Experimental investigation of axially loaded steel fiber reinforced high strength concrete-filled steel tube columns

An experimental study on the compressive behavior of steel fiber reinforced concrete-filled steel tube columns is presented. Specimens were tested to investigate the effects of the concrete strength, the thickness of steel tube and the steel fiber volume fraction on the ultimate strength and the ductility. The experimental results indicate that the addition of steel fibers in concrete can significantly improve the ductility and the energy dissipation capacity of the concrete-filled steel tube columns and delay the local buckling of the steel tube, but has no obvious effect on the failure mode. It has also been found that the addition of steel fibers is a more effective method than using thicker steel tube in enhancing the ductility, and more advantageous in the case of higher strength concrete. An analytical model to estimate the load capacity is proposed for steel tube columns filled with both plain concrete and steel fiber reinforced concrete. The predicted results are in good agreement with the experimental ones obtained in this work and literatures.

Ductility and Ultimate Capacity of Concrete-Filled Lattice Rectangular Steel Tube Columns

A kind of concrete-filled lattice rectangular steel tube(CFLRST)column was put forward.The numerical simulation was modeled to analyze the mechanical characteristic of CFLRST column.By comparing the load-deformation curves from the test results,the rationality and reliability of the finite element model has been confirmed,moreover,the change of the section stiffness and stress in the forcing process and the ultimate bearing capacity of the column were analyzed.Based on the model,the comparison of ultimate bearing capacity and ductility between CFLRST column and reinforced concrete(RC)column were also analyzed.The results of the finite element analysis show that the loading process of CFLRST column consists of elastic stage,yield stage and failure stage.The failure modes are mainly strength failure and failure of elastoplastic instability.CFLRST column has higher bearing capacities in comparison with reinforced concrete columns with the same steel ratio.In addition,the stiffness degeneration of CFLRST column is slower than RC column and CFLRST column has good ductility.

Behavior of High Strength Concrete Filled Square Steel Tube Stub Columns with Inner CFRP Tube Under Biaxial Eccentric Compression

This paper studies the contribution of CFRP(carbon fiber-reinforced polymer)to the mechanical behavior of high strength concrete-filled square steel tube(HCFST)under biaxial eccentric compression.The new type of composite member is composed of an inner CFRP tube and an outer steel tube with concrete filled in the two tubes.The finite element analysis was made by ABAQUS on the behavior of high strength concrete filled square steel tubular columns with inner CFRP circular tube subjected to bi-axial eccentric loading.The results obtained from the finite element analysis were verified with the experimental results.In addition,the load-deflection curves in the whole process were calculated and analyzed,which can be divided into three segments:Elastic phase,plastic phase,descending phase.Based on the load-deflection curves,the stresses analysis on the core concrete,CFRP tube and steel tube were conducted.The confinement effect of the CFRP tube improves the ductility of HCFST-CFRP stub column.CFRP ratio and eccentricity affect the ultimate bearing capacity of HCFST stub column.Finally,a calculation formula of ultimate bearing capacity was proposed in the paper.

Experimental study on the seismic behavior of high strength concrete fi lled double-tube columns

To study the seismic behavior of high strength concrete fi lled double-tube(CFDT) columns,each consisting of an external square steel tube and an internal circular steel tube,quasi-static tests on eight CFDT column specimens were conducted.The test variables included the width-to-thickness ratio(β1) and the area ratio(β2) of the square steel tube,the wall thickness of the circular steel tube,and the axial force(or the axial force ratio) applied to the CFDT columns.The test results indicate that for CFDT columns with a square steel tube with β1 of 50.1 and 24.5,local buckling of the specimen was found at a drift ratio of 1/150 and 1/50,respectively.The lateral force-displacement hysteretic loops of all specimens were plump and stable.Reducing the width-to-thickness ratio of the square steel tube,increasing its area ratio,or increasing the wall thickness of the internal circular steel tube,led to an increased fl exural strength and deformation capacity of the specimens.Increasing the design value of the axial force ratio from 0.8 to 1.0 may increase the fl exural strength of the specimens,while it may also decrease the ultimate deformation capacity of the specimen with β1 of 50.1.

