The Ag/Mg0.2Zn0.8O/ZnMn2O4/p^+-Si heterostructure devices were fabricated by sol-gel spin coating technique and the resistive switching behavior,conduction mechanism,endurance characteristic,and retention properties ...The Ag/Mg0.2Zn0.8O/ZnMn2O4/p^+-Si heterostructure devices were fabricated by sol-gel spin coating technique and the resistive switching behavior,conduction mechanism,endurance characteristic,and retention properties were investigated.A distinct bipolar resistive switching behavior of the devices was observed at room temperature.The resistance ratio R_(HRS)/RLRS of high resistance state and low resistance state is as large as four orders of magnitude with a readout voltage of 2.0 V.The dominant conduction mechanism of the device is trap-controlled space charge limited current(SCLC).The devices exhibit good durability under 1×10^3cycles and the degradation is invisible for more than 10^6 s.展开更多
The relationship of corrosion resistance and antifouling behavior of 19 Cu alloys exposed to seawater of Qingdao ,Xiamen,Yulin sea areas in China for 1,2,4,8 year intervals was studied .The experiments were carried on...The relationship of corrosion resistance and antifouling behavior of 19 Cu alloys exposed to seawater of Qingdao ,Xiamen,Yulin sea areas in China for 1,2,4,8 year intervals was studied .The experiments were carried on by analyzing the composition of corrosion films formed on the surface of alloy specimens during the immersion time and by using OM,SEM,EDXA and AES experiment methods.The results verify the view point that it is the cuprous oxide film which played an important role in antifouling property of Cu alloys in seawater and throw a light on the view point in details further.The influence of different sea areas on the antifouling property of Cu alloys is also discussed.展开更多
The influence of chemical composition on corrosion resistance of AZ91D magnesium alloys ingots has been investigated. Mass loss method was applied to evaluate the corrosion resistance of AZ91D alloys and the data were...The influence of chemical composition on corrosion resistance of AZ91D magnesium alloys ingots has been investigated. Mass loss method was applied to evaluate the corrosion resistance of AZ91D alloys and the data were analyzed by multiple regression. The results show that the corrosion resistance of this alloy can be improved by increasing Al, Zn and Mn in a certain degree, and will drop with increasing Si and heavy metals (Fe, Cu, Ni). It is found that ingots received from company F should be listed into unusable materials in terms of the corrosion resistance, while among the five suppliers, the only local company E supplied excellent AZ91D magnesium alloy ingots with the best corrosion resistance.展开更多
In this paper, Ni-based alloy composite coating reinforced by Ti (C, N) particles was fabricated on the mild steel through laser cladding technology. The microstrncture of laser cladding layer was analyzed by means ...In this paper, Ni-based alloy composite coating reinforced by Ti (C, N) particles was fabricated on the mild steel through laser cladding technology. The microstrncture of laser cladding layer was analyzed by means of optical microscopy (OM), X-ray diffraction (XRD) and scanning electron microscopy (SEM). The wear resistance test of the coating was evaluated using an M-2000 tester. The results showed that the Ni-based composite coating had an ability of rapid solidification to form dendritic crystals microstructure consisting of Ti ( C, N) particulates uniformly distributed in the matrix. It was found that some Ti( C,N) particles are similar to be round in shape, and the others are irregular. Laser cladding layer reinforced by Ti( C, N) particulates was found to possess good wear resistance property.展开更多
The existing form and reaction mechanism of Sb in heat resistane Mg-Gd-Y-Sb rare earth magnesium alloy were investigated by inductive coupled plasma emission spectroscopy(ICP),scanning electron microscopy(SEM),energy ...The existing form and reaction mechanism of Sb in heat resistane Mg-Gd-Y-Sb rare earth magnesium alloy were investigated by inductive coupled plasma emission spectroscopy(ICP),scanning electron microscopy(SEM),energy dispersive spectroscopy(EDS),and X-ray diffraction(XRD).It is found that Sb tends to form high melting point intermetallics with rare earth elements of Gd and Y.The existing form of Sb is determined to be GdSb and SbY,respectively,which has high melting point(GdSb:2142℃/SbY:1782℃).Meanwhile,the first principle calculation and electronegativity difference calculation were performed to further understand the reaction mechanism.Therefore,the forming heat and binding energy were calculated.The experimental results show that the binding tendency of Sb element to Gd and Y is much stronger than that of it with other elements in this alloy,which results in the formation of high melting point of Gd-Sb and Y-Sb intermetallics,and finally leads to the high temperature resistant further improvement of the Mg-Gd-Y magnesium alloy.展开更多
The influences of rare earth elements(cerium and lanthanum) on the microstructure and phases of Al-3.0 wt%Mg alloys used for electromagnetic shielding wire were characterized by scanning electron microscopy(SEM), ...The influences of rare earth elements(cerium and lanthanum) on the microstructure and phases of Al-3.0 wt%Mg alloys used for electromagnetic shielding wire were characterized by scanning electron microscopy(SEM), energy-dispersive spectroscopy(EDS), X-ray diffraction(XRD) and differential scanning calorimetry(DSC). The mechanical properties and electrical resistivity were also investigated. The results indicated that a certain content of rare earth could improve the purification of the aluminum molten, enhance the strength, and reduce the electrical resistivity of Al-3.0 wt%Mg alloys. The strength reached the top value when RE content was 0.3 wt% while the alloy with 0.2 wt% RE addition had the smallest electrical resistivity. The elongation varied little when RE addition was no more than 0.2 wt%. But the excessive addition of rare earth would be harmful to the microstructure and properties of Al-3.0 wt%Mg alloys.展开更多
