Influence of Non-smooth Surface on Tribological Properties of Glass Fiber-epoxy Resin Composite Sliding against Stainless Steel under Natural Seawater Lubrication

With the development of bionics, the bionic non-smooth surfaces are introduced to the field of tribology. Although non-smooth surface has been studied widely, the studies of non-smooth surface under the natural seawater lubrication are still very fewer, especially experimental research. The influences of smooth and non-smooth surface on the frictional properties of the glass fiber-epoxy resin composite（GF/EPR） coupled with stainless steel 316 L are investigated under natural seawater lubrication in this paper. The tested non-smooth surfaces include the surfaces with semi-spherical pits, the conical pits, the cone-cylinder combined pits, the cylindrical pits and through holes. The friction and wear tests are performed using a ring-on-disc test rig under 60 N load and 1000 r/min rotational speed. The tests results show that GF/EPR with bionic non-smooth surface has quite lower friction coefficient and better wear resistance than GF/EPR with smooth surface without pits. The average friction coefficient of GF/EPR with semi-spherical pits is 0.088, which shows the largest reduction is approximately 63.18% of GF/EPR with smooth surface. In addition, the wear debris on the worn surfaces of GF/EPR are observed by a confocal scanning laser microscope. It is shown that the primary wear mechanism is the abrasive wear. The research results provide some design parameters for non-smooth surface, and the experiment results can serve as a beneficial supplement to non-smooth surface study.

Experimental Study on Influence of Dimples on Lubrication Performance of Glass Fiber-epoxy Resin Composite under Natural Seawater Lubrication

Bionic non-smooth surface is widely applied in metal and ceramics materials. In order to introduce this technology to high pressure seawater pump, the influence of bionic non-smooth surface on the engineering plastics used in pump should be investigated. The comparative tests are carried out with a ring-on-disc configuration under 800, 1000, 1200 and 1400 r/min in order to research the influence of the bionic non-smooth surface on glass fiber-epoxy resin composite（GF/EPR） under natural seawater lubrication. The disc surfaces are textured with five kinds of pits, which are semi-spherical, conical, cone-cylinder combined, cylindrical pits and through holes, respectively. A smooth surface is tested as reference. The results show that the lubrication performance of dimpled GF/EPR sample is much better than that of the smooth sample under all rotational speeds. The semi-spherical pits surface has more obvious friction reduction than the others, which shows that the least reduction is approximately 43.29% of smooth surface under 1200 r/rain. However, the wear level is only marginally influenced by dimples. The surface morphology investigations disclose severe modifications caused by abrasive wear primarily. The results are helpful to vary friction properties of GF/EPR by non-smooth surface, or provide references to the design of non-smooth surfaces under certain condition.

Research on properties of hollow glass microspheres/epoxy resin composites applied in deep rock in-situ temperature-preserved coring

Deep petroleum resources are in a high-temperature environment.However,the traditional deep rock coring method has no temperature preserved measures and ignores the effect of temperature on rock porosity and permeability,which will lead to the distortion of the petroleum resources reserves assessment.Therefore,the hollow glass microspheres/epoxy resin(HGM/EP)composites were innovatively proposed as temperature preserved materials for in-situ temperature-preserved coring(ITP-Coring),and the physical,mechanical,and temperature preserved properties were evaluated.The results indicated that:As the HGM content increased,the density and mechanical properties of the composites gradually decreased,while the water absorption was deficient without hydrostatic pressure.For composites with 50 vol%HGM,when the hydrostatic pressure reached 60 MPa,the water absorption was above 30.19%,and the physical and mechanical properties of composites were weakened.When the hydrostatic pressure was lower than 40 MPa,the mechanical properties and thermal conductivity of composites were almost unchanged.Therefore,the composites with 50 vol%HGM can be used for ITPCoring operations in deep environments with the highest hydrostatic pressure of 40 MPa.Finally,to further understand the temperature preserved performance of composites in practical applications,the temperature preserved properties were measured.An unsteady-state heat transfer model was established based on the test results,then the theoretical change of the core temperature during the coring process was obtained.The above tests results can provide a research basis for deep rock in-situ temperature preserved corer and support accurate assessment of deep petroleum reserves.

Thermal and Mechanical Properties of Epoxy Resin Modified with N-(4-hydroxyphenyl)terahydrophthalic Anhydrideimide

A novel epoxy-imide resin based on diglycidyl ether of bisphenol-A and N-（4-hydroxyphenyl）terahydrophthalic anhydrideimide（HTAM） was synthesized. The structural characterization of the epoxy-imide resin was conducted by FT-IR spectra. 4,4＇-diaminodiphneylmethane（DDM） was used as a curing agent for the epoxy-imide resin. The thermal properties of the cured resin were evaluated with dynamic mechanical analyses（DMA） and thermogravimetric analysis（TGA）. The results showed that the cured resin exhibited a high glass transition temperature（Tg） of 186 ℃ when the molar amount of HTAM was 0.04 mol in the resin. The yields of the cured resin at 800 ℃ raised from 16.45% to 19.41%. The flexural properties were also measured, the flexural strength raised from 79.4 to 95.7 MPa, and the flexural modulus exhibited from 2.6 to 3.0 GPa.

