The catalytic pyrolyses of rayon have been studied respectively by thermo-gravimetric analysis (TGA) when rayon was treated with phosphoric acid (PA), three ammonium phosphate salts and ammonium sulfate (AS). The air ...The catalytic pyrolyses of rayon have been studied respectively by thermo-gravimetric analysis (TGA) when rayon was treated with phosphoric acid (PA), three ammonium phosphate salts and ammonium sulfate (AS). The air is favorable to the catalysis of dibasic ammonium phosphate (DAP), but not to those of ADP, PA, AP, and AS obviously. It is put forward that a peak’s shape character can be described with the ratio of height to half-height-width (H/W /2) of the peak on a differential thermo-gravimetric (DTG) curve. A flat cracking peak, presenting a more moderate dehydration reaction, has a smaller ratio and could lead to higher carbonization and activation yields. The experimental results prove this view. According to expectation, the order of catalysis is: DAP≥ADP>PA> APAS no catalyst.展开更多
The activated carbon fiber（ACF） was prepared from polyacrylonitrile-based pre-oxidized fiber（PANOF） by KOH direct activation. The influence of activation conditions including impregnation ratio（the mass ratio of ...The activated carbon fiber（ACF） was prepared from polyacrylonitrile-based pre-oxidized fiber（PANOF） by KOH direct activation. The influence of activation conditions including impregnation ratio（the mass ratio of PANOF to KOH）, activation temperature and activation time on the pore structure and electrochemical properties of ACF was investigated, and the corresponding activation mechanism was proposed. The ACF prepared at an activation temperature of 800℃ and an impregnation ratio（the mass ratio of PANOF to KOH） of 1：2 for an activation time of 1 b in 6 mol/L KOH solution exhibits a specific surface area of 3029 m^2/g, a mesoporosity of 84.2% and a specific capacitance of 288 F/g, and shows a good capacitive performance. The prepared ACF can be used as the electrode material for supercapacitors.展开更多
文摘The catalytic pyrolyses of rayon have been studied respectively by thermo-gravimetric analysis (TGA) when rayon was treated with phosphoric acid (PA), three ammonium phosphate salts and ammonium sulfate (AS). The air is favorable to the catalysis of dibasic ammonium phosphate (DAP), but not to those of ADP, PA, AP, and AS obviously. It is put forward that a peak’s shape character can be described with the ratio of height to half-height-width (H/W /2) of the peak on a differential thermo-gravimetric (DTG) curve. A flat cracking peak, presenting a more moderate dehydration reaction, has a smaller ratio and could lead to higher carbonization and activation yields. The experimental results prove this view. According to expectation, the order of catalysis is: DAP≥ADP>PA> APAS no catalyst.
基金Supported by the National Natural Science Foundation of China（No.21273097） and the Key Project of Jilin Province, China（No.20126010）.
文摘The activated carbon fiber（ACF） was prepared from polyacrylonitrile-based pre-oxidized fiber（PANOF） by KOH direct activation. The influence of activation conditions including impregnation ratio（the mass ratio of PANOF to KOH）, activation temperature and activation time on the pore structure and electrochemical properties of ACF was investigated, and the corresponding activation mechanism was proposed. The ACF prepared at an activation temperature of 800℃ and an impregnation ratio（the mass ratio of PANOF to KOH） of 1：2 for an activation time of 1 b in 6 mol/L KOH solution exhibits a specific surface area of 3029 m^2/g, a mesoporosity of 84.2% and a specific capacitance of 288 F/g, and shows a good capacitive performance. The prepared ACF can be used as the electrode material for supercapacitors.