An Experimental Study on the Behavior of Square Concrete-Filled High Strength Steel Tube Columns

The paper presents an experimental study on the behavior of square concrete-filled high strength steel tube columns until failure.Four specimens were tested to investigate the effect of high strength steel and plain strength concrete on the load carrying capacity of the square concrete-filled steel tube columns.The effect of the concrete which filled in the steel tube was also investigated.Also,the effect of high strength steel and the presence of concrete were also investigated.The main parameters in the tests were:(1) the ultimate strength of steel (800 Mpa),(2) the presence of concrete in steel tube (hollow steel tube and concrete-filled steel tube),and (3) slender ratio.The main objectives of these tests were three-step:(1) to describe a series of tests on composite columns,(2) to analyze the influence of several parameters,and (3) to compare the accuracy of the predictions by using the specifications in the code (AISC-LRFD,EC4 and AIJ etc.) for the design of high-strength composite columns.Experimental results indicate that the ultimate strength of steel and presence of concrete had significant influence on both the axial compressive load capacity and the ductile of the square steel tube.

内置工字型CFRP型材高强圆钢管高强混凝土轴压短柱组合效应分析

目的 研究内置工字型CFRP型材的高强圆钢管高强混凝土短柱在轴心压力作用下三种材料的组合效应。方法 采用有限元分析软件ABAQUS对其进行数值模拟,通过相关试验验证模型的准确性,并对典型构件的破坏形态、受力全过程曲线进行分析,揭示构件各组成部分之间的相互作用和工作机理,评估CFRP配置率、钢材屈服强度、混凝土抗压强度、约束效应系数对组合效应的影响。结果 在高强圆钢管高强混凝土柱中内置CFRP型材,对构件的延性及安全裕度有显著提高,并改善了高强圆钢管对高强混凝土的约束,提高了构件的组合效应。结论 CFRP配置率控制在5.9%~8.4%,约束效应系数在1.2~1.4,钢材屈服强度不大于770 MPa时,构件中三种材料组合效应最佳。

高强钢管超高性能混凝土界面黏结滑移性能试验

目的为了研究高强钢管超高性能混凝土的黏结滑移性能,方法考虑径厚比、长径比和钢纤维掺量3个参数的影响,设计并制作15根构件进行试验研究,通过推出试验,得到轴向荷载与加载端位移的荷载-位移曲线,以及高强钢管与超高性能混凝土之间的黏结强度,根据试验结果,对影响黏结强度的参数进行定性定量分析。结果结果表明:随着高强钢管长径比和径厚比的增加,黏结强度减小;随着钢纤维掺量增加,试件黏结强度先增加后减小,即当钢纤维掺量从1%增加到2%时,黏结强度增加,但当钢纤维掺量从2%增加到3%时,黏结强度反而降低;试件荷载-滑移曲线表现为两种形式,一是有明显的峰值点,峰值点后曲线急速下降(部分出现尾部上升的现象),二是曲线无明显峰值点,拐点后曲线持续缓慢增长。高强钢管超高性能混凝土的黏结破坏分为黏结阶段、滑动阶段和抗摩擦阶段。结论以长径比、径厚比、含钢率和套箍系数为参数,结合试验数据并对其进行回归分析,得到适用于高强钢管超高性能混凝土黏结强度的计算模型,并将计算结果与试验结果进行对比,计算值与试验值吻合较好,可为实际工程提供一定参考。

配筋空心方钢管高强混凝土纯弯构件受力性能有限元分析

目的 研究配筋空心钢管高强混凝土构件的抗弯性能,推动其在建筑结构中的应用。方法 采用有限元分析软件ABAQUS建立配筋空心钢管混凝土构件有限元模型,在验证模型准确的基础上,分析构件的受力全过程及钢材屈服强度、混凝土抗压强度、钢管壁厚、钢筋直径、普通钢筋数量对构件受弯性能的影响。结果 纯弯试件在荷载作用下受力过程可分为3个阶段:弹性阶段、弹塑性阶段和强化阶段;试件破坏形态均为受弯破坏,表现出较好地延性。结论 组合构件在弯矩作用下可以很好地协同工作;钢材屈服强度和钢管壁厚的增加对构件承载力的提高影响最显著,建议配置普通钢筋数量在6~8根为最优。