A resistance random access memory(RRAM) with a structure of Ag/ZnMn2O4/p-Si was fabricated by magnetron sputtering method. Reliable and repeated switching of the resistance of ZnMn2O4 fi lms was obtained between two...A resistance random access memory(RRAM) with a structure of Ag/ZnMn2O4/p-Si was fabricated by magnetron sputtering method. Reliable and repeated switching of the resistance of ZnMn2O4 fi lms was obtained between two well-defi ned states of high and low resistance with a narrow dispersion and 3V switching voltages. Resistance ratio of the high resistance state and low resistance state was found in the range of around 10^3 orders of magnitude and up to about 10^3 test cycles. The retention time of Ag/ZnMn2O4/p-Si device is longer than 10^6 seconds and the resistance ratio between two states remains higher than 10^3 at room temperature, showing a remarkable reliability performance of the RRAM devices for nonvolatile memory application. The equivalent simulation circuits for HRS(high resistance state) and LRS(low resistance state) were also studied by impedance spectroscopy.展开更多
A new kind of corrosion resistant steelfor cargo oiltanks(COT)was developed.The influences of finalrolling temperature,cooling rate,and finalcooling temperature on microstructure were investigated.The proper rolling...A new kind of corrosion resistant steelfor cargo oiltanks(COT)was developed.The influences of finalrolling temperature,cooling rate,and finalcooling temperature on microstructure were investigated.The proper rolling process parameters were obtained through multi-pass thermalsimulation test.The finalrolling temperature is about 820 ℃,the finalcooling temperature is about 600 ℃,and the cooling rate should be controlled between 10 ℃/s and 20 ℃/s.Based on the above analysis of the results,three groups of rolling samples by thermo mechanicalcontrolprocess are prepared.The tensile strength,yield strength,and toughness of the corrosion resistant steelare measured,which meet the requirements of DH36 steel,it can instruct the actualrolling production.The corrosion behaviour is also researched by weight loss and electrochemicalimpedance spectroscopic method,and it is found that the steelhas good corrosion resistance performance,the best one is No.3 steel,the corrosion rate of which is about 1/4 of the accepted criterion.展开更多
In the present paper,the development of Ti3Al-Nb-Mo-Si alloys for high oxidation resistance is reviewed.Beside of weight gain of alloys with different Nb and Si addition is tested,the evaluation of comprehensive mecha...In the present paper,the development of Ti3Al-Nb-Mo-Si alloys for high oxidation resistance is reviewed.Beside of weight gain of alloys with different Nb and Si addition is tested,the evaluation of comprehensive mechanical properties has been taken,include the room-temperature and 700℃ tensile properties,thermal stability,creep rupture and fracture toughness of the alloys,It has shown that the oxidation resistance and mechanical properties were significantly affected by the variation of Nb and Si contents.The composition with the best balance of properties is Ti-24Al-13Nb-1.5Mo-0.5Si and Ti-24Al-15Nb-1.5Mo,which is mush higher than that of Super,α_2 alloy (Ti-25Al-10Nb-3V-1Mo).展开更多
Four Zr–Cu–Fe–Al-based bulk metallic glasses(BMGs) with Zr contents greater than 65at% and minor additions of Nb were designed and prepared. The glass forming abilities, thermal stabilities, mechanical properties...Four Zr–Cu–Fe–Al-based bulk metallic glasses(BMGs) with Zr contents greater than 65at% and minor additions of Nb were designed and prepared. The glass forming abilities, thermal stabilities, mechanical properties, and corrosion resistance properties of the prepared BMGs were investigated. These BMGs exhibit moderate glass forming abilities along with superior fracture and yield strengths compared to previously reported Zr–Cu–Fe–Al BMGs. Specifically, the addition of Nb into this quaternary system remarkably increases the plastic strain to 27.5%, which is related to the high Poisson's ratio and low Young's and shear moduli. The Nb-bearing BMGs also exhibit a lower corrosion current density by about one order of magnitude and a wider passive region than 316 L steel in phosphate buffer solution(PBS, pH 7.4). The combination of the optimized composition with high deformation ability, low Young's modulus, and excellent corrosion resistance properties indicates that this kind of BMG is promising for biomedical applications.展开更多
The effect of aging on the mechanical properties and microstructures of a new ZG12Cr9 MolColNiVNbNB ferritic heat resistant steel was investigated in this work to satisfy the high steam parameters of the ultra-supercr...The effect of aging on the mechanical properties and microstructures of a new ZG12Cr9 MolColNiVNbNB ferritic heat resistant steel was investigated in this work to satisfy the high steam parameters of the ultra-supercritical power plant.The results show that the main precipitates during aging are Fe(Cr,Mo)23C6,V(Nb)C,and(Fe2Mo) Laves in the steel.The amounts of the precipitated phases increase during aging,and correspondingly,the morphologies of phases are similar to be round.Fe(Cr,Mo)23C6 appears along boundaries and grows with increasing temperature.In addition,it is revealed that the martensitic laths are coarsened and eventually happen to be polygonization.The hardness and strength decrease gradually,whereas the plasticity of the steel increases.What's more,the hardness of this steel after creep is similar to that of other 9%-12%Cr ferritic steels.Thus,ZG12Cr9 MolColNiVNbNB can be used in the project.展开更多
