Influence of hydrogen attack on mechanical and fatigue properties of 1020, 15CrMo and 2.25Cr-1Mo steels has been studied, which were exposed to gaseous hydrogen at pressure of 18MPa and 300-480℃ for up to 480h. The r...Influence of hydrogen attack on mechanical and fatigue properties of 1020, 15CrMo and 2.25Cr-1Mo steels has been studied, which were exposed to gaseous hydrogen at pressure of 18MPa and 300-480℃ for up to 480h. The results of fatigue test showed that hydrogen attack (HA) resulted in an obvious change in fatigue properties of 1020 and 15CrMo steels, however, 2.25Cr-1Mo steel showed a lower susceptibility to hydrogen attack due to the addition of Cr and Mo. Fatigue crack behaviour for 1020 steel is attributed to hydrogen attack damage and the crack closure induced by the rough cracking surface, which lead to a valley on △Kth~HA% plot. The change in the fatigue behaviour of 15CrMo steel is possibly caused by severe surface decarburization.展开更多
Microstructure evolution in neutron irradiated Reactor Pressure Vessel (RPV) steels was experimentally simulated through an improved degradation procedure in this study. The degradation procedure includes austenitiz...Microstructure evolution in neutron irradiated Reactor Pressure Vessel (RPV) steels was experimentally simulated through an improved degradation procedure in this study. The degradation procedure includes austenitizing at 1 150℃ and water quench, deformation 10% and 30% respectively, and then thermal aging at 500℃ for different period of time. The microstructure of the specimens was analyzed in details using transmission electron microscopy (TEM). The micro-hardness test results showed that all the hardness curves of undeformed, 10% pre-deformed and 30% pre-deformed specimens have two micro-hardness peaks with the first peak value corresponding to different thermal aging time of 1 hour, 5 hours and 10 hours, respectively. It was revealed that the hardness curves were influenced by the precipitation of Cu-rich precipitates (CRPs) and carbides, deposition of martensite and work hardening.展开更多
In order to get more precise bursting pressure formula of mild steel, hundreds of bursting experiments of mild steel pressure vessels such as Q235(Gr.D) and 20R(1020) are done. Based on statistical data of burstin...In order to get more precise bursting pressure formula of mild steel, hundreds of bursting experiments of mild steel pressure vessels such as Q235(Gr.D) and 20R(1020) are done. Based on statistical data of bursting pressure and modification of Faupel formula, a more precise modified formula is given out according to the experimental data. It is proved to be more accurate after examining other bursting pressure value presented in many references. This bursting formula is very accurate in these experiments using pressure vessels with different diameter and shell thickness. Obviously, this modified bursting formula can be used in mild steel pressure vessels with different diameter and thickness of shell.展开更多
An overview of a severe kind of environmentally-assisted cracking-stress corrosion cracking (SCC) of pressure vessel steel (PVS),such as stainless steel 304, alloy 600,690 and other nickel-based alloys in subcritical ...An overview of a severe kind of environmentally-assisted cracking-stress corrosion cracking (SCC) of pressure vessel steel (PVS),such as stainless steel 304, alloy 600,690 and other nickel-based alloys in subcritical (~300 ℃) aqueous environment was given. The mechanisms of SCC of metals under this inclement surrounding were briefly generalized. Herein,some pragmatic solutions to mitigate the SCC susceptibility and retard its propagation were presented. The titanium and cerium-based inhibitors addition countermeasure was highlighted.展开更多
The crystal structure evolution of the Cu-rich nano precipitates from bcc to 9R during thermal aging was studied in nuclear reactor pressure vessel (RPV) model steels. The specimens, contained higher copper and nick...The crystal structure evolution of the Cu-rich nano precipitates from bcc to 9R during thermal aging was studied in nuclear reactor pressure vessel (RPV) model steels. The specimens, contained higher copper and nickel contents than commercially available one, were heated at 890 ~C for 0.5 h and then water quenched followed by tempering at 0(50 ~C for I0 h and aging at 400 ~C for 1000 h. It was observed that bcc and 9R orthogonal structure, as well as 9R orthogonal and 9R monoclinic structure, coexist in a single Cu-rich nano precipitate. Further analyses pointed out that Cu-rich nano precipitates of bcc structure were not stable, it may preferentially transform to 9R orthogonal structure and then to 9R monoclinic structure. This results showed that the crystal structure evolution of the Cu-rich nano precipitates was complex.展开更多
