Effect of Modification Treatment on Chloride Ions Permeability and Microstructure of Recycled Brick-mixed Aggregate Concrete

The modification methods of pozzolan slurry combined with sodium silicate and silicon-based additive were respectively adopted to treat recycled coarse brick-mixed aggregate(RCBA)in this study.The compressive strength and chloride permeability resistance of recycled aggregate concrete(RAC)before and after modification treatment were tested,and the microstructure of RAC was analyzed by mercury intrusion porosimetry(MIP)and scanning electron microscopy(SEM).The results show that the physical properties of RCBA strengthened by modification treatment are improved,and the compressive strength and chloride permeability resistance of treated RAC are also significantly improved.The modification treatment optimizes the pore size distribution of RAC,which increases the number of gel pores and transition pores,and decreases the number of capillary pores and macro pores.The surface fractal dimension shows a significant correlation with chloride diffusion coefficient,indicating that the variation of chloride permeability of treated RAC is consistent with the microstructure evolution.

Influence of Recycled Concrete Fine Powder on Durability of Cement Mortar

In this paper,the durability of cement mortar prepared with a recycled-concrete fine powder(RFP)was examined;including the analysis of a variety of aspects,such as the carbonization,sulfate attack and chloride ion erosion resistance.The results indicate that the influence of RFP on these three aspects is different.The carbonization depth after 30 days and the chloride diffusion coefficient of mortar containing 10%RFP decreased by 13.3%and 28.19%.With a further increase in the RFP content,interconnected pores formed between the RFP particles,leading to an acceleration of the penetration rate of CO_(2)and Cl^(−).When the RFP content was less than 50%,the corrosion resistance coefficient of the compressive strength of the mortar was 0.84-1.05 after 90 days of sulfate attack.But the expansion and cracking of the mortar was effectively alleviated due to decrease of the gypsum production.Scanning electron microscope(SEM)analysis has confirmed that 10%RFP contributes to the formation of a dense microstructure in the cement mortar.

Effect of Aggregate Gradation on the Properties of 3D Printed Recycled Coarse Aggregate Concrete

A simplex centroid design method was employed to design the gradation of recycled coarse aggregate.The bulk density was measured while the specific surface area and average excess paste thickness were calculated with different gradations.The fluidity,dynamic yield stress,static yield stress,printed width,printed inclination,compressive strength and ultrasonic wave velocity of 3D printed recycled aggregate concrete(3DPRAC)were further studied.The experimental results demonstrate that,with the increase of small-sized aggregate(4.75-7 mm)content,the bulk density initially increases and then decreases,and the specific surface area gradually increases.The average excess paste thickness fluctuates with both bulk density and specific surface area.The workability of 3DPRAC is closely related to the average excess paste thickness.With an increase in average paste thickness,there is a gradual decrease in dynamic yield stress,static yield stress and printed inclination,accompanied by an increase in fluidity and printed width.The mechanical performance of 3DPRAC closely correlates with the bulk density.With an increase in the bulk density,there is an increase in the ultrasonic wave velocity,accompanied by a slight increase in the compressive strength and a significant decrease in the anisotropic coefficient.Furthermore,an index for buildability failure of 3DPRAC based on the average excess paste thickness is proposed.

Three-Dimensional Multi-Phase Microscopic Simulation of Service Life of Recycled Large Aggregate Self-Compacting Concrete

Recycled large aggregate self-compacting concrete (RLA-SCC) within multiple weak areas. These weak areas have poor resistance to chloride ion erosion, which affects the service life of RLA-SCC in the marine environment. A three-dimensional multi-phase mesoscopic numerical model of RLA-SCC was established to simulate the chloride ions transportation in concrete. Experiments of RLA-SCC immersing in chloride solution were carried out to verify the simulation results. The effects of recycled large aggregate (RLA) content and RLA particle size on the service life of concrete were explored. The results indicate that the mesoscopic numerical simulation results are in good agreement with the experimental results. At the same depth, the closer to the surface of the RLA, the greater the chloride ion concentration. The service life of RLA-SCC in marine environment decreases with the increase of RLA content. Compared with the service life of 20% content, the service life of 25% and 30% content decreased by 20% and 42% respectively. Increasing the particle size of RLA can effectively improve the service life of RLA-SCC in chloride environment. Compared with the service life of 50 mm particle size, the service life of 70 mm and 90 mm increased by 61% and 163%, respectively. .