By oxidation weight gain method, four groups of Fe-based superalloys with different content of chromium, aluminium and silicon were tested at 1 200 ℃ for 500 hours. According to the oxidation weight gains, the oxidat...By oxidation weight gain method, four groups of Fe-based superalloys with different content of chromium, aluminium and silicon were tested at 1 200 ℃ for 500 hours. According to the oxidation weight gains, the oxidation kinetic curves were plotted, and the equations were regressed by least square method and non-linear curve fitting. The effects of different scale compositions on the morphology and oxidation kinetic law were studied further by analysis of X-ray diffraction (XRD) and scanning electron microscope (SEM). It is found that the compounded scale is composed of Cr2O3, Al2O3, SiO2 and FeCr2O4, with compact structure and fine grains, possessing complete oxidation resistance at 1 200 ℃, and the oxidation kinetic curve follows the power function of y=axb (a0, 0b1). When the compounded scale lacks Al2O3 or SiO2, it becomes weak in oxidation resistance, but the oxidation kinetic curve still follows the power function with bigger parameter b. When Cr2O3 is absent, the kinetic curve shows two parts: the slow adding of oxidation weight gains at the beginning and the ascending line in the end. Such scale loses oxidation resistance completely.展开更多
Crystal morphologies and resistivity of polysilicon trap-rich layers of two-generation trap-rich silicon-on-insulator(TR-SOI) substrates are studied. It is found that the resistivity of the trap-rich layer of genera...Crystal morphologies and resistivity of polysilicon trap-rich layers of two-generation trap-rich silicon-on-insulator(TR-SOI) substrates are studied. It is found that the resistivity of the trap-rich layer of generation 2(TR-G2)is higher than that of generation 1(TR-G1), although the crystal morphologies of the trap rich layers are the same. In addition, the rf performance of two-generation TR-SOI substrates is investigated by coplanar waveguide lines and inductors. The results show that both the rf loss and the second harmonic distortion of TR-G2 are smaller than those of TR-G1. These results can be attributed to the higher resistivity values of both the trap-rich layer and the high-resistivity silicon(HR-Si) substrate of TR-G2. Moreover, the rf performance of the TR-SOI substrate with thicker buried oxide is slightly better. The second harmonics of various TR-SOI substrates are simulated and evaluated with the harmonic quality factor model as well. It can be predicted that the TR-SOI substrate will see further improvement in rf performance if the resistivities of both the trap-rich layer and HR-Si substrate increase.展开更多
This paper summarizes the corrosion behavior of Inconel 718 alloy, which is used in the oil and gas fields, including its uniform corrosion, pitting, intergranular corrosion, galvanic corrosion, stress corrosion, and ...This paper summarizes the corrosion behavior of Inconel 718 alloy, which is used in the oil and gas fields, including its uniform corrosion, pitting, intergranular corrosion, galvanic corrosion, stress corrosion, and hydrogen embrittlement. It also analyzes the main reasons for the good corrosion resistance of Inconel 718 alloy. This paper focuses on the effects of the heat-treatment process on corrosive behavior and provides guidelines for reasonable heat treatments in security service environments. Finally, this paper recommends further studies and applications of Inconel 718 in corrosion environments with high-temperature,high-pressure, and wet H2 S.展开更多
The magnesia based curable specimens with different Si3N4 contents were casted using sintered magnesite (w(MgO)=95%) as starting material, SiO2 micro-powder as binder, 0.3%, 4% and 5% β-Si3N4 powder replacing the...The magnesia based curable specimens with different Si3N4 contents were casted using sintered magnesite (w(MgO)=95%) as starting material, SiO2 micro-powder as binder, 0.3%, 4% and 5% β-Si3N4 powder replacing the equal addition of magnesia powder respectively. The slag resistance test was carried out at 1550℃ for 3h using Baosteel tundish slag and static crucible method. The result indicates that: introducing Si3N4 could obviously improve the slag resistance of MgO based castable, which increased with increasing Si3N4. Dense SiO2 sintered layer formed on the surface of magnesia based castable because of the oxidation of Si3N4 addition, which can prevent the further slag penetration. In the deep inner of castable, the partial-pressure of oxygen was very low, so Si3N4 can exist stably. Meanwhile in reducing atmosphere, Si3N4 was hard to be sintered, which resulted in the loose interior structure of MgO based castable.展开更多
We investigated synthesis and characterization of melamine-urea-formaldehyde(MUF) microcapsules containing n-alkane mixture as phase change core material for thermal energy storage and low-temperature protection. Th...We investigated synthesis and characterization of melamine-urea-formaldehyde(MUF) microcapsules containing n-alkane mixture as phase change core material for thermal energy storage and low-temperature protection. The phase change microcapsules(microPCMs) were prepared by an in situ polymerization using sodium dodecyl sulfate(SDS) and polyvinyl alcohol(PVA) as emulsifiers. Surface morphology, particle size, chemical structure, and thermal properties of microPCMs were, respectively, characterized by using scanning electron microscopy(SEM), field emission scanning electron microscopy(FESEM), Fourier transform infrared spectroscopy(FT-IR), differential scanning calorimetry(DSC), and thermal gravimetric analysis(TGA). Low-temperature resistance performances were measured at-15,-30,-45, and-60 ℃ after microPCMs were coated on a cotton fabric by foaming technology. The results showed that spherical microPCMs had 4.4 μm diameter and 100 nm wall thickness. The melting and freezing temperatures and the latent heats of the microPCMs were determined as 28.9 and 29.6 ℃ as well as 110.0 and 115.7 J/g, respectively. Encapsulation of n-alkane mixture achieved 84.9 %. TGA analysis indicated that the microPCMs had good chemical stability below 250 ℃. The results showed that the microencapsulated n-alkane mixture had good energy storage potential. After the addition of 10 % microPCMs, low-temperature resistance duration was prolonged by 126.9%, 145.5%, 128.6%, and 87.5% in environment of-15,-30,-45 and-60 ℃, respectively as compared to pure fabric. Based on the results, phase change microcapsule plays an effective role in lowtemperature protection field for the human body.展开更多
