ZrO_(2)-strengthened porous mullite insulation materials were prepared by foaming technology utilizing ZrSiO_(4) and Al_(2)O_(3) as primary materials and Y_(2)O_(3) as an additive.The effects of Y_(2)O_(3) contents on...ZrO_(2)-strengthened porous mullite insulation materials were prepared by foaming technology utilizing ZrSiO_(4) and Al_(2)O_(3) as primary materials and Y_(2)O_(3) as an additive.The effects of Y_(2)O_(3) contents on the phase composition,microstructure,mechanical properties,and heat conductivity of the porous mullite insulation materials were investigated.A suitable Y_(2)O_(3) content could promote phase transition of monoclinic ZrO_(2)(m-ZrO_(2))to tetragonal ZrO_(2)(t-ZrO_(2)),reduce pore size,and improve the strengths of as-prepared specimens.The cold crushing strength and bending strength of as-prepared specimens with a 119µm spherical pore size using 6 wt.%Y_(2)O_(3) were 35.2 and 13.0 MPa,respectively,with a heat conductivity being only 0.248 W/(m K).展开更多
基金supported by the Natural Science Foundation of Anhui Provincial Education Department(2023AH051130 and KJ2021ZD0040)the University Synergy Innovation Program of Anhui Province(GXXT-2019-015)+2 种基金National Natural Science Foundation of China(51972002)the Student Research Training Program(SRTP)of Anhui University of Technology(S202310360191)National Innovation and Entrepreneurship Training Program for College Students(202210360023).
文摘ZrO_(2)-strengthened porous mullite insulation materials were prepared by foaming technology utilizing ZrSiO_(4) and Al_(2)O_(3) as primary materials and Y_(2)O_(3) as an additive.The effects of Y_(2)O_(3) contents on the phase composition,microstructure,mechanical properties,and heat conductivity of the porous mullite insulation materials were investigated.A suitable Y_(2)O_(3) content could promote phase transition of monoclinic ZrO_(2)(m-ZrO_(2))to tetragonal ZrO_(2)(t-ZrO_(2)),reduce pore size,and improve the strengths of as-prepared specimens.The cold crushing strength and bending strength of as-prepared specimens with a 119µm spherical pore size using 6 wt.%Y_(2)O_(3) were 35.2 and 13.0 MPa,respectively,with a heat conductivity being only 0.248 W/(m K).