Preparation and Properties of Nano-TiO_2 Powders

This paper reports the preparation of nano-TiO2 (about 10 nm) powder by the method of precipitation. In detail, some breparation conditions were investigated in order to find out how to control the grain size and reduce the agglomeration of powders. Also, the reflex spectra of nano-scale powders with different grain size were studied. It tvas found that the wave length and width of reflex spectra are connected with the grain size of nano-TiO2 powders

Preparation and properties of CdS thin films grown by ILGAR method

CdS thin films were deposited by the ion layer gas reaction (TLGAR) method.Structural, chemical, topographical development as well as optical and electrical properties ofas-deposited and annealed thin films were investigated by XRD, SEM, XPS, AFM and UV-VIS. The resultsshowed that the thin films are uniform, compact and good in adhesion to the substrates, and thegrowth of the films is 2.8 nm/cycle. The evolution of structure undergoes from the cubic structureto the hexagonal one with a preferred orientation along the (002) plane after annealing at 673 K. Anamount of C, O and Cl impurities can be reduced by increasing the drying temperature or byannealing in N2 atmosphere. It was found that the band gap of the CdS films shifts to higherwavelength after annealing or increasing film thickness. The electrical resistivity decreases withincreasing annealing temperature and film thickness.

Preparation and Properties of Rare Earth Complexes with 5-Phenyl Pyrazoline Dithioformate

Nine complexes of rare earths with 5 phenyl pyrazoline dithioformate, Na[RE(S 2CNC 9H 9 N) 4· x H 2O (RE=La～Dy, Y, except for Ce and Pm) were synthesized in dry N 2 atmosphere and characterized by elemental analyses, molar conductance, IR spectra, thermal analyses. The results show that the ligands coordinate to the RE ion through two sulphur atom donors. Thermal analyses indicate that the thermal stability of the complex is not higher than that of sodium 5 phenyl pyrazoline dithioformate. The complexes are easily soluble in acetonitrile and tetrahydrofuran. The molar conductance values of the complexes measured in acetonitrile (1 24～1 32×10 -3 mol·dm -3 ) at 25 ℃ are in the range of 86～104 Ω -1 ·cm 2·mol -1 , indicating that they are 1∶1 electrolytes.

Preparation and tensile properties of DD5 single crystal castings

The preparation procedure of DD5 single crystal castings was optimized. The microstructure characteristics of DD5 single crystal superalloy were investigated by microstructure observation and segregation behavior examination. The results show that the grain orientation is optimized by constraining the spiral crystallizer in [001] orientation and spatial scale. Also, the γ＇ phase of inter-dendrites is larger and more irregular than that in dendrite arms. High temperature tensile tests of DD5 single crystal castings exhibit that the peak stress increases with increasing temperature, while the area reduction shows an opposite trend, when the temperature is below 800℃; meanwhile, when the temperature is between 800℃ and 1000℃, the fracture stress of the alloy is the same as the peak stress. The fracture mode changes from shear to ductile with increasing temperature from 600℃ and 1000℃.

Preparation and Magnetic Properties of SrFe12O19 Ferrites Suitable for Use in Self-Biased LTCC Circulators

Strontium ferrites with different Bi2O3 content are prepared by the solid phase method, and their magnetic properties are investigated primarily. The Bi2O3 additive and sintering temperature separately exhibit a strong effect on the sintering density, crystal structure, and magnetic properties of the ferrites. As to the ferrites with 3 wt% Bi2O3, the relatively high sintering density ρs, saturation magnetization Ms, and intrinsic coercivity HCi can be obtained at a low sintering temperature of 900℃ even much lower. Furthermore, the effective magnetic anisotropy constant Keff and magnetic anisotropy field Ha of the ferrites are calculated from the magnetization curve by the law of approach to saturation. It is suggested that the low-temperature sintered SrFe12O19 ferrites with Ms of 285.6 kA/m and Ha of 1564.6 kA/m possess a significant potentiality for applying in the self-biased low-temperature co-fired ceramics circulators from 34 to 40GHz.

Preparation of Silicon Carbide with High Properties

In order to prepare silicon carbide with high properties, three kinds of SiC powders A, B, and C with different composition and two kinds of additives, which were Y2O3-A12O3 system and Y2O3-La2O3 system, were used in this experiment. The properties of hot-pressed SiC ceramics were measured. With the same additives, different SiC powder resulted in different properties. On the other hand, with the same SiC powder, increasing the amount of the additive Y2O3Al2O3 improved properties of SiC ceramics at room temperature, and increasing the amount of the additive Y2O3-La2O3 improved property SiC ceramics at elevated temperature. In addition. the microstructure of SiC ceramics was studied by scanning electron microscopy.