高温后钢管高强混凝土柱的黏结性能

为了研究高温后钢管高强混凝土柱的黏结性能,通过有限元软件ABAQUS建立模型,并与已有试验结果进行验证,吻合良好。研究表明:钢管高强混凝土柱的黏结应力随着温度的升高呈现出先增加后减小的趋势;黏结应力随着混凝土强度的增大而增大,随着径厚比的增大而减小;长径比在2.74~7.72的范围内,随着长径比的增加,黏结力逐渐增加;黏结界面破坏的速度随温度的增加而减缓;随着温度的增加耗能因子呈现先增大后减小的趋势。

火灾后高强钢管混凝土柱轴压的参数化分析

为研究不同参数对火灾后高强钢管混凝土柱受轴压时的性能影响,利用ABAQUS有限元软件模拟火灾后高强钢管混凝土柱轴压模型,对该构件以钢管屈服强度、受火时间、混凝土强度为主要参数进行承载力-位移曲线分析,并剖析火灾后高强钢管混凝土柱典型曲线。结果表明:随着钢管屈服强度和混凝土强度增大,构件极限承载力增大;随着受火时间增加构件极限承载力出现下降趋势;从整体上看,受火时间分别为60、90、120 min时,构件中的混凝土承担主要载荷。

内置工字形CFRP的高强圆钢管高强混凝土纯弯构件抗弯刚度研究

目的研究内置工字形CFRP型材高强圆钢管高强混凝土纯弯构件的抗弯刚度,为该类构件的设计和工程应用提供参考。方法设计3个CHCFHST-CFRP构件,对其进行纯弯试验;应用ABAQUS有限元软件建立了纯弯构件数值模型,在数值模拟结果与试验结果吻合的基础上,分析各参数对构件抗弯刚度的影响;并且推导了适用于纯弯构件的抗弯刚度和挠度计算公式。结果试件均未出现断裂,钢管也未产生局部鼓曲,卸载后纯弯段有明显回弹;随着混凝土强度、钢管壁厚和型材尺寸的增长,构件抗弯刚度略有增长;与未配置CFRP型材的构件相比,配置CFRP型材后构件的抗弯刚度有了明显的增长。结论试件整体呈弯曲破坏模态,具有良好的变形能力,具有较强的耗能能力及刚度退化能力;利用笔者推导的公式得到的计算值与试验结果吻合较好,公式可用来计算此类构件的抗弯刚度与挠度。

基于性能的含可更换耗能梁段高强钢框筒结构抗震性能研究

含可更换耗能梁段的高强钢框筒结构(HSS-SFT-RSL)结合了耗能梁段耗能强、钢框筒抗侧刚度大、高强钢承载力高等优点,是一种抗震性能优良的结构体系.传统设计方法需要进行复杂的迭代和计算才能使结构达到预期性能目标,且无法较为准确地控制结构的塑性发展顺序和破坏模式,本文采用课题组提出的基于性能的塑性设计方法(PBPD)各设计一个30层HSS-SFT-RSL算例和含可更换剪切型耗能梁段的普通钢框筒结构(CS-SFT-RSL)算例,通过静力和动力弹塑性分析对比两算例的抗震性能.结果表明:采用PBPD法设计的两算例具有相似的顶点侧移角和破坏模式,HSS-SFT-RSL算例抗侧刚度略低,但极限承载力更高;在罕遇水准地震下,两算例各层耗能梁段均能参与耗能,层间侧移角沿结构高度分布均匀,避免了薄弱层,残余层间变形较小,有利于耗能梁段更换和结构震后功能的快速恢复.