The microstructure and phase evolution of Mg-10.16Li-8.14Al-1.46Er alloy of as-cast,250℃+12 h,300℃+12 h,and 400℃+12 h were studied by optical microscopy,scanning electron microscope,and X-ray diffraction.The mechan...The microstructure and phase evolution of Mg-10.16Li-8.14Al-1.46Er alloy of as-cast,250℃+12 h,300℃+12 h,and 400℃+12 h were studied by optical microscopy,scanning electron microscope,and X-ray diffraction.The mechanical properties of Mg-10.16Li-8.14Al-1.46Er alloy in different states were tested by microhardness tester and tension tester.The corrosion resistance of Mg-10.16Li-8.14Al-1.46Er alloy in different states was measured by electrochemical workstation combined with hydrogen evolution and mass loss tests.The results show that the microstructure of as-cast Mg-10.16Li-8.14Al-1.46Er alloy consists ofα,β,AlLi,Al3Er and MgAlLi_(2)phases.Changes of microstructure are morphology and quantity ofαphase,and second phases of MgAlLi_(2)and AlLi by heat treatments at different temperatures.The best comprehensive tensile properties of Mg-10.16Li-8.14Al-1.46Er at 400℃are attributed to theαphase structure,solution strengthening and second phase strengthening.After heat treatments at different temperatures,the corrosion resistance of Mg-10.16Li-8.14Al-1.46Er was improved compared with as-cast samples.The Mg-10.16Li-8.14Al-1.46Er alloy has the best corrosion resistance at 250℃due to the best homogenization at this temperature.展开更多
A series of monolithic MnO_(2)/iron mesh (IM) catalysts for oxidation of toluene were successfully prepared by using in situ hydrothermal growth.MnO_(2)can grow firmly on the IM substrates surface with a shedding rate...A series of monolithic MnO_(2)/iron mesh (IM) catalysts for oxidation of toluene were successfully prepared by using in situ hydrothermal growth.MnO_(2)can grow firmly on the IM substrates surface with a shedding rate of only 0.14%.Due to the highest O_(ads) and high-valent Mn^(4+) and Fe^(3+) elements,the temperature at 50% and 90% toluene conversion (T_(50%) and T_(90%)) was 252 and 265℃,respectively for the best performance catalyst (hydrothermal temperature of 80℃,hydrothermal time of 12 h,and precursor manganese ion concentration of 0.03 mol/L).The catalysts also presented good water resistance and cycle performance.In-situ DRIFTS results suggesting that toluene was first rapid transformed into the reaction intermediate species (benzoate species) and then converted to CO_(2)and H_(2)O.Therefore,this work provides a new direction for the research and application of IM-based monolithic catalysts.展开更多
Conventional MgO-C bricks(graphite content>14 wt.%)produce a great deal of greenhouse gas emission,while low-carbon MgO-C bricks have serious thermal shock resistance during high-temperature service.To enhance the ...Conventional MgO-C bricks(graphite content>14 wt.%)produce a great deal of greenhouse gas emission,while low-carbon MgO-C bricks have serious thermal shock resistance during high-temperature service.To enhance the high-temperature mechanical property and thermal shock resistance of low-carbon MgO-C bricks,a novel route of introducing ZrSiO_(4) powder into low-carbon MgO-C bricks was reported in such refractories with 2 wt.% flaky graphite.The results indicate that the low-carbon MgO-C brick with 0.5 wt.%ZrSiO_(4) addition has the maximum hot modulus of rupture at 1400℃ and the corresponding specimen fired in the carbon embedded atmosphere has the maximum residual strength ratio(98.6%)after three thermal shock cycles.It is found that some needle-like AlON and plate-like Al_(2)O_(3)-ZrO_(2) composites were in situ formed in the matrices after the low-carbon MgO-C bricks were coked at 1400℃,which can enhance the high-temperature mechanical property and thermal shock resistance due to the effect of fiber toughening and particle toughening.Moreover,CO_(2) emission of the newly developed low-carbon MgO-C bricks is reduced by 58.3% per ton steel after using them as the working lining of a 90 t vacuum oxygen decarburization ladle.展开更多
The electric arc spraying method was used to prepare the Zn-Al-Mg-RE-Si alloy coating with different content of silicon.The corrosion resisting property was measured by copper accelerated salt spray(CASS) and corrosio...The electric arc spraying method was used to prepare the Zn-Al-Mg-RE-Si alloy coating with different content of silicon.The corrosion resisting property was measured by copper accelerated salt spray(CASS) and corrosion weightless test.The influence of silicon content on the corrosion resisting property was investigated by XRD,SEM,polarization curve and electrochemical impedance spectroscopy(EIS) and the electrochemical property of coating in the corrosion process was analyzed.The results showed that the density of coating was improved significantly since the major nonequilibrium glass-like state phase was composed of silicon and other metals existed in the Zn-Al-Mg-RE-Si alloy coating,which prevented the corrosive medium and retarded the corrosion velocity because of compact corrosion products in the corrosion embryo.The Zn-Al-Mg-RE-Si coating had better corrosion resistance than the Zn-Al-Mg-RE because of more positive potential,half corrosion current density and double electrochemical reaction resistance.展开更多
基金Funded by the National Natural Science Foundation of China(No.51262003)the Guangxi Key Laboratory of Information Materials(Guilin University of Electronic Technology),China(No.1110908-10-Z)
文摘The Ag/Mg0.2Zn0.8O/ZnMn2O4/p^+-Si heterostructure devices were fabricated by sol-gel spin coating technique and the resistive switching behavior,conduction mechanism,endurance characteristic,and retention properties were investigated.A distinct bipolar resistive switching behavior of the devices was observed at room temperature.The resistance ratio R_(HRS)/RLRS of high resistance state and low resistance state is as large as four orders of magnitude with a readout voltage of 2.0 V.The dominant conduction mechanism of the device is trap-controlled space charge limited current(SCLC).The devices exhibit good durability under 1×10^3cycles and the degradation is invisible for more than 10^6 s.
