Corrosion resistance and electrical conductivity of V/Ce conversion coating on magnesium alloy AZ31B

A V/Ce conversion coating was deposited in the surface of AZ31B magnesium alloy in a solution containing vanadate and cerium nitrate.The coating composition and morphology were examined.The conversion coating appears to consist of a thin and cracked coating with a scattering of spherical particles.The corrosion behavior of the substrate and conversion coating was studied by potentiodynamic polarization and electrochemical impedance spectroscopy (EIS).Compared with AZ31B magnesium alloy,the corrosion current density of the conversion coating is decreased by two orders of magnitude.The total impedance of the V/Ce conversion coating rise to 1.6×10^(3)Ω·cm^(2)in contrast with2.2×10^(2)Ω·cm^(2)of the bare AZ31B.In addition,the electrical conductivity of the coating was assessed by conductivity meter and Mott-Schottky measurement.The results reveal a high dependence of the conductivity of the coating on the semiconductor properties of the phase compositions.

Corrosion resistance of in-situ Mg-Al hydrotalcite conversion film on AZ31 magnesium alloy by one-step formation

In situ growth of nano-sized layered double hydroxides （LDH） conversion film on AZ31 alloy was synthesized by a urea hydrolysis method. The formation mechanism of the film was proposed. Firstly, the dissolved Mg2＋ ions deposited into a precursor film consisted of MgCO3 and Mgs（CO3）4（OH）2·4H2O; secondly, the precursor translated into the crystalline Mg（OH）2 in alkaline conditions; finally, the Mg2＋ ions in Mg（OH）z were replaced by A13＋ ions, Mg（OH）2 translated into the more stable LDH structure, simultaneously, the OH- ions in the interlayer were exchanged by CO32-, thus led to the formation of the LDH （Mg6Alz（OHh6CO3·4H2O） film. The results indicated that the LDH film characterized by interlocking plate-like nanostructures and ion-exchange ability significantly improved the corrosion resistance of the AZ31 Mg alloy.

Corrosion resistance of cerium-doped zinc calcium phosphate chemical conversion coatings on AZ31 magnesium alloy

Zinc calcium phosphate （Zn-Ca-P） coating and cerium-doped zinc calcium phosphate （Zn-Ca-Ce-P） coating were prepared on AZ31 magnesium alloy. The chemical compositions, morphologies and corrosion resistance of coatings were investigated through energy-dispersive X-ray spectroscopy （EDS）, X-ray photoelectron spectroscopy （XPS）, X-ray diffraction （XRD）, electron probe micro-analysis （EPMA） and scanning electron microscopy （SEM） together with hydrogen volumetric and electrochemical tests. The results indicate that both coatings predominately contain crystalline hopeite （Zn3（PO4）2·4H2O）, Mg3（PO4）2 and Ca3（PO4）2, and traces of non-crystalline MgF2 and CaF2. The Zn-Ca-Ce-P coating is more compact than the Zn-Ca-P coating due to the formation of CePO4, and displays better corrosion resistance than the Zn-Ca-P coating. Both coatings protect the AZ31 Mg substrate only during an initial immersion period. The micro-galvanic corrosion between the coatings and their substrates leads to an increase of hydrogen evolution rate （HER） with extending the immersion time. The addition of Ce promotes the homogenous distribution of Ca and formation of hopeite. The Zn-Ca-Ce-P coating has the potential for the primer coating on magnesium alloys.

Effect of manganese on the formation of hybrid zirconiumbased conversion coating on low carbon steel surface

This study revealed the effect of Mn on the formation of hybrid zirconium-based conversion coatings(HZCC)on low carbon steel.The XPS results indicated that the Mn compounds on the surface of low carbon steel were mainly MnO and Mn_(2)SiO_(4).Combined with the electrochemical measurements,the corrosion resistance of HZCC showed an increase followed by a decrease with increasing Mn concentration,which was related to the Mn_(2)SiO_(4) and SiO_(2) on the surface of low carbon steel.The excessive Mn concentration resulted in the loss of SiO_(2) and aggregation of Mn_(2)SiO_(4) on the low carbon steel surface,which caused the aggregation of Zr compounds on the surface and reduced the uniformity of the coating.Meanwhile,a moderate amount of Mn addition would be beneficial to increase the adhesion of organic coatings.

