The grain boundary phase affects the magnetic properties and corrosion resistance of sintered NdFeB magnets.In this work,a small amount of In was added to NdFeB magnets by induction melting to systematically investiga...The grain boundary phase affects the magnetic properties and corrosion resistance of sintered NdFeB magnets.In this work,a small amount of In was added to NdFeB magnets by induction melting to systematically investigate its effect on the evolution of the microstructure,magnetic properties and corrosion resistance of NdFeB magnets.Microstructural analysis illustrated that minor In addition generated more grain boundary phases and an abundant amorphous phase at the triple-junction grain boundary.While the addition of In failed to enhance the magnetic isolation effect between adjacent matrix grains,its incorporation fortuitously elevated the electrochemical potential of the In-containing magnets.Besides,during corrosion,an In-rich precipitate phase formed,hindering the ingress of the corrosive medium into the magnet.Consequently,this significantly bolstered the corrosion resistance of the sintered NdFeB magnets.The phase formation,magnetic properties and corrosion resistance of In-doped NdFeB magnets are detailed in this work,which provides new prospects for the preparation of high-performance sintered NdFeB magnets.展开更多
Hexagonal boron nitride(h-BN)ceramics have become exceptional materials for heat-resistant components in hypersonic vehicles,owing to their superior thermal stability and excellent dielectric properties.However,their ...Hexagonal boron nitride(h-BN)ceramics have become exceptional materials for heat-resistant components in hypersonic vehicles,owing to their superior thermal stability and excellent dielectric properties.However,their densification during sintering still poses challenges for researchers,and their mechanical properties are rather unsatisfactory.In this study,SrAl_(2)Si_(2)O_(8)(SAS),with low melting point and high strength,was introduced into the h-BN ceramics to facilitate the sintering and reinforce the strength and toughness.Then,BN-SAS ceramic composites were fabricated via hot press sintering using h-BN,SrCO_(3),Al_(2)O_(3),and SiO_(2) as raw materials,and effects of sintering pressure on their microstructure,mechanical property,and thermal property were investigated.The thermal shock resistance of BN-SAS ceramic composites was evaluated.Results show that phases of as-preparedBN-SAS ceramic composites are h-BN and h-SrAl_(2)Si_(2)O_(8).With the increase of sintering pressure,the composites’densities increase,and the mechanical properties shew a rising trend followed by a slight decline.At a sintering pressure of 20 MPa,their bending strength and fracture toughness are(138±4)MPa and(1.84±0.05)MPa·m^(1/2),respectively.Composites sintered at 10 MPa exhibit a low coefficient of thermal expansion,with an average of 2.96×10^(-6) K^(-1) in the temperature range from 200 to 1200℃.The BN-SAS ceramic composites prepared at 20 MPa display higher thermal conductivity from 12.42 to 28.42 W·m^(-1)·K^(-1) within the temperature range from room temperature to 1000℃.Notably,BN-SAS composites exhibit remarkable thermal shock resistance,with residual bending strength peaking and subsequently declining sharply under a thermal shock temperature difference ranging from 600 to 1400℃.The maximum residual bending strength is recorded at a temperature difference of 800℃,with a residual strength retention rate of 101%.As the thermal shock temperature difference increase,the degree of oxidation on the ceramic surface and cracks due to thermal stress are also increased gradually.展开更多
The evolution of mechanical properties,localized corrosion resistance of a high purity Al-Zn-Mg-Cu alloy during non-isothermal aging(NIA)was investigated by hardness test,electrical conductivity test,tensile test,inte...The evolution of mechanical properties,localized corrosion resistance of a high purity Al-Zn-Mg-Cu alloy during non-isothermal aging(NIA)was investigated by hardness test,electrical conductivity test,tensile test,intergranular corrosion test,exfoliation corrosion test,slow strain rate tensile test and electrochemical test,and the mechanism has been discussed based on microstructure examination by optical microscopy,electron back scattered diffraction,scanning electron microscopy and scanning transmission electron microscopy.The NIA treatment includes a heating stage from 40℃to 180℃with a rate of 20℃/h and a cooling stage from 180℃to 40℃with a rate of 10℃/h.The results show that the hardness and strength increase rapidly during the heating stage of NIA since the increasing temperature favors the nucleation and the growth of strengthening precipitates and promotes the transformation of Guinier-Preston(GPI)zones toη'phase.During the cooling stage,the sizes ofη'phase increase with a little change in the number density,leading to a further slight increase of the hardness and strength.As NIA proceeds,the corroded morphology in the alloy changes from a layering feature to a wavy feature,the maximum corrosion depth decreases,and the reason has been analyzed based on the microstructural and microchemical feature of precipitates at grain boundaries and subgrain boundaries.展开更多
In order to study the effect of element Nb on the microstructure and properties of the biomedical β-type Ti-Mo based alloys,Ti-15Mo-xNb(x=5,10,15 and 20 in %) alloys were investigated.The dry wear resistance of β-...In order to study the effect of element Nb on the microstructure and properties of the biomedical β-type Ti-Mo based alloys,Ti-15Mo-xNb(x=5,10,15 and 20 in %) alloys were investigated.The dry wear resistance of β-type Ti-15Mo-xNb alloys against Gr15 ball was investigated on CJS111A ball-disk wear instrument.Experimental results indicate that crystal structure and morphology of the Ti-15Mo-xNb alloys are sensitive to their Nb contents.Ti-15Mo-xNb alloys match those for β phase peaks and no any phases are found.The Vickers hardness values of all the Ti-15Mo-xNb alloys are higher than HV200.The compression yield strength of the Ti-15Mo-5Nb alloy is the lowest and that of the Ti-15Mo-10Nb alloy is the highest.For all the Ti-15Mo-xNb alloys,the friction coefficient is not constant but takes a higher value.In dry condition,SEM study reveals deep parallel scars on the wear surfaces of all the Ti-15Mo-xNb alloys under different loads.The friction coefficient of the Ti-15Mo-5Nb alloy under 1 N is the lowest.The wear principal mechanism for Ti-15Mo-xNb alloys is adhesive wear.展开更多
