The positive bias temperature instability（PBTI） degradations of high-k/metal gate（HK/MG） n MOSFETs with thin TiN capping layers（1.4 nm and 2.4 nm） are systemically investigated. In this paper, the trap energy di...The positive bias temperature instability（PBTI） degradations of high-k/metal gate（HK/MG） n MOSFETs with thin TiN capping layers（1.4 nm and 2.4 nm） are systemically investigated. In this paper, the trap energy distribution in gate stack during PBTI stress is extracted by using ramped recovery stress, and the temperature dependences of PBTI（90℃,125℃, 160℃） are studied and activation energy（Ea） values（0.13 eV and 0.15 eV） are extracted. Although the equivalent oxide thickness（EOT） values of two TiN thickness values are almost similar（0.85 nm and 0.87 nm）, the 2.4-nm TiN one（thicker Ti N capping layer） shows better PBTI reliability（13.41% at 0.9 V, 90℃, 1000 s）. This is due to the better interfacial layer/high-k（IL/HK） interface, and HK bulk states exhibited through extracting activation energy and trap energy distribution in the high-k layer.展开更多
基金Project supported by the National High Technology Research and Development Program of China(Grant No.SS2015AA010601)the National Natural Science Foundation of China(Grant Nos.61176091 and 61306129)
文摘The positive bias temperature instability（PBTI） degradations of high-k/metal gate（HK/MG） n MOSFETs with thin TiN capping layers（1.4 nm and 2.4 nm） are systemically investigated. In this paper, the trap energy distribution in gate stack during PBTI stress is extracted by using ramped recovery stress, and the temperature dependences of PBTI（90℃,125℃, 160℃） are studied and activation energy（Ea） values（0.13 eV and 0.15 eV） are extracted. Although the equivalent oxide thickness（EOT） values of two TiN thickness values are almost similar（0.85 nm and 0.87 nm）, the 2.4-nm TiN one（thicker Ti N capping layer） shows better PBTI reliability（13.41% at 0.9 V, 90℃, 1000 s）. This is due to the better interfacial layer/high-k（IL/HK） interface, and HK bulk states exhibited through extracting activation energy and trap energy distribution in the high-k layer.