Preparation and Corrosion Resistance of Rare Earth Conversion Coatings on AZ91 Magnesium Alloy

The feasibility of forming pollution-free and environmentally benign Ce-based rare earth conversion coatings （short for RECCs） on AZ91 magnesium alloy to enhance corrosion resistance was studied. The effect of optimum processing parameters on corrosion resistance of RECCs, such as density of treating solution, temperature and time of coating formation were discussed. Protective performance of conversion coatings on magnesium alloy was evaluated by moisture/heating test, anodic polarization, etc. The results show that Ce-based RECCs under moisture/heating condition can remain intact, with high coverage and no obvious corrosion phenomenon. Corrosion potential increases and passive phenomenon occurs while current density decreases, therefore Ce-based RECCs can improve corrosion resistance of AZ91 magnesium alloy. The morphology of Ce-based RECCs prepared under optimum process through SEM observation is found to be a few particles coherent to the base coating, and the coating has no cracks and exhibits apparent corrosion resistance during corrosion courses of AZ91 magnesium alloy.

Effect of scratch on corrosion resistance of calcium phosphate conversion coated AZ80 magnesium alloy

In order to analyze the effect of scratch on the corrosion behaviour of a calcium phosphate conversion coating(CPCC)on AZ80,the electrochemical testing,scanning vibrating electrode technique(SVET),immersion test and hydrogen evolution experiment were performed to study the corrosion resistance of AZ80,AZ80 with CPCC and coated AZ80 with scratch.The results show that the coating improves the corrosion resistance of the AZ80 from a current density of(85±4)to(4±1)μA/cm^(2).When the coating was damaged,its protection on substrate would be reduced.The scratch with a length of around 12 mm on the coating reduced the corrosion resistance to a current density of(39±1)μA/cm^(2).In addition,the corrosion occurred initially in the scratch area and the corrosion site first occurred at the junction of the scratch and the coating.Besides,the micro corrosion mechanism of the specimen containing scratch was clarified.

Hydraulic Resistance and Capacitance in the Soil-Plant System

In this paper, the hydraulic resistances and capacitances were evaluated. based on the development of non-(?) model of water flow in the soil-plant system and the simulating experiment work.The results show that the mean hydraulic resistance in the soil-plant system is 6.79×109 MPa·S·m-3; the mean hydraulic capacitance in the system is 5.2×107m3·MPa-1. In the components of hydraulic capacitance in the system, the capacitance in soil (81.8×10-6m3·MPa ) is the biggest and its variability with suii water potential is extremely strong, the capacitance in plant (5.3×10-7m3·MPa-1) is much smaller than that in soil, and the capacitance in shoots (15.5×10-7m3·2MPa-1) is bigger than that in roots (8.4×10-7m3·2MPa-1). An interesting result is that the capacitance in plant is almost equivalent to that in the soil-plant system.

Growth and corrosion resistance of molybdate modified zinc phosphate conversion coatings on hot-dip galvanized steel

The modified zinc phosphate conversion coatings(ZPC) were formed on hot-dip galvanized(HDG) steel when 1.0 g/L sodium molybdate were added in a traditional zinc phosphate solution. The growth performance and corrosion resistance of the modified ZPC were investigated by SEM, open circuit potential(OCP), mass gain, potentiodynamic polarization and electrochemical impedance spectroscopy(EIS) measurements and compared with those of the traditional ZPC. The results show that if sodium molybdate is added in a traditional zinc phosphate solution, the nucleation of zinc phosphate crystals is increased obviously; zinc phosphate crystals are changed from bulky acicular to fine flake and a more compact ZPC is obtained. Moreover, the mass gain and coverage of the modified ZPC are also boosted. The corrosion resistance of ZPC is increased with an increase in coverage, and thus the corrosion protection ability of the modified ZPC for HDG steel is more outstanding than that of the traditional ZPC.

