High-purity aluminum titanate was synthesized via a water quenching method with waste-residue in the aluminum factory and industrial TiO2 as the main raw materials, which belongs to the comprehensive utilization of so...High-purity aluminum titanate was synthesized via a water quenching method with waste-residue in the aluminum factory and industrial TiO2 as the main raw materials, which belongs to the comprehensive utilization of solid wastes. Compared with the conventional method, it can reduce synthesis temperature, effectively inhibit decomposition and raise the content of AT; the addition of tiny silicon powder can improve the sintering and optimize the properties of AT. The crystalline phase structure and microstructure of each sample were characterized with XRD and SEM methods; the content of each crystalline phase in each sample was confirmed with Rietveld Quantification method; the properties of each sample were also tested. The experimental results showed that No. 4 is the optimum specimen, with the corresponding mass ratio of Al2O3/TiO2 to be 1.27 and the content of AT of 97.2 wt%. The addition of optimum tiny silicon powder is confirmed to be 8wt%; its corresponding bulk density is 2.63 g/cm^3, bending strength is 46.34 MPa, and the retention of one thermal vibration bending strength is 71.5%.展开更多
In the H2SO4 medium and in the presence of dodecylbenzene sulfonic acid sodiumsalt (DBS), dimethyl yellow (R) could emit strong and stable solid substrate room temperature phosphorescence (RTP) on filter paper. And Na...In the H2SO4 medium and in the presence of dodecylbenzene sulfonic acid sodiumsalt (DBS), dimethyl yellow (R) could emit strong and stable solid substrate room temperature phosphorescence (RTP) on filter paper. And NaIO4 could oxidize R to cause the RTP quenching. Arsenic(V) could catalyze the reaction of NaIO4 oxidizing R, which caused the RTP sharply quenching. The reducing value of phosphorescence intensity (ΔIp) for the system with DBS is 3.3 times higher than that without DBS. Moreover, the ΔIp is proportional to the concentration of As(V). Based on the facts above, a new RTP quenching method for the determination of trace As(V) has been established.展开更多
We report a reproducible approach in preparing high-quality overdoped Bi2 Sr2 CaCu2 08+δ (Bi2212) single crystals by annealing Bi2212 crystals in high oxygen pressure followed by a fast quenching. In this way, hig...We report a reproducible approach in preparing high-quality overdoped Bi2 Sr2 CaCu2 08+δ (Bi2212) single crystals by annealing Bi2212 crystals in high oxygen pressure followed by a fast quenching. In this way, high-quality overdoped and heavily overdoped Bi2212 single crystals are obtained by controlling the annealing oxygen pressure. We find that, beyond a limit of oxygen pressure that can achieve most heavily overdoped Bi2212 with a Tc N63 K, the annealed Bi2212 begins to decompose. This accounts for the existence of the hole-doping limit and thus the Tc limit in the heavily overdoped region of Bi2212 by the oxygen annealing process. These results provide a reliable way in preparing high-quality overdoped and heavily overdoped Bi2212 crystals that are important for studies of the physical properties, electronic structure and superconductivity mechanism of the cuprate superconductors.展开更多
Fe–Fe2O3–MnO2–sucrose–epoxy resin and O2 as reaction system and feed gas,separately,were used to prepare micro-nano hollow multiphase ceramic microspheres containing MnFe2O4absorbent by self-reactive quenching met...Fe–Fe2O3–MnO2–sucrose–epoxy resin and O2 as reaction system and feed gas,separately,were used to prepare micro-nano hollow multiphase ceramic microspheres containing MnFe2O4absorbent by self-reactive quenching method which is integrated with flame jet,selfpropagating high-temperature synthesis(SHS),and rapidly solidification.The morphologies and phase compositions of hollow microspheres were studied by scanning electron microscope(SEM),transmission electron microscope(TEM),X-ray diffraction(XRD),and energy dispersive spectroscopy.The results show that the quenching products are regular spherical substantially with hollow structure,particle size is between few hundreds nanometers and 5 lm.Phase compositions are diphase of Fe3O4,Mn3O4,and MnFe2O4,and the spinel soft magnetic ferrite MnFe2O4 with microwave magnetic properties is in majority.Collisions with each other,burst as well as‘‘refinement’’of agglomerate powders in flame field may be the main reasons for the formation of micro-nano hollow multiphase ceramic microspheres containing MnFeOabsorbent.展开更多
The state of Tb3+ is investigated in liposome. When the concentration of PC is below CMC (critical micell concentration), most of Tb3+ is associated with PC, the binding constant is about 3.35×103 L/mol. When the...The state of Tb3+ is investigated in liposome. When the concentration of PC is below CMC (critical micell concentration), most of Tb3+ is associated with PC, the binding constant is about 3.35×103 L/mol. When the concentration of PC is beyond CMC, most of Tb3+ is dimerized, the dimerization constant is about 3.92×104L/mol. In PC?CH?H2O system, the binding constant of Tb3+?CH complex 2.93×104L/mol is obtained.展开更多