文摘The relationship of corrosion resistance and antifouling behavior of 19 Cu alloys exposed to seawater of Qingdao ,Xiamen,Yulin sea areas in China for 1,2,4,8 year intervals was studied .The experiments were carried on by analyzing the composition of corrosion films formed on the surface of alloy specimens during the immersion time and by using OM,SEM,EDXA and AES experiment methods.The results verify the view point that it is the cuprous oxide film which played an important role in antifouling property of Cu alloys in seawater and throw a light on the view point in details further.The influence of different sea areas on the antifouling property of Cu alloys is also discussed.
文摘The influence of chemical composition on corrosion resistance of AZ91D magnesium alloys ingots has been investigated. Mass loss method was applied to evaluate the corrosion resistance of AZ91D alloys and the data were analyzed by multiple regression. The results show that the corrosion resistance of this alloy can be improved by increasing Al, Zn and Mn in a certain degree, and will drop with increasing Si and heavy metals (Fe, Cu, Ni). It is found that ingots received from company F should be listed into unusable materials in terms of the corrosion resistance, while among the five suppliers, the only local company E supplied excellent AZ91D magnesium alloy ingots with the best corrosion resistance.
文摘In this paper, Ni-based alloy composite coating reinforced by Ti (C, N) particles was fabricated on the mild steel through laser cladding technology. The microstrncture of laser cladding layer was analyzed by means of optical microscopy (OM), X-ray diffraction (XRD) and scanning electron microscopy (SEM). The wear resistance test of the coating was evaluated using an M-2000 tester. The results showed that the Ni-based composite coating had an ability of rapid solidification to form dendritic crystals microstructure consisting of Ti ( C, N) particulates uniformly distributed in the matrix. It was found that some Ti( C,N) particles are similar to be round in shape, and the others are irregular. Laser cladding layer reinforced by Ti( C, N) particulates was found to possess good wear resistance property.
基金Funded by the National Natural Science Foundation of China(No.U1837207)。
文摘The existing form and reaction mechanism of Sb in heat resistane Mg-Gd-Y-Sb rare earth magnesium alloy were investigated by inductive coupled plasma emission spectroscopy(ICP),scanning electron microscopy(SEM),energy dispersive spectroscopy(EDS),and X-ray diffraction(XRD).It is found that Sb tends to form high melting point intermetallics with rare earth elements of Gd and Y.The existing form of Sb is determined to be GdSb and SbY,respectively,which has high melting point(GdSb:2142℃/SbY:1782℃).Meanwhile,the first principle calculation and electronegativity difference calculation were performed to further understand the reaction mechanism.Therefore,the forming heat and binding energy were calculated.The experimental results show that the binding tendency of Sb element to Gd and Y is much stronger than that of it with other elements in this alloy,which results in the formation of high melting point of Gd-Sb and Y-Sb intermetallics,and finally leads to the high temperature resistant further improvement of the Mg-Gd-Y magnesium alloy.
基金Funded by the National Natural Science Foundation of China(No.51379070)the Fundamental Research Funds for the Central Universities(No.2017B40314)
文摘The influences of rare earth elements(cerium and lanthanum) on the microstructure and phases of Al-3.0 wt%Mg alloys used for electromagnetic shielding wire were characterized by scanning electron microscopy(SEM), energy-dispersive spectroscopy(EDS), X-ray diffraction(XRD) and differential scanning calorimetry(DSC). The mechanical properties and electrical resistivity were also investigated. The results indicated that a certain content of rare earth could improve the purification of the aluminum molten, enhance the strength, and reduce the electrical resistivity of Al-3.0 wt%Mg alloys. The strength reached the top value when RE content was 0.3 wt% while the alloy with 0.2 wt% RE addition had the smallest electrical resistivity. The elongation varied little when RE addition was no more than 0.2 wt%. But the excessive addition of rare earth would be harmful to the microstructure and properties of Al-3.0 wt%Mg alloys.