Research and Application of Recycled Concrete Technology in Prefabricated Buildings

The utilization of waste concrete as a raw material for recycled concrete in the domain of prefabricated components is garnering greater interest.This paper delineates and examines the concept,categorization,methodologies of preparation,applicable sectors,and evaluative metrics of recycled concrete technology,highlighting its prospective benefits.Nonetheless,for the successful integration of recycled concrete technology into prefabricated component applications,it is imperative to systematically enhance its physical,mechanical,and attributes,as well as its environmental efficacy.Moreover,to foster the continued advancement of recycled concrete technology,innovative initiatives,standardization,educational programs,demonstration projects,and collaborative efforts are crucial to promote broader adoption and realize improved outcomes within the realm of prefabricated components.In conclusion,recycled concrete technology is poised to play a pivotal role in prefabricated construction,offering robust support for propelling the construction industry towards a sustainable future.

Study on Durability of Recycled Aggregate Concrete in High-Temperature and Complex Environments

Recycled aggregate concrete refers to a new type of concrete material made by processing waste concrete materials through grading,crushing,and cleaning,and then mixing them with cement,water,and other materials in a certain gradation or proportion.This type of concrete is highly suitable for modern construction waste disposal and reuse and has been widely used in various construction projects.It can also be used as an environmentally friendly permeable brick material to promote the development of modern green buildings.However,practical applications have found that compared to ordinary concrete,the durability of this type of concrete is more susceptible to high-temperature and complex environments.Based on this,this paper conducts theoretical research on its durability in high-temperature and complex environments,including the current research status,existing problems,and application prospects of recycled aggregate concrete’s durability in such environments.It is hoped that this analysis can provide some reference for studying the influence of high-temperature and complex environments on recycled aggregate concrete and its subsequent application strategies.

Experimental Study on Mechanical Properties of Self-Compacting Recycled Concrete

The application of self-compacting recycled concrete can solve the problem of environmental pollution caused by construction waste but its mechanical properties have not been unified and need further study.The strength of recycled concrete is unstable,and its performance still needs further study.The combination of fixed sand and stone volume method and free water cement ratio method is used to determine the mix ratio of self-compacting recycled concrete.24 sets of slump expansion tests and 24 sets of cube axial compression tests were carried out to study the effect of recycled aggregate replacement rate on the flow performance and axial compressive strength of self-compacting recycled concrete,and the performance conversion formula of self-compacting recycled concrete was given.The results show that with the increase of the regenerated coarse aggregate substitution rate,the fluidity and filling property of the self-compacting regenerated concrete mix decreased.The failure of self-compacting recycled concrete is mainly due to the failure of strength between old mortar and new mixture.As the substitution rate increases from 0 to 100%,the axial compressive strength decreases by 15.2%.

Utilization of Recycled Concrete Powder in Cement Composite:Strength,Microstructure and Hydration Characteristics

Recycled concrete powder(RCP)is used more and more in cement-based materials,but its influence on the hydration process is still unclear.Therefore,this paper studied the influence of recycled concrete powder(RCP)on the hydration process of cement and provides a theoretical basis for the hydration mechanism of cement composite materials.The hydration heat method was used to systematically analyze the thermal evolution process of cement paste with or without RCP.Hydration products were identified using X-ray diffraction(XRD)and thermal analysis(TG–DSC).The pore structure change of cement pastes was analyzed by mercury intrusion porosimetry(MIP)method.The mechanical properties of mortar were also evaluated.Four recycled concrete powder(RCP)dosages,such as 10%,20%,30%and 40%are considered.The results indicate that with the increase of RCP content,the hydration heat release rate and total heat release amount of paste decreased,but the second heat release peak of hydration reaction advanced;the proportion of harmful pores and more harmful pores increases,the total porosity and the most probable pore size also increase;the fluidity and mechanical strength of mortar decrease,but the crystal type of hydration products does not change.When the content of RCP is less than 20%,it has little effect on the mechanical strength of mortar.When fly ash and silica fume are mixed,the fluidity difference of mortar decreases,and when the content of fly ash is the highest,the fluidity of mortar is the highest,which is 15mm higher than that of the control group.When RCP content is 15%,fly ash and silica fume content is 15%(FA:SF=3:2),the hydration heat of the clean pulp is the highest among all the compounding ratios,and the hydration reaction is the most complete;the proportion of harmless pores increased by 9.672%,the proportion of harmful pores and more harmful pores decreased,and the compactness of material structure increased;the compressive strength and flexural strength of mortar reached 50.6 MPa and 9 MPa respectively,both exceeding those of control mortar.

