Petroleum-based materials,such as plastic,are characterized by adverse environmental pollution;as a result,researchers have sought alternative degradable plastics that are environmentally friendly,such as polylactic a...Petroleum-based materials,such as plastic,are characterized by adverse environmental pollution;as a result,researchers have sought alternative degradable plastics that are environmentally friendly,such as polylactic acid(PLA).PLA has shown great potential to replace petroleum-based plastics.In this study,seven different samples of unmodified Pueraria lobata root powder(PRP)with different contents(i.e.,0,5,10,15,20,25,and 30 wt%)and three different modified PRPs(i.e.,treated with NaOH,NaOH-KH-550,and Formic)were used to reinforce polylactic acid(PLA)via solution casting process.These prepared PRP/PLA composite films were characterized using SEM,FTIR,UV-visible spectra analysis,TG,DSC,weight loss measurement(wt%),and mechanical measurements.The results showed that the PRP modified with KH-550(PRPK)intensified the interaction in the interface region between the PRP and the PLA matrix,thus increasing the tensile strength(54.5 MPa),elongation at break(2.8%),and Young’s modulus(3310 MPa)of the PRPK/PLA biofilms.Contact angle measurement showed that the PRP treatments contributed to the hydrophobicity of films.The transparency of PRP-10/PLA film atλ_(800)was 11.09%,and its UVA and UVB transmittance were 3.28 and 1.16,respectively.After blending PLA with PRP,the PRP/PLA composite films exhibited excellent biodegradability.In summary,PRPK improved the mechanical properties of PLA and prevented the films from ultraviolet light,suggesting that PRPK-5/PLA film could be used as packaging materials.展开更多
基金This research was funded by the Xiaohe Talent Project of Zhangjiajie City(No.2022xhrc01)the Research Foundation of Hunan Provincial Education Department(Nos.20A412+1 种基金19C1541)the Natural Science Research Project of Jishou University(No.Jd19005).
文摘Petroleum-based materials,such as plastic,are characterized by adverse environmental pollution;as a result,researchers have sought alternative degradable plastics that are environmentally friendly,such as polylactic acid(PLA).PLA has shown great potential to replace petroleum-based plastics.In this study,seven different samples of unmodified Pueraria lobata root powder(PRP)with different contents(i.e.,0,5,10,15,20,25,and 30 wt%)and three different modified PRPs(i.e.,treated with NaOH,NaOH-KH-550,and Formic)were used to reinforce polylactic acid(PLA)via solution casting process.These prepared PRP/PLA composite films were characterized using SEM,FTIR,UV-visible spectra analysis,TG,DSC,weight loss measurement(wt%),and mechanical measurements.The results showed that the PRP modified with KH-550(PRPK)intensified the interaction in the interface region between the PRP and the PLA matrix,thus increasing the tensile strength(54.5 MPa),elongation at break(2.8%),and Young’s modulus(3310 MPa)of the PRPK/PLA biofilms.Contact angle measurement showed that the PRP treatments contributed to the hydrophobicity of films.The transparency of PRP-10/PLA film atλ_(800)was 11.09%,and its UVA and UVB transmittance were 3.28 and 1.16,respectively.After blending PLA with PRP,the PRP/PLA composite films exhibited excellent biodegradability.In summary,PRPK improved the mechanical properties of PLA and prevented the films from ultraviolet light,suggesting that PRPK-5/PLA film could be used as packaging materials.