The effects of T916 thermo-mechanical process on microstructures, mechanical properties and ballistic resistance of 2519A aluminum alloy were investigated by optical microscopy (OM), transmission electron microscopy...The effects of T916 thermo-mechanical process on microstructures, mechanical properties and ballistic resistance of 2519A aluminum alloy were investigated by optical microscopy (OM), transmission electron microscopy (TEM), tensile tests and ballistic resistance test. After T916 treatment, the yield strength, tensile strength and elongation rate of 2519A aluminum alloy reach 501 MPa, 540 MPa and 14%, respectively. And the ballistic limit velocity of 2519A-T916 alloy (30 mm in thickness) is 715 rn/s. The microstructure varies near the sidewalls of crater. The interrupted ageing contributes to these excellent properties of the alloy. During T916 process, the precipitation of Guinier Preston (GP) zone is finer and denser during the interrupted ageing, thus resulting in well precipitated strengthening phase.展开更多
The microstructural characteristics, mechanical properties and creep resistance of Mg-(8%-12%) Zn-(2%-6%) A1 alloys were investigated to get a better overall understanding of these series alloys. The results indic...The microstructural characteristics, mechanical properties and creep resistance of Mg-(8%-12%) Zn-(2%-6%) A1 alloys were investigated to get a better overall understanding of these series alloys. The results indicate that the microstructure of the alloys ZA82, ZA102 and ZA122 with the mass ratio of Zn to A1 of 4-6 is mainly composed of a-Mg matrix and two different morphologies of precipitates (block τ-Mg32(Al, Zn)49 and dense lamellar ε-Mg51Zn20), the alloys ZA84, ZA104 and ZA124 with the mass ratio of 2-3 contain α-Mg matrix and only block r phases, and the alloys ZA86, ZA106 and ZA126 with the mass ratio of 1-2 consist of a-Mg matrix, block r precipitates, lamellar Ф-Al2Mg5Zn2 eutectics and flocculent β-Mg17Al12 compounds. The alloys studied with the mass ratio of Zn to A1 of 2-3 exhibit high creep resistance, and the alloy ZA124 with the continuous network of r precipitating along grain boundaries shows the highest creep resistance.展开更多
Effects of alloying processing on tensile test properties of Fe 3Al based alloys have been studied. Results show that microalloying of cerium is very effective on increasing the room temperature ductility of Fe 3Al...Effects of alloying processing on tensile test properties of Fe 3Al based alloys have been studied. Results show that microalloying of cerium is very effective on increasing the room temperature ductility of Fe 3Al based alloys. Surface analysis by XPS demonstrates that cerium addition causes the change in the oxide chemistry and provides rapid passivation of the specimen surface. The high temperature strength and creep resistance of Fe 3Al based alloys can be significantly enhanced by alloying additions of tungsten, niobium or molybdenum, especially when combined additions of tungsten with niobium or molybdenum are used. The additions of tungsten, niobium or molybdenum also result in the significant microstructural refinement and the formation of fine precipitates which are identified as M 6C type carbide in the alloys containing tungsten.展开更多
Zn is a commonly used alloying element for Mg alloys owing to its beneficial effects on mechanical properties. To improve the mechanical and corrosion properties of WE43B Mg alloys, the effects of 0–0.7wt% Zn additio...Zn is a commonly used alloying element for Mg alloys owing to its beneficial effects on mechanical properties. To improve the mechanical and corrosion properties of WE43B Mg alloys, the effects of 0–0.7wt% Zn addition on the microstructure and properties of sample alloys were investigated. Addition of Zn to as-cast WE43B alloy promoted the formation of the Mg12Nd phase;by contrast, after T6 heat treatment, the phase composition of WE43B alloys with and without Zn addition remained mostly the same. A long-period stacking ordered phase was predicted by CALPHAD calculation, but this phase was not observed in either the as-cast or heat-treated Zn-containing WE43B alloys. The optimum temperature and duration of T6 heat treatment were obtained using CALPHAD calculations and hardness measurements. Addition of Zn resulted in a slight reduction in the average grain size of the as-cast and T6 heat-treated WE43B alloys and endowed them with increased corrosion resistance with little effect on their mechanical properties.展开更多
The corrosion behavior and mechanical properties of 316 L stainless steel(SS) fabricated via selective laser melting(SLM) were clarified by potentiodynamic polarization measurements, immersion tests, and tensile exper...The corrosion behavior and mechanical properties of 316 L stainless steel(SS) fabricated via selective laser melting(SLM) were clarified by potentiodynamic polarization measurements, immersion tests, and tensile experiments. The microstructural anisotropy of SLMed 316 L SS was also investigated by electron back-scattered diffraction and transmission electron microscopy. The grain sizes of the SLMed 316 L SS in the XOZ plane were smaller than those of the SLMed 316 L SS in the XOY plane, and a greater number of low-angle boundaries were present in the XOY plane, resulting in lower elongation for the XOY plane than for the XOZ plane. The SLMed 316 L was expected to exhibit higher strength but lower ductility than the wrought 316 L, which was attributed to the high density of dislocations. The pitting potentials of the SLMed 316 L samples were universally higher than those of the wrought sample in chloride solutions because of the annihilation of MnS or(Ca,Al)-oxides during the rapid solidification. However, the molten pool boundaries preferentially dissolved in aggressive solutions and the damage of the SLMed 316 L in FeCl3 solution was more serious after long-term service, indicating poor durability.展开更多
Silver or copper ions are often chosen as antibacterial agents. But a few reports are concerned with these two antibacterial agents for preparation of antibacterial stainless steel (SS). The antibacterial properties...Silver or copper ions are often chosen as antibacterial agents. But a few reports are concerned with these two antibacterial agents for preparation of antibacterial stainless steel (SS). The antibacterial properties and corrosion resistance of AISI 420 stainless steel implanted by silver and copper ions were investigated. Due to the cooperative antibacterial effect of silver and copper ions, the Ag/Cu implanted SS showed excellent antibacterial activities against both Gram-negative Escherichia coli (E. coli) and Gram-positive Staphylococcus aureus (S. aureus) at a total implantation dose of 2~ 1017 ions/cm2. Electrochemical polarization curves revealed that the corrosion resistance of Ag/Cu implanted SS was slightly enhanced as compared with that of un-implanted SS, The implanted layer was characterized by X-ray photoelec- tron spectroscopy (XPS). Core level XPS spectra indicate that the implanted silver and copper ions exist in metallic state in the implanted layer.展开更多