A fluoroimmunoassay method using unlabeled europium chelate is described.The principle is similar to that of fluoroimmunoassay method using lanthanide chelate as labels.The procedure is simple because labeling process...A fluoroimmunoassay method using unlabeled europium chelate is described.The principle is similar to that of fluoroimmunoassay method using lanthanide chelate as labels.The procedure is simple because labeling process is omitted.The detection limit is about 10^(10) mol/L antigen.The relative standard deviation of immunoassay is less than 10%.The recoveries of human serum albumin and estradiol protein conjugate are 96-105% and 111% respectively.展开更多
A fluoroimmunoassay method using unlabeled Terbium chelate is described.The principle is similar to that of fluoroimmunoassay method using lanthanide chelate as labels.The procedure is simpte because labeling process ...A fluoroimmunoassay method using unlabeled Terbium chelate is described.The principle is similar to that of fluoroimmunoassay method using lanthanide chelate as labels.The procedure is simpte because labeling process is unnecessary.The recovery of HSA and albumin in urine is 107% and 95% respectively.The standard deviation is tess than 10%.展开更多
The mechanism of self-propagating high-temperature synthesis (SHS) of TiC-Cu cermets was studied using a combustion front quenching method. Microstructural evolution in the quenched sample was observed using scannin...The mechanism of self-propagating high-temperature synthesis (SHS) of TiC-Cu cermets was studied using a combustion front quenching method. Microstructural evolution in the quenched sample was observed using scanning electron microscope (SEM) with energy dispersive X-ray (EDX) spectrometry, and the combustion temperature was measured. The results showed that the combustion reaction started with local formation of Ti-Cu melt and could be described with the dissolution-precipitation mechanism, namely, Ti, Cu, and C particles dissolved into the Ti-Cu solution and TiC particles precipitated in the saturated Ti-Cu-C liquid solution. The local formation of Ti-Cu melt resulted from the solid diffusion between Ti and Cu particles.展开更多
In order to investigate the mechanism of combustion synthesis of TiC-Ti cermet, a mixture of Ti and C was used for a combustion front quenching test, and the microstructural evolution in the quenched sample was analyz...In order to investigate the mechanism of combustion synthesis of TiC-Ti cermet, a mixture of Ti and C was used for a combustion front quenching test, and the microstructural evolution in the quenched sample was analyzed by scanning electron microscopy (SEM) and energy dispersive X-ray (EDX). Also, a temperature-time profile of the combustion reaction was measured. Based on the experimental results, a reaction-dissolution-precipitation mechanism of the combustion synthesis of TiC-Ti was proposed.展开更多
A new material with heat-resistant and adiabatic characteristics and high strength was prepared using the combustion synthesis method by mixed powders of CrO3, Al, Al2O3, and NaF in atmospheric gas. The reaction dynam...A new material with heat-resistant and adiabatic characteristics and high strength was prepared using the combustion synthesis method by mixed powders of CrO3, Al, Al2O3, and NaF in atmospheric gas. The reaction dynamic process of the Al-CrO3-NaF-Al2O3-N2-O2 new material system by the combustion synthesis method was discussed based on the observation results by SEM, EDS, and XRD in combination with the combustion front quenching method (CFQM) and the relation curves between reaction free enthalpies and the corresponding temperatures. The combustion synthesis mechanism and the formation reasons of the phase in the combustion product were analyzed.展开更多
Heteroatom doping is an efficient approach to regulate the fluorescence properties of carbon dots.Using aminophenylboronic acid as the raw material,a combustion method was developed for the synthesis of boron,nitrogen...Heteroatom doping is an efficient approach to regulate the fluorescence properties of carbon dots.Using aminophenylboronic acid as the raw material,a combustion method was developed for the synthesis of boron,nitrogen-doped carbon dots(B,N-carbon dots).The B,N-carbon dots emitted green fluorescence and displayed high resistance to both photo bleaching and ionic strength.A facile fluorescence sensing approach for Cu^2+ was fabricated via static fluorescence quenching.Under optimal conditions,a rapid detection of Cu^2+ could be completed in 2 min with a linearity ranging from 1 μmol/L to 25 μmol/L and a detection limit of 0.3 μmol/L Furthermore,the proposed method showed potential applications for the detection of Cu^2+ in natural water samples.展开更多