MS1180方管连续辊弯成形角部开裂机理

方矩形管在辊弯成形中会产生角部开裂现象,这已成为严重制约方矩形管质量的关键问题,为解决其角部开裂缺陷展开深入研究,寻找控制开裂缺陷的方法。首先通过对MS1180进行单轴拉伸、缺口拉伸和平面应变实验得到了材料的力学特性,并分别利用3种拉伸试验将Ayada、Rice-Tracey和标准化Cockroft-Latham准则进行校准,得到了预测误差最小的一种断裂准则,并以此构建了方矩管辊弯开裂模型。其次利用辊弯成形COPRA RF设计软件和有限元MARC仿真专业软件,结合生产实际条件建立了方矩形管连续辊弯成形三维有限元模型,并进行辊弯实验验证模型的准确性。最后采用扫描电镜和金相显微镜对方矩形管开裂件以及断口进行微观观察,针对性的利用有限元模型探究了方矩形管连续辊弯成形时应力-应变分布规律,并分析了道次数量、角部成形半径和机架间距对方矩管角部应力-应变分布的影响。结果表明:发现材料起裂点位于角部近外层,对开裂断口进行分析,得到其开裂方式为准解理开裂,角部剪切面上所受的主应力过大导致其开裂;增加辊弯道次数量、方矩形管角部成形半径以及机架之间的间距能有效减少开裂问题的出现,为以后解决方矩形管角部开裂问题提供了理论基础。

钢管混凝土叠合柱-H型钢梁外套筒式连接节点抗震性能试验与有限元研究

以钢管混凝土叠合柱为研究对象,设计了一种高强对穿螺栓连接的外套筒式梁柱节点。为了研究该新型节点的抗震性能和破坏机理,对3个缩尺比为1∶2的节点进行了拟静力试验。观察节点损伤过程及破坏模式,分析了梁端荷载-位移滞回曲线、骨架曲线、节点延性及耗能能力,采用ABAQUS软件建立有限元模型,研究套筒宽厚比和加强肋板厚度对节点抗震性能影响。试验及有限元研究结果表明:节点滞回曲线饱满,延性系数介于3.13~4.19之间,等效黏滞阻尼系数介于0.211~0.296之间,节点域的变形较大且耗能能力较强;随着套筒厚度增大,核心区混凝土开裂减少,破坏位置由节点外移至梁端截面;减小套筒宽厚比和增大加强肋板厚度可以有效提高节点刚度。为保证外套筒式节点达到刚性节点要求,建议套筒宽厚比不大于25,加强肋板厚度不小于梁翼缘厚度。

方钢管螺旋筋约束自密实高强混凝土柱抗震性能试验研究

为研究方钢管螺旋筋约束自密实高强混凝土柱的抗震性能,以轴压比、剪跨比、有无配制螺旋筋以及螺旋筋间距作为设计参数,进行了7个试件的低周反复加载试验,获取了各试件的滞回曲线以及应变分布。试验结果表明:试件破坏特征主要为方钢管柱脚区域出现明显鼓曲形成塑性铰区域;随轴压比的提高,试件抗剪承载力、环线刚度和耗能能力均有提升,剪跨比对试件抗震性能的影响规律不明显。配制螺旋筋对峰值承载力和刚度的影响较小,而对试件延性及耗能的提升明显,与无配筋试件相比试件延性平均提升了15.4%,耗能平均提升了114.9%。螺旋筋间距越密对试件抗震性能提升效果更优;适当增大轴压比,控制剪跨比在5以内以及增设螺旋筋对提升其承载能力和变形能力有积极作用。

热输入量对890MPa臂架管焊接热影响区组织性能的影响

依据等强匹配原则,选用BHG-5焊丝对起重机臂架用890 MPa无缝钢管进行了斜Y型坡口焊接裂纹试验和不同热输入量的多层多道手动焊接试验,探究了材料的冷裂纹敏感性,以及不同热输入量对焊接接头组织和力学性能的影响。结果表明,预热温度为150℃时,可完全避免焊接冷裂纹的产生;随着热输入量的增加,焊缝金属接头强度变化不大,但焊接接头热影响区冲击韧性明显下降,选择小于20 kJ/cm热输入量焊接时可保证焊接接头具有较好的强韧性。

