Effect of characteristics and distribution of Mg_(17)Al_(12)precipitates on tensile and bending properties of high-Al-containing Mg alloys

This study investigates the effect of characteristics and distribution of Mg_(17)Al_(12)precipitates on the uniaxial tensile and three-point bending properties of extruded Mg alloys containing high Al contents.The extruded Mg–9Al–1Zn–0.3Mn(AZ91)alloy contains lamellar-structured Mg_(17)Al_(12)discontinuous precipitates along the grain boundaries,which are formed via static precipitation during natural air cooling.The extruded Mg–11Al–1Zn–0.3Mn(AZ111)alloy contains spherical Mg_(17)Al_(12)precipitates at the grain boundaries and inside the grains,which are formed via dynamic precipitation during extrusion.Due to inhomogeneous distribution of precipitates,the AZ111 alloy consists of two different precipitate regions:precipitate-rich region with numerous precipitates and finer grains and precipitate-scarce region with a few precipitates and coarser grains.The AZ111 alloy exhibits a higher tensile strength than the AZ91 alloy because its smaller grain size and more abundant precipitates result in stronger grain-boundary hardening and precipitation hardening effects,respectively.However,the tensile elongation of the AZ111 alloy is lower than that of the AZ91 alloy because the weak cohesion between the dynamic precipitates and the matrix facilitates the crack initiation and propagation.During bending,a macrocrack initiates on the outer surface of bending specimen in both alloys.The AZ111 alloy exhibits higher bending yield strength and lower failure bending strain than the AZ91 alloy.The bending specimens of the AZ91 alloy have similar bending formability,whereas those of the AZ111 alloy exhibit considerable differences in bending formability and crack propagation behavior,depending on the distribution and number density of precipitates in the specimen.In bending specimens of the AZ111 alloy,it is found that the failure bending strain(ε_(f,bending))is inversely proportional to the area fraction of precipitates in the outer zone of bending specimen(A_(ppt)),with a relationship ofε_(f,bending)=–0.1A_(ppt)+5.86.

Evolution of helium bubbles in FeCoNiCr-based high-entropy alloys containing γ′ nanoprecipitates

A series of high-entropy alloys(HEAs) containing nanoprecipitates of varying sizes is successfully prepared by a non-consuming vacuum arc melting method.In order to study the irradiation evolution of helium bubbles in the FeCoNiCrbased HE As with γ' precipitates,these samples are irradiated by 100-keV helium ions with a fluence of 5 × 10^(20) ions/m^(2) at 293 K and 673 K,respectively.And the samples irradiated at room temperature are annealed at different temperatures to examine the diffusion behavior of helium bubbles.Transmission electron microscope(TEM) is employed to characterize the structural morphology of precipitated nanoparticles and the evolution of helium bubbles.Experimental results reveal that nanosized,spherical,dispersed,coherent,and ordered L1_(2)-type Ni_(3)Ti γ' precipitations are introduced into FeCoNiCr(Ni_(3)Ti)_(0.1) HEAs by means of ageing treatments at temperatures between 1073 K and 1123 K.Under the ageing treatment conditions adopted in this work,γ' nanoparticles are precipitated in FeCoNiCr(Ni_(3)Ti)_(0.1) HE As,with average diameters of 15.80 nm,37.09 nm,and 62.50 nm,respectively.The average sizes of helium bubbles observed in samples after 673-K irradiation are 1.46 nm,1.65 nm,and 1.58 nm,respectively.The improvement in the irradiation resistance of FeCoNiCr(Ni_(3)Ti)_(0.1) HEAs is evidenced by the diminution in bubbles size.Furthermore,the FeCoNiCr(Ni_(3)Ti)_(0.1) HEAs containing γ' precipitates of 15.8 nm exhibits the minimum size and density of helium bubbles,which can be ascribed to the considerable helium trapping effects of heterogeneous coherent phase boundaries.Subsequently,annealing experiments conducted after 293-K irradiation indicate that HEAs containing precipitated phases exhibits smaller apparent activation energy(E_(a)) for helium bubbles,resulting in larger helium bubble size.This study provides guidance for improving the irradiation resistance of L1_(2)-strengthened high-entropy alloy.

