The tenacity of heat-affected zone （HAZ） will decline and the size of grains will increase, because of the overheating on HAZ when submerged are welding （SAW） is ased to thick plate with high heat input. The shapi...The tenacity of heat-affected zone （HAZ） will decline and the size of grains will increase, because of the overheating on HAZ when submerged are welding （SAW） is ased to thick plate with high heat input. The shaping will worsen when SAW is used to thin plate with high current at high speed. A new SAW technology, the pulsed direct current （DC） automatic SAW, will be put forward in this paper in order to overcome the above shortcomings. And a pulsed controller with micro-controller unit （MCU） as the core, nixie tube （NT） and keyboard as the man-machine conversation interface is developed. The main functions of the pulsed controller include the output of pulsed welding current and the working with twinwire. The research has widely prospects in application with significant meanings in theory and practical engineering.展开更多
Nickel alloys had gathered wide acceptance in the fabrication of components which require high temperature resistance and corrosion resistance, such as metallic bellows used in expansion joints used in aircraft, aeros...Nickel alloys had gathered wide acceptance in the fabrication of components which require high temperature resistance and corrosion resistance, such as metallic bellows used in expansion joints used in aircraft, aerospace and petroleum industry. Micro Plasma Arc Welding (MPAW) is one of the important arc welding processes commonly using in fabric- cation of Nickel alloys. In the present paper welding of Inconel 625 sheets using pulsed current micro plasma arc weld- ing was discussed. The paper mainly focuses on studying the weld quality characteristics like weld pool geometry pa- rameters, microstructure, grain size, hardness and tensile properties of Pulsed Current Micro Plasma Arc Welded In- conel 625 sheets at different welding speeds. Results reveals that at a welding speed of 260 mm/minute better weld quality characteristics can be obtained.展开更多
The interfacial reaction control of SiC_p/2124Al composites was investigated during pulsed argon arc welding. Meanwhile, the mechanical properties, the metallographic structure and interfacial microstructure of the in...The interfacial reaction control of SiC_p/2124Al composites was investigated during pulsed argon arc welding. Meanwhile, the mechanical properties, the metallographic structure and interfacial microstructure of the induced welding joint were tested and detected, respectively. The results reveal that the joint with excellent properties could be achieved by the proper selection of the special filling material and the addition of the pulse during welding. Moreover, the formation mechanism of the welding joint was discussed and the corresponding measures on further improving the quality of the welding joint of SiC_p/2124Al composites were put forward in the condition of pulsed argon arc welding.展开更多
Temperature distribution and weld bead profiles of constant current and pulsed current gas tungsten arc welded aluminium alloy joints were compared. The effects of pulsed current welding on tensile properties, hardnes...Temperature distribution and weld bead profiles of constant current and pulsed current gas tungsten arc welded aluminium alloy joints were compared. The effects of pulsed current welding on tensile properties, hardness profiles, microstructural features and residual stress distribution of aluminium alloy joints were reported. The use of pulsed current technique is found to improve the tensile properties of the weld compared with continuous current welding due to grain refinement occurring in the fusion zone.展开更多
Fused ternary CaF_(2)–SiO_(2)–MnO fluxes have been manufactured and applied to join EH36 shipbuilding steel under high heat input submerged arc welding.Five fluxes have been designed to clarify the effect of MnO con...Fused ternary CaF_(2)–SiO_(2)–MnO fluxes have been manufactured and applied to join EH36 shipbuilding steel under high heat input submerged arc welding.Five fluxes have been designed to clarify the effect of MnO content in CaF_(2)–SiO_(2)–MnO flux on the impact toughness of the weld metal,with the added amount of MnO from 10 to 50 wt.%at the expense of CaF_(2).With the increase in MnO content,the Charpy impact energy increases first and then decreases,experiencing a maximum value at 30 wt.%MnO.Microstructure of the weld metals has also been studied to account for impact toughness variations.It has been demonstrated that the highest acicular ferrite volume fraction in the weld metal is achieved at 30 wt.%MnO,which is concurrent to the maximum value of Charpy impact energy.It is believed that the Mn and O content variations in the weld metal contribute synergistically to such an interesting phenomenon.展开更多