A series of stable waterborne polysiloxaneurethane (WPSUR) dispersions were prepared using amino-terminated polydimethylsiloxane (NS), dimethylolpropionic acid (DMPA), castor oil, polypropylene glycol and toluen...A series of stable waterborne polysiloxaneurethane (WPSUR) dispersions were prepared using amino-terminated polydimethylsiloxane (NS), dimethylolpropionic acid (DMPA), castor oil, polypropylene glycol and toluene diisocyanate. Meanwhile, NS with different molecular weights was synthesized and used as the soft co-segment. Effects of types and contents of soft co-segments as well as chain extenders on the thermal degradation and stability for WPSUR films were examined. Results reveal that WPSUR films exhibit excellent water resistance and mechanical properties as compared with pure polyurethane (PU) films, and the NS soft co-segment possesses a remarkable effect on the second stage (stage Ⅱ), while the content of the hard segment is propitious to the initial stage (stage Ⅰ). Moreover, the highest temperature of stage Ⅱ (T2m) for WPSUR films using NS as soft co-segment is 413℃, approximately being 30℃ higher than that of those typical PUs using HDA and APDMS as the chain extenders, respectively.展开更多
A bisphenol epoxy resin was used as modifier to increase the heat resistance of condensed poly-nuclear aromatic (COPNA) resin. The basic properties of COPNA resin and modified resin were characterized by Fourier tra...A bisphenol epoxy resin was used as modifier to increase the heat resistance of condensed poly-nuclear aromatic (COPNA) resin. The basic properties of COPNA resin and modified resin were characterized by Fourier transform infrared spectroscopy (FT-IR), nuclear magnetic resonance spectroscopy (1H-NMR), vapor pressure osmometry (VPO) and elemental analysis (EA). Average structural parameters of resins were calculated by the improved Brown-Ladner method, and heat resistance of resins was tested by thermogravimetric analysis (TGA). The chemical structure, mechanical properties and heat resistivity of the resin/graphite composites prepared with different resins were compared. The results show that the adhesive property and heat resistance of COPNA resin can be remarkably improved by addition of 5 wt.% epoxy resin. The reason is that the reactions between epoxy groups of epoxy resin and hydroxyl groups of COPNA resin improve the heat resistance and adhesive property of COPNA resin. Electric motor brushes with good mechanical properties and low electrical resistivity were successfully prepared by using the modified resin as binder.展开更多
Traditional methods of coal thermal resistance characterization are informative but considerably timeconsuming and require utilization of a complex and expensive equipment. This limits the effectiveness of their appli...Traditional methods of coal thermal resistance characterization are informative but considerably timeconsuming and require utilization of a complex and expensive equipment. This limits the effectiveness of their application. In this paper, authors experimentally investigated potential application of thermally stimulated acoustic emission method for developing of relatively simple and rapid coals thermal resistance assessment method. Features of thermally stimulated acoustic emission of anthracite, lignites and bituminous coal samples subject to cyclic thermal loading have been experimentally investigated.For the first time, it has been shown that there exists a relationship of such patterns with structural parameters and properties of the coal samples, as well as their thermal resistance. The results indicate the possibility of applying the method of thermally stimulated acoustic emission to control processes of cryogenic disintegration and thermal resistance of fossil coals. The description of the equipment and methodological support needed for the implementation of this method have been provided.展开更多
During the recent years,some Mg based alloys have extensively been considered as a new generation of degradable and absorbable bio-medical materials.In this work,the Mg-2Zn-1Gd-1Ca(wt%)alloy as a new metallic bio-mate...During the recent years,some Mg based alloys have extensively been considered as a new generation of degradable and absorbable bio-medical materials.In this work,the Mg-2Zn-1Gd-1Ca(wt%)alloy as a new metallic bio-material was produced by the casting process followed by the heat treatment.The samples of the alloy were solution treated at temperatures of 500,550,and 600°C and then quench aged at temperatures of 125,150,and 175°C.The results of SEM-EDS examinations indicated that the alloy microstructure consists ofα-Mg matrix and the Ca_(2)Mg_(6)Zn_(3)and Mg_(3)Gd_(2)Zn_(3)secondary phases.With regard to the results of Vickers hardness test,the temperatures of 500°C and 150°C were selected as the optimum solutionizing and aging temperatures,respectively.Moreover,the dissolution of casting precipitates and production of lattice distortion occurring after the solution treatment led to the reduction in ultimate shear strength up to 21%.But,the precipitation hardening and morphological changes taking place during the aging treatment improved the ultimate shear strength up to 32%.Furthermore,the results of electro-chemical and weight-loss measurements in a simulated body fluid indicated that the heat-treated alloy is a promising candidate for the Mg based alloys recently considered for the bio-medical applications.展开更多
Mg?1Zn?0.5Ca alloys were prepared by traditional steel mould casting and water-cooled copper mould injection casting at higher cooling rate. Microstructure, mechanical properties and bio-corrosion resistance of two al...Mg?1Zn?0.5Ca alloys were prepared by traditional steel mould casting and water-cooled copper mould injection casting at higher cooling rate. Microstructure, mechanical properties and bio-corrosion resistance of two alloys were contrastively investigated. Grain size reduces remarkably and microstructure becomes homogenous when raising cooling rate. The bio-corrosion behaviour in 3.5% sodium chloride solution (3.5% NaCl) and Hank’s solution at 37°C was investigated using electrochemical polarization measurement and the results indicate that the alloy prepared at higher cooling rates has better corrosion resistance in both types of solution. Further mass loss immersion test in Hank’s solution reveals the same result. The reason of corrosion resistance improvement is that raising cooling rate brings about homogeneous microstructure, which leads to micro-galvanic corrosion alleviation. The tensile test results show that yield strength, ultimate tensile strength and elongation are improved by raising cooling rate and the improvement is mainly due to grain refinement.展开更多
