In the present study, impulse pressuring diffu- sion bonding technology （IPDB） was utilized between commercially pure titanium and 304 stainless steel （SS） using pure nickel （Ni） as interlayer metal. The interfa...In the present study, impulse pressuring diffu- sion bonding technology （IPDB） was utilized between commercially pure titanium and 304 stainless steel （SS） using pure nickel （Ni） as interlayer metal. The interfacial microstructures of the bonded joints were investigated by scanning electron microscopy （SEM） and energy dispersive spectroscope （EDS） analyses. It is found that with the aid of the Ni interlayer, the interdiffusion and reaction between Ti and SS can be effectively restricted and robust joints can be obtained. Intermetallic compounds （IMCs） including Ti2Ni, TiNi, and TiNi3 are detected at the Ti/Ni interface; however, only Ni-Fe solid solution is found at the Ni/SS interface. The maximum tensile strength of 358 MPa is obtained by IPDB for 90 s and the fracture takes place along the Ti2Ni and TiNi phase upon tensile loading. The existence of cleavage pattern on the fracture surface indi- cates the brittle nature of the joints.展开更多
基金financially supported by the National Natural Science Foundation of China(No.50675234)
文摘In the present study, impulse pressuring diffu- sion bonding technology （IPDB） was utilized between commercially pure titanium and 304 stainless steel （SS） using pure nickel （Ni） as interlayer metal. The interfacial microstructures of the bonded joints were investigated by scanning electron microscopy （SEM） and energy dispersive spectroscope （EDS） analyses. It is found that with the aid of the Ni interlayer, the interdiffusion and reaction between Ti and SS can be effectively restricted and robust joints can be obtained. Intermetallic compounds （IMCs） including Ti2Ni, TiNi, and TiNi3 are detected at the Ti/Ni interface; however, only Ni-Fe solid solution is found at the Ni/SS interface. The maximum tensile strength of 358 MPa is obtained by IPDB for 90 s and the fracture takes place along the Ti2Ni and TiNi phase upon tensile loading. The existence of cleavage pattern on the fracture surface indi- cates the brittle nature of the joints.