基金Funded by the National Natural Science Foundation of China(51262003)the Guangxi Key Laboratory of Information Materials(Guilin University of Electronic Technology),China(No.1110908-10-Z)
文摘A resistance random access memory(RRAM) with a structure of Ag/ZnMn2O4/p-Si was fabricated by magnetron sputtering method. Reliable and repeated switching of the resistance of ZnMn2O4 fi lms was obtained between two well-defi ned states of high and low resistance with a narrow dispersion and 3V switching voltages. Resistance ratio of the high resistance state and low resistance state was found in the range of around 10^3 orders of magnitude and up to about 10^3 test cycles. The retention time of Ag/ZnMn2O4/p-Si device is longer than 10^6 seconds and the resistance ratio between two states remains higher than 10^3 at room temperature, showing a remarkable reliability performance of the RRAM devices for nonvolatile memory application. The equivalent simulation circuits for HRS(high resistance state) and LRS(low resistance state) were also studied by impedance spectroscopy.
基金Funded by the National Key Technology Research and Development Program of the Ministry of Science and Technology of China during the“12th Five-Year Plan”(No.2011BAE25B03)
文摘A new kind of corrosion resistant steelfor cargo oiltanks(COT)was developed.The influences of finalrolling temperature,cooling rate,and finalcooling temperature on microstructure were investigated.The proper rolling process parameters were obtained through multi-pass thermalsimulation test.The finalrolling temperature is about 820 ℃,the finalcooling temperature is about 600 ℃,and the cooling rate should be controlled between 10 ℃/s and 20 ℃/s.Based on the above analysis of the results,three groups of rolling samples by thermo mechanicalcontrolprocess are prepared.The tensile strength,yield strength,and toughness of the corrosion resistant steelare measured,which meet the requirements of DH36 steel,it can instruct the actualrolling production.The corrosion behaviour is also researched by weight loss and electrochemicalimpedance spectroscopic method,and it is found that the steelhas good corrosion resistance performance,the best one is No.3 steel,the corrosion rate of which is about 1/4 of the accepted criterion.
文摘In the present paper,the development of Ti3Al-Nb-Mo-Si alloys for high oxidation resistance is reviewed.Beside of weight gain of alloys with different Nb and Si addition is tested,the evaluation of comprehensive mechanical properties has been taken,include the room-temperature and 700℃ tensile properties,thermal stability,creep rupture and fracture toughness of the alloys,It has shown that the oxidation resistance and mechanical properties were significantly affected by the variation of Nb and Si contents.The composition with the best balance of properties is Ti-24Al-13Nb-1.5Mo-0.5Si and Ti-24Al-15Nb-1.5Mo,which is mush higher than that of Super,α_2 alloy (Ti-25Al-10Nb-3V-1Mo).
基金financially supported by the National Natural Science Foundation of China (No. 51271018)the Proprietary Program of the State Key Laboratory for Advanced Metals and Materials,University of Science and Technology Beijing (Nos.2011Z-01 and 2012Z-01)
文摘Four Zr–Cu–Fe–Al-based bulk metallic glasses(BMGs) with Zr contents greater than 65at% and minor additions of Nb were designed and prepared. The glass forming abilities, thermal stabilities, mechanical properties, and corrosion resistance properties of the prepared BMGs were investigated. These BMGs exhibit moderate glass forming abilities along with superior fracture and yield strengths compared to previously reported Zr–Cu–Fe–Al BMGs. Specifically, the addition of Nb into this quaternary system remarkably increases the plastic strain to 27.5%, which is related to the high Poisson's ratio and low Young's and shear moduli. The Nb-bearing BMGs also exhibit a lower corrosion current density by about one order of magnitude and a wider passive region than 316 L steel in phosphate buffer solution(PBS, pH 7.4). The combination of the optimized composition with high deformation ability, low Young's modulus, and excellent corrosion resistance properties indicates that this kind of BMG is promising for biomedical applications.
基金supported by the Science and Technology Program of Sichuan Province,China(No.2013GZX0146)
文摘The effect of aging on the mechanical properties and microstructures of a new ZG12Cr9 MolColNiVNbNB ferritic heat resistant steel was investigated in this work to satisfy the high steam parameters of the ultra-supercritical power plant.The results show that the main precipitates during aging are Fe(Cr,Mo)23C6,V(Nb)C,and(Fe2Mo) Laves in the steel.The amounts of the precipitated phases increase during aging,and correspondingly,the morphologies of phases are similar to be round.Fe(Cr,Mo)23C6 appears along boundaries and grows with increasing temperature.In addition,it is revealed that the martensitic laths are coarsened and eventually happen to be polygonization.The hardness and strength decrease gradually,whereas the plasticity of the steel increases.What's more,the hardness of this steel after creep is similar to that of other 9%-12%Cr ferritic steels.Thus,ZG12Cr9 MolColNiVNbNB can be used in the project.