To improve the mechanical properties and wear resistance of ZA27 alloy, Si was introduced to the alloy, and the effect of Si alloying and T6 heat treatment on the microstructure, mechanical properties and wear resista...To improve the mechanical properties and wear resistance of ZA27 alloy, Si was introduced to the alloy, and the effect of Si alloying and T6 heat treatment on the microstructure, mechanical properties and wear resistance was investigated. The results show that with 0.55% Si, the microstructure of the alloy can be refined effectively, which leads to the increase of hardness. But the tensile strength and elongation decrease because Si undermines the integrity of the matrix. On the other hand, the dendrites are transformed into a desired α+η+(α+η)mixture with T6 heat treatment, which introduces a remarkable increase to the elongation and hardness of the alloy. The wear resistance of the ZA27 alloy with Si alloying is significantly better than that of the ZA27 alloy without Si. With the increase of Si addition, the wear resistance of the alloy firstly increases and then decreases.In the alloy without Si alloying, severe plastic deformation and large delamination were observed on the worn surface of the alloy. However, with the increase of Si, the main wear mechanism transformed to abrasive wear gradually. In addition, the T6 treatment can further improve the wear resistance of the alloy with Si alloying.展开更多
In this work the microstructure, mechanical properties and wear resistance of Fe-Al based alloys with various alloying elements were studied. The microstructures were examined by optical and scanning electron microsco...In this work the microstructure, mechanical properties and wear resistance of Fe-Al based alloys with various alloying elements were studied. The microstructures were examined by optical and scanning electron microscopy (SEM) equipped with an energy dispersive X-ray spectroscope (EDS). Two types of alloys were prepared by vacuum arc melting. One is Fe-28Al based alloys (D03 structured) with and without alloying elements such as Mo and Zr. The other one is Fe-35Al based alloys (B2 structured) produced with the same manner. For both types of alloys, Mo addition had found to exhibit an equiaxed microstructure, while dendritic structure was observed to show the effect of Zr addition. These microstructural features were more evinced with increasing content of alloying element. Concerning the mechanical properties and wear resistance, Fe-35Al based alloys were superior to Fe-28Al based alloys over the whole temperature range investigated.展开更多
In this study, Ce was introduced into the AZ80 alloy and the effects of Ce addition on the microstructure, mechanical properties and corrosion resistance of the as-cast AZ80 magnesium alloy were investigated. The resu...In this study, Ce was introduced into the AZ80 alloy and the effects of Ce addition on the microstructure, mechanical properties and corrosion resistance of the as-cast AZ80 magnesium alloy were investigated. The results show that the addition of Ce into the AZ80 alloy can not only refine the microstructure, but also result in the formation of the needle-like Al4Ce phase. These tiny Al4Ce phases are homogeneously distributed at grain boundaries and within grains. An appropriate Ce addition can also change the β-Mg17Al12 phase at the grain boundaries from continuous network to small island-like. At the same time, with the increase of Ce content from 0 to 2.0wt.%, the macro-hardness of the as-cast alloy is enhanced linearly, while impact toughness, tensile strength and elongation all firstly increase and then decrease. The AZ80 alloy containing 1.0wt.% Ce exhibits the optimal properties. Its macro-hardness, impact toughness, tensile strength and elongation are 61.90 HB, 15.50 J·cm-2, 171.80 MPa and 3.35%, increase by 9.95%, 63%, 13.3% and 36.7%, respectively compared with the base alloy. In addition, Ce can enhance the corrosion resistance of the AZ80 magnesium alloy.展开更多
The characteristics of microstructure, mechanical property and corrosion behavior of Cr26Mo3.5 super stainless steel joints by pulse tungsten inert gas(P-TIG)welding and laser welding were investigated. The results in...The characteristics of microstructure, mechanical property and corrosion behavior of Cr26Mo3.5 super stainless steel joints by pulse tungsten inert gas(P-TIG)welding and laser welding were investigated. The results indicate that the widths of the center equiaxed grain zone(EGZ)and the columnar grain zone(CGZ)increase with the increase of heat input in both welding processes. The precipitates of Nb and Ti carbides and nitrides are formed in the weld metal(WM)and the heat affected zone(HAZ). The joints by laser welding show better tensile and corrosion resistance properties than those by P-TIG welding due to the heat concentration and lower heat input. The tensile strength and elongation increase with the decrease of heat input, and the fracture mode of the joints turns into ductile-brittle mixed fracture from ductile fracture when the welding method turns into P-TIG welding from laser welding. Moreover, the corrosion resistance of all joints declines slightly with the increase of heat input. Hence, laser welding is more suitable for welding Cr26Mo3.5 super stainless steel in engineering applications.展开更多
In this present work, Pb was applied in the Mg97Zn1Y2 alloy to improve its microstructure and properties, using conventional casting methods. The microstructure and properties of the Mg97 Zn1 Y2 alloy and Mg97Zn1Y2-x ...In this present work, Pb was applied in the Mg97Zn1Y2 alloy to improve its microstructure and properties, using conventional casting methods. The microstructure and properties of the Mg97 Zn1 Y2 alloy and Mg97Zn1Y2-x Pb(x=0.6 wt.%, 1.2 wt.% and 1.8 wt.%) alloys were observed by optical microscopy, scanning electron microscopy method and analyzed by X-ray diffraction, hardness and strength measurement and electrochemical testing. After adding Pb to the Mg97Zn1Y2 alloy, a new particle phase Mg_2 Pb was identified along the grain boundaries, and dendrites were refined. In addtion, the hardness of Mg97Zn1Y2-xPb(x=0.6 wt.%, 1.2 wt.% and 1.8 wt.%) alloys was higher than that of the Mg97 Zn1Y2 alloy; with the increase of Pb content, the hardness of the alloy increased first and then decreased, followed by a final slight increase, and reached a maximum of 89.1 HV when the Pb content was 0.6 wt.%. The strength of the alloy increased first and then decreased as the Pb content increased. Moreover, adding a small amount of Pb to the alloy can effectively inhibit corrosion, and Mg97Zn1Y2-0.6 wt.%Pb exhibits the best corrosion resistance ability.展开更多
基金funded by Ningbo Key R&D Plan and“Unveiling and Leading”(Grant No.2023Z093)Ningbo Science and Technology Innovation 2025 Major Special Project(Grant No.2022Z106)Hezhou City Central Leading Local Science and Technology Development Special Fund Project(Grant No.HK ZY2022002).