Submerged arc welding （SAW） has shortcoming of over heat input, which increases grain size in heat-affected zone （ HAZ） and decreases welding quality and mechanical properties of the joints serioasly. With improve...Submerged arc welding （SAW） has shortcoming of over heat input, which increases grain size in heat-affected zone （ HAZ） and decreases welding quality and mechanical properties of the joints serioasly. With improvements of welding equipment, direct current （ DC） pulsed SAW （ PSAW） was utilized successfully in the research. Comparing DC PSAW with DC common SAW （ CSAW） , the metallographic structure was analyzed with optical and electron microscope, the width of HAZ was measured as well as the width and hardness of the coarse grained HAZ （CGHAZ）. The research shows that DC PSAW joint had higher welding penetration, narrower HAZ and CGHAZ, which benefited HAZ performance and welding quality.展开更多
The effects of alloying elements in welding wires and submerged arc welding process on the microstructures and low-temperature impact toughness of weld metals have been investigated. The results indicate that the opti...The effects of alloying elements in welding wires and submerged arc welding process on the microstructures and low-temperature impact toughness of weld metals have been investigated. The results indicate that the optimal contents of alloying elements in welding wires can improve the low-temperature impact toughness of weld metals because the proeutectoid ferrite and bainite formations can be suppressed, and the fraction of acicular ferrite increases. However, the contents of alloying elements need to vary along with the welding heat input. With the increase in welding heat input, the contents of alloying elements in welding wires need to be increased accordingly. The microstructures mainly consisting of acicular ferrite can be obtained in weld metals after four-wire submerged arc welding using the wires with a low carbon content and appropriate contents of Mn, Mo, Ti-B, Cu, Ni, and RE, resulting in the high low-temperature impact toughness of weld metals.展开更多
SAW308L submerged arc welding wire and SJ601A submerged arc welding flux were selected to weld the 12 mm 08Cr19MnNi3Cu2N low nickel and high nitrogen austenitic stainless steel plates with three different welding heat...SAW308L submerged arc welding wire and SJ601A submerged arc welding flux were selected to weld the 12 mm 08Cr19MnNi3Cu2N low nickel and high nitrogen austenitic stainless steel plates with three different welding heat input,and microstructure,tensile properties,microhardness and corrosion properties of the welded joints were studied.The results show that no defects are found in the three groups of welded joints,and the welded joints have better performance.The tensile strength of 08Cr19MnNi3Cu2N stainless steel welded joints with different heat input is slightly lower than that of the base metal,and fracture occurs in the weld zone,and the hardness of the weld zone is lower than that of the base metal.The weld microstructure of stainless steel welded joints with different heat input is composed of austenite+δferrite,and ferrite is uniformly distributed in austenite.With the increase of the welding heat input,the ferrite content in the weld zone decrease gradually,the grain size in the thermal affected zone increase gradually,and the impact toughness reduce.展开更多
The present study is concerned with the effect of filler metals such as austenitic stainless steel, ferritic stainless steel and duplex stainless steel on tensile and impact properties of the ferritic stainless steel ...The present study is concerned with the effect of filler metals such as austenitic stainless steel, ferritic stainless steel and duplex stainless steel on tensile and impact properties of the ferritic stainless steel conforming to AISI 409M grade. Rolled plates of 4 mm thickness were used as the base material for preparing single pass butt welded joints. Tensile and impact properties, microhardness, microstructure and fracture surface morphology of the joints fabricated by austenitic stainless steel, ferritic stainless steel and duplex stainless steel filler metals were evaluated and the results were reported. From this investigation, it is found that the joints fabricated by duplex stainless steel filler metal showed higher tensile strength and hardness compared to the joints fabricated by austenitic and ferritic stainless steel filler metals. Joints fabricated by austenitic stainless steel filler metal exhibited higher ductility and impact toughness compared with the joints fabricated by ferritic stainless steel and duplex stainless steel filler metals.展开更多
The effect of autogeneous arc welding processes on tensile and impact properties of ferritic stainless steel conformed to AISI 409M grade is studied. Rolled plates of 4 mm thickness have been used as the base material...The effect of autogeneous arc welding processes on tensile and impact properties of ferritic stainless steel conformed to AISI 409M grade is studied. Rolled plates of 4 mm thickness have been used as the base material for preparing single pass butt welded joints. Tensile and impact properties, microhardness, microstructure, and fracture surface morphology of continuous current gas tungsten arc welding （CCGTAW）, pulsed current gas tungsten arc welding （PCGTAW）, and plasma arc welding （PAW） joints are evaluated and the results are compared. It is found that the PAW joints of ferritic stainless steel show superior tensile and impact properties when compared with CCG-TAW and PCGTAW joints, and this is mainly due to lower heat input, finer fusion zone grain diameter, and higher fusion zone hardness.展开更多
