Effect of cooling rate on microstructure and tensile properties of powder metallurgy Ni-based superalloy

The effects of size distribution,morphology and volume fraction ofγ′phase and grain size on tensile properties of powder processed Ni-based superalloy were investigated by using two different quenching methods.Oil quenching and air cooling were adopted with cooling rate of 183°C/s and 4?15°C/s,respectively.The experimental results show that the average size of the secondaryγ′after oil quenching is 24.5 nm compared with 49.8 nm under air cooling,and corresponding volume fractions ofγ′are 29%and 34%,respectively.Meanwhile,the average grain size remains nearly equivalent from both oil-quenching and air-cooling specimens.The tensile strength at room temperature is higher for the oil-quenched specimen than the equivalent from the air-cooled specimen,but the difference approaches each other as the temperature increases to 650°C.The fractography clearly demonstrates that transgranular fracture governs the failure process at ambient temperature,in contrast to the intergranular fracture at 650°C or even higher temperature.These two mechanical responses indicate the strengthening effects ofγ′precipitates and grain boundary for polycrystalline Ni-based superalloys at different temperatures.

CRITICAL ISSUES OF POWDER METALLURGY TURBINE DISKS

P/M superalloy disks obtain their final strength by appropriate heat treatments; the maximum attainable strength depends on the rapid cooling rate from the solution annealing. A rapid quench of a large disk forging can cause two problems, surface cracking and shape distortion.In the past,many attempts employ the finite element code to model and to predict temperature evolution and induced stress distribution in a large turbine disk. The major difficulty was the correct description of alloy behavior; particularly the thermomechanical properties and the failure criteria of material during the cooling. High temperature fatigue resistance is always the key requirement for disk materials. New methodology of residual life management emphasizes the initiation as well as the propagation of the cracks developed under the service conditions. One of major challenges to P/M superalloys is the time-dependent behavior of fatigue cracking, which relates to the well-known SAGBO (stress-assisted grain boundary oxidation) phenomenon.A great effort has been done to understand the micro-mechanism of time-dependent fatigue crack propagation resulted in the second generation of P/M superalloys. Further improvement on temperature capability of disk alloys at rim area may lead to the idea of dual-property disks.Different grain structures at different portions of a large disk are possible,as the property requirements for different locations are different. This goal is achievable if the thermal history at specific disk locations can be controlled to develop desirable microstructures and properties.Some suggestions on the future direction of research efforts will be discused.

Spray forming and mechanical properties of a new type powder metallurgy superalloy

The deposited billet of a new type powder metallurgy （PM） superalloy FGH4095M for use in turbine disk manufac- turing has been fabricated using spray forming technology. The metallurgical quality of the deposited billet was analyzed in terms of density, texture, and grain size. Comparative research was done on the microstructure and mechanical properties between the flat disk preform prepared with hot isostatic pressing （HIP） and the same alloy forgings prepared with HIP followed by isothermal forging （IF）. The results show that the density of the spray-formed and nitrogen-atomized deposit billet is above 99% of the theoretical density, indicating a compact structure. The grains are uniform and fine. The billet has weak texture with a random distribution in the spray deposition direction and perpendicular to the direction of deposition. A part of atomizing nitrogen exists in the preform in the form of carbonitride. Nitrogen-induced microporosity causes the density reduction of the preform. Compared with the process of HIP＋IF, the superalloy FGH4095M after HIP has better mechanical properties at both room temperature and high temperature. The sizes of the 7~ phase are finer in microstructure of the preform after HIP in comparison with the forgings after HIP＋IE This work shows that SF＋HIP is a viable processing route for FGH4095M as a turbine-disk material.

THE ROLE OF NIOBIUM IN NICKEL-BASED SUPERALLOYS AND CHARACTERIZATION OF PM ALLOY EP741NP

The role of niobium in nickel-based superalloys is reviewed. The importance of niobium as a strengthener is discussed. New developments in nickel-based superalloys are also briefly mentioned, including some results that show improved resistance to sulfidation by niobium. Research results from a current program on the role of niobium in the Russian powder metallurgy alloy EP741NP are presented. Future research plans on the role of niobium in superalloys are also discussed.

CBN grain wear and its effects on material removal during grinding of FGH96 powder metallurgy superalloy

Grinding with cubic boron nitride(CBN)superabrasive is a widely used method of machining superalloy in aerospace industries.However,there are some issues,such as poor grinding quality and severe tool wear,in grinding of powder metallurgy superalloy FGH96.In addition,abrasive wheel wear is the significant factor that hinders the further application of CBN abrasive wheels.In this case,the experiment of grinding FGH96 with single CBN abrasive grain using different parameters was carried out.The wear characteristics of CBN abrasive grain were analyzed by experiment and simulation.The material removal behavior affected by CBN abrasive wear was also studied by discussing the pile-up ratio during grinding process.It shows that morphological characteristics of CBN abrasive grain and grinding infeed direction affect the CBN abrasive wear seriously by simulation analysis.Attrition wear,micro break,and macro fracture had an important impact on material removal characteristics.Besides,compared with the single cutting edge,higher pile-up ratio was obtained by multiple cutting edges,which reduced the removal efficiency of the material.Therefore,weakening multiple cutting edge grinding on abrasive grains in the industrial production,such as applying suitable dressing strategy,is an available method to improve the grinding quality and efficiency.

