In this study,lignin-containing microfibrillated cellulose(MFC)was prepared from corncob residue after xylose extraction via co-grinding with calcium hydroxide.The product was then compared with the MFC obtained by di...In this study,lignin-containing microfibrillated cellulose(MFC)was prepared from corncob residue after xylose extraction via co-grinding with calcium hydroxide.The product was then compared with the MFC obtained by direct grinding and applied to strengthen paper.The chemical composition and morphological structure analysis results showed that the corncob residue can be used to prepare lignin-containing MFC and does not require further purification.Moreover,the co-grinding with calcium hydroxide is easier to fibrillate corncob residue.The MFC obtained by cogrinding with calcium hydroxide had a higher aspect ratio,and its surface was coated with calcium carbonate nanoparticles.MFCs obtained by both the methods mentioned above had an obvious strengthening effect on paper.Compared with the paper without MFC,the tensile index,elongation,burst index,and folding strength of the paper with MFC obtained by co-grinding with calcium hydroxide significantly increased by 17.5%,22.1%,19.5%,and 157.1%,respectively.This study provides a novel idea for the utilization of corncob residue,which may enhance the value and promote the comprehensive utilization of corn by-products.展开更多
基金The authors are grateful for financial support from the National Key Research and Development Program of China(2017YFE0102500 and 2017YFB0307901).
文摘In this study,lignin-containing microfibrillated cellulose(MFC)was prepared from corncob residue after xylose extraction via co-grinding with calcium hydroxide.The product was then compared with the MFC obtained by direct grinding and applied to strengthen paper.The chemical composition and morphological structure analysis results showed that the corncob residue can be used to prepare lignin-containing MFC and does not require further purification.Moreover,the co-grinding with calcium hydroxide is easier to fibrillate corncob residue.The MFC obtained by cogrinding with calcium hydroxide had a higher aspect ratio,and its surface was coated with calcium carbonate nanoparticles.MFCs obtained by both the methods mentioned above had an obvious strengthening effect on paper.Compared with the paper without MFC,the tensile index,elongation,burst index,and folding strength of the paper with MFC obtained by co-grinding with calcium hydroxide significantly increased by 17.5%,22.1%,19.5%,and 157.1%,respectively.This study provides a novel idea for the utilization of corncob residue,which may enhance the value and promote the comprehensive utilization of corn by-products.