The welding coarse-grained heat-affected zones(CGHAZs) in the undoped and Ce-doped samples of SA508CL-3 reactor pressure vessel steel were simulated using a Gleeble 1500 D thermomechanical simulator with a peak temp...The welding coarse-grained heat-affected zones(CGHAZs) in the undoped and Ce-doped samples of SA508CL-3 reactor pressure vessel steel were simulated using a Gleeble 1500 D thermomechanical simulator with a peak temperature of 1320 oC at the heat inputs of 30, 50 and 100 kJ /cm, respectively. The ductile-to-brittle transition temperature(DBTT) of the simulated CGHAZs was evaluated along with microstructural and microchemical characterizations. The results indicated that Ce could substantially lower the DBTT of the CGHAZs by its microstructural and microchemical effects. After the thermal cycling of welding, the microstructure in the Ce-doped samples was apparently finer than that in the undoped samples, regardless of the lath bainite obtained at the heat inputs of 30 and 50 kJ /cm or the granular bainite acquired at the heat input of 100 kJ /cm, leading to lower DBTTs for the Ce-doped samples. Moreover, grain boundary segregation of Ce occurred apparently in the Ce-doped samples and exhibited a non-equilibrium characteristic. The segregation of Ce could play an important role in lowering the DBTT of CGHAZs or toughening the CGHAZs.展开更多
Dynamic strain aging (DSA) effect on SA508-III reactor pressure vessel (RPV) steel was investigated. The SA508-III RPV steel was subjected to tension tests at different strain rates (1.1× 10-5 s-1 and 6.6...Dynamic strain aging (DSA) effect on SA508-III reactor pressure vessel (RPV) steel was investigated. The SA508-III RPV steel was subjected to tension tests at different strain rates (1.1× 10-5 s-1 and 6.6× 10-5 s-1) and different temperatures (500 and 550 ℃) to evaluate the influence of strain rate and temperature on the serrated flow behavior, which is the repetitive and discontinuous yielding phenomenon on the stress-strain curves. The higher temperature leads to the higher density of precipitates, M23C6 carbides and needle-like Mo2C carbides. It was found that the samples under tension test of 6.6 × 10-5 s-1 and 500 ℃ possess superior mechanical properties and mainly show A-type serrations on the tension test curves. Then, the local regress method was used to filter the DSA curves, thus to show the real trend of the curves. It has been found that the less time of interaction between dislocations and precipitates under higher strain rates leads to a higher strength of the sample. The more tiny-stress drops on the 550 ℃ serration curve can be attributed to the hardening phase, M23C6 carbides and needle-like Mo2C carbides. The higher percentage of the small stress drops on the serration curves represents the higher mechanical strength.展开更多
文摘Influence of hydrogen attack on mechanical and fatigue properties of 1020, 15CrMo and 2.25Cr-1Mo steels has been studied, which were exposed to gaseous hydrogen at pressure of 18MPa and 300-480℃ for up to 480h. The results of fatigue test showed that hydrogen attack (HA) resulted in an obvious change in fatigue properties of 1020 and 15CrMo steels, however, 2.25Cr-1Mo steel showed a lower susceptibility to hydrogen attack due to the addition of Cr and Mo. Fatigue crack behaviour for 1020 steel is attributed to hydrogen attack damage and the crack closure induced by the rough cracking surface, which lead to a valley on △Kth~HA% plot. The change in the fatigue behaviour of 15CrMo steel is possibly caused by severe surface decarburization.
文摘Microstructure evolution in neutron irradiated Reactor Pressure Vessel (RPV) steels was experimentally simulated through an improved degradation procedure in this study. The degradation procedure includes austenitizing at 1 150℃ and water quench, deformation 10% and 30% respectively, and then thermal aging at 500℃ for different period of time. The microstructure of the specimens was analyzed in details using transmission electron microscopy (TEM). The micro-hardness test results showed that all the hardness curves of undeformed, 10% pre-deformed and 30% pre-deformed specimens have two micro-hardness peaks with the first peak value corresponding to different thermal aging time of 1 hour, 5 hours and 10 hours, respectively. It was revealed that the hardness curves were influenced by the precipitation of Cu-rich precipitates (CRPs) and carbides, deposition of martensite and work hardening.