Prediction on grinding force during grinding powder metallurgy nickel-based superalloy FGH96 with electroplated CBN abrasive wheel

In this article,a grinding force model,which is on the basis of cutting process of single abrasive grains combined with the method of theoretical derivation and empirical formula by analyzing the formation mechanism of grinding force,was established.Three key factors have been taken into accounts in this model,such as the contact friction force between abrasive grains and materials,the plastic deformation of material in the process of abrasive plowing,and the shear strain effect of material during the process of cutting chips formation.The model was finally validated by the orthogonal grinding experiment of powder metallurgy nickel-based superalloy FGH96 by using the electroplated CBN abrasive wheel.Grinding force values of prediction and experiment were in good consistency.The errors of tangential grinding force and normal grinding force were 9.8%and 13.6%,respectively.The contributions of sliding force,plowing force and chip formation force were also analyzed.In addition,the tangential forces of sliding,plowing and chip formation are 14%,19%and 11%of the normal forces on average,respectively.The pro-posed grinding forcemodel is not only in favor of optimizing the grinding parameters and improving grinding efficiency,but also contributes to study some other grinding subjects(e.g.abrasive wheel wear,grinding heat,residual stress).

An investigation on machined surface quality and tool wear during creep feed grinding of powder metallurgy nickel-based superalloy FGH96 with alumina abrasive wheels

In this study,the machined surface quality of powder metallurgy nickel-based superalloy FGH96(similar to Rene88DT)and the grinding characteristics of brown alumina(BA)and microcrystalline alumina(MA)abrasive wheels were comparatively analyzed during creep feed grinding.The infuences of the grinding parameters(abrasive wheel speed,workpiece infeed speed,and depth of cut)on the grinding force,grinding temperature,surface roughness,surface morphology,tool wear,and grinding ratio were analyzed comprehensively.The experimental results showed that there was no significant difference in terms of the machined surface quality and grinding characteristics of FGH96 during grinding with the two types of abrasive wheels.This was mainly because the grinding advantages of the MA wheel were weakened for the difficult-to-cut FGH96 material.Moreover,both the BA and MA abrasive wheeIs exhibited severe tool wear in the form of wheel clogging and workpiece material adhesion.Finally,an analytical model for prediction of the grinding ratio was established by combining the tool wear volume,grinding force,and grinding length.The acceptable errors between the predicted and experimental grinding ratios(ranging from 0.6 to 1.8)were 7.56%and 6.31%for the BA and MA abrasive wheels,respectively.This model can be used to evaluate quantitatively the grinding performance of an alumina abrasive wheel,and is therefore helpful for optimizing the grinding parameters in the creep feed grinding process.

Evolution of grain size and grain shape during thermomechanical processing in a powder metallurgical nickel-based superalloy

With a strain rate range of 0.01–10 s^(−1) and a deformation temperature range of 1110–1200℃,the isothermal compression test was performed on one powder metallurgy superalloy which is macroscopic segregation free.Using electron backscatter diffraction,the effect of strain rate and deformation temperature on grain shape and grain size of superalloys during thermal deformation was studied.The results established that exquisite and equiaxed dynamic recrystallization(DRX)grains are procured at supernal deformation temperature and high strain rate because of the high dislocation density.At the same time,the interaction between high DRX nucleation rate and low grain growth rate at high strain rate is favorable in making finer DRX grains.The equivalent medial grain size expanded with lowering strain rate and elevating proof temperature.Moreover,the grain shape was researched by the effective method of aspect ratio.Most aspect ratio of original grains is 0.61,and the aspect ratio has important implications for DRX and grain growth process.The average aspect ratio increases slightly when deformation temperature rises from 1110 to 1140℃,while the average aspect ratio increases memorably as the deformation temperature is higher than 1140℃.

Microstructure and microtexture evolution characteristics of a powder metallurgy Ni-based superalloy during static recrystallization

Static recrystallization(SRX)characteristics of a powder metallurgy superalloy were investigated by isothermal compression at 1080–1170°C under strain rates of 0.01–0.1 s−1,strains of 0.1,0.22,or 0.5,and holding time of 0–300 s.The impacts of temperature,strain rate,holding time,and strain on the SRXed grain size,volume fraction,and microtexture were explored by electron backscatter diffraction technique.It was found that temperature played a key role in these processes.As SRX progressed,the<110>fiber parallel to the axis compression direction gradually weakened and was replaced by the<001>fiber because<001>was the preferred recrystallization orientation and grain growth direction for the Ni-based superalloy.Moreover,high temperatures and low strain rates promoted the formation of the<001>fiber.Three nucleation mechanisms during SRX process were found:grain boundary bulging,primary twin assistance,and subgrain coalescence.Grain boundary bulging occurred under all process conditions;however,at low temperatures and high strain rates,the latter two mechanisms could provide additional nucleation modes.In addition,SRX size and volume fraction models were established.