文摘The grain boundary phase affects the magnetic properties and corrosion resistance of sintered NdFeB magnets.In this work,a small amount of In was added to NdFeB magnets by induction melting to systematically investigate its effect on the evolution of the microstructure,magnetic properties and corrosion resistance of NdFeB magnets.Microstructural analysis illustrated that minor In addition generated more grain boundary phases and an abundant amorphous phase at the triple-junction grain boundary.While the addition of In failed to enhance the magnetic isolation effect between adjacent matrix grains,its incorporation fortuitously elevated the electrochemical potential of the In-containing magnets.Besides,during corrosion,an In-rich precipitate phase formed,hindering the ingress of the corrosive medium into the magnet.Consequently,this significantly bolstered the corrosion resistance of the sintered NdFeB magnets.The phase formation,magnetic properties and corrosion resistance of In-doped NdFeB magnets are detailed in this work,which provides new prospects for the preparation of high-performance sintered NdFeB magnets.
基金National Natural Science Foundation of China (52072088, 52072089)Natural Science Foundation of Heilongjiang Province (LH2023E061)+1 种基金Scientific and Technological Innovation Leading Talent of Harbin Manufacturing (2022CXRCCG001)Fundamental Research Funds for the Central Universities (3072023CFJ1003)。
文摘Hexagonal boron nitride(h-BN)ceramics have become exceptional materials for heat-resistant components in hypersonic vehicles,owing to their superior thermal stability and excellent dielectric properties.However,their densification during sintering still poses challenges for researchers,and their mechanical properties are rather unsatisfactory.In this study,SrAl_(2)Si_(2)O_(8)(SAS),with low melting point and high strength,was introduced into the h-BN ceramics to facilitate the sintering and reinforce the strength and toughness.Then,BN-SAS ceramic composites were fabricated via hot press sintering using h-BN,SrCO_(3),Al_(2)O_(3),and SiO_(2) as raw materials,and effects of sintering pressure on their microstructure,mechanical property,and thermal property were investigated.The thermal shock resistance of BN-SAS ceramic composites was evaluated.Results show that phases of as-preparedBN-SAS ceramic composites are h-BN and h-SrAl_(2)Si_(2)O_(8).With the increase of sintering pressure,the composites’densities increase,and the mechanical properties shew a rising trend followed by a slight decline.At a sintering pressure of 20 MPa,their bending strength and fracture toughness are(138±4)MPa and(1.84±0.05)MPa·m^(1/2),respectively.Composites sintered at 10 MPa exhibit a low coefficient of thermal expansion,with an average of 2.96×10^(-6) K^(-1) in the temperature range from 200 to 1200℃.The BN-SAS ceramic composites prepared at 20 MPa display higher thermal conductivity from 12.42 to 28.42 W·m^(-1)·K^(-1) within the temperature range from room temperature to 1000℃.Notably,BN-SAS composites exhibit remarkable thermal shock resistance,with residual bending strength peaking and subsequently declining sharply under a thermal shock temperature difference ranging from 600 to 1400℃.The maximum residual bending strength is recorded at a temperature difference of 800℃,with a residual strength retention rate of 101%.As the thermal shock temperature difference increase,the degree of oxidation on the ceramic surface and cracks due to thermal stress are also increased gradually.
基金Project(202302AB080024)supported by the Department of Science and Technology of Yunnan Province,China。
文摘The evolution of mechanical properties,localized corrosion resistance of a high purity Al-Zn-Mg-Cu alloy during non-isothermal aging(NIA)was investigated by hardness test,electrical conductivity test,tensile test,intergranular corrosion test,exfoliation corrosion test,slow strain rate tensile test and electrochemical test,and the mechanism has been discussed based on microstructure examination by optical microscopy,electron back scattered diffraction,scanning electron microscopy and scanning transmission electron microscopy.The NIA treatment includes a heating stage from 40℃to 180℃with a rate of 20℃/h and a cooling stage from 180℃to 40℃with a rate of 10℃/h.The results show that the hardness and strength increase rapidly during the heating stage of NIA since the increasing temperature favors the nucleation and the growth of strengthening precipitates and promotes the transformation of Guinier-Preston(GPI)zones toη'phase.During the cooling stage,the sizes ofη'phase increase with a little change in the number density,leading to a further slight increase of the hardness and strength.As NIA proceeds,the corroded morphology in the alloy changes from a layering feature to a wavy feature,the maximum corrosion depth decreases,and the reason has been analyzed based on the microstructural and microchemical feature of precipitates at grain boundaries and subgrain boundaries.
基金Project(20080440850) supported by China Postdoctoral Science FoundationProject(ZJY0605-02) supported by the Natural Science Foundation of Heilongjiang Province,ChinaProject(HIT.NSRIF.2012002) supported by the Fundamental Research Funds for the Central Universities,China
文摘In order to study the effect of element Nb on the microstructure and properties of the biomedical β-type Ti-Mo based alloys,Ti-15Mo-xNb(x=5,10,15 and 20 in %) alloys were investigated.The dry wear resistance of β-type Ti-15Mo-xNb alloys against Gr15 ball was investigated on CJS111A ball-disk wear instrument.Experimental results indicate that crystal structure and morphology of the Ti-15Mo-xNb alloys are sensitive to their Nb contents.Ti-15Mo-xNb alloys match those for β phase peaks and no any phases are found.The Vickers hardness values of all the Ti-15Mo-xNb alloys are higher than HV200.The compression yield strength of the Ti-15Mo-5Nb alloy is the lowest and that of the Ti-15Mo-10Nb alloy is the highest.For all the Ti-15Mo-xNb alloys,the friction coefficient is not constant but takes a higher value.In dry condition,SEM study reveals deep parallel scars on the wear surfaces of all the Ti-15Mo-xNb alloys under different loads.The friction coefficient of the Ti-15Mo-5Nb alloy under 1 N is the lowest.The wear principal mechanism for Ti-15Mo-xNb alloys is adhesive wear.