基金Funded by Komatsu Ltd. of Japan (No. 31370011370804, Shandong University)the Friendly Joint Item between Shandong University & Komatsu Ltd
文摘By oxidation weight gain method, four groups of Fe-based superalloys with different content of chromium, aluminium and silicon were tested at 1 200 ℃ for 500 hours. According to the oxidation weight gains, the oxidation kinetic curves were plotted, and the equations were regressed by least square method and non-linear curve fitting. The effects of different scale compositions on the morphology and oxidation kinetic law were studied further by analysis of X-ray diffraction (XRD) and scanning electron microscope (SEM). It is found that the compounded scale is composed of Cr2O3, Al2O3, SiO2 and FeCr2O4, with compact structure and fine grains, possessing complete oxidation resistance at 1 200 ℃, and the oxidation kinetic curve follows the power function of y=axb (a0, 0b1). When the compounded scale lacks Al2O3 or SiO2, it becomes weak in oxidation resistance, but the oxidation kinetic curve still follows the power function with bigger parameter b. When Cr2O3 is absent, the kinetic curve shows two parts: the slow adding of oxidation weight gains at the beginning and the ascending line in the end. Such scale loses oxidation resistance completely.
基金Supported by the National Natural Science Foundation of China under Grant Nos 61376021 and 61674159the Program of Shanghai Academic/Technology Research Leader under Grant No 17XD1424500
文摘Crystal morphologies and resistivity of polysilicon trap-rich layers of two-generation trap-rich silicon-on-insulator(TR-SOI) substrates are studied. It is found that the resistivity of the trap-rich layer of generation 2(TR-G2)is higher than that of generation 1(TR-G1), although the crystal morphologies of the trap rich layers are the same. In addition, the rf performance of two-generation TR-SOI substrates is investigated by coplanar waveguide lines and inductors. The results show that both the rf loss and the second harmonic distortion of TR-G2 are smaller than those of TR-G1. These results can be attributed to the higher resistivity values of both the trap-rich layer and the high-resistivity silicon(HR-Si) substrate of TR-G2. Moreover, the rf performance of the TR-SOI substrate with thicker buried oxide is slightly better. The second harmonics of various TR-SOI substrates are simulated and evaluated with the harmonic quality factor model as well. It can be predicted that the TR-SOI substrate will see further improvement in rf performance if the resistivities of both the trap-rich layer and HR-Si substrate increase.
文摘This paper summarizes the corrosion behavior of Inconel 718 alloy, which is used in the oil and gas fields, including its uniform corrosion, pitting, intergranular corrosion, galvanic corrosion, stress corrosion, and hydrogen embrittlement. It also analyzes the main reasons for the good corrosion resistance of Inconel 718 alloy. This paper focuses on the effects of the heat-treatment process on corrosive behavior and provides guidelines for reasonable heat treatments in security service environments. Finally, this paper recommends further studies and applications of Inconel 718 in corrosion environments with high-temperature,high-pressure, and wet H2 S.
文摘The magnesia based curable specimens with different Si3N4 contents were casted using sintered magnesite (w(MgO)=95%) as starting material, SiO2 micro-powder as binder, 0.3%, 4% and 5% β-Si3N4 powder replacing the equal addition of magnesia powder respectively. The slag resistance test was carried out at 1550℃ for 3h using Baosteel tundish slag and static crucible method. The result indicates that: introducing Si3N4 could obviously improve the slag resistance of MgO based castable, which increased with increasing Si3N4. Dense SiO2 sintered layer formed on the surface of magnesia based castable because of the oxidation of Si3N4 addition, which can prevent the further slag penetration. In the deep inner of castable, the partial-pressure of oxygen was very low, so Si3N4 can exist stably. Meanwhile in reducing atmosphere, Si3N4 was hard to be sintered, which resulted in the loose interior structure of MgO based castable.
基金Funded by Tianjin Research Program of Application Foundation and Advanced Technology(No.15JCZDJC38400)the National Natural Science Foundation of China(Nos.51303131 and 51303128)
文摘We investigated synthesis and characterization of melamine-urea-formaldehyde(MUF) microcapsules containing n-alkane mixture as phase change core material for thermal energy storage and low-temperature protection. The phase change microcapsules(microPCMs) were prepared by an in situ polymerization using sodium dodecyl sulfate(SDS) and polyvinyl alcohol(PVA) as emulsifiers. Surface morphology, particle size, chemical structure, and thermal properties of microPCMs were, respectively, characterized by using scanning electron microscopy(SEM), field emission scanning electron microscopy(FESEM), Fourier transform infrared spectroscopy(FT-IR), differential scanning calorimetry(DSC), and thermal gravimetric analysis(TGA). Low-temperature resistance performances were measured at-15,-30,-45, and-60 ℃ after microPCMs were coated on a cotton fabric by foaming technology. The results showed that spherical microPCMs had 4.4 μm diameter and 100 nm wall thickness. The melting and freezing temperatures and the latent heats of the microPCMs were determined as 28.9 and 29.6 ℃ as well as 110.0 and 115.7 J/g, respectively. Encapsulation of n-alkane mixture achieved 84.9 %. TGA analysis indicated that the microPCMs had good chemical stability below 250 ℃. The results showed that the microencapsulated n-alkane mixture had good energy storage potential. After the addition of 10 % microPCMs, low-temperature resistance duration was prolonged by 126.9%, 145.5%, 128.6%, and 87.5% in environment of-15,-30,-45 and-60 ℃, respectively as compared to pure fabric. Based on the results, phase change microcapsule plays an effective role in lowtemperature protection field for the human body.