Preparation and Magnetic Properties of (Fe_7Co_3)_(0.15)(SiO_2)_(0.85)Granular Solids Using the Sol-Gel Method

(Fe7Co3)0.15(SiO2)0.85 granular alloy solid was prepared successfully using sol-gel method. The samples with different reducing temperatures were investigated by X-ray diffractometer(XRD),transmission electron micrography(TEM) and vibrating sample magnetometer(VSM). The av-erage particIe sizes of the samples were also calculated from Scherrer formula. The magnetic properties of (Fe7Co3 )o. 15 (SiO2)0.85 were studied in detail.

THE USE OF ANTI-HUMAN GLIOMA MONOCLONAL ANTIBODIES FOR TARGETING CHEMOTHERAPY OF BRAIN GLIOMAS(PREPARATION AND CYTOTOXIC PROPERTIES OF ANTIBODY-ADRIAMYCIN IMMUNOCONJUGATES)

Immunoconjugates are antibody-drug hybrid molecules which combine the exquisite selectivity or monoclonal antibodies with the potent toxicity of anticancer agents. A monoclonal antibody SZ39 against human brain gliomas was used as a drug carrier. Adriamycin (ADR) was bound covalently to SZ39 to form a SZ39-ADR conjugate. The cytotoxic activity of the SZ39-ADR conjugate was tested in vitro and demonstrated potent and specific killing of cells derived from a human malignant glioma. 50% inhibitory concentration (IC50) for SZ39-ADR to 'target' cells was 8.14×10-9 M. An index of specificity between 'target' and 'non-target' cells was calculated to be 88-fold. These data suggest that the SZ39-ADR may use as a potent and cell type-specific agent and is a likely candidate for the targeting chemotherapy of malignant gliotnas.

THIN FILM PREPARATION OF AMORPHOUS Ti-Ni ALLOY AND THEIR HYDROGEN ABSORPTION PROPERTIES

Amorphous Ti_(0.88)Ni_(1.00) and Ti_(1.69)Ni_(1.00) alloy films are prepared by means of ion beam sputtering using TiNi and Ti_2Ni alloy targets, respectively. Their hydrogen absorption properties are investigated by a galvanostatic method. The results show th the discharge capacity of the Ti_(1.69)Ni_(1.00) sample is higher than that of the Ti_(0.88)Ni_(1.00) sample. And the film electrodes have high durability and long cycle life.

Preparation and optical characteristics of ZnO films by chelating sol-gel method

The effect of different annealing temperatures on the structure, morphology,and optical properties of ZnO thin films prepared by the chelating sol-gel method was investigated.Zinc-oxide thin films were coated on quartz glass substrates by dip coating. Zinc nitrate, absoluteethanol, and citric acid were used as precursor, solvent, and chelating agent, respectively. Theresults show that ZnO films derived from zinc-citrate have lower crystallization temperature (below400℃), and that the crystal structure is wurtzite. The films, treated over 500℃, consist ofnano-particles and show to be porous at 600℃. The particle size of the film increases with theincrease of the annealing temperature. The largest particle size is 60 nm at 600℃. The opticaltransmittances related to the annealing temperatures become 90% higher in the visible range. Thefilm shows a starting absorption at 380 nm, and the optical band-gap of the thin film (fired at500℃) is 3.25 eV and close to the intrinsic band-gap of ZnO (3.2 eV).

Hard Magnetic Properties of Sm-Fe-C Based Alloys Prepared by Mechanical Alloying

The structure and magnetic properties of SmyFe100-1.5yC0.5y(y=8～20) alloys prepared by mechanical alloying (MA) from Sm, Fe and graphite have been investigated systematically. In order to improve hard magnetic properties of the alloys prepared by mechanical alloying, a new method consisting of re-milling and re-annealing was developed. After being re-milled and re-annealed, the Curie temperature TC of the Sm-Fe-C alloys changes. The TC of 2:17 phase increases, whereas the TC of 2:14:1 phase decreases. After being re-annealed at low temperatures, the grain sizes of hard phases are smaller than those in the alloys annealed at high temperatures. The effects of Co or Ti substitution for Fe are studied.

Structural, Optical and Luminescence Properties of ZnO Thin Films Prepared by Sol-Gel Spin-Coating Method： Effect of Precursor Concentration

Transparent zinc oxide（ZnO） thin films are fabricated by a simple sol-gel spin-coating technique on glass substrates with different solution concentrations（0.3-1.2 M） using zinc acetate dehydrate [Zn（CH_3COO）_2·2H_2O] as precursor and isopropanol and monoethanolamine（MEA） as solvent and stabilizer, respectively. The molar ratio of zinc acetate dehydrate to MEA is 1.0. X-ray diffraction, ultraviolet-visible spectroscopy and photoluminescence spectroscopy are employed to investigate the effect of solution concentration on the structural and optical properties of the ZnO thin films. The obtained results of all thin films are discussed in detail and are compared with other experimental data.