基金Project(2012CB619501)supported by the National Basic Research Program of China
文摘The effects of T916 thermo-mechanical process on microstructures, mechanical properties and ballistic resistance of 2519A aluminum alloy were investigated by optical microscopy (OM), transmission electron microscopy (TEM), tensile tests and ballistic resistance test. After T916 treatment, the yield strength, tensile strength and elongation rate of 2519A aluminum alloy reach 501 MPa, 540 MPa and 14%, respectively. And the ballistic limit velocity of 2519A-T916 alloy (30 mm in thickness) is 715 rn/s. The microstructure varies near the sidewalls of crater. The interrupted ageing contributes to these excellent properties of the alloy. During T916 process, the precipitation of Guinier Preston (GP) zone is finer and denser during the interrupted ageing, thus resulting in well precipitated strengthening phase.
基金Project(10KJB430012) supported by the Natural Science Foundation of the Jiangsu Higher Education Institutions of ChinaProject (BK2011063) supported by the Nantong Science and Technology Commission of China
文摘The microstructural characteristics, mechanical properties and creep resistance of Mg-(8%-12%) Zn-(2%-6%) A1 alloys were investigated to get a better overall understanding of these series alloys. The results indicate that the microstructure of the alloys ZA82, ZA102 and ZA122 with the mass ratio of Zn to A1 of 4-6 is mainly composed of a-Mg matrix and two different morphologies of precipitates (block τ-Mg32(Al, Zn)49 and dense lamellar ε-Mg51Zn20), the alloys ZA84, ZA104 and ZA124 with the mass ratio of 2-3 contain α-Mg matrix and only block r phases, and the alloys ZA86, ZA106 and ZA126 with the mass ratio of 1-2 consist of a-Mg matrix, block r precipitates, lamellar Ф-Al2Mg5Zn2 eutectics and flocculent β-Mg17Al12 compounds. The alloys studied with the mass ratio of Zn to A1 of 2-3 exhibit high creep resistance, and the alloy ZA124 with the continuous network of r precipitating along grain boundaries shows the highest creep resistance.
文摘Effects of alloying processing on tensile test properties of Fe 3Al based alloys have been studied. Results show that microalloying of cerium is very effective on increasing the room temperature ductility of Fe 3Al based alloys. Surface analysis by XPS demonstrates that cerium addition causes the change in the oxide chemistry and provides rapid passivation of the specimen surface. The high temperature strength and creep resistance of Fe 3Al based alloys can be significantly enhanced by alloying additions of tungsten, niobium or molybdenum, especially when combined additions of tungsten with niobium or molybdenum are used. The additions of tungsten, niobium or molybdenum also result in the significant microstructural refinement and the formation of fine precipitates which are identified as M 6C type carbide in the alloys containing tungsten.
基金financial support from the Ministry of Education and Science of the Russian Federation, Agreement No. 03.G25.31.0274 (27 May 2017)
文摘Zn is a commonly used alloying element for Mg alloys owing to its beneficial effects on mechanical properties. To improve the mechanical and corrosion properties of WE43B Mg alloys, the effects of 0–0.7wt% Zn addition on the microstructure and properties of sample alloys were investigated. Addition of Zn to as-cast WE43B alloy promoted the formation of the Mg12Nd phase;by contrast, after T6 heat treatment, the phase composition of WE43B alloys with and without Zn addition remained mostly the same. A long-period stacking ordered phase was predicted by CALPHAD calculation, but this phase was not observed in either the as-cast or heat-treated Zn-containing WE43B alloys. The optimum temperature and duration of T6 heat treatment were obtained using CALPHAD calculations and hardness measurements. Addition of Zn resulted in a slight reduction in the average grain size of the as-cast and T6 heat-treated WE43B alloys and endowed them with increased corrosion resistance with little effect on their mechanical properties.
基金financially supported by the Shanghai Materials Genome Institute No. 5 (No. 16DZ2260605)the Shanghai Sailing Program (No. 17YF1405400)the Project to Strengthen Industrial Development at the Grass-roots Level (No. TC160A310/19)
文摘The corrosion behavior and mechanical properties of 316 L stainless steel(SS) fabricated via selective laser melting(SLM) were clarified by potentiodynamic polarization measurements, immersion tests, and tensile experiments. The microstructural anisotropy of SLMed 316 L SS was also investigated by electron back-scattered diffraction and transmission electron microscopy. The grain sizes of the SLMed 316 L SS in the XOZ plane were smaller than those of the SLMed 316 L SS in the XOY plane, and a greater number of low-angle boundaries were present in the XOY plane, resulting in lower elongation for the XOY plane than for the XOZ plane. The SLMed 316 L was expected to exhibit higher strength but lower ductility than the wrought 316 L, which was attributed to the high density of dislocations. The pitting potentials of the SLMed 316 L samples were universally higher than those of the wrought sample in chloride solutions because of the annihilation of MnS or(Ca,Al)-oxides during the rapid solidification. However, the molten pool boundaries preferentially dissolved in aggressive solutions and the damage of the SLMed 316 L in FeCl3 solution was more serious after long-term service, indicating poor durability.
