Studies on ultrafine particle catalyst have attracted many researchers' attention by its large surface area,higher activity and selectivity.Based on the mechanism of α-Fe and Fe_xC_y as the catalytical active spe...Studies on ultrafine particle catalyst have attracted many researchers' attention by its large surface area,higher activity and selectivity.Based on the mechanism of α-Fe and Fe_xC_y as the catalytical active species this paper reports for the first time the preparation method of Fe_3C ultrafine parti- cle catalyst,from highly dispersed amorphous Fe powder and free carbon.The Fe powder and free car- bon,prepared by laser pyrolysis technique,was then treated by washing and heating at high tempera- ture protected with N_2.The catalyst prepared under different experimental conditions was characterazed by means of XRD,electronic diffraction and TEM.It shows that the crystlline grain size is in a range of 1-4nm and composed of Fe_3C and α-Fe.It has been found that the ultrafine particle iron-carbonide catalyst exhibited much higher activity and selectivity to light olefins.At the standard atmosphere and 380℃ reaction temperature,the conversion of CO reached a maximum of 80%.展开更多
Ultrafine particle (UFP)alumina has been prepared by supereritical fluid drying process of inorganic salt with organic solvent system, which is reported for the first time. UFP-alumina prepared from this system is fea...Ultrafine particle (UFP)alumina has been prepared by supereritical fluid drying process of inorganic salt with organic solvent system, which is reported for the first time. UFP-alumina prepared from this system is featured by its hish specific surface area, large pore volume, small perticle size and low bulk density.展开更多
基金The project was supported by the National Natural Science Foundation of China.
文摘Studies on ultrafine particle catalyst have attracted many researchers' attention by its large surface area,higher activity and selectivity.Based on the mechanism of α-Fe and Fe_xC_y as the catalytical active species this paper reports for the first time the preparation method of Fe_3C ultrafine parti- cle catalyst,from highly dispersed amorphous Fe powder and free carbon.The Fe powder and free car- bon,prepared by laser pyrolysis technique,was then treated by washing and heating at high tempera- ture protected with N_2.The catalyst prepared under different experimental conditions was characterazed by means of XRD,electronic diffraction and TEM.It shows that the crystlline grain size is in a range of 1-4nm and composed of Fe_3C and α-Fe.It has been found that the ultrafine particle iron-carbonide catalyst exhibited much higher activity and selectivity to light olefins.At the standard atmosphere and 380℃ reaction temperature,the conversion of CO reached a maximum of 80%.
文摘Ultrafine particle (UFP)alumina has been prepared by supereritical fluid drying process of inorganic salt with organic solvent system, which is reported for the first time. UFP-alumina prepared from this system is featured by its hish specific surface area, large pore volume, small perticle size and low bulk density.