Structure and Magnetic Properties of Fe-N Films Prepared by Dual Ion Beam Sputtering

Fe-N films were prepared on Si substrate by dual ion beam sputtering (DIBS). It is found that the crystal structure of the films varies from α-Fe, to ε-Fe2-3N, ε-Fe2-3N +γ-Fe4N, and finally γ'-Fe4N with the increase in substrate temperature (TS). The magnetic properties of the films were investigated by a vibrating sample magnetometer (VSM). The structure of the films is insensitive to the ratios of N2/Ar in main ion source(MIS), and is mainly influenced by the substrate temperature (Ts).

Effect of Chromium on Structure and Tribological Properties of Hydrogenated Cr/a-C:H Films Prepared via a Reactive Magnetron Sputtering System

Hydrogenated Cr-incorporated carbon films （Cr/a-C：H） are deposited successfully by using a dc reactive mag- netron sputtering system. The structure and mechanical properties of the as-deposited Cr/a-C：H films are characterized systematically by field-emission scanning electron microscope, x-ray diffraction, Raman spectra, nanoindentation and scratch. It is shown that optimal Cr metal forms nanocrystalline carbide to improve the hardness, toughness and adhesion strength in the amorphous carbon matrix, which possesses relatively higher nano-hardness of 15. 7 CPa, elastic modulus of 126.8 GPa and best adhesion strength with critical load （Lc） of 36 N for the Cr/a-C：H film deposited at CH4 flow rate of 20sccm. The friction and wear behaviors of as-deposited Cr/a-C：H films are evaluated under both the ambient air and deionized water conditions. The results reveal that it can achieve superior low friction and anti-wear performance for the Cr/a-C：H film deposited at CH4 flow rate of 20sccm under the ambient air condition, and the friction coetllcient and wear rate tested in deionized water condition are relatively lower compared with those tested under the ambient air condition for each film. Superior combination of mechanical and tribological properties for the Cr/a-C：H film should be a good candidate for engineering applications.

Microstructure and Mechanical Property of 2024 Aluminium Alloy Prepared by Rapid Solidification and Mechanical Milling

Rapidly solidified 2024 aluminium alloy powders were mechanically milled, then consolidated to bulk form. The microstructural changes of the powders in mechanical milling (MM) and consolidation process were characterized by X-ray diffraction analyses and transmission electron microscopy observations. The results showed that mechanical milling reduced the grain size to nanometer, dissolved the Al2Cu intermetallic compound into the aluminium matrix and produced an aluminium supersaturated solid solution. During consolidation process. the grain size increased to submicrometer, and the Al2Cu and Al2(Cu, Mg, Si, Fe, Mn) compounds precipitated owing to heating. Increasing consolidation temperature and time results in obvious grain growth and coarsening of second phase particles. The tensile yield strength of the consolidated alloy with submicrometer size grains increases with decreasing grain size, and it follows the famous HallPetch relation

Preparation and Nonlinearity properties of Pd Nanoparticles

Pd nanoparticles less than 8 nm were photoinduced by a near-IR femtosecond laser. The sign of the refraction nonlinearity is negative for the Pd nanoparticles with TiO2, while it is positive for those without TiO2.

Current Status and Prospect of Infrared Radiation Ceramics for Energy-saving Applications in High Temperature Furnaces

Nowadays,it is a great challenge to reduce energy consumption and exhaust emission for human activities,in particular,high temperature industries.Among many efforts made to realize energy savings for high temperature furnaces and kilns,the use of high emissivity materials is considered to be an effective route to increase their thermal efficiency by enhancing heat transfer.Most materials with high refractoriness and superior chemical stability have weak infrared absorption and radiation properties;however,their emissivity in infrared regions（1 —25 μm） could be effectively increased by ion doping.This is attributed to three main mechanisms：1） distortion of the crystal lattice;2） increase of free carrier absorption; 3） formation of impurity energy level.In this paper,the development and advancement of various material systems with high emissivity including non-oxides and oxide based ceramics were reviewed.It is also suggested that the establishment of evaluation models or instruments for energy savings would be beneficial to design and application of high emissivity materials in various high-temperature environment.Furthermore,more efforts should be made on durability of high emissivity materials at high service temperatures and on the standardization of testing methods for emissivity.