基金funded by the National Natural Science Foundation of China(No.51801185)Key Research Project of the Higher Education Institutions of Henan Province,Henan Provincial Department of Education,China(No.19A460007)TrainingProgram for Young Backbone Teachers of the Higher Education Institutions of Henan Province,China.
文摘The microstructure and phase evolution of Mg-10.16Li-8.14Al-1.46Er alloy of as-cast,250℃+12 h,300℃+12 h,and 400℃+12 h were studied by optical microscopy,scanning electron microscope,and X-ray diffraction.The mechanical properties of Mg-10.16Li-8.14Al-1.46Er alloy in different states were tested by microhardness tester and tension tester.The corrosion resistance of Mg-10.16Li-8.14Al-1.46Er alloy in different states was measured by electrochemical workstation combined with hydrogen evolution and mass loss tests.The results show that the microstructure of as-cast Mg-10.16Li-8.14Al-1.46Er alloy consists ofα,β,AlLi,Al3Er and MgAlLi_(2)phases.Changes of microstructure are morphology and quantity ofαphase,and second phases of MgAlLi_(2)and AlLi by heat treatments at different temperatures.The best comprehensive tensile properties of Mg-10.16Li-8.14Al-1.46Er at 400℃are attributed to theαphase structure,solution strengthening and second phase strengthening.After heat treatments at different temperatures,the corrosion resistance of Mg-10.16Li-8.14Al-1.46Er was improved compared with as-cast samples.The Mg-10.16Li-8.14Al-1.46Er alloy has the best corrosion resistance at 250℃due to the best homogenization at this temperature.
基金supported by the Fundamental Research Funds for the Central Universities (No. 2021ZY79)Beijing Municipal Education Commission through the Innovative Transdisciplinary Program "Ecological Restoration Engineering” (No. GJJXK210102)+2 种基金National Natural Science Foundation of China (Nos. 42075169, U1810209)National Key R&D Program of China (No. 2021YFE0110800)Chinese-Serbian collaboration project (No. 451-03-1205/2021-09)。
文摘A series of monolithic MnO_(2)/iron mesh (IM) catalysts for oxidation of toluene were successfully prepared by using in situ hydrothermal growth.MnO_(2)can grow firmly on the IM substrates surface with a shedding rate of only 0.14%.Due to the highest O_(ads) and high-valent Mn^(4+) and Fe^(3+) elements,the temperature at 50% and 90% toluene conversion (T_(50%) and T_(90%)) was 252 and 265℃,respectively for the best performance catalyst (hydrothermal temperature of 80℃,hydrothermal time of 12 h,and precursor manganese ion concentration of 0.03 mol/L).The catalysts also presented good water resistance and cycle performance.In-situ DRIFTS results suggesting that toluene was first rapid transformed into the reaction intermediate species (benzoate species) and then converted to CO_(2)and H_(2)O.Therefore,this work provides a new direction for the research and application of IM-based monolithic catalysts.
基金Enterprise Research and Development Project of Beijing Lirr High-Temperature Materials Co.,Ltd.(2020-02)Key Scientific Research Project for Universities and Colleges in Henan Province(19A430028)+1 种基金the Excellent Youth Research Project of Anhui Province(2022AH030135)the PhD Research Funding of Suzhou University(2021BSK041).
文摘Conventional MgO-C bricks(graphite content>14 wt.%)produce a great deal of greenhouse gas emission,while low-carbon MgO-C bricks have serious thermal shock resistance during high-temperature service.To enhance the high-temperature mechanical property and thermal shock resistance of low-carbon MgO-C bricks,a novel route of introducing ZrSiO_(4) powder into low-carbon MgO-C bricks was reported in such refractories with 2 wt.% flaky graphite.The results indicate that the low-carbon MgO-C brick with 0.5 wt.%ZrSiO_(4) addition has the maximum hot modulus of rupture at 1400℃ and the corresponding specimen fired in the carbon embedded atmosphere has the maximum residual strength ratio(98.6%)after three thermal shock cycles.It is found that some needle-like AlON and plate-like Al_(2)O_(3)-ZrO_(2) composites were in situ formed in the matrices after the low-carbon MgO-C bricks were coked at 1400℃,which can enhance the high-temperature mechanical property and thermal shock resistance due to the effect of fiber toughening and particle toughening.Moreover,CO_(2) emission of the newly developed low-carbon MgO-C bricks is reduced by 58.3% per ton steel after using them as the working lining of a 90 t vacuum oxygen decarburization ladle.
基金Project supported by the National High Technology Research and Development Program ("863" Program) of China (2004AA001220)
文摘The electric arc spraying method was used to prepare the Zn-Al-Mg-RE-Si alloy coating with different content of silicon.The corrosion resisting property was measured by copper accelerated salt spray(CASS) and corrosion weightless test.The influence of silicon content on the corrosion resisting property was investigated by XRD,SEM,polarization curve and electrochemical impedance spectroscopy(EIS) and the electrochemical property of coating in the corrosion process was analyzed.The results showed that the density of coating was improved significantly since the major nonequilibrium glass-like state phase was composed of silicon and other metals existed in the Zn-Al-Mg-RE-Si alloy coating,which prevented the corrosive medium and retarded the corrosion velocity because of compact corrosion products in the corrosion embryo.The Zn-Al-Mg-RE-Si coating had better corrosion resistance than the Zn-Al-Mg-RE because of more positive potential,half corrosion current density and double electrochemical reaction resistance.