十字形钢管束高强混凝土组合剪力墙的抗剪承载力研究

为研究不同参数对十字形钢管束高强混凝土组合剪力墙抗剪承载力的影响,通过ABAQUS有限元软件建立了十字形钢管束高强混凝土组合剪力墙的有限元模型,重点考察钢材强度、混凝土强度、钢板厚度、钢管厚度、轴压比、墙体长度、墙体高度、腔体长度等参数对此类组合剪力墙抗剪承载力的影响。分析结果表明:随着钢材强度、钢板厚度、钢管厚度、墙体长度的增加和墙体高度的减小,试件的抗剪承载力呈显著增大趋势;随着混凝土强度的提高和腔体长度的减小,试件的抗剪承载力略呈增大趋势;当轴压比较小时(n∈(0,0.3]),轴压比对试件的抗剪承载力有一定的提高作用;当轴压比较大时(n∈(0.3,0.8]),随着轴压比的增加其抗剪承载力逐渐降低。最后,提出了十字形钢管束高强混凝土组合剪力墙的抗剪承载力计算公式。

高强度钢板混凝土组合剪力墙力学性能试验研究

文中主要就高强度钢板混凝土组合剪力墙力学性能及抗震性能进行研究。研究表明,高强度钢板混凝土组合剪力墙荷载-位移曲线及钢板的荷载-应变曲线均包括弹性阶段、弹塑性阶段以及失效阶段。随着轴压比的降低,试件的峰值荷载、顶点侧移、极限位移以及对应的水平荷载均不断增加;钢板的峰值荷载、极限应变均不断增加,剪力墙的骨架曲线末端未出现下降阶段;试件的等效黏滞阻尼系数不断降低,其耗能能力越低。三种轴压比剪力墙的刚度退化曲线基本一致,均呈现钟形,随着顶点侧移的增加,剪力墙的刚度先快速降低后稳定缓慢降低。

Pressurization System in Low Pressure Tube Hydroforming

Advanced high strength steels are the group of material with high strength and good formability, because high strength lesser gauge thickness can be used without compromising the function of component. In terms of economic forming process, hydroforming is the manufacturing option which uses a fluid medium to form a component by using high internal pressure. This process gained steep interest in the automotive and aerospace industries because of its many advantages such as part consolidation, good quality of the formed part etc. The main advantage is that the uniform pressure can be transferred to whole projected part at the same time. Low pressure tube hydroforming considered an inexpensive option for forming these advanced high strength steel. This paper investigates the pressurization system used during the low pressure tube hydroforming cycle. It is observed that the usage of ramp pressure cycle during forming the part from low pressure tube hydroforming results in lesser die holding force. Also, the stress, strain and thickness distribution of the part during low pressure tube hydroforming are critically analysed.

偏心率对工字型CFRP-高强圆钢管高强混凝土短柱力学性能的影响

目的研究偏心率对内置工字型CFRP型材的高强圆钢管高强混凝土短柱力学性能的影响。方法利用ABAQUS有限元软件建立了工字型CFRP-高强圆钢管高强混凝土短柱模型,分析不同偏心率下构件的受力-变形关系、各材料分担荷载以及应力发展,探究混凝土强度、钢材屈服强度、含钢率和CFRP型材对组合柱力学性能的影响。结果随着偏心率的增大,构件延性提高,初始刚度与极限承载力降低,且降低幅度减小,偏心率与极限承载力呈非线性关系;偏心率越小,加入CFRP型材对组合柱承载力的提高越显著。结论偏心率越大,混凝土强度的利用率越低,钢管力学性能发挥越充分。偏心率小于0.328时,建议采用增大混凝土强度的方式增加构件极限承载力;偏心率大于0.328时,建议采取增大钢材屈服强度和含钢率的方式增加构件的极限承载力。