Precipitates Generation Mechanism and Surface Quality Improvement for Aluminum Alloy 6061 in Diamond Cutting

To improve the surface quality for aluminum alloy 6061(Al6061) in ultra-precision machining, we investigated the factors affecting the surface finish in single point diamond turning(SPDT)by studying influence of the precipitates generation of Al6061 on surface integrity and surface roughness.Based on the Johnson-Mehl-Avrami solid phase transformation kinetics equation, theoretical and experimental studies were conducted to build the relationship between the aging condition and the type, size and number of the precipitates for Al6061. Diamond cutting experiments were conducted to machine Al6061 samples under different aging conditions. The experimental results show that, the protruding on the chip surface is mainly Mg_(2)Si and the scratches on the machined surface mostly come from the iron-containing phase(α-, β-AlFeSi).Moreover, the generated Mg_(2)Si and α-, β-AlFeSi affect the surface integrity and the diamond turned surface roughness. Especially, the achieved surface roughness in SPDT is consistent with the variation of the number of AlFeSi and Mg_(2)Si with the medium size(more than 1 μm and less than 2 μm) in Al6061.

In situ TEM investigation of electron irradiation and aging-induced high-density nanoprecipitates in an Mg-10Gd-3Y-1Zn-0.5Zr alloy

In-situ electron irradiation and aging are applied to introduce high-density precipitates in an Mg-10Gd-3Y-1Zn-0.5Zr(GWZ1031K,wt.%)alloy to improve the hardness.The results show that the hardness of the Mg alloy after irradiation for 10 h and aging for 9 h at 250℃ is 1.64 GPa,which is approximately 64% higher than that of the samples before being treated.It is mainly attributed to γ'precipitates on the basal plane after irradiation and the high-density nanoscale β'precipitates on the prismatic plane after aging,which should be closely related to the irradiation-induced homogenous clusters.The latter plays a key role in precipitation hardening.This result paves a way to improve the mechanical properties of metallic materials by tailoring the precipitation through irradiation and aging.

A novel immiscible high entropy alloy strengthened via L1_(2)-nanoprecipitate

The low-cost Fe-Cu,Fe-Ni,and Cu-based high-entropy alloys exhibit a widespread utilization prospect.However,these potential applications have been limited by their low strength.In this study,a novel Fe_(31)Cu_(31)Ni_(28)Al_(4)Ti_(3)Co_(3) immiscible high-entropy alloy(HEA)was developed.After vacuum arc melting and copper mold suction casting,this HEA exhibits a unique phase separation microstructure,which consists of striped Cu-rich regions and Fe-rich region.Further magnification of the striped Cu-rich region reveals that it is composed of a Cu-rich dot-like phase and a Fe-rich region.The aging alloy is further strengthened by a L1_(2)-Ni_(3)(AlTi)nanoprecipitates,achieving excellent yield strength(1185 MPa)and uniform ductility(~8.8%).The differential distribution of the L1_(2) nanoprecipitate in the striped Cu-rich region and the external Fe-rich region increased the strength difference between these two regions,which increased the strain gradient and thus improved hetero-deformation induced(HDI)hardening.This work provides a new route to improve the HDI hardening of Fe-Cu alloys.

Microstructure and phase precipitate behavior of Inconel 740H during aging

The microstructure and phase precipitate behavior and their effects on the room temperature hardness and impact toughness of Inconel 740H aged at 750 ℃ for 10000 h were investigated by SEM, TEM and mechanical analysis. The as-received alloy shows a low hardness value of HB 168 and a highest toughness value of 96 J. After an aging treatment at 800 ℃ for 16 h and cooled in air （standard heat-treated condition）, fine γ′ phase particles precipitate within the grains and small carbide particles are located at the grain boundaries. The hardness increases to HB 304 and the impact toughness decreases to 15 J after standard heat treatment. A maximum hardness value of HB 331 is achieved for the alloy aged at 750 ℃ for 300 h. With increasing the aging time from 300 to 10000 h, a decrease of the hardness and toughness is observed along with an enhanced quantity of M23C6 particles and the coarsening of γ′ phase.