Naval grade high strength low alloy(HSLA) steels can be easily welded by all types of fusion welding processes. However, fusion welding of these steels leads to the problems such as cold cracking, residual stress, dis...Naval grade high strength low alloy(HSLA) steels can be easily welded by all types of fusion welding processes. However, fusion welding of these steels leads to the problems such as cold cracking, residual stress, distortion and fatigue damage. These problems can be eliminated by solid state welding process such as friction stir welding(FSW). In this investigation, a comparative evaluation of mechanical(tensile, impact,hardness) properties and microstructural features of shielded metal arc(SMA), gas metal arc(GMA) and friction stir welded(FSW) naval grade HSLA steel joints was carried out. It was found that the use of FSW process eliminated the problems related to fusion welding processes and also resulted in the superior mechanical properties compared to GMA and SMA welded joints.展开更多
文摘The tenacity of heat-affected zone （HAZ） will decline and the size of grains will increase, because of the overheating on HAZ when submerged are welding （SAW） is ased to thick plate with high heat input. The shaping will worsen when SAW is used to thin plate with high current at high speed. A new SAW technology, the pulsed direct current （DC） automatic SAW, will be put forward in this paper in order to overcome the above shortcomings. And a pulsed controller with micro-controller unit （MCU） as the core, nixie tube （NT） and keyboard as the man-machine conversation interface is developed. The main functions of the pulsed controller include the output of pulsed welding current and the working with twinwire. The research has widely prospects in application with significant meanings in theory and practical engineering.
文摘Nickel alloys had gathered wide acceptance in the fabrication of components which require high temperature resistance and corrosion resistance, such as metallic bellows used in expansion joints used in aircraft, aerospace and petroleum industry. Micro Plasma Arc Welding (MPAW) is one of the important arc welding processes commonly using in fabric- cation of Nickel alloys. In the present paper welding of Inconel 625 sheets using pulsed current micro plasma arc weld- ing was discussed. The paper mainly focuses on studying the weld quality characteristics like weld pool geometry pa- rameters, microstructure, grain size, hardness and tensile properties of Pulsed Current Micro Plasma Arc Welded In- conel 625 sheets at different welding speeds. Results reveals that at a welding speed of 260 mm/minute better weld quality characteristics can be obtained.
文摘The interfacial reaction control of SiC_p/2124Al composites was investigated during pulsed argon arc welding. Meanwhile, the mechanical properties, the metallographic structure and interfacial microstructure of the induced welding joint were tested and detected, respectively. The results reveal that the joint with excellent properties could be achieved by the proper selection of the special filling material and the addition of the pulse during welding. Moreover, the formation mechanism of the welding joint was discussed and the corresponding measures on further improving the quality of the welding joint of SiC_p/2124Al composites were put forward in the condition of pulsed argon arc welding.
文摘Temperature distribution and weld bead profiles of constant current and pulsed current gas tungsten arc welded aluminium alloy joints were compared. The effects of pulsed current welding on tensile properties, hardness profiles, microstructural features and residual stress distribution of aluminium alloy joints were reported. The use of pulsed current technique is found to improve the tensile properties of the weld compared with continuous current welding due to grain refinement occurring in the fusion zone.
基金The authors sincerely thank the State Key Laboratory of Refractories and Metallurgy(Grant No.G202206)National Natural Science Foundation of China(Grant Nos.U20A20277 and 52150610494)National Key Research and Development Program of China(Grant No.2022YFE0123300).
文摘Fused ternary CaF_(2)–SiO_(2)–MnO fluxes have been manufactured and applied to join EH36 shipbuilding steel under high heat input submerged arc welding.Five fluxes have been designed to clarify the effect of MnO content in CaF_(2)–SiO_(2)–MnO flux on the impact toughness of the weld metal,with the added amount of MnO from 10 to 50 wt.%at the expense of CaF_(2).With the increase in MnO content,the Charpy impact energy increases first and then decreases,experiencing a maximum value at 30 wt.%MnO.Microstructure of the weld metals has also been studied to account for impact toughness variations.It has been demonstrated that the highest acicular ferrite volume fraction in the weld metal is achieved at 30 wt.%MnO,which is concurrent to the maximum value of Charpy impact energy.It is believed that the Mn and O content variations in the weld metal contribute synergistically to such an interesting phenomenon.
