and there are some orientation effects in （101） direction.展开更多
基金supported by the Science Foun-dation of Educational Commission and Provincial Key Laboratory Program of Liaoning Province of China(Grant No.2008593 and CL-200902)~~
文摘Titanium dioxide(TiO2) films were prepared by cone - jet mode electrospraying a titanium ethoxideprecursor solution onto a silicon substrate.The effects of spraying time,substrate temperature and aging on thesurface morphology of the films prepared were studied.Thin films obtained after spraying for 600 s were aged atroom temperature to form a porous TiO2 network with pores in the size range of 100 - 500 nm.Thicker filmswere prepared by spraying for 3 000 s,but these cracked on drying although it can be concluded that films pre-pared using a higher substrate temperature were denser.By this method,SiC coating was also prepared on anAl2O3 substrate using polysilane as a precursor.The result implies the potential of an industrial production ofdye sensitized solar cells by electrospraying technique.
基金The work was partially supported by a grant from the National Natural Science Foundation of China and the ResearchGrants Counc
文摘Porous TiO2 thin films were prepared from alkoxide solutions with and without polyethylene glycol （PEG） by sol-gel route on soda lime glass, and were characterized by atomic force microscopy （AFM）, transmission electron microscopy （TEM） and X-ray diffiaction （XRD）. The results show that TiO2 film prepared from precursor solution with- out PEG is composed of spherical particles of about 100 nm and several nanometer mesoporous pores. With the increase of the amount of PEG added to the precursor solution, the diameter and the depth of the pores in the resultant films increas on the decomposition of PEG during heat-treatment, which lead to the increase of the surface roughness of the films. XRD and TEM results show that the single anatase phase is precipitated and there are some orientation effects in （101） direction.