On the uncertainty of interwell connectivity estimations from the capacitance-resistance model

The capacitance-resistance model （CRM） is an alternative to conventional reservoir simulation. CRM, a simplification of complex numerical models, uses production and injection rates to infer a reservoir description. There is no prior geologic model. The principal output of CRM fitting is the fraction of injected fluid （usually water） that is produced at a producer at steady-state. These fractions are interwell connectivities. Interwell connectivities are fundamental information needed to manage waterfloods in oil reservoirs. The data-driven CRM is a fast tool to estimate these parameters in mature fields and allows one to make full use of the dynamic data available. This paper considers the problem of setting an upper bound on the uncertainty of interwell connectivities for linear-constrained models. Using analytical bounds and numerical simulations, we derive a consistent upper limit on the uncertainty of interwell connections that can be used to quantify the information content of a given dataset.

Input signal design to estimate interwell connectivities in mature fields from the capacitance-resistance model

Interwell connectivities are fundamental parameters required to manage waterfloods in oil reservoirs. Data-driven models, such as the capacitance-resistance model （CRM）, are fast tools to estimate these parameters from time-correlations of input （injection rates） and output （production rates） signals. Noise and structure of the input time-series impose limits on the information that can be extracted from a given data-set. This work uses the CRM to study general prescriptions for the design of input signals that enhance the information content of injection/production data in the estimation of well-to-well interactions. Numerical schemes and general features of the optimal input signal strategy are derived for this problem.

Effect of displacement on resistance and capacitance of polyaniline film

This paper investigates the properties of displacement sensors based on polyaniline （PANI） films. About 1 wt% of PANI micropowder is mixed and stirred in a solution of 90 wt% water and 10 wt% alcohol at room temperature. The films of PANI axe deposited from solution by drop-casting on Ag electrodes, which are preliminary deposited on glass substrates. The thicknesses of the PANI films are in the range of 20 μm-80 μm. A displacement sensor with polyaniline film as an active material is designed and fabricated. The investigations showed that, on average, the AC resistance of the sensor decreases by 2 times and the capacitance accordingly increases by 1.6 times as the displacement changes in the range of 0 mm-0.5 mm. The polyaniline is the only active material of the displacement sensor. The resistance and capacitance of the PANI changes under the pressure of spring and elastic rubber, and this pressure is created by the downward movement of the micrometer.

Improving Corrosion Resistance of C_f/Mg Composites using Rare Earth Conversion Coatings

The surface of carbon fiber reinforced Mg matrix (Cf/Mg) composites was modified by treatment of rare earth conversion coating, and nontoxic, non-pollution Ce conversion coatings were prepared. The effect of the coatings on corrosion behaviors of composites was investigated by electrochemical polarization technology and electrochemical impedance spectroscopy (EIS) in 3.5% NaCl solution. The higher Ecorr and lower icorr were obtained by Ce conversion coatings. EIS results showed that the higher values of R2 were obtained by treatment containing CeCl3, the high corrosion resistance occured in treatment containing CeCl3, the low corrosion resistance in uncoating sample, the coating of treatment containing Ce(NO3)3 was medium. The microstructure of Ce conversion coatings was observed by scanning electron microscopy (SEM), and the elements of corresponding for coatings was characterized by energy dispersive spectrometer (EDS). The micro-cracks and Ce-riched spherical particles were characteristics of these coatings.

Corrosion resistance,composition and structure of RE chemical conversion coating on magnesium alloy

Golden yellow rare earths chemical conversion coating was obtained on the surface of magnesium alloy by immersing in cerium sulfate solution.The corrosion resistance of RE conversion coating was evaluated using inmersion test and potentiodynamic polarization measurements in 3.5%NaCl solution.The morphologies of samples before corrosion and after corrosion were observed by SEM.The structures and compositions of the RE conversion coating were studied by means of XPS,XRD and IR.The results show that,the conversion coating consists of mainly two kinds of element Ce and O,the valences of cerium are +3 and +4,and OH exists in the coating.The anti-corrosion property of magnesium alloy is increased obviously by rare earths conversion coating,Its self-corrosion current density decreases and the coating has self-repairing capability in the corrosion process in 3.5%NaCl solution.