Anisotropic and temperature-dependent growth mechanism of S-phase precipitates in Al-Cu-Mg alloy in relation with GPB zones

By employing atomic-resolution imaging and first principles energy calculations, the growth behavior of S-phase precipitates in a high strength A1-Cu-Mg alloy was investigated. It is demonstrated that the nucleation and growth of the S-phase precipitate are rather anisotropic and temperature-dependent companying with low dimensional phase transformation. There are actually two types of Guinier-Preston （GP） zones that determine the formation mechanism of S-phase at high aging temperatures higher than 180 ℃. One is the precursors of the S-phase itself, the other is the structural units or the precursors of the well-known Guinier-Preston-Bagaryatsky （GPB） zones. At high temperatures the later GPB zone units may form around S-phase precipitate and cease its growth in the width direction, leading to the formation of rod-like S-phase crystals; whereas at low temperatures the S-phase precipitates develop without the interference with GPB zones, resulting in S-phase orecioitates with lath-like momhology.

Effect of normalizing cooling process on microstructure and precipitates in low-temperature silicon steel

Microstructure, precipitate and magnetic characteristic of fmal products with different normalizing cooling processes for Fe-3.2%Si low-temperature hot-rolled grain-oriented silicon steel were analyzed and compared with the hot-rolled plate by optical microscopy （OM）, transmission electron microscopy （TEM）, and energy dispersive spectrometry （EDS）. The results show that, the surface microstructure is uniform, the proportion of recrystallization in matrix increases, and the banding textures are narrowed; the precipitates, whose quantity in normalized plate is more than that in hot-rolled plate greatly, are mainly A1N, MnS, composite precipitates （Cu,Mn）S and so on. Normalizing technology with a temperature of 1120 ℃, holding for 3 min, and a two-stage cooling is a most advantaged method to obtain oriented silicon steel with sharper Goss texture and higher magnetic properties, owing to the uniform surface microstructures and the obvious inhomogeneity of microstructures along the thickness. The normalizing technology with the two-stage cooling is the optimum process, which can generate more fine precipitates dispersed over the matrix, and be beneficial for finished products to get higher magnetic properties.

Formation of precipitates and recrystallization resistance in Al-Sc-Zr alloys

Al-x%Sc-0.11%Zr alloys （x=0, 0.02, 0.05, 0.08, 0.11, 0.15） were produced by a chill cast procedure. The effect of Sc content on the precipitation of Al3（Sc,Zr） during heat treatment at 475 °C for 12 h was studied. Nucleation, precipitation and distribution of Al3（Sc,Zr） precipitates were found to be strongly related to the Sc content. With increasing the Sc content, the average radius of the precipitates decreases, while the number density of the precipitates increases, as investigated by transmission electron microscopy （TEM）. The distribution of the precipitates becomes more and more homogeneous when the Sc content is increased. The recrystallization resistance of samples that was 90% cold rolled and isothermal annealed for half an hour in the temperature range of 200-600 °C was investigated. The results show that the recrystallization temperature varies from 250 °C for the alloy without Sc to about 600 °C for the alloy containing 0.15% Sc because of the high density of Al3（Sc,Zr） precipitates.

Non-isothermal retrogression kinetics for grain boundary precipitate of 7A55 aluminum alloy

The retrogression kinetics for grain boundary precipitate （GBP） of 7A55 aluminum alloy was investigated by transmission electron microscopy （TEM） observation. The results reveal that the coarsening behavior of GBP obeys “LSW” theory, namely, the cube of GBP average size has a linear dependence relation to retrogression time, and the coarsening rate accelerates at the elevated retrogression temperature. The GBP coarsening activation energy Qo of （115.2±1.3） kJ/mol is obtained subsequently. Taking the retrogression treatment schedule of 190℃, 45 min derived from AA7055 thin plate as reference, the non-isothermal retrogression model for GBP coarsening behavior is established based on “LSW”theory and “iso-kinetics” solution, which includes an Arrhenius form equation. After that, the average size of GBP r（t） is predicted successfully at any non-isothermal process T（t） when the initial size of GBP r0 is given. Finally, the universal characterization method for the microstructure homogeneity along the thickness direction of TA55 aluminum alloy thick plate is also set up.

Morphology and crystallography of β precipitate phase in Mg-Gd-Y-Nd-Zr alloy

Morphology and crystal structure of β precipitate phase in Mg-7Gd-5Y-1Nd-0.5Zr (mass fraction, %) alloy were characterized by optical microscopy, scanning electron microscopy and transmission electron microscopy. Compositions were determined for β phase using thin foil energy dispersive spectroscopy. Precipitation at 400 ℃ involves formation of platelet and block-shaped β phase. The orientation relationship is and between β precipitate phase and α-Mg matrix with habit planes parallel to , and a composition of Mg5(Y0.4Gd0.4Nd0.2) is suggested for the β phase in Mg-7Gd-5Y-1Nd-0.5Zr alloy.