Damage assessment for seismic response of recycled concrete filled steel tube columns

A model for evaluating structural damage of recycled aggregate concrete filled steel tube （RCFST） columns under seismic effects is proposed in this paper. The proposed model takes the lateral deformation and the effect of repeated cyclic loading into account. Available test results were collected and utilized to calibrate the parameters of the proposed model. A seismic test for six RCFST columns was also performed to validate the proposed damage assessment model. The main test parameters were the recycled coarse aggregate （RCA） replacement percentage and the bond-slip property. The test results indicated that the seismic performance of the RCFST member depends on the RCA contents and their damage index increases as the RCA replacement percentage increases. It is also indicated that the damage degree of RCFST changes with the variation of the RCA replacement percentage. Finally, comparisons between the RCA contents, lateral deformation ratio and damage degree were implemented. It is suggested that an improvement procedure should be implemented in order to compensate for the performance difference between the RCFST and normal concrete filled steel tubes （CFST）.

Compressive Strength, Pore Size Distribution and Chloride-ion Penetration of Recycled Aggregate Concrete Incorporating Class-F Fly Ash

The effects of fly ash on the compressive strength, pore size distribution and chloride-ion penetration of recycled aggregate concrete were investigated. Two series of concrete mb：tures were prepared. The concrete mixtures in series I had a water-to-binder ratio and a cement content of 0.55 and 410 kg/ m^3 , respectively. The concrete rnixtures in series II had a water-to-binder ratio and a cement content of 0.45 and 400 kg/ ml respectively. Recycled aggregate was ased as 20% , 50% , and 100% replacements of natural coarse aggregate in the concrete mixtures in both series. In cutdition, fly ash was used as 0% , 25% and 35% by weight replacements of cement. The results show that the compressive strengths of the concrete decreased as the recycled aggregate and the fly ash contents increased. The total porosity and average porosity diameter of the concrete increased us the recycled aggregate content increased. Furtherrruore , an increase in the recycled aggregate content decreased the resistance to chloride ion penetration. Nevertheless, the replacement of cement by 25% fly ush improved the resistance to chloride ion penetration and pore diameters and reduced the total porosity of the recycled aggregate concrete.

Study of the seismic response of a recycled aggregate concrete frame structure

Based on six-degree-of-freedom three-dimensional shaking table tests, the seismic response of a recycled aggregate concrete （RAC） frame was obtained. The analysis results indicate that the maximum story shear force and overturning moment reduce proportionally along the height of the model under the same earthquake wave. The story shear force, base shear coefficient and overturning moment of the structure increase progressively as the acceleration amplitude increases. The base shear coefficient is primarily controlled by the peak ground acceleration （PGA）. The relationships between the PGA and the shear coefficient as well as between the PGA and the dynamic amplification factor are obtained by mathematical fitting. The dynamic amplification factor decreases rapidly at the elastic-plastic stage, but decreases slowly with the development of the elastic-plasticity stage. The results show that the RAC frame structure has reasonable deformability when compared with natural aggregate concrete frame structures. The maximum inter-story drift ratios of the RAC frame model under frequent and rare intensity 8 test phases are 1/266 and 1/29, respectively, which are larger than the allowable value of 1/500 and 1/50 according to Chinese seismic design requirements. Nevertheless, the RAC frame structure does not collapse under base excitations with PGAs from 0.066 g up to 1.170 g.