The process to prepare pure phase of hexagonal Y2O2S was investigated. Effect of mixed flux of Na2CO3 and S amounts was studied. The phase composition and morphology were characterized by X-ray diffraction (XRD) and...The process to prepare pure phase of hexagonal Y2O2S was investigated. Effect of mixed flux of Na2CO3 and S amounts was studied. The phase composition and morphology were characterized by X-ray diffraction (XRD) and scanning electron microscopy (SEM). The results showed that the single phase of Y2O2S with smooth morphology could not be obtained as the molar ratio of Y2O3, Na2CO3 and S was in the range of 1:(0.5-1):(2-3) until the molar ratio was increased to 1:1.5:4. Different Er3+ concentration doped Y2O2S:Er powders were prepared with molar ratio of the raw materials 1:1.5:4. The quenching concentration of Er3+ in Y2O2S was more than 2 mol.%, which was due to the interaction of electric quadrupoles between Er3+ ions.展开更多
基金Supported by the Natural Science Foundation of Fujian Province (No. T0750005)the Science and Technology Developing Foundation of Fuzhou University (No. 2007-XQ-02)
文摘High-purity aluminum titanate was synthesized via a water quenching method with waste-residue in the aluminum factory and industrial TiO2 as the main raw materials, which belongs to the comprehensive utilization of solid wastes. Compared with the conventional method, it can reduce synthesis temperature, effectively inhibit decomposition and raise the content of AT; the addition of tiny silicon powder can improve the sintering and optimize the properties of AT. The crystalline phase structure and microstructure of each sample were characterized with XRD and SEM methods; the content of each crystalline phase in each sample was confirmed with Rietveld Quantification method; the properties of each sample were also tested. The experimental results showed that No. 4 is the optimum specimen, with the corresponding mass ratio of Al2O3/TiO2 to be 1.27 and the content of AT of 97.2 wt%. The addition of optimum tiny silicon powder is confirmed to be 8wt%; its corresponding bulk density is 2.63 g/cm^3, bending strength is 46.34 MPa, and the retention of one thermal vibration bending strength is 71.5%.
文摘In the H2SO4 medium and in the presence of dodecylbenzene sulfonic acid sodiumsalt (DBS), dimethyl yellow (R) could emit strong and stable solid substrate room temperature phosphorescence (RTP) on filter paper. And NaIO4 could oxidize R to cause the RTP quenching. Arsenic(V) could catalyze the reaction of NaIO4 oxidizing R, which caused the RTP sharply quenching. The reducing value of phosphorescence intensity (ΔIp) for the system with DBS is 3.3 times higher than that without DBS. Moreover, the ΔIp is proportional to the concentration of As(V). Based on the facts above, a new RTP quenching method for the determination of trace As(V) has been established.
基金Supported by the National Natural Science Foundation of China under Grant Nos 11190022,11334010 and 11534007the National Basic Research Program of China under Grant No 2015CB921000the Strategic Priority Research Program(B)of Chinese Academy of Sciences under Grant No XDB07020300
文摘We report a reproducible approach in preparing high-quality overdoped Bi2 Sr2 CaCu2 08+δ (Bi2212) single crystals by annealing Bi2212 crystals in high oxygen pressure followed by a fast quenching. In this way, high-quality overdoped and heavily overdoped Bi2212 single crystals are obtained by controlling the annealing oxygen pressure. We find that, beyond a limit of oxygen pressure that can achieve most heavily overdoped Bi2212 with a Tc N63 K, the annealed Bi2212 begins to decompose. This accounts for the existence of the hole-doping limit and thus the Tc limit in the heavily overdoped region of Bi2212 by the oxygen annealing process. These results provide a reliable way in preparing high-quality overdoped and heavily overdoped Bi2212 crystals that are important for studies of the physical properties, electronic structure and superconductivity mechanism of the cuprate superconductors.
基金supported by the ational Natural Science Foundation of China (No. 51172282)
文摘Fe–Fe2O3–MnO2–sucrose–epoxy resin and O2 as reaction system and feed gas,separately,were used to prepare micro-nano hollow multiphase ceramic microspheres containing MnFe2O4absorbent by self-reactive quenching method which is integrated with flame jet,selfpropagating high-temperature synthesis(SHS),and rapidly solidification.The morphologies and phase compositions of hollow microspheres were studied by scanning electron microscope(SEM),transmission electron microscope(TEM),X-ray diffraction(XRD),and energy dispersive spectroscopy.The results show that the quenching products are regular spherical substantially with hollow structure,particle size is between few hundreds nanometers and 5 lm.Phase compositions are diphase of Fe3O4,Mn3O4,and MnFe2O4,and the spinel soft magnetic ferrite MnFe2O4 with microwave magnetic properties is in majority.Collisions with each other,burst as well as‘‘refinement’’of agglomerate powders in flame field may be the main reasons for the formation of micro-nano hollow multiphase ceramic microspheres containing MnFeOabsorbent.