基金supported by the National Natural Science Foundation of China (Nos. 50771075 and 51171133) the Program for New Century Excellent Talents in University of Ministries of the Education of China (No.NECT-07-0650)
文摘Silver or copper ions are often chosen as antibacterial agents. But a few reports are concerned with these two antibacterial agents for preparation of antibacterial stainless steel (SS). The antibacterial properties and corrosion resistance of AISI 420 stainless steel implanted by silver and copper ions were investigated. Due to the cooperative antibacterial effect of silver and copper ions, the Ag/Cu implanted SS showed excellent antibacterial activities against both Gram-negative Escherichia coli (E. coli) and Gram-positive Staphylococcus aureus (S. aureus) at a total implantation dose of 2~ 1017 ions/cm2. Electrochemical polarization curves revealed that the corrosion resistance of Ag/Cu implanted SS was slightly enhanced as compared with that of un-implanted SS, The implanted layer was characterized by X-ray photoelec- tron spectroscopy (XPS). Core level XPS spectra indicate that the implanted silver and copper ions exist in metallic state in the implanted layer.
基金supported by the Science and Technology Department of Zhejiang Province(No.2006C11050)
文摘A series of stable waterborne polysiloxaneurethane (WPSUR) dispersions were prepared using amino-terminated polydimethylsiloxane (NS), dimethylolpropionic acid (DMPA), castor oil, polypropylene glycol and toluene diisocyanate. Meanwhile, NS with different molecular weights was synthesized and used as the soft co-segment. Effects of types and contents of soft co-segments as well as chain extenders on the thermal degradation and stability for WPSUR films were examined. Results reveal that WPSUR films exhibit excellent water resistance and mechanical properties as compared with pure polyurethane (PU) films, and the NS soft co-segment possesses a remarkable effect on the second stage (stage Ⅱ), while the content of the hard segment is propitious to the initial stage (stage Ⅰ). Moreover, the highest temperature of stage Ⅱ (T2m) for WPSUR films using NS as soft co-segment is 413℃, approximately being 30℃ higher than that of those typical PUs using HDA and APDMS as the chain extenders, respectively.
基金supported by the National Natural Science Foundation of China (Nos. 51172285, 51372277)the Fundamental Research Funds for the Central Universities (14CX02060A)the Natural Science Foundation of Shandong Province (ZR2011EL030)
文摘A bisphenol epoxy resin was used as modifier to increase the heat resistance of condensed poly-nuclear aromatic (COPNA) resin. The basic properties of COPNA resin and modified resin were characterized by Fourier transform infrared spectroscopy (FT-IR), nuclear magnetic resonance spectroscopy (1H-NMR), vapor pressure osmometry (VPO) and elemental analysis (EA). Average structural parameters of resins were calculated by the improved Brown-Ladner method, and heat resistance of resins was tested by thermogravimetric analysis (TGA). The chemical structure, mechanical properties and heat resistivity of the resin/graphite composites prepared with different resins were compared. The results show that the adhesive property and heat resistance of COPNA resin can be remarkably improved by addition of 5 wt.% epoxy resin. The reason is that the reactions between epoxy groups of epoxy resin and hydroxyl groups of COPNA resin improve the heat resistance and adhesive property of COPNA resin. Electric motor brushes with good mechanical properties and low electrical resistivity were successfully prepared by using the modified resin as binder.
基金kindly supported by the Russian Foundation for Basic Research (RFBR) (No. 16-05-00033A)
文摘Traditional methods of coal thermal resistance characterization are informative but considerably timeconsuming and require utilization of a complex and expensive equipment. This limits the effectiveness of their application. In this paper, authors experimentally investigated potential application of thermally stimulated acoustic emission method for developing of relatively simple and rapid coals thermal resistance assessment method. Features of thermally stimulated acoustic emission of anthracite, lignites and bituminous coal samples subject to cyclic thermal loading have been experimentally investigated.For the first time, it has been shown that there exists a relationship of such patterns with structural parameters and properties of the coal samples, as well as their thermal resistance. The results indicate the possibility of applying the method of thermally stimulated acoustic emission to control processes of cryogenic disintegration and thermal resistance of fossil coals. The description of the equipment and methodological support needed for the implementation of this method have been provided.
基金The authors would like to thank Iran National Science Foundation and the research board of Sharif University of Technology,Tehran,Iran,for the financial support and the provision of research facilities used in this work.
文摘During the recent years,some Mg based alloys have extensively been considered as a new generation of degradable and absorbable bio-medical materials.In this work,the Mg-2Zn-1Gd-1Ca(wt%)alloy as a new metallic bio-material was produced by the casting process followed by the heat treatment.The samples of the alloy were solution treated at temperatures of 500,550,and 600°C and then quench aged at temperatures of 125,150,and 175°C.The results of SEM-EDS examinations indicated that the alloy microstructure consists ofα-Mg matrix and the Ca_(2)Mg_(6)Zn_(3)and Mg_(3)Gd_(2)Zn_(3)secondary phases.With regard to the results of Vickers hardness test,the temperatures of 500°C and 150°C were selected as the optimum solutionizing and aging temperatures,respectively.Moreover,the dissolution of casting precipitates and production of lattice distortion occurring after the solution treatment led to the reduction in ultimate shear strength up to 21%.But,the precipitation hardening and morphological changes taking place during the aging treatment improved the ultimate shear strength up to 32%.Furthermore,the results of electro-chemical and weight-loss measurements in a simulated body fluid indicated that the heat-treated alloy is a promising candidate for the Mg based alloys recently considered for the bio-medical applications.
基金Project(20921002)supported by the Innovative Research Groups of the National Natural Science Foundation of ChinaProject(21221061)supported by the National Natural Science Foundation of China+1 种基金Project(201105007)supported by the Science and Technology Program of Jilin Province,ChinaProject(20140325003GX)supported by the Science and Technology Support Project of Jilin Province,China
文摘Mg?1Zn?0.5Ca alloys were prepared by traditional steel mould casting and water-cooled copper mould injection casting at higher cooling rate. Microstructure, mechanical properties and bio-corrosion resistance of two alloys were contrastively investigated. Grain size reduces remarkably and microstructure becomes homogenous when raising cooling rate. The bio-corrosion behaviour in 3.5% sodium chloride solution (3.5% NaCl) and Hank’s solution at 37°C was investigated using electrochemical polarization measurement and the results indicate that the alloy prepared at higher cooling rates has better corrosion resistance in both types of solution. Further mass loss immersion test in Hank’s solution reveals the same result. The reason of corrosion resistance improvement is that raising cooling rate brings about homogeneous microstructure, which leads to micro-galvanic corrosion alleviation. The tensile test results show that yield strength, ultimate tensile strength and elongation are improved by raising cooling rate and the improvement is mainly due to grain refinement.
