The successful manufacture of thick composites is challenging since the highly exothermic nature of thermoset resins and limited temperature control make avoiding the onset of detrimental thermal gradients within the ...The successful manufacture of thick composites is challenging since the highly exothermic nature of thermoset resins and limited temperature control make avoiding the onset of detrimental thermal gradients within the composite relatively difficult.This phenomenon is mainly caused by exothermic heat reactions.The so-called Michaud's model has been largely used in the literature to reduce the gap between experience and simulation with regard to the effective prediction of the temperature cycle in these processes.In this work,another solution is proposed to simulate the curing process for thick composites,namely preheating the resin to activate the curing reaction before resin injection into the mold.A good agreement between the experiment and the simulation is found.Moreover,in order to minimize the thermal gradient in the final composite,the thermophysical properties of the fiber and the torque(temperature,time)of the Plate have been varied leading to interesting results.展开更多
The chemorheological behaviors of a low viscosity epoxy resin system （Huntsman 1564/3486） for vacuum infusion moulding process （VIMP） were studied with viscosity experiments.The dual-Arrhenius rheological model an...The chemorheological behaviors of a low viscosity epoxy resin system （Huntsman 1564/3486） for vacuum infusion moulding process （VIMP） were studied with viscosity experiments.The dual-Arrhenius rheological model and the engineering viscosity model were established and compared with the experimental data.The result showed that the viscosity in the earlier stage calculated by dual-Arrhenius model were smaller than the experimental data,while the data calculated by the engineering model were larger.Combining the two models together can predict the rheological behaviors of the resin system in a more credible manner.The processing windows of the resin system for VIMP were determined based on the two models.The optimum processing temperature is 30-45 ℃.展开更多
A three-dimensional finite element analysis of process-induced residual stress in resin transfer molding (RTM) process is presented. The finite element method (FEM) was employed to solve the coupled equations involved...A three-dimensional finite element analysis of process-induced residual stress in resin transfer molding (RTM) process is presented. The finite element method (FEM) was employed to solve the coupled equations involved in the transient heat transfer and the cure kinetics of the resin, and the distributions of internal temperature and cure degree of the composite at any instant time were obtained. The self-consistent field micro-mechanics model was used to predict the cure-dependent mechanical properties of the composites. Thermal expansion and cure shrinkage were included in the analysis. The thermo-elastic mechanical governing equations were solved using the incremental stress-strain relationship based FEM and the residual stress development was predicted. The present results were validated by the comparisons with the pertinent literature. The numerical example of a half cylinder was presented. The results show that it is necessary to carry out the three-dimensional analysis due to the complex distributions of temperatures, cure degrees and process-induced stress for thick parts, which can be predicted at any point within composite structures in the present analysis.展开更多
Sub-micron sized phenolic epoxy resin waterborne particles were prepared by phase inversion emulsification. Micro-phase separation occurred during the curing process at high temperature. The as-prepared samples posses...Sub-micron sized phenolic epoxy resin waterborne particles were prepared by phase inversion emulsification. Micro-phase separation occurred during the curing process at high temperature. The as-prepared samples possessed one glass transition temperature （Tg） and two exothermal processes during DSC heating scannings. After being thermally treated above the exothermal peak temperature, they possessed two glass transition temperatures with the disappearance of exothermal peaks, whilst a core/shell structure was formed. This was likely related with the outward diffusion of reactive oligomers to the outer layer of particles.展开更多
The rheological behavior of a low epoxy resin system-SR8100/SD8734 for RTM in aviation industry was studied with viscosity experiments. The dual-Arrhenius rheological model and the improved engineering viscosity model...The rheological behavior of a low epoxy resin system-SR8100/SD8734 for RTM in aviation industry was studied with viscosity experiments. The dual-Arrhenius rheological model and the improved engineering viscosity model were introduced and compared with the experimental data. The results indicated that the viscosity in the earlier stage calculated by dual-Arrhenius model matched the experimental data. As rising to 400 m.Pas, the viscosity calculated by the improved engineering model was closer to the experimental data. The processing windows of the resin system for RTM were determined by combining the two models, which could predict the theological behavior of the resin system in a more credible way. 30-45 ℃ was the optimum processing temperature.展开更多
在树脂传递模塑(Resin transfer molding,RTM)工艺中,边缘效应很容易导致制件产生空隙、干斑等缺陷,其根本原因是在纤维增强体和模具模腔之间的间隙区域树脂的流动阻力小,使得树脂在这一区域流动速度更快。基于达西定律并结合流体体积(V...在树脂传递模塑(Resin transfer molding,RTM)工艺中,边缘效应很容易导致制件产生空隙、干斑等缺陷,其根本原因是在纤维增强体和模具模腔之间的间隙区域树脂的流动阻力小,使得树脂在这一区域流动速度更快。基于达西定律并结合流体体积(Volume of Fluid,VOF)界面追踪方法建立了树脂在纤维增强体中的流动模型,开展RTM工艺边缘效应的数值模拟研究,模型可以准确模拟边缘效应的影响,同时研究树脂粘度及树脂注射压力等工艺参数对于流动时间的影响。研究结果可以对RTM工艺的改善优化提供帮助。展开更多
文摘The successful manufacture of thick composites is challenging since the highly exothermic nature of thermoset resins and limited temperature control make avoiding the onset of detrimental thermal gradients within the composite relatively difficult.This phenomenon is mainly caused by exothermic heat reactions.The so-called Michaud's model has been largely used in the literature to reduce the gap between experience and simulation with regard to the effective prediction of the temperature cycle in these processes.In this work,another solution is proposed to simulate the curing process for thick composites,namely preheating the resin to activate the curing reaction before resin injection into the mold.A good agreement between the experiment and the simulation is found.Moreover,in order to minimize the thermal gradient in the final composite,the thermophysical properties of the fiber and the torque(temperature,time)of the Plate have been varied leading to interesting results.