Chloromycetin resistance of clinically isolated E coli is conversed by using EGS technique to repress the Chloromycetin acetyl transferase

AIM： To explore the possibility of repression of chloromycetin （Cm） acyl transferase by using external guided sequence （EGS） in order to converse the clinical E coli isolates from Cm- resistant to Cm- sensitive. METHODS： EGS directed against chloromycetin acetyl transferase gene （cat） was cloned to vector pEGFP-C1 which contains the kanamycin （Kin） resistance gene. The recombinant plasmid pEGFP-C1＋EGScatl＋cat2 was constructed and the blank vector without EGS fragment was used as control plasmids. By using the CaCl2 transformation method, the recombinant plasmids were introduced into the clinically isolated Cm resistant but Km sensitive E coli strains. Transformants were screened on LB agar plates containing Kin. Extraction of plasmids and PCR were applied to identify the positive clones. The growth curve of EGS transformed bacteria cultured in broth with Cm resistance was determined by using spectrophotometer at A600. Drug sensitivity was tested in solid culture containing Cm by using KB method. RESULTS： Transformation studies were carried out on 16 clinically isolated Cm-resistant （250 μg/mL of Cm） E colistrains by using pEGFP-C1-EGScatlcat2 recombinant plasmid. Transformants were screened on LB-agar plates containing Km after the transformation using EGS. Of the 16 tested strains, 4 strains were transformed successfully. Transformants with EGS plasmid showed growth inhibition when grown in liquid broth culture containing 200 μg/mL of Cm. In drug sensitivity test, these strains were sensitive to Cm on LB-agar plates containing 200 μg/mL of Cm. Extraction of plasmids and PCR amplification showed the existence of EGS plasmids in these four transformed strains. These results indicated that the Cat of the four clinical isolates had been suppressed and the four strains were converted to Cm sensitive ones. CONCLUSION： The EGS directed against Cat is able to inhibit the expression of Cat, and hence convert Cm- resistant bacteria to Cm-sensitive ones. Thus, the EGS has the capability of converting the phenotype of clinical drug-resistant isolates strains to drug-sensitive ones.

Effect of silicon carbide-based iron catalyst on reactor optimization for non-oxidative direct conversion of methane

The conversion of methane to olefins,aromatics,and hydrogen(MTOAH)can be used to stably obtain hydrocarbons when the effect of the catalytic surface is optimized from the reaction engineering perspective.In this study,Fe/Si C catalysts were packed into a quartz tube reactor.The catalytic surfaces of Si C and the impregnated Fe species decreased the apparent activation energies(E_a)of methane consumption in the blank reactor between 965 and 1020℃.Consequently,the hydrocarbon yield increased by 2.4times at 1020℃.Based on the model reactions of ethane,ethylene,and acetylene mixed with hydrogen in the range of 500-1020℃,an excess amount of Fe in the reactor favored the C-C coupling reaction over the selective hydrogenation of acetylene;consequently,coke formation was favored over the hydrogenation reaction.The gas-phase reactions and catalyst properties were optimized to increase hydrocarbon yields while reducing coke selectivity.The 0.2Fe catalyst-packed reactor(0.26 wt%Fe)resulted in a hydrocarbon yield of 7.1%and a coke selectivity of<2%when the ratio of the void space of the postcatalyst zone to the catalyst space was adjusted to be≥2.Based on these findings,the facile approach of decoupling the reaction zone between the catalyst surface and the gas-phase reaction can provide insights into catalytic reactor design,thereby facilitating the scale-up from the laboratory to the commercial scale.

Phosphate film free of chromate, fluoride and nitrite on AZ31 magnesium alloy and its corrosion resistance

A phosphate solution free of chromate, fluoride and nitrite was prepared and an environment-friendly film was obtained on AZ31 magnesium alloy surface via the chemical deposition method. The morphology, composition, phase structure and its corrosion resistance were studied. The effects of film-forming temperature and free acid on corrosion resistance, microstructure and electrochemical behavior of the film were discussed. The results indicate that the corrosion resistance of AZ31 with the phosphate film was better than blank AZ31 substrate, which was most attributed to the great inhibitive action on the anodic dissolution and cathodic hydrogen evolution of the film.