Shaking table experimental study of recycled concrete frame-shear wall structures

In this study, four 1/5 scaled shaking table tests were conducted to investigate the seismic performance of recycled concrete frame-shear wall structures with different recycled aggregates replacement rates and concealed bracing detail. The four tested structures included one normal concrete model, one recycled coarse aggregate concrete model, and two recycled coarse and fi ne aggregate concrete models with or without concealed bracings inside the shear walls. The dynamic characteristics, dynamic response and failure mode of each model were compared and analyzed. Finite element models were also developed and nonlinear time-history response analysis was conducted. The test and analysis results show that the seismic performance of the recycled coarse aggregate concrete frame-shear wall structure is slightly worse than the normal concrete structure. The seismic resistance capacity of the recycled concrete frame-shear wall structure can be greatly improved by setting up concealed bracings inside the walls. With appropriate design, the recycled coarse aggregate concrete frame-shear wall structure and recycled concrete structure with concealed bracings inside the walls can be applied in buildings.

Seismic behavior of large-scale FRP–recycled aggregate concrete–steel columns with shear connectors

The application of fi ber-reinforced polymer (FRP) composites for the development of high-performance composite structural systems has received signifi cant recent research attention. A composite of FRP–recycled aggregate concrete (RAC)–steel column (FRSC), consisting of an outer FRP tube, an inner steel tube and annular RAC fi lled between two tubes, is proposed herein to facilitate green disposal of demolished concrete and to improve the ductility of concrete columns for earthquake resistance. To better understand the seismic behavior of FRSCs, quasi-static tests of large-scale basalt FRSCs with shear connectors were conducted. The infl uence of the recycled coarse aggregate (RCA) replacement percentage, shear connectors and axial loading method on the lateral load and deformation capacity, energy dissipation and cumulative damage were analyzed to evaluate the seismic behavior of FRSCs. The test results show that FRSCs have good seismic behavior, which was evidenced by high lateral loads, excellent ductility and energy dissipation capacity, indicating RAC is applicable in FRSCs. Shear connectors can signifi cantly postpone the steel buckling and increase the lateral loads of FRSCs, but weaken the deformation capacity and energy dissipation performance.

Effects of Polypropylene Fibers on the Physical and Mechanical Properties of Recycled Aggregate Concrete

The viability of using polypropylene fibers(PPF) in concrete was largely studied. Yet, few of the existing research studies investigated the effects of PPF on the properties of concrete containing recycled concrete aggregate(RCA). Mixes with different RCA replacement ratios and different PPF content were designed and tested. The test results showed that the addition of PPF did not change significantly the compressive strength and the density of the concrete, but slightly decreased its modulus of elasticity and Poisson’s ratio. The drop in the splitting tensile strength and the flexural strength due to RCA inclusions was to a large extent compensated by the PPF addition. The water absorption decreased and the percent voids increased with increased PPF addition. Correlations between the RCA content, the PPF content and the properties of concrete were studied. Useful regression models were proposed to predict the properties of concrete in relevant ranges of RCA and PPF content.

Effect of waste concrete with different strength on mechanical properties of recycled fine aggregate mortar

The influence of source concrete (SC) with different compression strengths on the workability and mechanical properties of recycled mortar made with river sand substituted by 100% fine recycled concrete aggregates (FRCA) is experimentally investigated. The basic physical performance test shows that with the increase in SC strength, FRCA exhibit lower water absorption and crushing index, meanwhile keeping higher densities. Mechanical property tests, including compressive strength, flexural strength and uniaxial compressive stress-strain tests, show that compressive strength,flexural strength and elasticity modulus of recycled sand mortars increase roughly with the increase in SC strength. The proposed mixture design method demonstrates that all of the components can be kept as the same as those in natural mortar mixture design and FRCA must be pre-wetted before making mortar mixture. Meanwhile, the reuse of higher strength SC can ensure that recycled mortar mixtures are able to achieve similar mechanical performance when compared to natural mortar designs.