文摘To improve the mechanical properties and wear resistance of ZA27 alloy, Si was introduced to the alloy, and the effect of Si alloying and T6 heat treatment on the microstructure, mechanical properties and wear resistance was investigated. The results show that with 0.55% Si, the microstructure of the alloy can be refined effectively, which leads to the increase of hardness. But the tensile strength and elongation decrease because Si undermines the integrity of the matrix. On the other hand, the dendrites are transformed into a desired α+η+(α+η)mixture with T6 heat treatment, which introduces a remarkable increase to the elongation and hardness of the alloy. The wear resistance of the ZA27 alloy with Si alloying is significantly better than that of the ZA27 alloy without Si. With the increase of Si addition, the wear resistance of the alloy firstly increases and then decreases.In the alloy without Si alloying, severe plastic deformation and large delamination were observed on the worn surface of the alloy. However, with the increase of Si, the main wear mechanism transformed to abrasive wear gradually. In addition, the T6 treatment can further improve the wear resistance of the alloy with Si alloying.
文摘In this work the microstructure, mechanical properties and wear resistance of Fe-Al based alloys with various alloying elements were studied. The microstructures were examined by optical and scanning electron microscopy (SEM) equipped with an energy dispersive X-ray spectroscope (EDS). Two types of alloys were prepared by vacuum arc melting. One is Fe-28Al based alloys (D03 structured) with and without alloying elements such as Mo and Zr. The other one is Fe-35Al based alloys (B2 structured) produced with the same manner. For both types of alloys, Mo addition had found to exhibit an equiaxed microstructure, while dendritic structure was observed to show the effect of Zr addition. These microstructural features were more evinced with increasing content of alloying element. Concerning the mechanical properties and wear resistance, Fe-35Al based alloys were superior to Fe-28Al based alloys over the whole temperature range investigated.
基金funded by the National Natural Science Foundation of China(No.50571073)the Ph.D.Programs Foundation of the Ministry of Education of China(20111402110004)the Natural Science Foundation of Shanxi Province(Nos.2009011028-3 and 2012011022-1)
文摘In this study, Ce was introduced into the AZ80 alloy and the effects of Ce addition on the microstructure, mechanical properties and corrosion resistance of the as-cast AZ80 magnesium alloy were investigated. The results show that the addition of Ce into the AZ80 alloy can not only refine the microstructure, but also result in the formation of the needle-like Al4Ce phase. These tiny Al4Ce phases are homogeneously distributed at grain boundaries and within grains. An appropriate Ce addition can also change the β-Mg17Al12 phase at the grain boundaries from continuous network to small island-like. At the same time, with the increase of Ce content from 0 to 2.0wt.%, the macro-hardness of the as-cast alloy is enhanced linearly, while impact toughness, tensile strength and elongation all firstly increase and then decrease. The AZ80 alloy containing 1.0wt.% Ce exhibits the optimal properties. Its macro-hardness, impact toughness, tensile strength and elongation are 61.90 HB, 15.50 J·cm-2, 171.80 MPa and 3.35%, increase by 9.95%, 63%, 13.3% and 36.7%, respectively compared with the base alloy. In addition, Ce can enhance the corrosion resistance of the AZ80 magnesium alloy.
基金Supported by the Research Institute,Baoshan Iron&Steel Co.,Ltd
文摘The characteristics of microstructure, mechanical property and corrosion behavior of Cr26Mo3.5 super stainless steel joints by pulse tungsten inert gas(P-TIG)welding and laser welding were investigated. The results indicate that the widths of the center equiaxed grain zone(EGZ)and the columnar grain zone(CGZ)increase with the increase of heat input in both welding processes. The precipitates of Nb and Ti carbides and nitrides are formed in the weld metal(WM)and the heat affected zone(HAZ). The joints by laser welding show better tensile and corrosion resistance properties than those by P-TIG welding due to the heat concentration and lower heat input. The tensile strength and elongation increase with the decrease of heat input, and the fracture mode of the joints turns into ductile-brittle mixed fracture from ductile fracture when the welding method turns into P-TIG welding from laser welding. Moreover, the corrosion resistance of all joints declines slightly with the increase of heat input. Hence, laser welding is more suitable for welding Cr26Mo3.5 super stainless steel in engineering applications.
基金financially supported by the National Natural Science Foundation of China(51665012)the Jiangxi province Science Foundation for Outstanding Scholarship(20171BCB23061,2018ACB21020)
文摘In this present work, Pb was applied in the Mg97Zn1Y2 alloy to improve its microstructure and properties, using conventional casting methods. The microstructure and properties of the Mg97 Zn1 Y2 alloy and Mg97Zn1Y2-x Pb(x=0.6 wt.%, 1.2 wt.% and 1.8 wt.%) alloys were observed by optical microscopy, scanning electron microscopy method and analyzed by X-ray diffraction, hardness and strength measurement and electrochemical testing. After adding Pb to the Mg97Zn1Y2 alloy, a new particle phase Mg_2 Pb was identified along the grain boundaries, and dendrites were refined. In addtion, the hardness of Mg97Zn1Y2-xPb(x=0.6 wt.%, 1.2 wt.% and 1.8 wt.%) alloys was higher than that of the Mg97 Zn1Y2 alloy; with the increase of Pb content, the hardness of the alloy increased first and then decreased, followed by a final slight increase, and reached a maximum of 89.1 HV when the Pb content was 0.6 wt.%. The strength of the alloy increased first and then decreased as the Pb content increased. Moreover, adding a small amount of Pb to the alloy can effectively inhibit corrosion, and Mg97Zn1Y2-0.6 wt.%Pb exhibits the best corrosion resistance ability.