Electric field assisted chemical conversion process of AZ91D magnesium alloy in HCO_3^-/CO_3^(2-) solution

A new method for synthesizing Mg-Al hydrotalcite conversion coating on AZ91D Mg alloy was developed by the application of electric field （EF）. By using EF technique, the formation time of the coating can be significantly reduced. The SEM results indicate that a continuous and compact Mg-Al hydrotalcite coating is formed on the surface of Mg alloy after short time EF treatment. However, a long time treatment would make the coating partially exfoliate. The corrosion current density （Jcor ） of the coated sample （EF1＋1 h） is approximately two orders of magnitude lower than that of Mg alloy substrate. The test of electrochemical impedance spectroscopy （EIS） and immersion corrosion also suggest that the coating can effectively protect Mg alloy against corrosion.

pH Influence on Performance of Phytic Acid Conversion Coatings on AZ31 Magnesium Alloy in Simulated Body Fluid

Phytic acid （PA） conversion coating on AZ31 magnesium alloy is prepared by a deposition method. pH influences on the formation process, microstructure and properties of the conversion coating are investigated. Electrochemical tests including polarization curve and electrochemical impedance spectroscopy are used to examine the corrosion resistance, and scanning electron microscopy is used to observe the microstructure. The chemical nature of conversion coating is investigated by energy dispersive spectroscopy. And thermodynamic method is used to analyze the optimum pH. The results show that PA conversion coating can improve the corrosion resistance of AZ31 Mg alloy. The maximum efficiency achieves 89.19% when the AZ31 Mg alloy is treated by PA solution with pH=5. It makes the corrosion potential of sample shift positively about 156 mV and corrosion current density is nearly an order of magnitude less than that of the untreated sample. The thermodynamic analysis shows that the corrosion resistance of PA coatings is affected by not only the concentration of PA ion and Mg2＋ but also the release rate of hydrogen.

CORROSION BEHAVIOR OF A ZIRCONIUM-TITANIUM BASED PHOSPHONIC ACID CONVERSION COATING ON AA6061 ALUMINIUM ALLOY

The conversion coating was formed by dipping AA6061 in a fluorotitanate/zirconate acid and amino trimethylene phosphonic acid （ATMP） solution at room temperature. The formation process and the anti-corrosion performance of the conversion coating were investigated using electrochemical test and salt spray test （SST）, respectively. The electrochemical test shows that the Zr/Ti and ATMP coating improves the corrosion resistance of AA6061 as good as the chromate （VI） coating. But the results of SST show that the corrosion resistance of Zr/Ti and ATMP coating is not as good as the chromate （VI） coating. The corrosion area is less than 2% after 72 h.

Preparation and Performance of Rare Earths Chemical Conversion Film on Magnesium Alloy

Golden yellow cerium conversion film was obtained on magnesium alloys surface by immersion method and the preparation parameters were established. The influence of different process parameters on the surface morphology and performance of the conversion film were analyzed by means of SEM and electrochemical method. Formation dynamics about cerium conversion film on magnesium alloy in solution containing cerium salt and the anti-corrosion behavior of the conversion film in 3.5% NaCl solution were studied by electrochemical method respectively. The results shows that the conversion film is more compact at room temperature when concentration of cerium sulfate is 10 g·L-1 in the solution; the open circuit potential of the magnesium sample moves up to positive direction about 100 mV, the surface of conversion film becomes even and lustrous, and the adhesion intensity of conversion film increases when adding aluminum nitrate into the solution containing cerium salt. The pH value of the solution and immersion time of the sample in the solution also affect the surface morphology and anti-corrosion property of the conversion film. After covered by rare earths conversion film, the anti-corrosion property of magnesium alloy is obviously improved. Rare earth conversion film has self-repairing capability in corrosion medium.