基金Supported by the 863 National Project of China (No.2007AA03Z563)the Specialized Project of the HUNAN Province of China(No.2006GK1002)
文摘The chemorheological behaviors of a low viscosity epoxy resin system （Huntsman 1564/3486） for vacuum infusion moulding process （VIMP） were studied with viscosity experiments.The dual-Arrhenius rheological model and the engineering viscosity model were established and compared with the experimental data.The result showed that the viscosity in the earlier stage calculated by dual-Arrhenius model were smaller than the experimental data,while the data calculated by the engineering model were larger.Combining the two models together can predict the rheological behaviors of the resin system in a more credible manner.The processing windows of the resin system for VIMP were determined based on the two models.The optimum processing temperature is 30-45 ℃.
基金the National Natural Science Foundation of China(Grant No.10502016)Development Program for Outstanding Young Teachers in Harbin Institute of Technology(Grant No.HITQNJS.2006.020)
文摘A three-dimensional finite element analysis of process-induced residual stress in resin transfer molding (RTM) process is presented. The finite element method (FEM) was employed to solve the coupled equations involved in the transient heat transfer and the cure kinetics of the resin, and the distributions of internal temperature and cure degree of the composite at any instant time were obtained. The self-consistent field micro-mechanics model was used to predict the cure-dependent mechanical properties of the composites. Thermal expansion and cure shrinkage were included in the analysis. The thermo-elastic mechanical governing equations were solved using the incremental stress-strain relationship based FEM and the residual stress development was predicted. The present results were validated by the comparisons with the pertinent literature. The numerical example of a half cylinder was presented. The results show that it is necessary to carry out the three-dimensional analysis due to the complex distributions of temperatures, cure degrees and process-induced stress for thick parts, which can be predicted at any point within composite structures in the present analysis.
基金This work was financially supported by the National Natural Science Foundation of China(No.20104008).
文摘Sub-micron sized phenolic epoxy resin waterborne particles were prepared by phase inversion emulsification. Micro-phase separation occurred during the curing process at high temperature. The as-prepared samples possessed one glass transition temperature （Tg） and two exothermal processes during DSC heating scannings. After being thermally treated above the exothermal peak temperature, they possessed two glass transition temperatures with the disappearance of exothermal peaks, whilst a core/shell structure was formed. This was likely related with the outward diffusion of reactive oligomers to the outer layer of particles.
基金Funded by the Freedom Explore Program of Central South University(No.721500254)the Hunan Provincial Innovation Foundation for Postgraduate(No.CX2012B052)
文摘The rheological behavior of a low epoxy resin system-SR8100/SD8734 for RTM in aviation industry was studied with viscosity experiments. The dual-Arrhenius rheological model and the improved engineering viscosity model were introduced and compared with the experimental data. The results indicated that the viscosity in the earlier stage calculated by dual-Arrhenius model matched the experimental data. As rising to 400 m.Pas, the viscosity calculated by the improved engineering model was closer to the experimental data. The processing windows of the resin system for RTM were determined by combining the two models, which could predict the theological behavior of the resin system in a more credible way. 30-45 ℃ was the optimum processing temperature.
文摘在树脂传递模塑(Resin transfer molding,RTM)工艺中,边缘效应很容易导致制件产生空隙、干斑等缺陷,其根本原因是在纤维增强体和模具模腔之间的间隙区域树脂的流动阻力小,使得树脂在这一区域流动速度更快。基于达西定律并结合流体体积(Volume of Fluid,VOF)界面追踪方法建立了树脂在纤维增强体中的流动模型,开展RTM工艺边缘效应的数值模拟研究,模型可以准确模拟边缘效应的影响,同时研究树脂粘度及树脂注射压力等工艺参数对于流动时间的影响。研究结果可以对RTM工艺的改善优化提供帮助。