The relationships between the selective laser melting(SLM)processing parameters including laser power,scanning speed and hatch space,the relative density,the microstructure,and resulting mechanical properties of Ti-6A...The relationships between the selective laser melting(SLM)processing parameters including laser power,scanning speed and hatch space,the relative density,the microstructure,and resulting mechanical properties of Ti-6Al-2Zr-1Mo-1V alloy were investigated in this work.The result shows that laser power acts a dominant role in determining the relative density in comparison with scanning speed and hatch space.The optimal SLM process window for fabricating relative density>99%samples is located in the energy density range of 34.72 J·mm^(-3)to 52.08 J·mm^(-3),where the laser power range is between 125 W and 175 W.An upward trend is found in the micro-hardness as the energy density is increased.The optimum SLM processing parameters of Ti-6Al-2Zr-1Mo-1V alloy are:laser power of 150 W,scanning speed of 1,600 mm·s^(-1),hatch space of 0.08 mm,and layer thickness of 0.03 mm.The highest ultimate tensile strength,yield strength,and ductility under the optimum processing parameter are achieved,which are 1,205 MPa,1,099 MPa,and 8%,respectively.The results of this study can be used to guide SLM production Ti-6Al-2Zr-1Mo-1V alloy parts.展开更多
High-frequency magnetic properties, such as core loss, coercivity and amplitude permeabilityof a newly-developed nanocrystalline Fe72.5Cu1Nb2V2Si13.5B9 alloy in the wide ranges of f =20-103 kHz, Bm = 0.01~0.6 T and Bm...High-frequency magnetic properties, such as core loss, coercivity and amplitude permeabilityof a newly-developed nanocrystalline Fe72.5Cu1Nb2V2Si13.5B9 alloy in the wide ranges of f =20-103 kHz, Bm = 0.01~0.6 T and Bmf = 10~40 (T.kHz) have been measured. A largeamount of experimental data have been fitted by a computer, thus obtaining several expressionsrepresenting the influence of frequency on high-frequency magnetic properties, that are useful inpractical applications.展开更多
基金supported by Liaoning Doctoral Research Start-up Fund project(Grant No.2023-BS-215).
文摘The relationships between the selective laser melting(SLM)processing parameters including laser power,scanning speed and hatch space,the relative density,the microstructure,and resulting mechanical properties of Ti-6Al-2Zr-1Mo-1V alloy were investigated in this work.The result shows that laser power acts a dominant role in determining the relative density in comparison with scanning speed and hatch space.The optimal SLM process window for fabricating relative density>99%samples is located in the energy density range of 34.72 J·mm^(-3)to 52.08 J·mm^(-3),where the laser power range is between 125 W and 175 W.An upward trend is found in the micro-hardness as the energy density is increased.The optimum SLM processing parameters of Ti-6Al-2Zr-1Mo-1V alloy are:laser power of 150 W,scanning speed of 1,600 mm·s^(-1),hatch space of 0.08 mm,and layer thickness of 0.03 mm.The highest ultimate tensile strength,yield strength,and ductility under the optimum processing parameter are achieved,which are 1,205 MPa,1,099 MPa,and 8%,respectively.The results of this study can be used to guide SLM production Ti-6Al-2Zr-1Mo-1V alloy parts.
文摘High-frequency magnetic properties, such as core loss, coercivity and amplitude permeabilityof a newly-developed nanocrystalline Fe72.5Cu1Nb2V2Si13.5B9 alloy in the wide ranges of f =20-103 kHz, Bm = 0.01~0.6 T and Bmf = 10~40 (T.kHz) have been measured. A largeamount of experimental data have been fitted by a computer, thus obtaining several expressionsrepresenting the influence of frequency on high-frequency magnetic properties, that are useful inpractical applications.