文摘Submerged arc welding （SAW） has shortcoming of over heat input, which increases grain size in heat-affected zone （ HAZ） and decreases welding quality and mechanical properties of the joints serioasly. With improvements of welding equipment, direct current （ DC） pulsed SAW （ PSAW） was utilized successfully in the research. Comparing DC PSAW with DC common SAW （ CSAW） , the metallographic structure was analyzed with optical and electron microscope, the width of HAZ was measured as well as the width and hardness of the coarse grained HAZ （CGHAZ）. The research shows that DC PSAW joint had higher welding penetration, narrower HAZ and CGHAZ, which benefited HAZ performance and welding quality.
基金supported by the Research and Development Project of Science and Technology of Hebei Province, China (No.03212211D and No.002121186D)
文摘The effects of alloying elements in welding wires and submerged arc welding process on the microstructures and low-temperature impact toughness of weld metals have been investigated. The results indicate that the optimal contents of alloying elements in welding wires can improve the low-temperature impact toughness of weld metals because the proeutectoid ferrite and bainite formations can be suppressed, and the fraction of acicular ferrite increases. However, the contents of alloying elements need to vary along with the welding heat input. With the increase in welding heat input, the contents of alloying elements in welding wires need to be increased accordingly. The microstructures mainly consisting of acicular ferrite can be obtained in weld metals after four-wire submerged arc welding using the wires with a low carbon content and appropriate contents of Mn, Mo, Ti-B, Cu, Ni, and RE, resulting in the high low-temperature impact toughness of weld metals.
文摘SAW308L submerged arc welding wire and SJ601A submerged arc welding flux were selected to weld the 12 mm 08Cr19MnNi3Cu2N low nickel and high nitrogen austenitic stainless steel plates with three different welding heat input,and microstructure,tensile properties,microhardness and corrosion properties of the welded joints were studied.The results show that no defects are found in the three groups of welded joints,and the welded joints have better performance.The tensile strength of 08Cr19MnNi3Cu2N stainless steel welded joints with different heat input is slightly lower than that of the base metal,and fracture occurs in the weld zone,and the hardness of the weld zone is lower than that of the base metal.The weld microstructure of stainless steel welded joints with different heat input is composed of austenite+δferrite,and ferrite is uniformly distributed in austenite.With the increase of the welding heat input,the ferrite content in the weld zone decrease gradually,the grain size in the thermal affected zone increase gradually,and the impact toughness reduce.
文摘The present study is concerned with the effect of filler metals such as austenitic stainless steel, ferritic stainless steel and duplex stainless steel on tensile and impact properties of the ferritic stainless steel conforming to AISI 409M grade. Rolled plates of 4 mm thickness were used as the base material for preparing single pass butt welded joints. Tensile and impact properties, microhardness, microstructure and fracture surface morphology of the joints fabricated by austenitic stainless steel, ferritic stainless steel and duplex stainless steel filler metals were evaluated and the results were reported. From this investigation, it is found that the joints fabricated by duplex stainless steel filler metal showed higher tensile strength and hardness compared to the joints fabricated by austenitic and ferritic stainless steel filler metals. Joints fabricated by austenitic stainless steel filler metal exhibited higher ductility and impact toughness compared with the joints fabricated by ferritic stainless steel and duplex stainless steel filler metals.
文摘The effect of autogeneous arc welding processes on tensile and impact properties of ferritic stainless steel conformed to AISI 409M grade is studied. Rolled plates of 4 mm thickness have been used as the base material for preparing single pass butt welded joints. Tensile and impact properties, microhardness, microstructure, and fracture surface morphology of continuous current gas tungsten arc welding （CCGTAW）, pulsed current gas tungsten arc welding （PCGTAW）, and plasma arc welding （PAW） joints are evaluated and the results are compared. It is found that the PAW joints of ferritic stainless steel show superior tensile and impact properties when compared with CCG-TAW and PCGTAW joints, and this is mainly due to lower heat input, finer fusion zone grain diameter, and higher fusion zone hardness.
基金The Director,Naval Material Research Laboratory(NMRL),Ambernath for financial support through CARS project No:G8/15250/2011 dated29.02.2012
文摘Naval grade high strength low alloy(HSLA) steels can be easily welded by all types of fusion welding processes. However, fusion welding of these steels leads to the problems such as cold cracking, residual stress, distortion and fatigue damage. These problems can be eliminated by solid state welding process such as friction stir welding(FSW). In this investigation, a comparative evaluation of mechanical(tensile, impact,hardness) properties and microstructural features of shielded metal arc(SMA), gas metal arc(GMA) and friction stir welded(FSW) naval grade HSLA steel joints was carried out. It was found that the use of FSW process eliminated the problems related to fusion welding processes and also resulted in the superior mechanical properties compared to GMA and SMA welded joints.