The grain refinement and macrosegregation control of GCrl5 bearing steel were investigated under a type of rarely-used electromagnetic stirring, vertical electromagnetic stirring （V-EMS）, in continuous casting. V-EM...The grain refinement and macrosegregation control of GCrl5 bearing steel were investigated under a type of rarely-used electromagnetic stirring, vertical electromagnetic stirring （V-EMS）, in continuous casting. V-EMS can create an upward electromagnetic force and generate longitudinal loop convection, which ena- bles the better mixing of the upper part with the lower part of the liquid steel. The results showed that ap- plying V-EMS can enlarge the region of the equiaxed grain, decrease the secondary dendrite arm spacing （SDAS） and reduce the segregation of both carbon and sulfur. After applying V-EMS, liquid steel with a high solute concentration is brought to the dendrite tips, making the dendrite arms partially melt. The length of the dendrite fragment is approximately 1.8 mm, 10 to 12 times the SDAS. Upon increasing the amount of cooling water from 2.0 to 3.5 m3/h, the dendrite fragments exhibit an obvious aggregation fol- lowing V-EMS. Finally, a criterion for dendrite fragmentation under V-EMS was derived based on the dendrite fragmentation theory of Campanella et al.展开更多
A volume averaged columnar solidification model,which couples the flow,temperature and solute concentration fields,is applied to simulate experimental continuous casting cases with and without vertical electromagnetic...A volume averaged columnar solidification model,which couples the flow,temperature and solute concentration fields,is applied to simulate experimental continuous casting cases with and without vertical electromagnetic stirring(V-EMS).The calculated distribution of magnetic induction intensity and final macrosegregation maps are consistent with the experimental results.Calculation results reveal that the V-EMS promotes longitudinal melt flow,accelerates heat dissipation and solidification and finally reduces the central segregation of carbon.However,when V-EMS is applied,the solute distribution becomes asymmetric because the melt flow shows opposite directions between the near and far sides from stirrer.An obvious positive segregation band is observed at about 1/4 width of the billet near the stirrer in both calculated and experimental results.The position and degree of such positive segregation could be affected by installation height of stirrer,as demonstrated by additional simulation cases.展开更多
A three-dimensional mathematical model was established to investigate the behavior of molten steel flow and steel/slag interface with different processes and electromagnetic parameters under two different static magne...A three-dimensional mathematical model was established to investigate the behavior of molten steel flow and steel/slag interface with different processes and electromagnetic parameters under two different static magnetic field configurations [ruler-type electromagnetic brake （EMBr ruler） and vertical electromagnetic brake （V-EMBr）] in a continuous casting mold. The results showed that the brake effect of EMBr ruler is significantly influenced by its configuration parameters, the distance between the pole and bottom of the submerged entry nozzle （SEN）, and the port angle of the SEN outlet; therefore, it is not helpful to depress the diffusion of jet flow along the thickness direction of mold. For a constant SEN depth and port angle, there is a reasonable pole position （P = 0 mm） where the pole simultaneously covers three key zones, i.e., the jet flow impact zone and the upward and downward backflow zones. For V-EMBr, the magnetic field can simultaneously cover the three key zones and depress the diffusion of jet flow along the casting and thickness directions of the mold. Both the meniscus height and the impact intensity of the jet flow can be obviously depressed by V-EMBr even if the SEN depth and port angle have changed in the continuous casting process.展开更多
基金supported by the National Natural Science Foundation of China(No.50834009)the Key Project of the Ministry of Education of China(No.311014)the 111 Project of China(No.B07015)
文摘The grain refinement and macrosegregation control of GCrl5 bearing steel were investigated under a type of rarely-used electromagnetic stirring, vertical electromagnetic stirring （V-EMS）, in continuous casting. V-EMS can create an upward electromagnetic force and generate longitudinal loop convection, which ena- bles the better mixing of the upper part with the lower part of the liquid steel. The results showed that ap- plying V-EMS can enlarge the region of the equiaxed grain, decrease the secondary dendrite arm spacing （SDAS） and reduce the segregation of both carbon and sulfur. After applying V-EMS, liquid steel with a high solute concentration is brought to the dendrite tips, making the dendrite arms partially melt. The length of the dendrite fragment is approximately 1.8 mm, 10 to 12 times the SDAS. Upon increasing the amount of cooling water from 2.0 to 3.5 m3/h, the dendrite fragments exhibit an obvious aggregation fol- lowing V-EMS. Finally, a criterion for dendrite fragmentation under V-EMS was derived based on the dendrite fragmentation theory of Campanella et al.
基金financial support from the National Natural Science Foundation of China(Grant No.U1760206)the National Key R&D Program of China(Grant No.2017YFE0107900)+1 种基金the 111 Project 2.0 of China(Grant No.BP0719037)the financial support provided by the ESA-MAP MICAST project contract 14347/01/NL/SH.
文摘A volume averaged columnar solidification model,which couples the flow,temperature and solute concentration fields,is applied to simulate experimental continuous casting cases with and without vertical electromagnetic stirring(V-EMS).The calculated distribution of magnetic induction intensity and final macrosegregation maps are consistent with the experimental results.Calculation results reveal that the V-EMS promotes longitudinal melt flow,accelerates heat dissipation and solidification and finally reduces the central segregation of carbon.However,when V-EMS is applied,the solute distribution becomes asymmetric because the melt flow shows opposite directions between the near and far sides from stirrer.An obvious positive segregation band is observed at about 1/4 width of the billet near the stirrer in both calculated and experimental results.The position and degree of such positive segregation could be affected by installation height of stirrer,as demonstrated by additional simulation cases.
基金This work was financially supported by the National Natural Science Foundation of China （No. 51574083） and the Program of Introducing Talents of Discipline to Universities （The 111 Project of China, No. B07015）. The authors would also like to thank the referees for their work which has contributed to this paper.
文摘A three-dimensional mathematical model was established to investigate the behavior of molten steel flow and steel/slag interface with different processes and electromagnetic parameters under two different static magnetic field configurations [ruler-type electromagnetic brake （EMBr ruler） and vertical electromagnetic brake （V-EMBr）] in a continuous casting mold. The results showed that the brake effect of EMBr ruler is significantly influenced by its configuration parameters, the distance between the pole and bottom of the submerged entry nozzle （SEN）, and the port angle of the SEN outlet; therefore, it is not helpful to depress the diffusion of jet flow along the thickness direction of mold. For a constant SEN depth and port angle, there is a reasonable pole position （P = 0 mm） where the pole simultaneously covers three key zones, i.e., the jet flow impact zone and the upward and downward backflow zones. For V-EMBr, the magnetic field can simultaneously cover the three key zones and depress the diffusion of jet flow along the casting and thickness directions of the mold. Both the meniscus height and the impact intensity of the jet flow can be obviously depressed by V-EMBr even if the SEN depth and port angle have changed in the continuous casting process.