Precipitates identification in R_2PdSi_3(R= Pr,Tb and Gd) single crystal growth

Floating zone method with optical radiation heating was applied to growing a class of R2PdSi3（R=Pr,Tb and Gd） single crystals due to its containerless melting and high stability of the floating zone.One serious problem during the single crystal growth,precipitates of secondary phases,was discussed from the following four parts：precipitates from the raw materials and preparation process,precipitates formed during the growing process,precipitates in the melts and precipitates in the grown crystals.Annealing treatment and composition shift can effectively reduce the precipitates which are not formed during the crystallization but precipitated on post-solidification cooling from the as-grown crystal matrix because of the retrograde solubility of Si.

Precipitation behaviour of Al_3Zr precipitate in Al-Cu-Zr and Al-Cu-Zr-Ti-V alloys

The precipitation behaviours of Al3Zr precipitate in the Al-Cu-Zr and Al-Cu-Zr-Ti-V alloys were studied by transmission electron microscopy. Metastable Al3Zr precipitates are homogeneously nucleated in dendrite centres resulting in homogeneous distribution. However, the precipitation in the interdendritic regions is complex and the precipitation morphologies, helical-like and stripe-like shapes, were observed, which are composed of many spherical Al3Zr precipitates. The stripe-like precipitate clusters have preferential orientations along with the -100- Al directions, which is inferred to be related to θ′（Al2Cu） and θ phases. Addition of Cu can accelerate the L12→D023 structural transformation of the Al3Zr precipitate.

ANALYSIS ON THE BEHAVIOR OF PRECIPITATES IN ULTRA-THIN HOT STRIP OF PLAIN LOW CARBON STEEL PRODUCED BY COMPACT STRIP PRODUCTION

This paper investigated the mechanism of precipitation and its influence upon prop-erties of ultra-thin hot strips of low carbon steel produced by CSP techniques using experiment and thermodynamics theory. The experimental results show that there are lots of fine and dispersive precipitates in microstructures. By analysis, most of aluminum nitrides are in grains, while coexisted precipitates of MnS are along grain boundaries. Coexisted precipitates compose cation-vacancy type oxides such as Al2O3 in the core, while MnS is at the fringe of surface. The precipitation behavior of AIN and MnS in the hot strip is studied by thermodynamic calculation. At last, implica-tions between strengthening effect and techniques are analyzed using obtained solubility products.

Mechanical properties and characteristics of nanometer-sized precipitates in hot-rolled low-carbon ferritic steel

The microstructures and properties of hot-rolled low-carbon ferritic steel have been investigated by optical microscopy, field-emission scanning electron microscopy, transmission electron microscopy, and tensile tests after isothermal transformation from 600°C to 700°C for 60 min. It is found that the strength of the steel decreases with the increment of isothermal temperature, whereas the hole expansion ratio and the fraction of high-angle grain boundaries increase. A large amount of nanometer-sized carbides were homogeneously distributed throughout the material, and fine（Ti, Mo）C precipitates have a significant precipitation strengthening effect on the ferrite phase because of their high density. The nanometer-sized carbides have a lattice parameter of 0.411-0.431 nm. After isothermal transformation at 650°C for 60 min, the ferrite phase can be strengthened above 300 MPa by precipitation strengthening according to the Ashby-Orowan mechanism.

Effects of precipitates and inclusions on the fracture toughness of hot rolling X70 pipeline steel plates

In order to investigate the fracture toughness, crack tip opening displacement （CTOD） experiments were conducted on two X70 pipeline steel plates with different rolling processes. Atter the experiments, optical microscopy （OM）, scanning electron microscopy （SEM） and transmission electron microscopy （TEM） were employed to observe the microstructure and fracture morphology. The effects of precipi- tates on the fracture toughness and the crack initiation mechanism induced by inclusions were analyzed. The CTOD result shows that the steel with a lower finishing cooling temperature has a higher fracture toughness. Inchisiom with different shapes and two kinds of precipi- tates with different sizes were observed. It can be concluded that precipitates with different sizes have different effects and mechanisms on the fracture toughness. Distinguished fi＇om the earlier researches, inclusions enriched in silicon can be also served as the crack initiation.

