Effects of Steel Slag Powder on Workability and Durability of Concrete

The workability and durability of a type of sustainable concrete made with steel slag powder were investigated. The hydrated products of cement paste with ground granulated blast furnace slag（GGBFS） alone or with a combined admixture of GGBFS-steel slag powder were investigated by X-ray diffraction（XRD）. Furthermore, the mechanism of chemically activated steel slag powder was also studied. The experimental results showed that when steel slag powder was added to concrete, the slumps through the same time were lower. The initial and fi nal setting times were slightly retarded. The dry shrinkages were lower, and the abrasion resistance was better. The chemically activated steel slag powder could improve compressive strengths, resistance to chloride permeation and water permeation, as well as carbonization resistance. XRD patterns indicated that the activators enhanced the formation of calcium silicate hydrate（C-S-H） gel and ettringite（AFt）. This research contributes to sustainable disposal of wastes and has the potential to provide several important environmental benefi ts.

Principle and Feasibility of Electric or Magnetic Field Deflection-Projection Based Rapid Prototyping Technique

Rapid prototype manufacturing(RPM) is a new advanced manufacturing technology, which is based on the philosophy of materials increasing of lay by lay forming. Zero adventure rapid design/manufacturing can be realized with rapid prototypes of 3D CAD of products. Rapid prototyping has been an effective tool of R&D of new products. A novel rapid prototyping and manufacturing (RP&M) technique is brought forward. The principle of the process is to form layered sections and to make the prototype or part layer by layer by deflection projection of electric charged powder granules passing through electric or magnetic field and by controllable line and field scan of the powder granule beam. The feasibility issue of the process is theoretically and experimentally investigated.It shows that deflection projection of electric charged powder granules beam passing through electric field can be significant and feasible to the rapid prototyping technique.

Direct reduction of hematite powders in a fluidized bed reactor

Ultrafine hematite powder was reduced to produce ultrafine iron powder in a 50%Ar-50%H2 atmosphere at 450-550 ℃ in a fluidized bed reactor. The ultrafine hematite powder shows the typical agglomerating fluidization behavior with large agglomerates fluidized at the bottom of the bed and small agglomerates fluidized at the upper part of the bed. It was found that defluidization occurred even at the low temperature of 450 C with low metallization rate. Defluidization was attributed mainly to the sintering of the newly formed iron particles. Granuation was employed to improve the fluidization quality and to tackle the defluidization problem, where granules fluidized like a Geldart＇s group A powder. Granulation was found to effectively reduce defluidization during reduction, without however sacrificing reduction speed. The asreduced iron powders from both the ultrafine and the granulated hematite exhibited excellent sintering activity, that is, fast sintering at temperature of as low as ~580℃, which is much superior as compared to that of nano/ultrafine iron powders made by other processes.