文摘The state of Tb3+ is investigated in liposome. When the concentration of PC is below CMC (critical micell concentration), most of Tb3+ is associated with PC, the binding constant is about 3.35×103 L/mol. When the concentration of PC is beyond CMC, most of Tb3+ is dimerized, the dimerization constant is about 3.92×104L/mol. In PC?CH?H2O system, the binding constant of Tb3+?CH complex 2.93×104L/mol is obtained.
基金This work was supported by National Natural Science Foundation of China.
文摘A fluoroimmunoassay method using unlabeled europium chelate is described.The principle is similar to that of fluoroimmunoassay method using lanthanide chelate as labels.The procedure is simple because labeling process is omitted.The detection limit is about 10^(10) mol/L antigen.The relative standard deviation of immunoassay is less than 10%.The recoveries of human serum albumin and estradiol protein conjugate are 96-105% and 111% respectively.
基金supported by National Commission of Natural Science Foundation of China.
文摘A fluoroimmunoassay method using unlabeled Terbium chelate is described.The principle is similar to that of fluoroimmunoassay method using lanthanide chelate as labels.The procedure is simpte because labeling process is unnecessary.The recovery of HSA and albumin in urine is 107% and 95% respectively.The standard deviation is tess than 10%.
基金This work was financially supported by the Natural Science Foundation of Shaanxi Province, China (No.2004E107)
文摘The mechanism of self-propagating high-temperature synthesis (SHS) of TiC-Cu cermets was studied using a combustion front quenching method. Microstructural evolution in the quenched sample was observed using scanning electron microscope (SEM) with energy dispersive X-ray (EDX) spectrometry, and the combustion temperature was measured. The results showed that the combustion reaction started with local formation of Ti-Cu melt and could be described with the dissolution-precipitation mechanism, namely, Ti, Cu, and C particles dissolved into the Ti-Cu solution and TiC particles precipitated in the saturated Ti-Cu-C liquid solution. The local formation of Ti-Cu melt resulted from the solid diffusion between Ti and Cu particles.
文摘In order to investigate the mechanism of combustion synthesis of TiC-Ti cermet, a mixture of Ti and C was used for a combustion front quenching test, and the microstructural evolution in the quenched sample was analyzed by scanning electron microscopy (SEM) and energy dispersive X-ray (EDX). Also, a temperature-time profile of the combustion reaction was measured. Based on the experimental results, a reaction-dissolution-precipitation mechanism of the combustion synthesis of TiC-Ti was proposed.
基金the National High-Tech Research and Development Program of China (863 Program) (No. 2006AA03Z351).
文摘A new material with heat-resistant and adiabatic characteristics and high strength was prepared using the combustion synthesis method by mixed powders of CrO3, Al, Al2O3, and NaF in atmospheric gas. The reaction dynamic process of the Al-CrO3-NaF-Al2O3-N2-O2 new material system by the combustion synthesis method was discussed based on the observation results by SEM, EDS, and XRD in combination with the combustion front quenching method (CFQM) and the relation curves between reaction free enthalpies and the corresponding temperatures. The combustion synthesis mechanism and the formation reasons of the phase in the combustion product were analyzed.
基金financially supported by the National Natural Science Foundation of China(No.21375112)the Marine hightech industry development projects of Fujian Province(No.2015-19)
文摘Heteroatom doping is an efficient approach to regulate the fluorescence properties of carbon dots.Using aminophenylboronic acid as the raw material,a combustion method was developed for the synthesis of boron,nitrogen-doped carbon dots(B,N-carbon dots).The B,N-carbon dots emitted green fluorescence and displayed high resistance to both photo bleaching and ionic strength.A facile fluorescence sensing approach for Cu^2+ was fabricated via static fluorescence quenching.Under optimal conditions,a rapid detection of Cu^2+ could be completed in 2 min with a linearity ranging from 1 μmol/L to 25 μmol/L and a detection limit of 0.3 μmol/L Furthermore,the proposed method showed potential applications for the detection of Cu^2+ in natural water samples.
基金Project supported by Military Coordination Scientific Research Projects (JPPT-1486)the Priority Academic Program Development of Jiangsu Higher Education Institutions (CXZZ11_0333)
文摘The process to prepare pure phase of hexagonal Y2O2S was investigated. Effect of mixed flux of Na2CO3 and S amounts was studied. The phase composition and morphology were characterized by X-ray diffraction (XRD) and scanning electron microscopy (SEM). The results showed that the single phase of Y2O2S with smooth morphology could not be obtained as the molar ratio of Y2O3, Na2CO3 and S was in the range of 1:(0.5-1):(2-3) until the molar ratio was increased to 1:1.5:4. Different Er3+ concentration doped Y2O2S:Er powders were prepared with molar ratio of the raw materials 1:1.5:4. The quenching concentration of Er3+ in Y2O2S was more than 2 mol.%, which was due to the interaction of electric quadrupoles between Er3+ ions.