Carbon nanotubes-Nafion （CNTs-Nation） composites were prepared by impregnated CNTs with Nation in ethanol solution and characterized by FT-IR. Pt-Ru catalysts supported on CNTs-Nafion composites were synthesized by ...Carbon nanotubes-Nafion （CNTs-Nation） composites were prepared by impregnated CNTs with Nation in ethanol solution and characterized by FT-IR. Pt-Ru catalysts supported on CNTs-Nafion composites were synthesized by microwave-assisted polyol process. The physical and electrochemical properties of the catalysts were characterized by X-ray diffraction （XRD）, transmission electron microscope （TEM）, CO stripping voltammetry, cyclic voltammetry （CV） and chronoamperometry （CA）. The results showed that the Nation incorporation in CNTs-Nation composites did not significantly alter the oxygen-containing groups on the CNTs surface. The Pt-Ru catalyst supported on CNTs-Nafion composites with 2 wt% Naton showed good dispersion and the best CO oxidation and methanol electro-oxidation activities.展开更多
Nafion-stabilized Pt nanoparticle colloidal solution is synthesized through ethylene glycol reduction.Pt/Nafion added with carbon black as electric conduction material（labeled Pt/Nafion-XC72） shows excellent electro...Nafion-stabilized Pt nanoparticle colloidal solution is synthesized through ethylene glycol reduction.Pt/Nafion added with carbon black as electric conduction material（labeled Pt/Nafion-XC72） shows excellent electrochemical property compared with Pt/C.After a 300-cycle discharging durability test,the cell performance of membrane electrode assembly（MEA） with the Pt/Nafion-XC72 and Pt/C catalysts indicates a 29.9% and 92.2% decrease,respectively.The charge transfer resistances of Pt/Nafion-XC72 and Pt/C increase by 27.2% and 101.9%,respectively.The remaining electrochemically active surface area of Pt is about 61.7% in Pt/Nafion-XC72 and about 38.1% in Pt/C after the durability test.The particle size of Pt/C increases from about 5.1 nm to about 10.8 nm but only from 3.6 nm to 5.8 nm in the case of Pt/Nafion-XC72.These data suggest that Pt/Nafion-XC72 as a catalyst can enhance the durability of PEMFCs compared with Pt/C.展开更多
Pt?Au-SPE electrodes made by the successive chemical deposition of Au and Pt on Nafion membranes were tested and compared with the single metal-SPE electrodes for surface oxidation, CO adsorption and oxidation. Part o...Pt?Au-SPE electrodes made by the successive chemical deposition of Au and Pt on Nafion membranes were tested and compared with the single metal-SPE electrodes for surface oxidation, CO adsorption and oxidation. Part of the surface of the binary metal electrodes behaves differently from either Au or Pt single metal-SPE electrode for COads oxidation, revealing surface modulation effects in the binary metal electrode. However, these mudulated surfaces have no appreciable contribution to the electrode activity for CO oxidation. The electrode activity for CO oxidation is mainly governed by the total Pt surface area of the binary electrodes. The predeposited Au was found to be favorable for higher dispersion of the successively deposited Pt.展开更多
基金supported by National Natural Science Foundation of China (NO.0576023)Key Project of Science and Technology Department of Guangdong Province (NO.2008B010800036 NO.2008B010800037)
文摘Carbon nanotubes-Nafion （CNTs-Nation） composites were prepared by impregnated CNTs with Nation in ethanol solution and characterized by FT-IR. Pt-Ru catalysts supported on CNTs-Nafion composites were synthesized by microwave-assisted polyol process. The physical and electrochemical properties of the catalysts were characterized by X-ray diffraction （XRD）, transmission electron microscope （TEM）, CO stripping voltammetry, cyclic voltammetry （CV） and chronoamperometry （CA）. The results showed that the Nation incorporation in CNTs-Nation composites did not significantly alter the oxygen-containing groups on the CNTs surface. The Pt-Ru catalyst supported on CNTs-Nafion composites with 2 wt% Naton showed good dispersion and the best CO oxidation and methanol electro-oxidation activities.
基金supported by the National Basic Research Program of China(973 Program,Grant No.2012CB215500the National High-Tech Research and Development Program of China(863 Plan)(No.2012AA052002)the National Natural Science Foundation of China(No.21406024)
文摘Nafion-stabilized Pt nanoparticle colloidal solution is synthesized through ethylene glycol reduction.Pt/Nafion added with carbon black as electric conduction material（labeled Pt/Nafion-XC72） shows excellent electrochemical property compared with Pt/C.After a 300-cycle discharging durability test,the cell performance of membrane electrode assembly（MEA） with the Pt/Nafion-XC72 and Pt/C catalysts indicates a 29.9% and 92.2% decrease,respectively.The charge transfer resistances of Pt/Nafion-XC72 and Pt/C increase by 27.2% and 101.9%,respectively.The remaining electrochemically active surface area of Pt is about 61.7% in Pt/Nafion-XC72 and about 38.1% in Pt/C after the durability test.The particle size of Pt/C increases from about 5.1 nm to about 10.8 nm but only from 3.6 nm to 5.8 nm in the case of Pt/Nafion-XC72.These data suggest that Pt/Nafion-XC72 as a catalyst can enhance the durability of PEMFCs compared with Pt/C.
文摘Pt?Au-SPE electrodes made by the successive chemical deposition of Au and Pt on Nafion membranes were tested and compared with the single metal-SPE electrodes for surface oxidation, CO adsorption and oxidation. Part of the surface of the binary metal electrodes behaves differently from either Au or Pt single metal-SPE electrode for COads oxidation, revealing surface modulation effects in the binary metal electrode. However, these mudulated surfaces have no appreciable contribution to the electrode activity for CO oxidation. The electrode activity for CO oxidation is mainly governed by the total Pt surface area of the binary electrodes. The predeposited Au was found to be favorable for higher dispersion of the successively deposited Pt.