Effect of SiO 2 content and sintering process on the composition and properties of Pure Carbon Reaction Bonded Silicon Carbide (PCRBSC) ceramics prepared with C-SiO 2 green body by infiltrating silicon was presented...Effect of SiO 2 content and sintering process on the composition and properties of Pure Carbon Reaction Bonded Silicon Carbide (PCRBSC) ceramics prepared with C-SiO 2 green body by infiltrating silicon was presented.The infiltrating mechanism of C-SiO 2 preform was also explored.The experimental results indicate that the shaping pressure increases with the addition of SiO 2 to the preform,and the pore size of the body turned finer and distributed in a narrower range,which is beneficial to decreasing the residual silicon content in the sintered materials and to avoiding shock off,thus increasing the conversion rate of SiC.SiO 2 was deoxidized by carbon at a high temperature and the gaseous SiO and CO produced are the main reason to the crack of the body at an elevated temperature.If the green body is deposited at 1800℃ in vacuum before infiltration crack will not be produced in the preform and fully dense RBSC can be obtained.The ultimate material has the following properties:a density of 3.05-3.12g/cm3,a strength of 580±32MPa and a hardness of (HRA)91-92.3.展开更多
文摘Effect of SiO 2 content and sintering process on the composition and properties of Pure Carbon Reaction Bonded Silicon Carbide (PCRBSC) ceramics prepared with C-SiO 2 green body by infiltrating silicon was presented.The infiltrating mechanism of C-SiO 2 preform was also explored.The experimental results indicate that the shaping pressure increases with the addition of SiO 2 to the preform,and the pore size of the body turned finer and distributed in a narrower range,which is beneficial to decreasing the residual silicon content in the sintered materials and to avoiding shock off,thus increasing the conversion rate of SiC.SiO 2 was deoxidized by carbon at a high temperature and the gaseous SiO and CO produced are the main reason to the crack of the body at an elevated temperature.If the green body is deposited at 1800℃ in vacuum before infiltration crack will not be produced in the preform and fully dense RBSC can be obtained.The ultimate material has the following properties:a density of 3.05-3.12g/cm3,a strength of 580±32MPa and a hardness of (HRA)91-92.3.