Formation of carbonitride precipitates in hardfacing alloy with niobium addition

Niobium, as the most effective second-phase forming element, was added in the Fe-Crl3-C-N hard- facing alloy to get carbonitride precipitates. Morphology and composition of carbonitride in the hardfacing alloy were studied by optical microscopy, scanning electron microscopy, and electron probe microanalyzer. The ther- modynamics and the effect on the matrix of the formation of carbonitride were also discussed. It was found that niobium carbonitrides are complex Nb（C, N） precipitate distributed on grain boundary and matrix of the hardfacing alloy. Under as-welded condition, primary carbonitride particles were readily precipitated from the hardfacing alloy with large size and morphology as they were formed already during solidification. Under heat treatment condi- tion, a large number of secondary carbonitrides can pre- cipitate out with very fine size and make a great secondary hardening effect on the matrix. As a result, addition of niobium in the hardfacing alloy can prevent the formation of chromium-rich phase on grain boundaries and inter- granular chromium depletion.

Simulation on function mechanism of T1(Al_2CuLi) precipitate in localized corrosion of Al-Cu-Li alloys

To clarify the corrosion mechanism associated with the precipitate of T1(Al2CuLi)in Al-Li alloys,the simulated bulk precipitate of T1 was fabricated through melting and casting.Its electrochemical behavior and coupling behavior with α(Al)in 3.5% NaCl solution were investigated.Meanwhile,the simulated Al alloy containing T1 particle was prepared and its corrosion morphology was observed.The results show that there exists a dynamic conversion corrosion mechanism associated with the precipitate of T1.At the beginning,the precipitate of T1 is anodic to the alloy base and corrosion occurs on its surface.However,during its corrosion process,its potential moves to a positive direction with immersion time increasing,due to the preferential dissolution of Li and the enrichment of Cu.As a result,the corroded T1 becomes cathodic to the alloy base at a later stage,leading to the anodic dissolution and corrosion of the alloy base at its adjacent periphery.It is suggested that the localized corrosion associated with the precipitate of T1 in Al-Li alloys is caused by the alternate anodic dissolution of the T1 precipitate and the alloy base at its adjacent periphery.

Morphological evolution of γ'precipitates in a nickel-based superalloy during various solution treatments

The morphological evolution of the γ' phase in nickel-based superalloy жc6y during various solution heat treatments was investigated. The significant changes of the γ' precipitates were observed in the solution-treated samples. The coarsening and dissolution of γ' phase simulta-neously occurred at intermediate temperatures. In some areas, the primary precipitates became blunt and the adjacent ones were intercon-nected with each other via a diffuse neck, indicating a coarsening process of the primary γ' population. The coarsening was dominated by the precipitate agglomeration mechanism (PAM) rather than by the well-known Ostwald ripening mechanism. In other areas, the partial dissolu-tion of the γ' precipitates began to occur, spreading gradually from dendrite cores to interdendritic regions. In addition, a flower-like γ' struc-ture was developed during the subsolvus solution treatments. The observable long filaments composed of erraticly shaped precipitates were caused by the heterogeneous nucleation of the cooling precipitates during water quenching.

Effect of long-term service on the precipitates in P92 steel

The precipitates in P92 steel after long-term service in an ultra-supercritical unit were investigated by field-emission scanning electron microscopy and transmission electron microscopy and were found to mainly consist of M23 C6 carbides,Laves phase,and MX carbonitrides.No Z-phase was observed.M23 C6 carbides and Laves phase were found not only on prior austenite grain boundaries,martensite lath boundaries,and subgrain boundaries but also in lath interiors,where two types of MX carbonitrides—Nb-rich and V-rich particles—were also observed but the "winged" complexes were hardly found.Each kind of precipitate within the martensite laths exhibited multifarious morphologies,suggesting that a morphological change of precipitates occurred during long-term service.The M23 C6 carbides and Laves phase coarsened substantially,and the latter grew faster than the former.However,MX carbonitrides exhibited a relatively low coarsening rate.The effect of the evolution of the precipitate phases on the creep rupture strength of P92 steel was discussed.