文摘In order to get more precise bursting pressure formula of mild steel, hundreds of bursting experiments of mild steel pressure vessels such as Q235(Gr.D) and 20R(1020) are done. Based on statistical data of bursting pressure and modification of Faupel formula, a more precise modified formula is given out according to the experimental data. It is proved to be more accurate after examining other bursting pressure value presented in many references. This bursting formula is very accurate in these experiments using pressure vessels with different diameter and shell thickness. Obviously, this modified bursting formula can be used in mild steel pressure vessels with different diameter and thickness of shell.
文摘An overview of a severe kind of environmentally-assisted cracking-stress corrosion cracking (SCC) of pressure vessel steel (PVS),such as stainless steel 304, alloy 600,690 and other nickel-based alloys in subcritical (~300 ℃) aqueous environment was given. The mechanisms of SCC of metals under this inclement surrounding were briefly generalized. Herein,some pragmatic solutions to mitigate the SCC susceptibility and retard its propagation were presented. The titanium and cerium-based inhibitors addition countermeasure was highlighted.
基金financially supported by the National Basic Research Program of China(No.2011CB610503)National Natural Science Foundation of China(No.50931003)Ministry of Major Subject of Shanghai(No.S30107)
文摘The crystal structure evolution of the Cu-rich nano precipitates from bcc to 9R during thermal aging was studied in nuclear reactor pressure vessel (RPV) model steels. The specimens, contained higher copper and nickel contents than commercially available one, were heated at 890 ~C for 0.5 h and then water quenched followed by tempering at 0(50 ~C for I0 h and aging at 400 ~C for 1000 h. It was observed that bcc and 9R orthogonal structure, as well as 9R orthogonal and 9R monoclinic structure, coexist in a single Cu-rich nano precipitate. Further analyses pointed out that Cu-rich nano precipitates of bcc structure were not stable, it may preferentially transform to 9R orthogonal structure and then to 9R monoclinic structure. This results showed that the crystal structure evolution of the Cu-rich nano precipitates was complex.
基金supported by the National Natural Science Foundation of China(51071060)
文摘The welding coarse-grained heat-affected zones(CGHAZs) in the undoped and Ce-doped samples of SA508CL-3 reactor pressure vessel steel were simulated using a Gleeble 1500 D thermomechanical simulator with a peak temperature of 1320 oC at the heat inputs of 30, 50 and 100 kJ /cm, respectively. The ductile-to-brittle transition temperature(DBTT) of the simulated CGHAZs was evaluated along with microstructural and microchemical characterizations. The results indicated that Ce could substantially lower the DBTT of the CGHAZs by its microstructural and microchemical effects. After the thermal cycling of welding, the microstructure in the Ce-doped samples was apparently finer than that in the undoped samples, regardless of the lath bainite obtained at the heat inputs of 30 and 50 kJ /cm or the granular bainite acquired at the heat input of 100 kJ /cm, leading to lower DBTTs for the Ce-doped samples. Moreover, grain boundary segregation of Ce occurred apparently in the Ce-doped samples and exhibited a non-equilibrium characteristic. The segregation of Ce could play an important role in lowering the DBTT of CGHAZs or toughening the CGHAZs.
文摘Dynamic strain aging (DSA) effect on SA508-III reactor pressure vessel (RPV) steel was investigated. The SA508-III RPV steel was subjected to tension tests at different strain rates (1.1× 10-5 s-1 and 6.6× 10-5 s-1) and different temperatures (500 and 550 ℃) to evaluate the influence of strain rate and temperature on the serrated flow behavior, which is the repetitive and discontinuous yielding phenomenon on the stress-strain curves. The higher temperature leads to the higher density of precipitates, M23C6 carbides and needle-like Mo2C carbides. It was found that the samples under tension test of 6.6 × 10-5 s-1 and 500 ℃ possess superior mechanical properties and mainly show A-type serrations on the tension test curves. Then, the local regress method was used to filter the DSA curves, thus to show the real trend of the curves. It has been found that the less time of interaction between dislocations and precipitates under higher strain rates leads to a higher strength of the sample. The more tiny-stress drops on the 550 ℃ serration curve can be attributed to the hardening phase, M23C6 carbides and needle-like Mo2C carbides. The higher percentage of the small stress drops on the serration curves represents the higher mechanical strength.