Freeze-thaw Durability of Recycled Aggregate Concrete:An Overview

The characteristics of surface appearances,mass loss,relative dynamic modulus of elasticity and strength loss of different recycled aggregate concretes(RAC) exposed to freeze-thaw cycles were analyzed.It was found that the freeze-thaw resistance of RAC could be determined by the recycled aggregate compositions and admixtures.Both the saturation degree and the air void structure were the key factors influencing the freeze-thaw damage on concrete.Some major proposed freeze-thaw deterioration mechanisms were utilized to interpret the freeze-thaw damage on recycled aggregate concrete.Meanwhile,some potential measures to enhance the freeze-thaw resistance of concrete were summarized and discussed.

Effect of Recycled Coarse Aggregate on Concrete Compressive Strength

The effect of recycled coarse aggregate on concrete compressive strength was investigated based on the concrete skeleton theory. For this purpose, 30 mix proportions of concrete with target cube compressive strength ranging from 20 to 60 MPa were cast with normal coarse aggregate and recycled coarse aggregate from different strength parent concretes. Results of 28-d test show that the strength of different types of recycled aggregate affects the concrete strength obviously. The coarse aggregate added to mortar matrix plays a skeleton role and improves its compressive strength. The skeleton effect of coarse aggregate increases with the increasing strength of coarse aggregate, and normal coarse aggregate plays the highest, whereas the lowest concrete strength occurs when using the weak recycled coarse aggregate. There is a linear relationship between the concrete strength and the corresponding mortar matrix strength. Coarse aggregate skeleton formula is established, and values from experimental tests match the derived expressions.

The Complete Stress-strain Curve of Recycled Aggregate Concrete under Uniaxial Compression Loading

The mechanical performance of recycled aggregate concrete （RAC） is investigated. An experiment on the complete stress-strain curve under uniaxial compression loading of RAC is carried out. The experimental results indicate that the peak stress, peak strain, secant modulus of the peak point and original point increase with the strength grade of RAC enhanced. On the contrary, the residual stress of RAC decreases with the strength grade enhancing, and the failure of RAC is often broken at the interface between the recycled aggregate and the mortar matrix. Finally, the constitutive model of stress-strain model of RAC has been constituted, and the results from the constitutive model of stress-strain meet the experiment results very well.

Effect of flexural loading on degradation progress of recycled aggregate concrete subjected to sulfate attack and wetting-drying cycles

The degradation progress of recycled aggregate concrete(RAC) subjected to sulfate attack under wetting-drying cycles and flexural loading is studied. Three different stress ratios(0, 0.3 and 0.5) were applied in this test. The variations of relative dynamic elastic modulus Erd and water-soluble SO2-4 contents in RAC were used to evaluate degradation progress. The changes in mineral products and microstructures of interior concrete were investigated by means of X-ray diffraction(XRD), the environmental scanning electron microscope(ESEM) and X-ray computed tomography(X-CT). The results indicate that flexural loading accelerates the degradation of RAC under sulfate attack and wetting-drying cycles by expediting the transmission of SO2-4 into interior concrete. Furthermore, the accelerated effect of flexural loading is more obvious with the increase of stress ratio, that is because higher stress ratios can accelerate the extension of microcracks and generate more channels for the transmission of SO2-4. Also, more expansive products(gypsum and ettringite) are generated by the reaction of Ca(OH)2 with SO2-4, which can further accelerate the degradation of RAC.

Effect of Curing Age on Chloride Diffusion Coefficient of Recycled Aggregate Concrete Subjected to Compressive Stresses

The effect of curing age on chloride diffusion coefficient of recycled aggregate concrete subjected to different compressive stresses was investigated.A compression loading setup was both designed and fabricated.The chloride diffusion coefficients of recycled aggregate concrete under compressive stresses were measured by the rapid chloride ion migration(RCM)method.The experimental results show that the chloride diffusion coefficients of recycled aggregate concrete(RAC)under different compressive stress ratios generally decrease with the increase of curing age.For RAC subjected to the same compressive stress ratios,the chloride diffusion coefficients approximately have power functions with curing ages and the relationship models are proposed.Moreover,the influence of curing age on chloride diffusion coefficient firstly decreases and then increases as the compressive stress ratio increases.