MICROLEAKAGE OF CLASS V RESIN-MODIFIED GLASS IONOMER CEMENT AND COMPOMER RESTORATIONS IN VITRO

Objective To assess the microleakage of Class V restorations made with two resin-modified glass ionomer cements （RMGICs） and two polyacid-modified composite resins （PMCRs）. Methods Restorations of the four materials （ GC Fuji Ⅱ LC, Vitremer^TM, Dyract AP and F2000^TM ） were placed in facial Class V cavity preparations in forty noncarious human molar teeth. Teeth were randomly assigned to 4 experimental groups of 10 teeth each. After thermal cycling（ ×20, 5 -55℃ ） , the interface between dentin and restorations was spattercoated with gold and observed under scanning electron microscopy （SEM）. Then the square and average width of margin gaps of central 1/3 interface were recorded with image analysis software. Results The data indicated no significant differences between all the restorative materials for both occlusal and gingival margins. Further analysis revealed there were statistically significant differences between occlusal margins and gingival margins for VitremerTM and Dyract AP, respectively. Conclusion None of the tested materials guaranteed margins free of microleakage. Resin-modified glass ionomer cements showed similar margin gaps to the polyacid-modified composite resins tested.

Research on thermal insulation materials properties under HTHP conditions for deep oil and gas reservoir rock ITP-Coring

Deep oil and gas reservoirs are under high-temperature conditions,but traditional coring methods do not consider temperature-preserved measures and ignore the influence of temperature on rock porosity and permeability,resulting in distorted resource assessments.The development of in situ temperaturepreserved coring(ITP-Coring)technology for deep reservoir rock is urgent,and thermal insulation materials are key.Therefore,hollow glass microsphere/epoxy resin thermal insulation materials(HGM/EP materials)were proposed as thermal insulation materials.The materials properties under coupled hightemperature and high-pressure(HTHP)conditions were tested.The results indicated that high pressures led to HGM destruction and that the materials water absorption significantly increased;additionally,increasing temperature accelerated the process.High temperatures directly caused the thermal conductivity of the materials to increase;additionally,the thermal conduction and convection of water caused by high pressures led to an exponential increase in the thermal conductivity.High temperatures weakened the matrix,and high pressures destroyed the HGM,which resulted in a decrease in the tensile mechanical properties of the materials.The materials entered the high elastic state at 150℃,and the mechanical properties were weakened more obviously,while the pressure led to a significant effect when the water absorption was above 10%.Meanwhile,the tensile strength/strain were 13.62 MPa/1.3%and 6.09 MPa/0.86%at 100℃ and 100 MPa,respectively,which meet the application requirements of the self-designed coring device.Finally,K46-f40 and K46-f50 HGM/EP materials were proven to be suitable for ITP-Coring under coupled conditions below 100℃ and 100 MPa.To further improve the materials properties,the interface layer and EP matrix should be optimized.The results can provide references for the optimization and engineering application of materials and thus technical support for deep oil and gas resource development.

Passive daytime radiative cooling coatings with renewable self-cleaning functions

Passive daytime radiative cooling(PDRC)technology is emerging as one of the most promising solutions to the global problem of spacing cooling,but its practical application is limited due to reduced cooling effectiveness caused by daily wear and tear,as well as dirt contamination.To tackle this problem,we report a novel strategy by introducing a renewable armor structure for prolonging the anti-fouling and cooling effectiveness properties of the PDRC coatings.The armor structure is designed by decorating fluorinated hollow glass microspheres(HGM)inside rigid resin composite matrices.The HGM serve triple purposes,including providing isolated cavities for enhanced solar reflectance,reinforcing the matrices to form robust armored structures,and increasing thermal emittance.When the coatings are worn,the HGM on the surface expose their concave cavities with numerous hydrophobic fragments,generating a highly rough surface that guarantee the superhydrophobic function.The coatings show a high sunlight reflectance(0.93)and thermal emittance(0.94)in the long-wave infrared window,leading to a cooling of 5℃ below ambient temperature under high solar flux(∼900 W/m^(2)).When anti-fouling functions are reduced,they can be regenerated more than 100 cycles without compromising the PDRC function by simple wearing treatment.Furthermore,these coatings can be easily prepared using a one-pot spray method with low-cost materials,exhibit strong adhesion to a variety of substrates,and demonstrate exceptional environmental stability.Therefore,we anticipate their immediate application opportunities for spacing cooling.